CN103042771B - A kind of Composite layer leather doubling glass and preparation method thereof - Google Patents
A kind of Composite layer leather doubling glass and preparation method thereof Download PDFInfo
- Publication number
- CN103042771B CN103042771B CN201310022107.1A CN201310022107A CN103042771B CN 103042771 B CN103042771 B CN 103042771B CN 201310022107 A CN201310022107 A CN 201310022107A CN 103042771 B CN103042771 B CN 103042771B
- Authority
- CN
- China
- Prior art keywords
- layer
- glass
- dermatine
- intermediate layer
- leather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of Composite layer leather doubling glass and preparation method thereof, belong to building member manufacture technology field, comprise upper layer, upper intermediate layer and bottom, or comprise upper layer, upper intermediate layer, bottom, lower intermediate layer and cutting optimal, bottom is float glass process white glass layer, upper intermediate layer and lower intermediate layer are middle membrane of glass layer, and upper layer and cutting optimal are artificial leather layer; Dermatine layer, middle membrane of glass layer and float glass process white glass layer or dermatine layer, middle membrane of glass layer, float glass process white glass layer, middle membrane of glass layer and dermatine layer stacked from top to bottom, and sintering connect.The invention has the beneficial effects as follows: can be used for decoration, indoor wall decoration outside titanium light rail moving door, one side wooden frame moving door, furred ceiling facing decoration, furniture, main material smooth nonhygroscopic, modification, bonding are not firmly, anticollision intensity enhancing, its colour image be greatly selective, play sound deadening; Also can be used for a point partition decorative, reduce house load-bearing, effectively utilize house usable floor area, soundproof effect is good.
Description
Technical field
The present invention is a kind of composite bed doubling glass and preparation method thereof, and particularly a kind of Composite layer leather doubling glass and preparation method thereof, belongs to building member manufacture technology field.
Background technology
In present various Household wardrobe light rail moving door, the kind of door there are glass door, timber, lagging remove from office door, color film doubling glass moving door etc., glass door is in use with in daily life, the easy fragmentation of glass is fallen ground and hurts sb.'s feelings, night the glass-reflected shadow, scaring can be caused to user, there is potential risk and trouble and worry; Glass back is pasted a watercolor and is done background, and pattern color easily fades, paper moisture-sensitive and be full of cracks; Timber mostly is wave wood and moulds hollow slab type or wave density board does moving door, and its surface is all pasted with woodgrained paper, paper moisture-sensitive come unstuck foamings, scratch, sheet material is yielding, easy-weathering, affects attractive in appearance and use; With the moving door that the surface air brushing of full wafer density board makes, its speed of making moist is faster and weight is large, and not light, pattern easily fades, and distributes pungent peculiar smell after making moist; It is that in main material surface brush, liquid glue pastes dermatine moving door that lagging leather door mostly is density board, in manufacturing process, with liquid glue, dermatine is pasted density board on the surface, the Pi Menhui made like this produces the distortion of main material because making moist, long-time use there will be leather and main material and to come unstuck layering, affect moving door attractive in appearance, after making moist, also can send pungent peculiar smell; Color film doubling glass moving door, its moving door Strength Safety increases, and color film is at bottom, and centre is glued membrane, and skin is glass, but also can be injured after colliding glass because glass is at skin, this also difficulty avoid the glass-reflected shadow at night, scaring can be caused to user.
People decorate for outside one side wooden frame moving door, furred ceiling facing decoration, furniture in addition, and indoor wall decoration, attractive in appearance not, can not noise reduction, large to house load-bearing for point partition decorative, the defects such as house usable floor area utilization rate is low, soundproof effect difference also expect there is new improvement.
Summary of the invention
The object of the invention is in above-mentioned prior art, all kinds of moving door is frangible, easy-weathering, yielding, easily come off, each class A of geometric unitA facing is attractive in appearance not, can not noise reduction, divide the defect that partition decorative is large to house load-bearing, usable floor area utilization rate is low, soundproof effect is poor, provide a kind of Composite layer leather doubling glass, can reach all kinds of moving door non-friable, indeformable, do not come off, pattern is rich and varied and pattern is colour-fast, indeformable, can noise reduction, point partition decorative is little to house load-bearing, usable floor area utilizes high, that soundproof effect is good object.
