A kind of blank pastel that fades
Technical field
The present invention relates to writing implement, specifically a kind of blank pastel that fades.
Background technology
In modern teaching, although water-soluble chalk, white board marker have replaced traditional chalk to a certain extent, their development is very not smooth.The use of a large amount of organic solvents in the non-biodegradable of some pigment and the ink has certain harm to environmental and human health impacts.The various new chalk that occurs at present, although color is various and be easy to write, its writing is fugitive color not, is difficult to wipe.
Summary of the invention
The object of the present invention is to provide a kind of blank pastel that fades, this chalk fluent writing, writing on blank is clear, wipes and can fade with erasing agent, and skin is not had hormesis, environmental protection.
A kind of blank pastel that fades provided by the invention, its feed composition and content thereof are by massfraction: emulsifying wax 40-45, stearic acid 20-25, talcum powder 14-18, polyoxyethylene glycol 6-10, sodium polyacrylate 1-2, chromogenic reagent 2-4, glycerine 5-6, white carbon black 0.6-0.8.
Preferably component and content thereof are according to the mass fraction: emulsifying wax 44, stearic acid 22, talcum powder 16, polyoxyethylene glycol 7, sodium polyacrylate 1.6, chromogenic reagent 3, glycerine 5, white carbon black 0.7.
Described chromogenic reagent is Methylene blue, C.I. 42685, acid No. 3 in green one or more.
Described emulsifying wax plays carrier in component of the present invention.
Described talcum powder is more than 1200 orders, plays a part lubricated.
Described polyoxyethylene glycol is polyethylene glycol 6000, plays in the present invention the binding agent effect.
Described glycerine can replace by spent glycol.Play in the present invention solvent, moisturizing.
A kind of blank that fades provided by the invention preparation method of pastel, step is: according to said components and the good raw material of proportioning weighing, after with glycerine that chromogenic reagent is wetting, add emulsifying wax, be heated to 75-95 ℃, after it melts fully, add polyoxyethylene glycol, talcum powder, sodium polyacrylate, stearic acid, white carbon black, stir, inject mould, behind its cooling forming, take out and get final product.
Compared with prior art, the blank pastel that fades provided by the invention, fluent writing, writing are clear on blank, wipe erasing agent with the erasing agent among the CN101709174A and wipe and to fade, leave no trace, and skin is not had hormesis, environmental protection, durable.
Embodiment
The present invention will be further described below in conjunction with embodiment.Use therein emulsifying wax is that Shanghai Kenduola Wax Industry Co., Ltd. produces, chromogenic reagent is that Zhejiang Longsheng Dye Chemical Co., Ltd produces, talcum powder is the forever 1200 purpose talcum powder produced of large chemical reagent company limited of Tianjin, and polyoxyethylene glycol is polyethylene glycol 6000.
The preparation of embodiment 1, blue chalk:
Take by weighing the red adding of 0.6 gram Methylene blue 1.0 gram glycerine stir wetting after, adding 8.36 gram emulsifying waxs is heated to 90 ℃, stirs it is melted fully, then progressively add 1.34 gram polyoxyethylene glycol, 3.0 gram talcum powder, 0.3 gram sodium polyacrylate, respectively fusing, stir, after adding at last 4.18 gram stearic acid and 0.5 gram white carbon black stirring.Then cooling injects mould slightly, takes out sample behind its complete cooling and shaping.
The preparation of embodiment 2, sanguine:
Take by weighing 0.4 gram C.I. 42685 add 1.0 gram glycerine stir wetting after, adding 8.40 gram emulsifying waxs is heated to 90 ℃, stirs it is melted fully, then progressively add 1.40 gram polyoxyethylene glycol, 3.0 gram talcum powder, 0.3 gram sodium polyacrylate, respectively fusing, stir, after adding at last 4.20 gram stearic acid and 0.5 gram white carbon black stirring.Then cooling injects mould slightly, takes out sample behind its complete cooling and shaping.
The preparation of embodiment 3, green chalk:
Take by weighing 0.4 gram acid No. 3 green, after adding 1.0 gram glycerine stirrings are wetting, adding 8.36 gram emulsifying waxs is heated to 90 ℃, stirs it is melted fully, then progressively add 1.34 gram polyoxyethylene glycol, 3.0 gram talcum powder, 0.3 gram sodium polyacrylate, respectively fusing, stir, after adding at last 4.18 gram stearic acid and 0.5 gram white carbon black stirring.Then cooling injects mould slightly, takes out sample behind its complete cooling and shaping.
The preparation of embodiment 4, purple chalk:
Take by weighing 0.2 gram C.I. 42685 and 0.2 gram Methylene blue add 1.0 gram ethylene glycol stir wetting after, adding 8.36 gram emulsifying waxs is heated to 90 ℃, stirs it is melted fully, then progressively add 1.37 gram polyoxyethylene glycol, 2.8 gram talcum powder, 0.3 gram sodium polyacrylate, respectively fusing, stir, after adding at last 4.20 gram stearic acid and 0.4 gram white carbon black stirring.Then cooling injects mould slightly, takes out sample behind its complete cooling and shaping.