CN103059707A - 一种用于三聚氰胺底材的聚氨酯漆 - Google Patents

一种用于三聚氰胺底材的聚氨酯漆 Download PDF

Info

Publication number
CN103059707A
CN103059707A CN2011103206854A CN201110320685A CN103059707A CN 103059707 A CN103059707 A CN 103059707A CN 2011103206854 A CN2011103206854 A CN 2011103206854A CN 201110320685 A CN201110320685 A CN 201110320685A CN 103059707 A CN103059707 A CN 103059707A
Authority
CN
China
Prior art keywords
parts
component
polyurethane paint
ground
trimeric cyanamide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011103206854A
Other languages
English (en)
Other versions
CN103059707B (zh
Inventor
陈寿生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Zhanchen Intelligent Property Management Co ltd
China Zhanchen New Materials Group Co.,Ltd.
Shanghai Zhanchen Paint Co ltd
Zhuhai Zhanchen New Material Co ltd
Original Assignee
Shanghai Fuchen Chemical Co Ltd
Beijing Zhanchen Chemical Co Ltd
Zhanchen Paint Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Fuchen Chemical Co Ltd, Beijing Zhanchen Chemical Co Ltd, Zhanchen Paint Group Co Ltd filed Critical Shanghai Fuchen Chemical Co Ltd
Priority to CN201110320685.4A priority Critical patent/CN103059707B/zh
Publication of CN103059707A publication Critical patent/CN103059707A/zh
Application granted granted Critical
Publication of CN103059707B publication Critical patent/CN103059707B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于三聚氰胺底材的聚氨酯漆，包括以下重量份数范围的组分：A组份：豆油醇酸树脂60～80份；溶剂28～44份；分散剂0~0.5份；消泡剂0.1-0.3份；流平剂0.1-0.3份；防沉剂0～1份；填料0～20份；B组份：TDI加成物35-48份；HDI三聚体10-15份；聚氨酯级溶剂42-50份。本发明的有益效果是：解决一般涂料在三聚氰胺木板材上无法附着的问题，方便和简化了施工过程，提高了效率。

