CN101713247A - Waterproof five-layer solid wood floor - Google Patents

Waterproof five-layer solid wood floor Download PDF

Info

Publication number
CN101713247A
CN101713247A CN200910035572A CN200910035572A CN101713247A CN 101713247 A CN101713247 A CN 101713247A CN 200910035572 A CN200910035572 A CN 200910035572A CN 200910035572 A CN200910035572 A CN 200910035572A CN 101713247 A CN101713247 A CN 101713247A
Authority
CN
China
Prior art keywords
solid wood
layer
waterproof
rotary
cut plates
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910035572A
Other languages
Chinese (zh)
Inventor
陈士民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAC DOUGLAS FLOOR (SUZHOU) CO Ltd
Original Assignee
MAC DOUGLAS FLOOR (SUZHOU) CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAC DOUGLAS FLOOR (SUZHOU) CO Ltd filed Critical MAC DOUGLAS FLOOR (SUZHOU) CO Ltd
Priority to CN200910035572A priority Critical patent/CN101713247A/en
Publication of CN101713247A publication Critical patent/CN101713247A/en
Pending legal-status Critical Current

Abstract

The invention discloses a waterproof five-layer solid wood floor comprising a substrate board (20). The substrate board (20) is a five-layer solid composite board and sequentially comprises a surface longitudinal peeling solid single board (21), a surface transversal peeling solid single board (22), a middle longitudinal finger-joint splicing board (23), a bottom transversal peeling solid single board (24) and a bottom longitudinal peeling solid single board (25) which are cohered by binder and thermally pressed into a whole; the upper part of the substrate board (20) is provided with a thermosetting resin wood-grained paper decorative layer facing (10) with good waterproofing; and the surface of the thermosetting resin wood-grained paper decorative layer facing (10) is provided with an aluminum oxide wear-resistant layer (50). The floor has smooth and attractive mortise, high product level, stable product material, good waterproofing effect, good expansion and deformation resistance even in water, excellent surface scraping resistance, high wear resistance, low manufacture cost and environmental protection.

