CN103091162A - 一种测量热轧板卷规定总延伸强度Rt值的方法 - Google Patents

一种测量热轧板卷规定总延伸强度Rt值的方法 Download PDF

Info

Publication number
CN103091162A
CN103091162A CN2013100093904A CN201310009390A CN103091162A CN 103091162 A CN103091162 A CN 103091162A CN 2013100093904 A CN2013100093904 A CN 2013100093904A CN 201310009390 A CN201310009390 A CN 201310009390A CN 103091162 A CN103091162 A CN 103091162A
Authority
CN
China
Prior art keywords
tensile sample
rolled sheet
mould
sheet coil
proof strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100093904A
Other languages
English (en)
Other versions
CN103091162B (zh
Inventor
周志超
张卫东
徐鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Shougang Co Ltd
Original Assignee
Shougang Corp
Hebei Shougang Qianan Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shougang Corp, Hebei Shougang Qianan Iron and Steel Co Ltd filed Critical Shougang Corp
Priority to CN201310009390.4A priority Critical patent/CN103091162B/zh
Publication of CN103091162A publication Critical patent/CN103091162A/zh
Application granted granted Critical
Publication of CN103091162B publication Critical patent/CN103091162B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种测量热轧板卷拉伸试样规定总延伸强度Rt值的方法，属于金属材料力学性能试验技术领域，该方法包括对拉伸试样进行压平。该方法在避免加工硬化的前提下消除拉伸试样弯曲度，从而消除Rt值测量误差。

Description

一种测量热轧板卷规定总延伸强度Rt值的方法
技术领域
本发明涉及金属材料力学性能试验技术领域，特别涉及一种测量热轧板卷规定总延伸强度Rt值的方法。
背景技术
在当今热轧板卷的生产过程中，产品检验在提高钢材产品质量、扩大品种、降低成本、优化轧钢生产工艺等方面发挥着非常重要的作用，甚至已成为整个生产过程中的限制性环节。拉伸试验是金属材料力学试验中最基本的试验，拉伸力学性能是金属材料的基本力学性能之一，其性能指标是评定金属材料质量的重要依据。影响金属材料拉伸力学性能测量的因素是多种多样的，针对不同的影响因素需采用相应的方法来使其对数据的影响降至最小。
现有技术中，对热轧板卷规定总延伸强度Rt值进行测量时，对矩形拉伸试样不进行压平处理，由于热轧板卷矩形拉伸试样样坯本身存在瓢曲，试样机加工完毕后直接进行拉伸试验，测得的规定总延伸强度Rt值波动较大，数据不稳定，初检合格率很低，对检验造成严重影响。经过系统分析，确认是由于试样自身弯曲度造成了检测数据波动较大且不稳定。
发明内容
为了解决上述问题，本发明提出了一种能够在避免加工硬化的前提下消除拉伸试样弯曲度，从而消除Rt值测量误差的测量热轧板卷规定总延伸强度Rt值的方法。
本发明提供的测量热轧板卷拉伸试样规定总延伸强度Rt值的方法包括对拉伸试样进行压平。
作为优选，所述对拉伸试样进行压平的方法包括以下步骤：
将拉伸试样摆放于模具上，
在所述拉伸试样与模具之间放置垫片并确定保压时间，
对所述拉伸试样进行压平。
所述优选，所述模具包括上下两件模具，所述拉伸试样摆放于所述上下两件模具之间。
作为优选，所述拉伸试样在摆放时与所述下模具的纵向中心成30°角。
作为优选，所述模具的压平回弹量为5mm。
作为优选，在所述拉伸试样与模具之间放置的垫片和保压时间是根据拉伸试样的弯曲度选取的，
当所述弯曲度为0.3～0.5mm时，选取厚度为1mm的垫片，保压时间10秒；
当弯曲度＞0.5mm时，选取厚度为2mm的垫片，保压时间20～25秒。
作为优选，所述弯曲度的测量方法包括以下步骤：
将拉伸试样平放于水平面上，使所述拉伸试样的弯曲角度朝上放置；
在所述拉伸试样上放置一水平尺，所述水平尺分别与所述拉伸试样的两端最高点接触，所述拉伸试样最低点到所述水平尺的下表面的距离即为所述拉伸试样的弯曲度。
本发明提供的测量热轧板卷规定总延伸强度Rt值的方法能够在避免加工硬化的前提下消除拉伸试样弯曲度，从而消除Rt值测量误差。
附图说明
图1为本发明实施例提供的测量热轧板卷规定总延伸强度Rt值的方法在对拉伸试样进行压平时的模具示意图；
图2为本发明实施例提供的测量热轧板卷规定总延伸强度Rt值的方法在对拉伸试样弯曲度进行测量时的示意图。
具体实施方式
为了深入了解本发明，下面结合具体实施例对本发明进行详细说明。
按照GB/T228-2002《金属材料室温拉伸试验方法》，在对热轧板卷拉伸试样规定总延伸强度Rt值进行测量时，通常需要测量试样厚度、宽度并计算试样的横截面积，在试样平行长度的屈服期间控制应变率在0.0025/s以下，自动测得规定总延伸率为0.5%时的应力。
本发明提供的测量热轧板卷拉伸试样规定总延伸强度Rt值的方法包括对拉伸试样进行压平。
其中，对拉伸试样进行压平的方法包括以下步骤：
步骤1：将拉伸试样摆放于模具上。
其中，参见附图1，模具包括上下两件模具，分别为上模具1和下模具2，拉伸试样摆放于上模具1和下模具2之间。
其中，拉伸试样在摆放时与下模具2的纵向中心成30°角。
其中，模具的压平回弹量为5mm。
步骤2：在拉伸试样与模具之间放置的垫片并确定保压时间。
其中，在拉伸试样与模具之间放置的垫片和保压时间是根据拉伸试样的弯曲度选取的。当弯曲度为0.3～0.5mm时，选取厚度为1mm的垫片，保压时间10秒；当弯曲度＞0.5mm时，选取厚度为2mm的垫片，保压时间20～25秒。
其中，弯曲度的测量方法包括以下步骤：
步骤21：参见附图2，将拉伸试样4平放于水平面上，使拉伸试样4的弯曲角度朝上放置；
步骤22：在拉伸试样4上放置一水平尺3，水平尺3分别与拉伸试样4的两端最高点接触，拉伸试样最低点5到水平尺3的下表面的距离即为拉伸试样的弯曲度h。
步骤3：对拉伸试样进行压平。
本发明提供的测量热轧板卷规定总延伸强度Rt值的方法能够在避免加工硬化的前提下消除拉伸试样弯曲度，从而消除Rt值测量误差。
以上所述的具体实施方式，对本发明的目的、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施方式而已，并不用于限制本发明，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (7)