Description

一种用于三聚氰胺底材的聚氨酯漆
技术领域
本发明涉及到一种聚氨酯漆，特别涉及一种在三聚氰胺底材上使用的聚氨酯漆。
背景技术
聚氨酯漆在三聚氰胺底材上直接涂装附着力差，容易掉漆。现有技术通过打磨底材提高涂料的附着力，但是打磨需要人力工时，且存在打磨不好导致的附着力更差的可能。
发明内容
针对上述提到的现有技术中的不足，本发明提供一种附着力好，无需在三聚氰胺底材上打磨，可以直接涂装的聚氨酯漆。
本发明解决其技术问题采用的技术方案是：
一种用于三聚氰胺底材的聚氨酯漆，包括以下重量份数范围的组分：A组份：豆油醇酸树脂60～80 份；溶剂28～44 份；分散剂0~0.5份；消泡剂0.1-0.3 份 ；流平剂0.1-0.3 份 ；防沉剂0～1份；填料0～20 份；B组份：TDI加成物35-48份；HDI三聚体10-15份；聚氨酯级溶剂42-50份。
优选的，所述的溶剂选用甲苯和/或二甲苯和/或醋酸丁酯和/或丙二醇甲醚醋酸酯。
优选的，所述的填料为滑石粉和/或二氧化硅。
优选的，所述的用于三聚氰胺底材的聚氨酯漆，包括以下重量份数计的组分：A 组份：豆油醇酸树脂60份；二甲苯6份；醋酸丁酯15份；丙二醇甲醚醋酸酯8份；甲苯15份；消泡剂0.2份；流平剂0.2份；B组份： TDI加成物48份；HDI三聚体10份；聚氨酯级溶剂42份。
优选的，所述的用于三聚氰胺底材的聚氨酯漆，包括以下重量份数计的组分：A 组份：豆油醇酸树脂60份；二甲苯5份；醋酸丁酯15份；丙二醇甲醚醋酸酯8份；分散剂0.5份；消泡剂0.2份；流平剂0.2份；防沉剂0.5份；二氧化硅4份；滑石粉15份；B组份： TDI加成物48份； HDI三聚体10份；聚氨酯级溶剂42份。
优选的，所述的豆油醇酸树脂采用的是70%固含的二甲苯溶液豆油改性的豆油醇酸树脂。
优选的，所述的消泡剂选用有机硅消泡剂。
优选的，所述的流平剂优选有机硅流平剂。
优选的，所述的防沉剂选用膨润土或有机酰胺防沉蜡。
优选的，所述的TDI加成物选用拜耳公司产品L-75；所述的HDI三聚体选用拜耳公司产品N3390。
本发明的有益效果是：解决一般涂料在三聚氰胺木板材上无法附着的问题，具有在三聚氰胺木底材上有优异的附着力，可以直接在三聚氰胺木底材上涂装；采用喷涂施工方式，可以大大提高劳动生产率。
具体实施方式
下面将结合具体实施例详细描述本发明内容：
本发明的用于三聚氰胺底材的聚氨酯漆包括以下重量份数范围的组分：A组份：豆油醇酸树脂60～80 份；溶剂28～44 份；分散剂0~0.5份；消泡剂0.1-0.3 份 ；流平剂0.1-0.3 份 ；防沉剂0～1份；填料0～20 份；B组份：TDI加成物35-48份；HDI三聚体10-15份；聚氨酯级溶剂42-50份。
上述组分中：
所述的豆油醇酸树脂优选采用的是70%固含的二甲苯溶液豆油改性的醇酸树脂，可选用DSM合成树脂有限公司产品3735X60树脂。
所述的溶剂优选甲苯和/或二甲苯和/或醋酸丁酯和/或丙二醇甲醚醋酸酯。
所述的消泡剂优选有机硅消泡剂，可以选用BYK 公司BYK066或者华夏公司HX-2300。
所述的流平剂优选有机硅流平剂，可以选用BYK 公司BYK310或者迪高公司TEGO450。
所述的防沉剂优选膨润土或有机酰胺防沉蜡。
所述的填料为滑石粉和/或二氧化硅。
所述的TDI加成物可以选用拜耳公司产品L-75。
所述的HDI三聚体可以选用拜耳公司产品N3390。
所述的聚氨酯级溶剂优选醋酸丁酯。
本发明的制备方法为本领域常规的方法，将各组分搅拌混合即可。
本发明用于三聚氰胺底材的聚氨酯漆在具体实施过程中可采用以下方案：
实施例1：包括以下重量份数计的组分：A 组份：豆油醇酸树脂60份；二甲苯6份；醋酸丁酯15份；丙二醇甲醚醋酸酯8份；甲苯15份；消泡剂0.2份；流平剂0.2份；B组份：拜耳公司产品L-75的TDI加成物48份；拜耳公司产品N3390的HDI三聚体10份；醋酸丁酯42份。
A组分的制备方法：先用二甲苯和醋酸丁酯溶解豆油醇酸树脂，搅拌，加入消泡剂、流平剂，再加入丙二醇甲醚醋酸酯和甲苯溶剂，充分分散。
B组分的制备方法：用醋酸丁酯将拜耳公司产品L-75的TDI加成物和拜耳公司产品N3390的HDI三聚体充分溶解。
将此产品A、B组份混合均匀后，喷涂于三聚氰胺板材上，常温干燥，用百格法测试附着力，附着力1级。漆膜表面无痱子等不良缺陷，此产品为亮光漆涂装。
实施例2：包括以下重量份数计的组分：A 组份：豆油醇酸树脂60份；二甲苯5份；醋酸丁酯15份；丙二醇甲醚醋酸酯8份；分散剂0.5份；消泡剂0.2份；流平剂0.2份；有机酰胺防沉蜡0.5份；二氧化硅4份；滑石粉15份；B组份：拜耳公司产品L-75的TDI加成物48份；拜耳公司产品N3390的HDI三聚体10份；醋酸丁酯42份。
A组分的制备方法：先用二甲苯、醋酸丁酯溶剂溶解豆油醇酸树脂，搅拌，加入分散剂、消泡剂、流平剂和有机酰胺防沉蜡，充分分散；加入二氧化硅和滑石粉，分散充分；分散至细度≤25微米，再加入丙二醇甲醚醋酸酯分散均匀。
B组分的制备方法：用醋酸丁酯将拜耳公司产品L-75的TDI加成物和拜耳公司产品N3390的HDI三聚体充分溶解。
将此产品A、B组份混合均匀后，喷涂于三聚氰胺底材上，常温干燥24h，用百格法测试附着力，附着力2级。漆膜表面无痱子等不良缺陷，此产品为三聚氰胺底材透明哑光面漆涂装。
实施例3：包括以下重量份数计的组分：A 组份：豆油醇酸树脂75份；二甲苯6份；醋酸丁酯10份；丙二醇甲醚醋酸酯8份；甲苯10份；消泡剂0.1份；流平剂0.1份；B组份：TDI加成物45份；HDI三聚体12份；聚氨酯级溶剂45份。
A组分的制备方法：先用二甲苯和醋酸丁酯溶解豆油醇酸树脂，搅拌，加入消泡剂、流平剂，再加入丙二醇甲醚醋酸酯和甲苯溶剂，充分分散。
B组分的制备方法：用聚氨酯级溶剂将TDI加成物和HDI三聚体充分溶解。
将此产品A、B组份混合均匀后，喷涂于三聚氰胺板材上，常温干燥。
实施例4：包括以下重量份数计的组分：A 组份：豆油醇酸树脂80份；二甲苯5份；醋酸丁酯15份；丙二醇甲醚醋酸酯8份；分散剂0.3份；消泡剂0.3份；流平剂0.3份；膨润土1份；二氧化硅5份；滑石粉15份；B组份： TDI加成物35份； HDI三聚体15份；聚氨酯级溶剂50份。
A组分的制备方法：先用二甲苯、醋酸丁酯溶剂溶解豆油醇酸树脂，搅拌，加入分散剂、消泡剂、流平剂和膨润土，充分分散；加入二氧化硅和滑石粉，分散充分；再加入丙二醇甲醚醋酸酯分散均匀。
B组分的制备方法：用聚氨酯级溶剂将TDI加成物和HDI三聚体充分溶解。
将此产品A、B组份混合均匀后，喷涂于三聚氰胺板材上，常温干燥。