The technical scheme that the present invention takes to achieve these goals is: a kind of Composite layer leather doubling glass, comprise bottom, described bottom is float glass process white glass layer, also comprises upper layer and upper intermediate layer, is three layers of Composite layer leather doubling glass of upper layer, upper intermediate layer, bottom; Described upper layer is artificial leather layer, and upper layer thickness is 0.65-1.2mm; Described upper intermediate layer is middle membrane of glass layer, and upper intermediate layer thickness is 0.15-0.40mm; Described underlayer thickness is 5-19mm; Described dermatine layer, middle membrane of glass layer stacked from top to bottom with float glass process white glass layer and sintering be connected.
Described dermatine layer is PU polyurethane leather layer or PVC polychloroethylene leather layer.
Described PU polyurethane leather layer is XK-002PU polyurethane leather layer, TLP-109PU polyurethane leather layer, TLP-016PU polyurethane leather layer; Described PVC polychloroethylene leather layer is 02643PVC polychloroethylene leather layer or 79-002PVC polychloroethylene leather layer.
Described upper layer thickness is 0.75mm, and described upper intermediate layer thickness is 0.38mm, and described underlayer thickness is 5,6,8,10,12,15 or 19mm.
Also comprising lower intermediate layer and cutting optimal, is five layers of Composite layer leather doubling glass of upper layer, upper intermediate layer, bottom, lower intermediate layer and cutting optimal; Described lower intermediate layer is middle membrane of glass layer, and lower intermediate layer thickness is 0.15-0.40mm; Described cutting optimal is artificial leather layer, and cutting optimal thickness is 0.65-1.2mm; Described underlayer thickness is 5-12mm; The middle membrane of glass layer in the dermatine layer of described upper layer, the middle membrane of glass layer in upper intermediate layer, the float glass process white glass layer of bottom, lower intermediate layer stacked from top to bottom with the dermatine layer of cutting optimal and sintering be connected.
The dermatine layer of described cutting optimal is PU polyurethane leather layer or PVC polychloroethylene leather layer.
The PU polyurethane leather layer of described cutting optimal is XK-002PU polyurethane leather layer, TLP-109PU polyurethane leather layer, TLP-016PU polyurethane leather layer; The PVC polychloroethylene leather layer of described cutting optimal is 02643PVC polychloroethylene leather layer or 79-002PVC polychloroethylene leather layer.
Described underlayer thickness is 5,6,8,10 or 12mm, and described lower intermediate layer thickness is 0.38mm, and described cutting optimal thickness is 0.75mm.
Described dermatine layer is the monochromatic dermatine layer that its surface is manufactured with any painting and calligraphy, is produced at leather surface by computer collocation flat-plate ink jet printer.
Concrete procedure of processing:
(1). with anhydrous ethyl ester benzophenone cleaner special, conventional cleaning is first carried out to machined material, again by order from top to bottom dermatine layer, middle membrane of glass layer and float glass process white glass layer, or dermatine layer, middle membrane of glass layer, float glass process white glass layer, middle membrane of glass layer and dermatine layer to be stacked gradually;
(2). putting into specification is that the body of heater of the colour sandwich glass forming machine of 2600x2000mm vacuumizes, and makes vacuum arrival-0.09Mpa;
(3). heat to 100-130 degree sintering, be then incubated 15-30 minute;
(4). cool to normal temperature again with the furnace and come out of the stove.
Compared with prior art, the invention has the beneficial effects as follows:
(1) smooth surface, soft, main material is smooth nonhygroscopic, not modification;
(2) bonding firmly, not easily delamination, and anticollision intensity strengthens greatly;
(3) glass and leather are formed by high temperature sintering, and leather smells disappears, clean, health;
(4) decorate with leathering line, its colour image is greatly selective, can meet all kinds of consumer demand;
(5) safety in utilization is strong, top leather, middle level glued membrane, bottom glass, after design novel like this makes consumer clash into glass, and also can not by the glass scratch of internal layer;
(6) be widely used, Be very effective, can be usually used in decorating outside titanium light rail moving door, one side wooden frame moving door, furred ceiling facing decoration, furniture, and indoor wall decoration, play sound deadening; Also can be used for a point partition decorative, reduce house load-bearing, effectively utilize house usable floor area, there is obvious soundproof effect.
