CN103113872A - 采油用高效降压增注剂及其生产方法 - Google Patents
采油用高效降压增注剂及其生产方法 Download PDFInfo
- Publication number
- CN103113872A CN103113872A CN2013100444474A CN201310044447A CN103113872A CN 103113872 A CN103113872 A CN 103113872A CN 2013100444474 A CN2013100444474 A CN 2013100444474A CN 201310044447 A CN201310044447 A CN 201310044447A CN 103113872 A CN103113872 A CN 103113872A
- Authority
- CN
- China
- Prior art keywords
- production method
- temperature
- trimethylamine
- dimethylamine
- decompression
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种采油用高效降压增注剂,其特征在于:其组份按质量比为环氧氯丙烷:二甲胺:三甲胺:过硫酸铵:亚硫酸氢钠:乙二胺:三乙烯四胺为1.0-2.0:1.0-2.5:1.0-4.0:0.01-0.1:0.015-0.15:0.01-0.2:0.02-0.06。同时公开了它的生产方法,其特征在于:取环氧氯丙烷加入搪瓷反应釜中;将按比例在室温下配制的二甲胺、三甲胺混合液缓慢向釜内加料;加料完成后加入过硫酸铵后再加入亚硫酸氢钠,保持釜内温度不高于5℃;加料完成后将釜内温度升至60-90度,反应7-9小时,即得中间产物;将中间产物降温至40℃,缓慢加入乙二胺和三乙烯四胺的混合液。在40℃再反应2小时得成品。
Description
技术领域
本发明涉及一种采油助剂及其生产方法,尤其涉及一种采油用高效降压增注剂及其生产方法。
背景技术
众所周知,在低渗透地层的油气田注水开发中,由于储层岩石的渗流通道狭窄或含有粘土矿物,导致地层的注水压力高、注入量小、采油成本高、采收率很低。这样的油藏在我国和国外的各油田均大量存在。这类油藏的开发中,一般都通过注入降压增注剂段塞来处理油藏,使后续注水降低注入压力和增加注入量。目前油田上使用的降压增注剂以线性阳离子聚合物和单分子季铵盐类表面活性剂及其复配物为主。这些类型的降压增注剂的吸附作用较弱,有效期较短,降压增注效果有限。
发明内容
本发明的目的在于为了克服现有技术的不足而提供一种大大降低低渗透油藏注水压力、增加注入量、在节约注水采油成本的同时提高原油的采收率的采油用高效降压增注剂及其生产方法。该采油用高效降压增注剂其组份按质量比为:环氧氯丙烷:二甲胺: 三甲胺:过硫酸铵:亚硫酸氢钠:乙二胺:三乙烯四胺为1.0-2.0: 1.0-2.5: 1.0-4.0: 0.01-0.1: 0.015-0.15: 0.01-0.2: 0.02-0.06。
采油用高效降压增注剂的生产方法如下:
a、取一定量的环氧氯丙烷加入带夹套的搪瓷反应釜中。将预先按比例在室温下配制的二甲胺和三甲胺混合液,通过加料漏斗缓慢向釜内加料。此次加料完成后依次加入引发剂过硫酸铵和还原剂亚硫酸氢钠。以上的加料须控制加料速度,用冰水循环保证及时换热,保持釜内温度不高于5℃;引发剂加料完成后通过电加热将釜内温度升至60-90℃,反应7-9小时即得中间产物;
b、中间产物的交联。将中间产物降温至40℃,缓慢加入乙二胺和三乙烯四胺的混合液。加毕在40℃反应2小时即得成品。
从本发明的技术方案可以看出,采油用高效降压增注剂(以下简称为PWAS)具有网状结构,且在网状结构上密集分布带正电的季铵阳离子基团。
PWAS可稳定粘土矿物,有利于降低低渗透地层的注水压力。PWAS在带负电荷的粘土表面产生化学吸附形成致密排列,压缩粘土矿物晶层表面的水化层,能有效抑制粘土矿物的膨胀或使已经膨胀粘土矿物收缩。抑制粘土矿物膨胀有利于保护地下流体的渗流通道。使已经膨胀粘土矿物收缩,可以扩大流体的渗流通道。这些作用可以有效地改善储层岩石的渗透性,有利于降低流体的流动压差,即降低地层的注入压力并提高注入量。