Claims (10)

1.一种用于三聚氰胺底材的聚氨酯漆，其特征在于：包括以下重量份数范围的组分：A组份：豆油醇酸树脂60～80 份；溶剂28～44 份；分散剂0~0.5份；消泡剂0.1-0.3 份 ；流平剂0.1-0.3 份 ；防沉剂0～1份；填料0～20 份；B组份：TDI加成物35-48份；HDI三聚体10-15份；聚氨酯级溶剂42-50份。
2.根据权利要求1所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：所述的溶剂选用甲苯和/或二甲苯和/或醋酸丁酯和/或丙二醇甲醚醋酸酯。
3.根据权利要求1所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：所述的填料为滑石粉和/或二氧化硅。
4.根据权利要求2所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：包括以下重量份数计的组分：A 组份：豆油醇酸树脂60份；二甲苯6份；醋酸丁酯15份；丙二醇甲醚醋酸酯8份；甲苯15份；消泡剂0.2份；流平剂0.2份；B组份： TDI加成物48份；HDI三聚体10份；聚氨酯级溶剂42份。
5.根据权利要求2所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：包括以下重量份数计的组分：A 组份：豆油醇酸树脂60份；二甲苯5份；醋酸丁酯15份；丙二醇甲醚醋酸酯8份；分散剂0.5份；消泡剂0.2份；流平剂0.2份；防沉剂0.5份；二氧化硅4份；滑石粉15份；B组份： TDI加成物48份； HDI三聚体10份；聚氨酯级溶剂42份。
6.根据权利要求1至5任意一项所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：所述的豆油醇酸树脂采用的是70%固含的二甲苯溶液豆油改性的豆油醇酸树脂。
7.根据权利要求1至5任意一项所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：所述的消泡剂选用有机硅消泡剂。
8.根据权利要求1至5任意一项所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：所述的流平剂优选有机硅流平剂。
9.根据权利要求1至5任意一项所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：所述的防沉剂选用膨润土或有机酰胺防沉蜡。
10.根据权利要求1至5任意一项所述的用于三聚氰胺底材的聚氨酯漆，其特征在于：所述的TDI加成物选用拜耳公司产品L-75；所述的HDI三聚体选用拜耳公司产品N3390。
CN201110320685.4A 2011-10-20 2011-10-20 一种用于三聚氰胺底材的聚氨酯漆 Active CN103059707B (zh)