Accompanying drawing explanation
Fig. 1 is: three layers of Composite layer leather doubling glass schematic diagram;
Fig. 2 is: five layers of Composite layer leather doubling glass schematic diagram;
Fig. 3 is: dermatine layer is the dermatine layer figure (actual be cromogram, print as artwork master) that its surface is manufactured with any painting and calligraphy.
Description of reference numerals: intermediate layer on 1 bottom, 2,3 upper layers, 4 times intermediate layers, 5 cutting optimal.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, the invention will be further described, but not as a limitation of the invention.
Embodiment 1:
As shown in Figure 1, a kind of Composite layer leather doubling glass, comprises bottom 1, upper intermediate layer 2, upper layer 3, is three layers of Composite layer leather doubling glass; Described bottom 1 is float glass process white glass layer, and described upper intermediate layer 2 is middle membrane of glass layer, and described upper layer 3 is artificial leather layer; Bottom 1 thickness is 5mm, and upper intermediate layer 2 thickness is 0.38mm, and upper layer 3 thickness is 0.75mm; Described dermatine layer, middle membrane of glass layer stacked from top to bottom with float glass process white glass layer and sintering be connected.
Described dermatine layer is XK-002PU polyurethane leather layer.
Concrete procedure of processing:
(1). with anhydrous ethyl ester benzophenone cleaner special, conventional cleaning is first carried out to machined material, then by order from top to bottom, dermatine layer, middle membrane of glass layer and float glass process white glass layer is stacked gradually;
(2). putting into specification is that the body of heater of the colour sandwich glass forming machine of 2600x2000mm vacuumizes, and makes vacuum arrival-0.09Mpa;
(3). heat to 100-130 degree sintering, be then incubated 15-30 minute;
(4). cool to normal temperature again with the furnace and come out of the stove.
This product is usually used in decorating outside titanium light rail moving door, one side wooden frame moving door, furred ceiling facing decoration, furniture, and indoor wall is decorated, played sound deadening.
Embodiment 2-7:
The thickness of described bottom 1 is in table 1:
Remaining with embodiment 1.
Embodiment 8-11:
The concrete title of described upper layer 3 is in table 2:
Remaining with embodiment 1.
Embodiment 12:
As shown in Figure 2, a kind of Composite layer leather doubling glass, comprises upper layer 3, upper intermediate layer 2, bottom 1, lower intermediate layer 4 and cutting optimal 5, is five layers of Composite layer leather doubling glass; Described bottom 1 is float glass process white glass layer, and described upper intermediate layer 2 and lower intermediate layer 4 are middle membrane of glass layer, and described upper layer 3 and cutting optimal 5 are artificial leather layer; Bottom 1 thickness is 5mm, and upper intermediate layer 2 and lower intermediate layer 4 thickness are 0.38mm, and upper layer 3 and cutting optimal 5 thickness are 0.75mm; The float glass process white glass layer of the dermatine layer of described upper layer 3, the middle membrane of glass layer in upper intermediate layer 2, bottom 1, the middle membrane of glass layer in lower intermediate layer 4 stacked from top to bottom with the dermatine layer of cutting optimal 5 and sintering be connected.
The dermatine layer of described upper layer 3 and cutting optimal 5 is XK-002PU polyurethane leather layer.
Concrete procedure of processing:
(1). with anhydrous ethyl ester benzophenone cleaner special, conventional cleaning is first carried out to machined material, then stacked by order from top to bottom for the dermatine layer of the middle membrane of glass layer in the float glass process white glass layer of the middle membrane of glass layer in the dermatine layer of upper layer, upper intermediate layer, bottom, lower intermediate layer and cutting optimal.
All the other structures and concrete procedure of processing are with embodiment 1.
This product is usually used in a point partition decorative, reduces house load-bearing, effectively utilizes house usable floor area, has obvious soundproof effect.
Embodiment 13-16:
The thickness of described bottom 1 is in table 3:
Remaining with embodiment 12.
Embodiment 17-20:
The concrete title of described upper layer 3 and cutting optimal 5 is in table 4:
Remaining with embodiment 12.