1.一种测量热轧板卷拉伸试样规定总延伸强度Rt值的方法，其特征在于，包括对拉伸试样进行压平。
2.根据权利要求1所述的测量热轧板卷拉伸试样规定总延伸强度Rt值的方法，其特征在于，所述对拉伸试样进行压平的方法包括以下步骤：
将拉伸试样摆放于模具上，
在所述拉伸试样与模具之间放置垫片并确定保压时间，
对所述拉伸试样进行压平。
3.根据权利要求2所述的测量热轧板卷拉伸试样规定总延伸强度Rt值的方法，其特征在于，所述模具包括上下两件模具，所述拉伸试样摆放于所述上下两件模具之间。
4.根据权利要求3所述的测量热轧板卷拉伸试样规定总延伸强度Rt值的方法，其特征在于，所述拉伸试样在摆放时与所述下模具的纵向中心成30°角。
5.根据权利要求3所述的测量热轧板卷拉伸试样规定总延伸强度Rt值的方法，其特征在于，所述模具的压平回弹量为5mm。
6.根据权利要求3所述的测量热轧板卷拉伸试样规定总延伸强度Rt值的方法，其特征在于，在所述拉伸试样与模具之间放置的垫片和保压时间是根据拉伸试样的弯曲度选取的，
当所述弯曲度为0.3～0.5mm时，选取厚度为1mm的垫片，保压时间10秒；
当弯曲度＞0.5mm时，选取厚度为2mm的垫片，保压时间20～25秒。
7.根据权利要求6所述的测量热轧板卷拉伸试样规定总延伸强度Rt值的方法，其特征在于，所述弯曲度的测量方法包括以下步骤：
将拉伸试样平放于水平面上，使所述拉伸试样的弯曲角度朝上放置；
在所述拉伸试样上放置一水平尺，所述水平尺分别与所述拉伸试样的两端最高点接触，所述拉伸试样最低点到所述水平尺的下表面的距离即为所述拉伸试样的弯曲度。
CN201310009390.4A 2013-01-10 2013-01-10 一种测量热轧板卷规定总延伸强度Rt值的方法 Active CN103091162B (zh)