Description

Waterproof five-layer solid wood floor
Technical field
The present invention relates to a kind of building and ornament materials, especially a kind of waterproof five-layer solid wood floor.
Background technology
In recent years, indoor decoration adopts wooden floor, solid wooden compound floor, three-layer wood composite flooring, impregnated-paper laminated wood floor (consolidated floor) to make floor decorative material in a large number.
Wooden floor need adopt the former carpentery workshop raw material of a large amount of heavy calibers, and generally speaking, the timber utilization rate of wooden floor only is 30%-40%, need select decades for use even go up century-old high-quality solid wood, and raw material selection standard height needs to consume a large amount of forest reserves.Thereby, there is the problem that high-quality timber is in short supply, timber utilization rate is not high.And consuming the destruction that a large amount of forest reserves can cause ecological environment, this problem is paid more and more attention also.And in the use, wooden floor also exists yielding, easy harmomegathus, the not wear-resisting and defective that involves great expense, more is difficult to solve waterproof, protection against the tide, anti-problem such as damage by worms, so influenced result of use and application life.
And impregnated-paper laminated wood floor (consolidated floor) adopts density fiber board as base material, does not rely on the heavy caliber log, helps protecting environment, but have an outstanding shortcoming meet exactly water can foam rise big.Water was unavoidable on ground was spilt, sprinkled in the room.Thereby, limited its use, especially in the kitchen, the use in nearly water place such as washroom or moist place.
Though the solid wooden compound floor stability is better than wooden floor, it is making moist for a long time or is soaking, and surface color can produce blackout, go mouldy, and surface paint complex manufacturing, and surperficial scratch-resistant, abrasion resistance all relatively are short of, and output is not high, and aberration is big again.
Three-layer wood composite flooring, though increase at aspect stablizing and stock utilization aspect, but, surface paint can make surface discolouration because meeting water, paint can come off, and not environmental protection again, three-layer wood composite flooring another one shortcoming is that the famous and precious heavy caliber timber in top layer must reach more than the 2mm thickness, and century-old above non-renewable resources consumption is big, makes moist or meets behind the water coefficient of deformation in addition.In this structure, as adopting thermosetting resin wood grain paper decorative layer facing, the surface layer plate that then fits with it is necessary for vertical plates of solid wood, otherwise can influence the appearance effect of surface heat thermosetting resin woodgrained paper decorative layer facing; And then in order to reach crisscross anti-deformation, anti-flexible purpose, then mesosphere board just can only adopt horizontal scab or finger plate, and promptly three layers for indulging structure in length and breadth.Such structure is brought a new shortcoming again, and solid wooden compound floor offers tenon, groove, and its tenon, groove are located in thicker mesosphere board position, because of it is horizontally-spliced plate or finger plate, so its tenon, groove are just rough, influence attractive in appearancely, reduced the class of product.
Summary of the invention
The objective of the invention is: a kind of waterproof five-layer solid wood floor is provided, its stable material quality, is difficult for harmomegathus, distortion, good water-proof effect is met water and can not foamed and rise greatly, is adapted at family or public place and uses; Floor surface hardness height, abrasion resistance height; Pattern variety is many, and decorative effect is rich and varied; Simultaneously, floor tongue-and-groove smooth and beautiful appearance; Can satisfy people's user demand, can protect forest resources again, the protection environment.
Technical scheme of the present invention is: a kind of waterproof five-layer solid wood floor, it comprises backing material plate, described backing material plate is the five-layer solid wood composite plate, comprise the vertical rotary-cut plates of solid wood of surface layer, the horizontal solid wood rotary cut venner of surface layer, central longitudinal successively to finger jigsaw, the horizontal rotary-cut plates of solid wood of bottom, the vertical rotary-cut plates of solid wood of bottom, five is synthetic whole by the hot pressing of cementing agent bonding between layer by layer; The top of backing material plate is provided with the good thermosetting resin wood grain paper decorative layer facing of water resistance, and thermosetting resin wood grain paper decorative layer facing surface is provided with the alundum (Al wearing layer.
Below technique scheme is further explained:
The vertical rotary-cut plates of solid wood of described surface layer can be vertical lignum cinnamomi camphorae rotary-cut plates of solid wood.
The horizontal rotary-cut plates of solid wood of described surface layer can be horizontal lignum cinnamomi camphorae rotary-cut plates of solid wood.
Described central longitudinal can be vertical lignum cinnamomi camphorae finger scab to the finger scab.
The horizontal rotary-cut plates of solid wood of described bottom can be horizontal lignum cinnamomi camphorae rotary-cut plates of solid wood.
The vertical rotary-cut plates of solid wood of described bottom can be vertical lignum cinnamomi camphorae rotary-cut plates of solid wood.
That is, four layers of rotary cut venner or any one deck of middle finger scab in the five-layer solid wood composite plate of backing material plate all can use lignum cinnamomi camphorae to do the mothproof processing of insect protected, and can constitute the multiple combination of one or more layers lignum cinnamomi camphorae layer.
Described backing material plate thickness is 8mm to 25mm.Wherein, the preferred substrates plate thickness is 8mm to 18mm.
The bottom surface of backing material plate can also be provided with moisture sealer, also moisture sealer can be set.Moisture sealer can be aluminum-plastic composite membrane, also can be that copper is moulded composite membrane, plastic sheeting or thermosetting resin balance layer.
The bottom surface of described backing material plate also is provided with thermosetting resin wood grain paper decorative layer facing.
Advantage of the present invention is:
1. waterproof five-layer solid wood floor of the present invention, its tongue-and-groove smooth and beautiful appearance, product specification height; Its backing material plate is crisscross, effectively anti-deformation, anti-flexible; Any one deck all can use lignum cinnamomi camphorae in five layers, because the natural mothproof smell of a kind of insect protected that volatilizes of lignum cinnamomi camphorae energy can play extraordinary anthelminthic effect, can solve the problem of damaging by worms in the use of floor.
2. waterproof five-layer solid wood floor of the present invention, is difficult for harmomegathus, distortion at stable material quality, good water-proof effect, and meeting water can foaming and intumescing, is adapted at family or public place and uses.Its surperficial scratch-resistant, abrasion resistance height; The surface pattern variety is many, and decorative effect is rich and varied.
3. waterproof five-layer solid wood floor of the present invention provides a kind of brand-new floor to constitute mentality of designing.
4. waterproof five-layer solid wood floor of the present invention can adopt fast growing wood, has reduced the use of high-grade timber, and the protection rare tree species protects forest resources, and preserves the ecological environment
5. waterproof five-layer solid wood floor of the present invention, the cost of product is low, with short production cycle, output is high, is beneficial to popularization, and market prospects are good.
Description of drawings
The invention will be further described below in conjunction with drawings and Examples:
Fig. 1 is the structural representation of the embodiment of the invention one;
Fig. 2 is the structural representation of the embodiment of the invention two.
Wherein: 10 thermosetting resin wood grain paper decorative layer facings; 20 backing material plates; The vertical rotary-cut plates of solid wood of 21 surface layers; The horizontal rotary-cut plates of solid wood of 22 surface layers; 23 central longitudinal are spliced laminate, the horizontal rotary-cut plates of solid wood of 24 bottoms to finger; The vertical rotary-cut plates of solid wood of 25 bottoms; 30 moisture sealers; 50 alundum (Al wearing layers.
The specific embodiment
Embodiment one:
As shown in Figure 1, a kind of waterproof five-layer solid wood floor, it comprises backing material plate 20, described backing material plate 20 is the five-layer solid wood composite plate, comprise that successively the vertical plates of solid wood 21 of surface layer, the horizontal rotary cut venner 22 of surface layer, central longitudinal are synthetic whole by the hot pressing of cementing agent bonding layer by layer to finger scab 23, the horizontal rotary cut venner 24 of bottom, the vertical plates of solid wood 25, five of bottom; The top of backing material plate 20 is provided with the good thermosetting resin wood grain paper decorative layer facing 10 of water resistance, and thermosetting resin wood grain paper decorative layer facing surface is provided with alundum (Al wearing layer 50.Overlay on the five-layer solid wood composite base material through high temperature hot pressing.
The five-layer solid wood composite plate is for indulging structure in length and breadth, effective anti-deformation, anti-flexible.
Any one deck all can adopt lignum cinnamomi camphorae in the five-layer solid wood composite plate, and the natural mothproof smell of a kind of insect protected that volatilizes of lignum cinnamomi camphorae energy can play extraordinary anthelminthic effect, can solve the problem of damaging by worms in the use of floor.Lignum cinnamomi camphorae leaf, really, can control diarrhoea, Gao Re and rheumatalgia according to introducing in the 1686th page of the Chinese medicine voluminous dictionary volume two.(in the present embodiment, the horizontal rotary cut venner 24 of bottom is selected horizontal lignum cinnamomi camphorae rotary-cut plates of solid wood for use.Other four layers all can be adopted fast growing wood.)
Backing material plate 20 thickness can be provided with according to the finished product needs, are typically chosen in 8mm to 25mm, are preferably 18mm in the present embodiment.
Embodiment two:
The difference of present embodiment and embodiment one is: as shown in Figure 2, the bottom surface of backing material plate 20 also is provided with moisture sealer 30, invades further to prevent steam, and moisture sealer 30 adopts aluminum-plastic composite membrane.
Embodiment three:
The difference of present embodiment and embodiment one is: the bottom surface of backing material plate 20 also is provided with thermosetting resin balance waterproofing course, both can prevent the steam intrusion, can keep the balance on floor again, and the floor is difficult for warpage.
Should be pointed out that for the present invention also to have the embodiment of multiple conversion and remodeling, be not limited to the specific embodiment of above-mentioned embodiment through proving absolutely.The foregoing description is as just explanation of the present invention, rather than limitation of the present invention.In a word, protection scope of the present invention should comprise those conspicuous to those skilled in the art conversion or substitute and remodeling.

