CN103060688A - Wear-resisting steel plate for mining machinery - Google Patents
Wear-resisting steel plate for mining machinery Download PDFInfo
- Publication number
- CN103060688A CN103060688A CN2012105950957A CN201210595095A CN103060688A CN 103060688 A CN103060688 A CN 103060688A CN 2012105950957 A CN2012105950957 A CN 2012105950957A CN 201210595095 A CN201210595095 A CN 201210595095A CN 103060688 A CN103060688 A CN 103060688A
- Authority
- CN
- China
- Prior art keywords
- wear
- percent
- resisting
- steel plate
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a wear-resisting steel plate for mining machinery. Wear-resisting alloy steel comprises the following components in percent by weight: 0.7 to 0.9 percent of C, 0.6 to 0.8 percent of Si, 1.6 to 1.8 percent of Mn, less than or equal to 0.02 percent of P, less than or equal to 0.005 percent of S, 0.04 to 0.06 percent of La, 0.2 to 0.3 percent of V, 0.2 to 0.4 percent of Ti, 0.02 to 0.04 percent of N, 0.02 to 0.06 percent of Al, 0.003 to 0.005 percent of B, and the balance of Fe and inevitable impurities. The wear-resisting steel plate contains compounds such as titanium carbide, vanadium carbide, 3-nitrogen vanadium, titanium boride and aluminum nitride, which are dispersed and distributed in a steel substrate.
Description
Technical field
The present invention relates to technical field of ferrous metallurgy, particularly a kind of mining machinery wear-resisting steel plate.
Background technology
It is abominable especially that wear-resisting steel plate is widely used in working conditions, requires on the engineering goods such as high strength, high-wear resistance.Such as various mining machineries, grab bucket, stacker-reclaimer, conveying warp architecture etc.Therefore, this kind wear-resisting steel plate requires to have higher hardness.The present general alloy content of domestic wear resisting steel is higher, although can satisfy the requirement of hardness, plasticity and toughness are relatively relatively poor, affected to a certain extent its application on different mechanical fields.
Before the present invention, " a kind of ultrahigh-strength wear-resistant steel and production method thereof " patent of Wuhan Iron and Steel Company's invention, the composition range of this steel is: C 0.10-0.17%, Si 0.25-0.50%, Mn 1.20-1.50%, P≤0.018%, S≤0.008%, Cr 0.20-0.50%, Ni 0.25-0.50%, Mo 0.10-0.40%, Als 0.02-0.06%, B≤0.005%, RE≤150g/ ton steel; This steel adopts controlled rolling+modified production technique, does not contain V in this composition of steel, the about 1300MPa of tensile strength, and Brinell hardness number HB reaches about 400.But this steel contains the noble metal elements such as higher Ni, Mo, and cost is relatively high.
Also have " a kind of high-strength abrasion-proof plate and preparation method thereof " and " a kind of quenching and tempering type abrasion resistant steel and heat treating method thereof " patent of Wuyang Iron And Steel Company invention, its composition is respectively: C0.12-0.16%, Si 0.10-0.70%, Mn0.90-1.50%, P≤0.020%, S≤0.010%, Cr0.20-0.70%, Ni0.05-0.30%, V0.03-0.08%, Nb0.01-0.06%, Mo0.10-0.50%, Ti0.01-0.06%, Al0.02-0.08%, B0.0005-0.0030% and C0.14-0.18%, Si0.20-0.40%, Mnl.20-1.40%, P≤0.015%, S≤0.005%, Cr0.50-0.70%, Ni0.40-0.55%, V 0.03-0.08%, Nb 0.02-0.03%, Ti 0.015-0.030%, Mo 0.40-0.50%, Al0.02-0.045%, B 0.0015-0.0030%; All add Nb, Ni, the precious metal elements such as Mo, V of different content in the composition of two patents, greatly increased production cost.Wherein also contain Cu in second patent, the cost of two patents is all higher.The tempering temperature of first patent belongs to low-temperaturetempering at 150-250 ℃, and normal industrial tempering temperature is at 400-700 ℃, and organization of production and control are all difficult in the industrial production in batches, have greatly affected the normal production of heat treatment furnace.
Summary of the invention
For the deficiencies in the prior art, one of purpose of the present invention is to provide a kind of mining machinery wear-resisting steel plate, and this steel plate has good obdurability, higher hardness, and wear resisting property is excellent, and cost is low.
For achieving the above object, the present invention adopts following technical scheme:
A kind of mining machinery wear-resisting steel plate, described wear-resisting alloy steel is comprised of following component in (weight) per-cent: C:0.7-0.9%, Si:0.6-0.8%, Mn:1.6-1.8%, P≤0.02%, S≤0.005%, La:0.04-0.06%, V:0.2-0.3%, Ti:0.2-0.4%, N:0.02-0.04%, Al:0.02-0.06%, B:0.003-0.005%, all the other are iron Fe and inevitable impurity, contain titanium carbide in the described wear-resisting steel plate, vanadium carbide, vanadium three nitrogen, the disperse in steel matrix of the compound such as titanium boride and aluminium nitride, these compounds distributes.
Preferably, described wear-resisting alloy steel is comprised of following component in (weight) per-cent: C:0.8%, Si:0.7%, Mn:1.7%, P≤0.02%, S≤0.005%, La:0.05%, V:0.25%, Ti:0.3%, N:0.03%, Al:0.04%, B:0.004%, all the other are iron Fe and inevitable impurity.
