CN103086609A - Glass frosting treatment agent - Google Patents
Glass frosting treatment agent Download PDFInfo
- Publication number
- CN103086609A CN103086609A CN2011103442096A CN201110344209A CN103086609A CN 103086609 A CN103086609 A CN 103086609A CN 2011103442096 A CN2011103442096 A CN 2011103442096A CN 201110344209 A CN201110344209 A CN 201110344209A CN 103086609 A CN103086609 A CN 103086609A
- Authority
- CN
- China
- Prior art keywords
- treatment agent
- glass
- frosting treatment
- glass frosting
- guar gum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a glass frosting treatment agent. The glass frosting treatment agent comprises ammonium bifluoride, aluminum fluosilicate, sodium dodecyl sulfate, guar gum and organic additives according to a mass ratio of (275-365): (130-165): (0.3-1.0): (1.0-3.0): (1-50). The glass frosting treatment agent does not need acid immersion after glass frosting. The glass treated by the glass frosting treatment agent does not produce traces after contacting with the hand, and is beautiful.
Description
Technical field
The present invention relates to glass manufacturing area, relate in particular to a kind of glass frosting treatment agent.
Background technology
Glass frosting can make glass have the outward appearance of dim beauty, is widely used in daily life and industrial production.The glass frosting processing industry is made mat glass, is the frosting powder to be added water mix with sour, then is sprayed on glassly, will soak in acid solution after glass cleaning again.But when soaking in acid solution, because acid has stronger volatility and corrodibility, also very strict to the requirement of operator's working specification, the operator accidentally will be by sulfuric acid or hcl corrosion clothes or skin; And the mat glass that frosting powder of the prior art is made during staff contact mat glass, is easily left a trace, and is not attractive in appearance.
Summary of the invention
The purpose of this invention is to provide a kind of glass frosting treatment agent, after giving glass frosting, do not need acid soak, and during staff contact mat glass, can not leave a trace, attractive in appearance.
In order to solve the problems of the technologies described above, glass frosting treatment agent provided by the invention is achieved in that
A kind of glass frosting treatment agent comprises: ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive;
The mass ratio of described ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 275~365: 130~165: 0.3~1.0: 1.0~3.0: 1~50.
Optionally, the mass ratio of described ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 295~325: 145~155: 0.5~0.8: 1.5~2.5: 20~30.
Optionally, the mass ratio of described ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 315: 150: 0.6: 2: 25.
Optionally, the mass ratio of described ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 310: 148: 0.7: 2.1: 28.
Ammonium bifluoride, white or the crystallization of water white transparency rhombic system, slightly tart flavour; Be slightly soluble in alcohol, very easily be dissolved in cold water, decompose in hot water, the aqueous solution is strongly-acid.
Aluminum fluosilicate, white powder.Relative density 3.58.Be soluble in hot water, be slowly dissolved in cold water.Produced by silicofluoric acid and the effect of fresh hydrogen aluminum oxide.
Sodium laurylsulfonate, white or light yellow crystallization or powder are soluble in hot water, are dissolved in hot ethanol, are insoluble to sherwood oil.Belong to anion surfactant, have excellent infiltration, washing, wetting, decontamination and emulsifying effect.
Guar gum has outstanding dispersive ability in cold water and hot water, can not produce clustering phenomena, has improved the convenience of manufacturing and production operation; Can expand rapidly and dissolve in wide PH scope, even in the very high system of salt content, still keep stable; With negatively charged ion, zwitter-ion and tensio-active agent, good consistency is arranged, can be used in the product of various surfactants, increase the deposition of particle; Carry and act synergistically with polymer silicone oil and anti-dandruff dose when using in formula, and plentiful degree and the stability of raising foam.
After glass frosting treatment agent provided by the invention added water acid adding wiring solution-forming, glass soaked therein to take out in 1~2 minute to clean to dry and gets final product, and does not soak in acid easily after not needing to clean, and reduces acid solution to the corrosion of processing units, and operator are also safer.And; the mat glass surface particles of using glass frosting treatment agent provided by the invention to make is larger; the staff touch-surface; can not stay impression of the hand; for glass color faces such as tea table glass color face and smoke exhaust ventilators; often meeting by the place that staff touches, can not stay impression of the hand, keeps clean attractive in appearance always.
Embodiment
In order to make purpose of the present invention, technical scheme and advantage clearer, below in conjunction with embodiment, the present invention is further elaborated.Should be appreciated that specific embodiment described herein only in order to explain the present invention, is not intended to limit the present invention.