Embodiment 21:
As shown in Figure 1,3, a kind of Composite layer leather doubling glass, comprises bottom 1, upper intermediate layer 2, upper layer 3, is three layers of Composite layer leather doubling glass; The dermatine layer of described upper layer 3 is the monochromatic dermatine layer that its surface is manufactured with any painting and calligraphy, and produced at leather surface by computer collocation flat-plate ink jet printer, its concrete preparation method is well-known technology, does not repeat them here.
Remaining with embodiment 1.
Embodiment 22:
As shown in Figure 2,3, a kind of Composite layer leather doubling glass, comprises bottom 1, upper intermediate layer 2, upper layer 3, lower intermediate layer 4 and cutting optimal 5, is five layers of Composite layer leather doubling glass; The dermatine layer of described upper layer 3, cutting optimal 5 or upper layer 3 and cutting optimal 5 is the monochromatic dermatine layer that its surface is manufactured with any painting and calligraphy, produced at leather surface by computer collocation flat-plate ink jet printer, its concrete preparation method is well-known technology, does not repeat them here.
Remaining with embodiment 12.
Above-described embodiment, 22 kinds of just the present invention's more preferably detailed description of the invention, the usual change that those skilled in the art carries out within the scope of technical solution of the present invention and replacing all should be included in protection scope of the present invention.
Claims (6)
1. a Composite layer leather doubling glass, comprises bottom, and described bottom is float glass process white glass layer, it is characterized in that: also comprise upper layer and upper intermediate layer, is three layers of Composite layer leather doubling glass of upper layer, upper intermediate layer, bottom; Described upper layer is artificial leather layer, and upper layer thickness is 0.65-1.2mm; Described upper intermediate layer is middle membrane of glass layer, and upper intermediate layer thickness is 0.15-0.40mm; Described underlayer thickness is 5-19mm; Described dermatine layer, middle membrane of glass layer stacked from top to bottom with float glass process white glass layer and sintering be connected.
2. a kind of Composite layer leather doubling glass according to claim 1, it is characterized in that: described upper layer thickness is 0.75mm, described upper intermediate layer thickness is 0.38mm, and described underlayer thickness is 5,6,8,10,12,15 or 19mm.
3. a kind of Composite layer leather doubling glass according to claim 1, is characterized in that: also comprise lower intermediate layer and cutting optimal, is five layers of Composite layer leather doubling glass of upper layer, upper intermediate layer, bottom, lower intermediate layer and cutting optimal; Described lower intermediate layer is middle membrane of glass layer, and lower intermediate layer thickness is 0.15-0.40mm; Described cutting optimal is artificial leather layer, and cutting optimal thickness is 0.65-1.2mm; Described underlayer thickness is 5-12mm; The middle membrane of glass layer in the dermatine layer of described upper layer, the middle membrane of glass layer in upper intermediate layer, the float glass process white glass layer of bottom, lower intermediate layer stacked from top to bottom with the dermatine layer of cutting optimal and sintering be connected.
4. a kind of Composite layer leather doubling glass according to claim 3, is characterized in that: described underlayer thickness is 5,6,8,10 or 12mm, and described lower intermediate layer thickness is 0.38mm, and described cutting optimal thickness is 0.75mm.
5. a kind of Composite layer leather doubling glass according to claim 1 or 3, is characterized in that: described dermatine layer is the monochromatic dermatine layer that its surface is manufactured with any painting and calligraphy.
6. the preparation method of a kind of Composite layer leather doubling glass according to claim 1 or 3, is characterized in that: concrete procedure of processing:
(1). with anhydrous ethyl ester benzophenone cleaner special, conventional cleaning is first carried out to machined material, again by order from top to bottom dermatine layer, middle membrane of glass layer and float glass process white glass layer, or dermatine layer, middle membrane of glass layer, float glass process white glass layer, middle membrane of glass layer and dermatine layer to be stacked gradually;
(2). putting into specification is that the body of heater of the colour sandwich glass forming machine of 2600x2000mm vacuumizes, and makes vacuum arrival-0.09Mpa;
(3). heat to 100-130 degree sintering, be then incubated 15-30 minute;
(4). cool to normal temperature again with the furnace and come out of the stove.