CN103086628A - 沥青混合料抗剥落剂 - Google Patents

沥青混合料抗剥落剂 Download PDF

Info

Publication number
CN103086628A
CN103086628A CN201310015063XA CN201310015063A CN103086628A CN 103086628 A CN103086628 A CN 103086628A CN 201310015063X A CN201310015063X A CN 201310015063XA CN 201310015063 A CN201310015063 A CN 201310015063A CN 103086628 A CN103086628 A CN 103086628A
Authority
CN
China
Prior art keywords
coal gangue
parts
antistripping agent
building waste
micro mist
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310015063XA
Other languages
English (en)
Other versions
CN103086628B (zh
Inventor
孙家瑛
顾昕
谢京来
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo Institute of Technology of ZJU
Original Assignee
Ningbo Institute of Technology of ZJU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo Institute of Technology of ZJU filed Critical Ningbo Institute of Technology of ZJU
Priority to CN201310015063.XA priority Critical patent/CN103086628B/zh
Publication of CN103086628A publication Critical patent/CN103086628A/zh
Application granted granted Critical
Publication of CN103086628B publication Critical patent/CN103086628B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种沥青混合料抗剥落剂，它由如下重量份数的组分构成：建筑垃圾微粉30～50份、碱渣微粉10～25份、煤矸石焚烧灰10～15份、外加剂1～3份。所述的建筑垃圾微粉由除去有机物的建筑垃圾（基本由20%的废弃混凝土和80%的废弃砖瓦组成）粉磨而成；所述的煤矸石焚烧灰为在750～900℃，保温2.5～3小时活化处理后的煤矸石焚烧灰；所述的外加剂是硫铝酸盐、硅酸盐水泥熟料、三乙醇胺中的一种或其中几种的混合物。本发明与现有技术的同类产品相比，它提供一种能够防止氯盐与水双重对沥青造成损害，且不会受热分解，也不会对环境造成危害，价格便宜的沥青混合料抗剥落剂。