A kind of glass frosting treatment agent comprises: ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive;
The mass ratio of ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 275~365: 130~165: 0.3~1.0: 1.0~3.0: 1~50.
A kind of glass frosting treatment agent comprises: the mass ratio of ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 295~325: 145~155: 0.5~0.8: 1.5~2.5: 20~30.
A kind of glass frosting treatment agent comprises: the mass ratio of ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 315: 150: 0.6: 2: 25.
A kind of glass frosting treatment agent comprises: the mass ratio of ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 310: 148: 0.7: 2.1: 28.
In order to further illustrate glass frosting treatment agent provided by the invention, below provide detailed embodiment.
Embodiment one
Take the 365g ammonium bifluoride, the 145g aluminum fluosilicate, the 1.0g sodium laurylsulfonate, the organic additive of 1g guar gum, 50g and appropriate hydrogenchloride sodium mix, and get glass frosting treatment agent of the present invention.The glass frosting treatment agent adds and is sprayed on after the water acid adding on glassly, does not need to soak in acid solution again, namely makes surface particles large, without the mat glass of impression of the hand.
Embodiment two
Take the 275g ammonium bifluoride, the 165g aluminum fluosilicate, the 0.3g sodium laurylsulfonate, the organic additive of 2.5g guar gum, 20g and appropriate hydrogenchloride sodium mix, and get glass frosting treatment agent of the present invention.The glass frosting treatment agent adds and is sprayed on after the water acid adding on glassly, does not need to soak in acid solution again, namely makes surface particles large, without the mat glass of impression of the hand.
Embodiment three
Take the 325g ammonium bifluoride, the 145g aluminum fluosilicate, the 0.8g sodium laurylsulfonate, the organic additive of 3g guar gum, 30g and appropriate hydrogenchloride sodium mix, and get glass frosting treatment agent of the present invention.The glass frosting treatment agent adds and is sprayed on after the water acid adding on glassly, does not need to soak in acid solution again, namely makes surface particles large, without the mat glass of impression of the hand.
Embodiment four
Take the 295g ammonium bifluoride, the 155g aluminum fluosilicate, the 0.5g sodium laurylsulfonate, the organic additive of 1.5g guar gum, 1g and appropriate hydrogenchloride sodium mix, and get glass frosting treatment agent of the present invention.The glass frosting treatment agent adds and is sprayed on after the water acid adding on glassly, does not need to soak in acid solution again, namely makes surface particles large, without the mat glass of impression of the hand.
Embodiment five
Take the 315g ammonium bifluoride, the 150g aluminum fluosilicate, the 0.6g sodium laurylsulfonate, the organic additive of 2g guar gum, 25g and appropriate hydrogenchloride sodium mix, and get glass frosting treatment agent of the present invention.The glass frosting treatment agent adds and is sprayed on after the water acid adding on glassly, does not need to soak in acid solution again, namely makes surface particles large, without the mat glass of impression of the hand.
Embodiment six
Take the 310g ammonium bifluoride, the 148g aluminum fluosilicate, the 0.7g sodium laurylsulfonate, the organic additive of 2.1g guar gum, 28g and appropriate hydrogenchloride sodium mix, and get glass frosting treatment agent of the present invention.The glass frosting treatment agent adds and is sprayed on after the water acid adding on glassly, does not need to soak in acid solution again, namely makes surface particles large, without the mat glass of impression of the hand.
The above is only preferred embodiment of the present invention, not in order to limiting the present invention, all any modifications of doing within the spirit and principles in the present invention, is equal to and replaces and improvement etc., within all should being included in protection scope of the present invention.
Claims (4)
1. a glass frosting treatment agent, is characterized in that, comprising: ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive;
The mass ratio of described ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 275~365: 130~165: 0.3~1.0: 1~50.
2. glass frosting treatment agent according to claim 1, is characterized in that, the mass ratio of described ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 295~325: 145~155: 0.5~0.8: 20~30.
3. glass frosting treatment agent according to claim 2, is characterized in that, the mass ratio of described ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 315: 150: 0.6: 25.
4. glass frosting treatment agent according to claim 2, is characterized in that, the mass ratio of described ammonium bifluoride, aluminum fluosilicate, sodium laurylsulfonate, guar gum and organic additive is: 310: 148: 0.7: 28.