Wear resisting steel of the present invention can adopt following preparation method:
1) smelt: comprise desulfurizing iron, the converter top bottom blowing, vacuum-treat, adjusting component satisfies above-mentioned requirements, and the control tapping temperature is about 1540-1580 ℃;
2) continuous casting: control Metal in Tundish superheating temperature is about 25-45 ℃, and continuous casting becomes base;
3) rolling: slab heating temperature is about 1210-1230 ℃, and start rolling temperature is about 1150-1170 ℃, and finishing temperature is about 900-920 ℃, rolls rear control speed of cooling and is about 15-25 ℃/second; Control is cooled to about 400-450 ℃;
About 4) thermal treatment: quenching temperature 980-1010 ℃, heat-up time 3.5-4.5min/mm * thickness of slab; About 220-240 ℃ of tempering holding temperature, soaking time 5-6min/mm * thickness of slab.
The Cr that all contains high level in the wear resisting steel of prior art, although the Cr element can significantly improve the hardness of steel, and can improve wear resisting property, itself and carbon easily form thick carbide, thereby significantly reduce the toughness of steel, so do not add the Cr element in the wear resisting steel of the present invention.
Carbon content design during steel of the present invention adopts, intensity, hardness and the wear resistance by carbon raising steel itself on the one hand forms hardness and the wear resisting property that an amount of carbide significantly improves steel by carbon and other alloying elements such as titanium, vanadium on the other hand.
On the basis of great many of experiments, V, Ti, N, the Al in the steel of the present invention, the alloy element content of B have been determined, between these alloying elements and and carbon between form the compounds such as titanium carbide, vanadium carbide, vanadium three nitrogen, titanium boride, aluminium nitride so that the hardness of steel and wear-resisting increasing substantially.
The present invention adds an amount of rare-earth elements of lanthanum, so that it can cooperate form and the distribution that improves above-claimed cpd, thereby indirectly assists obdurability and the wear resistance that improves steel.
In sum, the above-mentioned alloying element in the steel of the present invention complements each other, synergy.So that the hardness of wear resisting steel of the present invention improves, its Brinell hardness number can reach HB580-620, can guarantee good wear resisting property.Its tensile strength is no less than 1200MPa, and unit elongation is greater than 8%, and as seen its obdurability is good.
Embodiment
Further specify the present invention below by embodiment, but the invention is not restricted to following embodiment.
Embodiment one
A kind of mining machinery wear-resisting steel plate, described wear-resisting alloy steel is comprised of following component in (weight) per-cent: C:0.7%, Si:0.8%, Mn:1.6%, P≤0.02%, S≤0.005%, La:0.06%, V:0.2%, Ti:0.4%, N:0.02%, Al:0.06%, B:0.003%, all the other are iron Fe and inevitable impurity, contain titanium carbide, vanadium carbide, vanadium three nitrogen, titanium boride and aluminium nitride compound in the described wear-resisting steel plate, the disperse in steel matrix of these compounds distributes.
Embodiment two
A kind of mining machinery wear-resisting steel plate, described wear-resisting alloy steel is comprised of following component in (weight) per-cent: C:0.9%, Si:0.6%, Mn:1.8%, P≤0.02%, S≤0.005%, La:0.04%, V:0.3%, Ti:0.2%, N:0.04%, Al:0.02%, B:0.005%, all the other are iron Fe and inevitable impurity, contain titanium carbide, vanadium carbide, vanadium three nitrogen, titanium boride and aluminium nitride compound in the described wear-resisting steel plate, the disperse in steel matrix of these compounds distributes.
Embodiment three
A kind of mining machinery preparation method of wear-resisting steel plate, described wear-resisting alloy steel is comprised of following component in (weight) per-cent: C:0.8%, Si:0.7%, Mn:1.7%, P≤0.02%, S≤0.005%, La:0.05%, V:0.25%, Ti:0.3%, N:0.03%, Al:0.04%, B:0.004%, all the other are iron Fe and inevitable impurity, contain titanium carbide, vanadium carbide, vanadium three nitrogen, titanium boride and aluminium nitride compound in the described wear-resisting steel plate, the disperse in steel matrix of these compounds distributes.
Applicant's statement, the present invention illustrates detailed process equipment and process flow process of the present invention by above-described embodiment, but the present invention is not limited to above-mentioned detailed process equipment and process flow process, does not mean that namely the present invention must rely on above-mentioned detailed process equipment and process flow process and could implement.The person of ordinary skill in the field should understand, any improvement in the present invention to the interpolation of the equivalence replacement of each raw material of product of the present invention and ancillary component, the selection of concrete mode etc., all drops within protection scope of the present invention and the open scope.
Claims (2)
1. mining machinery wear-resisting steel plate, it is characterized in that, described wear-resisting alloy steel is comprised of following component in (weight) per-cent: C:0.7-0.9%, Si:0.6-0.8%, Mn:1.6-1.8%, P≤0.02%, S≤0.005%, La:0.04-0.06%, V:0.2-0.3%, Ti:0.2-0.4%, N:0.02-0.04%, Al:0.02-0.06%, B:0.003-0.005%, all the other are iron Fe and inevitable impurity, contain titanium carbide in the described wear-resisting steel plate, vanadium carbide, vanadium three nitrogen, the disperse in steel matrix of the compound such as titanium boride and aluminium nitride, these compounds distributes.
2. a kind of mining machinery wear-resisting steel plate as claimed in claim 1 is characterized in that, described wear-resisting alloy steel is comprised of following component in (weight) per-cent: C:0.8%, Si:0.7%, Mn:1.7%, P≤0.02%, S≤0.005%, La:0.05%, V:0.25%, Ti:0.3%, N:0.03%, Al:0.04%, B:0.004%, all the other are iron Fe and inevitable impurity.