Description

沥青混合料抗剥落剂
 技术领域
本发明涉及一种沥青混合料抗剥落剂。
背景技术
由于我国沿海地区地处东南季风区，所以每年5~6月都将受到梅雨气候的影响；而海洋性气候使该地区空气湿度和氯盐保持较高的水平；且由于地处太平洋西岸，每年6~9月台风也将对该地区产生较大的影响，由于沿海道路及城区道路及港口交通直接受到海风侵袭，这将会使海水或海水水雾被带到沥青混合料路面上。在水与氯盐双重作用下会加快造成沥青混凝土路面损害程度，因此沿海地区沥青路面对防止水与氯盐双重损害有更高的要求。目前解决这一问题的主要办法是在沥青中加入沥青抗剥落剂。沥青抗剥落剂是与集料表面形成物理吸附或依靠其特殊的化学结构使其与集料进行化合反应，在它们之间形成强而有力的化学纽带，从而提高了沥青与集料的粘附性。目前常用的抗剥落剂为胺类和磷酸酯类产品，但其主要解决的是淡水对沥青路面的损害，且其热稳定性不好，受热易分解出有害气体，不利于环保。
发明内容
本发明针对现有技术的上述不足，提供一种不会受热分解，也不会对环境造成危害，且价格便宜，能够防止氯盐和水双重对沥青造成损害的抗剥落剂。
本发明的技术方案是提供一种沥青混合料抗剥落剂，其原料组分配比按重量份数计包括：建筑垃圾微粉30～50份、碱渣微粉10～25份、煤矸石焚烧灰10～15份、外加剂1～3份。 
所述抗剥落剂中的建筑垃圾微粉为除去有机物的建筑垃圾粉磨而成，建筑垃圾基本是以20%左右的废弃混凝土和80%左右的废弃砖瓦组成。
所述的抗剥落剂中的煤矸石焚烧灰为活化处理后的煤矸石焚烧灰。
所述的抗剥落剂材料的外加剂是下述中的一种或其中几种的混合物：硫铝酸盐、硅酸盐水泥熟料、三乙醇胺。
所述的抗剥落剂中的建筑垃圾微粉、碱渣微粉的细度均为150目～200目，即建筑垃圾微粉、碱渣微粉的直径均为0.1mm～0.075mm。
所述的抗剥落剂中的建筑垃圾微粉、碱渣微粉、煤矸石焚烧灰、外加剂进行混磨，细度为150目即可，即建筑垃圾微粉、碱渣微粉、煤矸石焚烧灰、外加剂进行混磨后的混合物的直径为0.1mm。
本发明的抗剥落剂成分中添加了外加剂，它能起到加快促进建筑垃圾微粉、碱渣微粉、煤矸石焚烧灰与沥青的融合作用，从而可以提高沥青与集料粘附能力，使沥青混合料具备了抗氯盐和水双重侵害的能力。此外将在生产再生混凝土骨料过程中产生的建筑垃圾微粉、碱渣及煤矸石焚烧灰加以充分利用，减少了对环境的污染，降低了成本。
具体实施实例
下面结合具体实施实例说明，但本发明不限于以下具体实施实例
实施例1
（1）将建筑垃圾除去有机物后进行粉磨，要求细度为150目；
（2）将碱渣粉磨至细度为150目；
（3）将煤矸石焚烧灰加热至温度为750℃时停止加热，然后对煤矸石焚烧灰保温3小时；
（4）将硫铝酸盐作为外加剂；
（5）将步骤（1）之建筑垃圾微粉300kg、步骤（2）之碱渣微粉250kg、步骤（3）之煤矸石焚烧灰150kg、步骤（4）之外加剂10kg混磨制成沥青混合料抗剥落剂，要求细度为150目。
在沥青混合料中掺2%（重量百分比）本发明抗剥落剂，替代沥青混合料中填料。使沥青混合料石料表面粘附性等级从3提高到5。
实施例2
（1）将500kg除去有机物的建筑垃圾粉磨作为建筑垃圾微粉，要求细度为150目；
（2）将碱渣微粉粉磨至细度为150目；
（3）将煤矸石焚烧灰加热至温度为900℃时停止加热，然后对煤矸石焚烧灰保温2.5小时；
（4）将硅酸盐水泥熟料、三乙醇胺的混合物作为外加剂；
（5）将步骤（1）之建筑垃圾微粉500kg、步骤（2）之碱渣微粉100kg、步骤（3）之煤矸石焚烧灰150kg、步骤（4）之外加剂10kg混磨制成沥青混合料抗剥落剂，要求细度为150目。
在沥青混合料中掺2%（重量百分比）本发明抗剥落剂，替代沥青混合料中填料。使沥青混合料石料表面粘附性等级从3提高到5。
实施例3
（1）将400kg除去有机物的建筑垃圾粉磨作为建筑垃圾微粉，要求细度为150目；
（2）将碱渣微粉粉磨至细度为150目；
（3）  将煤矸石焚烧灰加热至温度为800℃时停止加热，然后对煤矸石焚烧灰保温2.5小时；
（4）将硫铝酸盐、硅酸盐水泥熟料、三乙醇胺的混合物作为外加剂；
（5）将步骤（1）之建筑垃圾微粉400kg、步骤（2）之碱渣微粉200kg、步骤（3）之煤矸石焚烧灰130kg、步骤（4）之外加剂20kg混磨制成沥青混合料抗剥落剂，要求细度为150目。
在沥青混合料中掺2%（重量百分比）本发明抗剥落剂，替代沥青混合料中填料。使沥青混合料石料表面粘附性等级从3提高到5。

Claims (8)

1.一种沥青混合料抗剥落剂，其特征在于：它由如下重量份数的组分构成：建筑垃圾微粉30～50份、碱渣微粉10～25份、煤矸石焚烧灰10～15份、外加剂1～3份。
2.根据权利要求1所述的沥青混合料抗剥落剂，其特征在于： 所述的建筑垃圾微粉为除去有机物的建筑垃圾粉磨而成。
3.根据权利要求2所述的沥青混合料抗剥落剂，其特征在于：所述的建筑垃圾基本由20%的废弃混凝土和80%的废弃砖瓦组成。
4.根据权利要求1所述的沥青混合料抗剥落剂，其特征在于：所述的煤矸石焚烧灰为经过加热、保温、冷却活化处理后的煤矸石焚烧灰。
5.根据权利要求4所述的沥青混合料抗剥落剂，其特征在于：加热至温度为750～900℃时停止加热，保温时间为2.5～3小时，然后使其冷却降温至室温。
6.根据权利要求1所述的沥青混合料抗剥落剂，其特征在于：所述的外加剂是下述中的一种或其中几种的混合物：硫铝酸盐、硅酸盐水泥熟料、三乙醇胺。
7.根据权利要求1所述的沥青混合料抗剥落剂，其特征在于：所述的建筑垃圾微粉、碱渣微粉的细度均为150目～200目。
8.根据权利要求1所述的沥青混合料抗剥落剂，其特征在于：建筑垃圾微粉、碱渣微粉、煤矸石焚烧灰、外加剂进行混磨至细度为150目即可。
CN201310015063.XA 2013-01-16 2013-01-16 沥青混合料抗剥落剂 Expired - Fee Related CN103086628B (zh)