PWAS可以通过阻止地层粘土微粒的分散和运移,防治微粒对渗流通道的运移堵塞,降低注水的注入压力并提高注入量。在PWAS的作用下,可抑制地层微粒的膨胀,进而阻止微粒的释放,减少微粒运移在岩石孔隙喉道处产生的堵塞,进而起到降低注水压力、提高注入量的作用。
PWAS可以通过复配表面活性剂等成分,有效降低岩石颗粒与地层流体间的界面张力,减小流体的流动阻力,进而起到降低注水压力、提高注入量的作用。
PWAS具有网状多点吸附的特征,可在岩石表面形成单分子层紧密吸附。处理地层的有效期长、处理成本低。
PWAS耐酸、耐高温、耐高盐、分子量可调。PWAS还可以作为普通注水、低渗透地层的酸化、压裂、井下作业等的粘土稳定剂使用,具有较广阔的应用前景。完全达到了本发明的发明目的。
具体实施方式
实施例1,采油用高效降压增注剂其组份按质量比为:环氧氯丙烷:二甲胺:三甲胺:过硫酸铵:亚硫酸氢钠:乙二胺:三乙烯四胺为1.5:2.0:1.8:0.08:0.02:0.01:0.03。其生产方法如下:
a、取一定量的环氧氯丙烷加入带夹套的搪瓷反应釜中。将预先按比例在室温下配制的二甲胺、三甲胺混合液,通过加料漏斗缓慢向釜内加料。加料完成后,加入引发剂过硫酸铵后再加入还原剂亚硫酸氢钠。以上的加料须控制加料速率,用冰水循环保证及时换热,保持釜内温度不高于5℃;引发剂加料完成后通过电加热将釜内温度升至60℃,反应9小时得中间产物;
b、中间产物的交联。将中间产物降温至40℃,缓慢加入乙二胺和三乙烯四胺的混合液。加毕在40℃反应2小时得成品。
实施例2,采油用高效降压增注剂其组份按质量比为:
环氧氯丙烷:二甲胺:三甲胺:过硫酸铵:亚硫酸氢钠:乙二胺:三乙烯四胺为1.3:2.0:2.5:0.01:0.018:0.03:0.05。其生产方法如下:
a、取一定量的环氧氯丙烷加入带夹套的搪瓷反应釜中。将预先按比例在室温下配制的二甲胺、三甲胺混合液,通过加料漏斗缓慢向釜内加料。加料完成后,加入引发剂过硫酸铵后再加入还原剂亚硫酸氢钠。以上的加料须控制加料速率,用冰水循环保证及时换热,保持釜内温度不高于5℃;引发剂加料完成后通过电加热将釜内温度升至90℃,反应7小时得中间产物;
b、中间产物的交联。将中间产物降温至40℃,缓慢加入乙二胺和三乙烯四胺的混合液。加毕在40℃反应2小时得成品。
实施例3,采油用高效降压增注剂其组份按质量比为:环氧氯丙烷:二甲胺:三甲胺:过硫酸铵:亚硫酸氢钠:乙二胺:三乙烯四胺为1.3:2.5:1.5:0.01:0.015:0.08:0.02。其生产方法如下:
a、取一定量的环氧氯丙烷加入带夹套的搪瓷反应釜中。将预先按比例在室温下配制的二甲胺、三甲胺混合液,通过加料漏斗缓慢向釜内加料。加料完成后,加入引发剂过硫酸铵后再加入还原剂亚硫酸氢钠。以上的加料须控制加料速率,用冰水循环保证及时换热,保持釜内温度不高于5℃;引发剂加料完成后通过电加热将釜内温度升至80℃,反应8小时得中间产物;
b、中间产物的交联。将中间产物降温至40℃,缓慢加入乙二胺和三乙烯四胺的混合液。加毕在40℃反应2小时得成品。
Claims (4)
1.一种采油用高效降压增注剂,其特征在于:其组份按质量比为环氧氯丙烷:二甲胺:三甲胺:过硫酸铵:亚硫酸氢钠:乙二胺:三乙烯四胺为1.0-2.0: 1.0-2.5: 1.0-4.0: 0.01-0.1: 0.015-0.15: 0.01-0.2: 0.02-0.06。
2.一种采油用高效降压增注剂的生产方法,其特征在于: 按下列歩骤进行
(a)取一定量的环氧氯丙烷加入带夹套的搪瓷反应釜中,将预先按比例在室温下配制的二甲胺、三甲胺混合液,通过加料漏斗缓慢向釜内加料,加料完成后,加入引发剂过硫酸铵后再加入还原剂亚硫酸氢钠,以上的加料须控制加料速率,用冰水循环保证及时换热,保持釜内温度不高于5℃;引发剂加料完成后通过电加热将釜内温度升至数十度,反应数小时得中间产物;
(b)中间产物的交联,将中间产物降温至40℃,缓慢加入乙二胺和三乙烯四胺的混合液,加毕在40℃反应2小时得成品。
3.根据权利要求2所述的一种采油用高效降压增注剂的生产方法,其特征在于:所说的反应温度为60-90℃,反应时间为7-9小时。
4.根据权利要求2所述的一种采油用高效降压增注剂的生产方法,其特征在于:二甲胺、三甲胺同时加料,以乙二胺和三乙烯四胺作为交联剂进行交联。