CN103102748A - 一种用于室外钢结构的防火涂料 - Google Patents
一种用于室外钢结构的防火涂料 Download PDFInfo
- Publication number
- CN103102748A CN103102748A CN2012104517183A CN201210451718A CN103102748A CN 103102748 A CN103102748 A CN 103102748A CN 2012104517183 A CN2012104517183 A CN 2012104517183A CN 201210451718 A CN201210451718 A CN 201210451718A CN 103102748 A CN103102748 A CN 103102748A
- Authority
- CN
- China
- Prior art keywords
- steel structure
- fire
- dimethylbenzene
- acrylic resin
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种用于室外钢结构的防火涂料,所述涂料各组分的重量百分比:改性高氯化聚乙烯(HHCPE0)15%~25%、丙烯酸树脂5%~10%、乙酸丁酯15%~20%、二甲苯15%~20%、聚磷酸铵(APP)20%~25%、季戊四醇(PE)10%~15%、三聚氰胺(MEL)10%~15%、添加剂1%~5%;上述配方的制备方法为:先将改性高氯化聚乙烯和丙烯酸树脂充分溶解于二甲苯和乙酸丁酯混合溶剂中,然后加入其余组分,高速搅拌30min,经砂磨机研磨2~3次,至细度<80微米即得。本品涂覆于钢结构建筑物表面,具有一定的装饰作用,与火灾时能迅速形成耐火隔热保护层,提高钢结构的耐火极限。
Description
技术领域
本发明涉及涂料技术领域,尤其是指一种用于室外钢结构的防火涂料。
背景技术
经济和社会的迅速发展推动了建筑材料的不断升级和换代,钢材作为主要承重构件在建筑中得到了大量应用,钢材虽在常温下具有优良的物理和力学性能,但其耐火性能远比砖石结构和钢筋混凝土结构要差,当钢材达到临界温度后,便失去承载能力,而通常在建筑火灾中,10min之内火场的温度即可达到钢材的临界温度,在这样的火场下,钢材的承载能力急剧下降,导致建筑物坍塌,因此,钢结构的表层防火十分重要。
目前用于钢结构的防火方式有疏导法和截流法,疏导法的应用仅有充水冷却保护法,耐截流法的应用较多,主要有耐火材料包封法、屏蔽法、水喷淋法、防火涂料法等等,综合各方面因素,在钢构上直接喷涂防火材料是最理想、最可靠、最经济实用的方法。而与发达国家同类技术相比,我国的防火涂料性能还存在一定的差距,而且所研发的防火涂料均以室内防火为主,室外防火涂料研究成果不多,不能满足日益增长的需求。
发明内容
本发明的目的在于提供一种附着力强,耐候性强,成本低的用于室外钢结构的防火涂料。
为实现上述目的,本发明所提供的技术方案为:一种用于室外钢结构的防火涂料,所述涂料各组分的重量百分比:
改性高氯化聚乙烯(HHCPE0) 15%~25%
丙烯酸树脂 5%~10%
乙酸丁酯 15%~20%
二甲苯 15%~20%
聚磷酸铵(APP) 20%~25%
季戊四醇(PE) 10%~15%
三聚氰胺(MEL) 10%~15%
添加剂 1%~5%;
上述配方的制备方法为:先将改性高氯化聚乙烯和丙烯酸树脂充分溶解于二甲苯和乙酸丁酯混合溶剂中,然后加入其余组分,高速搅拌30min,经砂磨机研磨2~3次,至细度<80微米即得。
本品作为室外钢结构建筑物防火涂层,可改善超薄膨胀型钢结构防火涂料的耐湿热性,克服涂料的“盐析”问题,是一种质量稳定,性能优异的室外钢结构超薄膨胀型 防火涂料。本品涂覆于钢结构建筑物表面,具有一定的装饰作用,与火灾时能迅速形成耐火隔热保护层,提高钢结构的耐火极限。
具体实施方式
下面对本发明作进一步说明,本发明的较佳实施例为:本实施例所述的用于室外钢结构的防火涂料各组分的重量百分比:
改性高氯化聚乙烯(HHCPE0) 15%
丙烯酸树脂 8%
乙酸丁酯 18%
二甲苯 15%
聚磷酸铵(APP) 22%
季戊四醇(PE) 11%
三聚氰胺(MEL) 10%%
添加剂 1%;
上述配方的制备方法为:先将改性高氯化聚乙烯和丙烯酸树脂充分溶解于二甲苯和乙酸丁酯混合溶剂中,然后加入其余组分,高速搅拌30min,经砂磨机研磨2~3次,至细度<80微米即得。
本方案涂料的使用方法:
1.使用前被防火涂物表面要将油污尘土等清除干净。
2.防火涂料固体含量较高,使用前一定要将涂料搅拌均可。
3.刷、滚、喷涂均可,每隔六小时即可涂刷第二道。
4.涂刷厚度可根据防火规范要求而定,通常为2-6道。
5.没用完的防火涂料,要重新封严。
本品作为室外钢结构建筑物防火涂层,可改善超薄膨胀型钢结构防火涂料的耐湿热性,克服涂料的“盐析”问题,是一种质量稳定,性能优异的室外钢结构超薄膨胀型 防火涂料。本品涂覆于钢结构建筑物表面,具有一定的装饰作用,与火灾时能迅速形成耐火隔热保护层,提高钢结构的耐火极限。
以上所述之实施例只为本发明之较佳实施例,并非以此限制本发明的实施范围,故凡依本发明之形状、原理所作的变化,均应涵盖在本发明的保护范围内。
Claims (1)
1.一种用于室外钢结构的防火涂料,其特征在于:所述涂料各组分的重量百分比:
改性高氯化聚乙烯(HHCPE0) 15%~25%
丙烯酸树脂 5%~10%
乙酸丁酯 15%~20%
二甲苯 15%~20%
聚磷酸铵(APP) 20%~25%
季戊四醇(PE) 10%~15%
三聚氰胺(MEL) 10%~15%
添加剂 1%~5%;
上述配方的制备方法为:先将改性高氯化聚乙烯和丙烯酸树脂充分溶解于二甲苯和乙酸丁酯混合溶剂中,然后加入其余组分,高速搅拌30min,经砂磨机研磨2~3次,至细度<80微米即得。