Claims (10)

1. waterproof five-layer solid wood floor, it is characterized in that: it comprises backing material plate (20), described backing material plate (20) is the five-layer solid wood composite plate, comprise the vertical rotary-cut plates of solid wood of surface layer (21), the horizontal rotary-cut plates of solid wood of surface layer (22), central longitudinal successively to finger scab (23), the horizontal rotary-cut plates of solid wood of bottom (24), the vertical rotary-cut plates of solid wood of bottom (25), five is synthetic whole by the hot pressing of cementing agent bonding between layer by layer; The top of backing material plate (20) is provided with the good thermosetting resin wood grain paper decorative layer facing (10) of water resistance, and thermosetting resin wood grain paper decorative layer facing (10) surface is provided with alundum (Al wearing layer (50).
2. waterproof five-layer solid wood floor according to claim 1 is characterized in that: the vertical rotary-cut plates of solid wood of described surface layer (21) is vertical lignum cinnamomi camphorae rotary-cut plates of solid wood.
3. waterproof five-layer solid wood floor according to claim 1 is characterized in that: the horizontal rotary-cut plates of solid wood of described surface layer (22) is horizontal lignum cinnamomi camphorae rotary-cut plates of solid wood.
4. waterproof five-layer solid wood floor according to claim 1 is characterized in that: described central longitudinal is vertical lignum cinnamomi camphorae finger scab to finger scab (23).
5. waterproof five-layer solid wood floor according to claim 1 is characterized in that: the horizontal rotary-cut plates of solid wood of described bottom (24) is horizontal lignum cinnamomi camphorae rotary-cut plates of solid wood.
6. waterproof five-layer solid wood floor according to claim 1 is characterized in that: the vertical rotary-cut plates of solid wood of described bottom (25) is vertical lignum cinnamomi camphorae rotary-cut plates of solid wood.
7. waterproof five-layer solid wood floor according to claim 1 is characterized in that: described backing material plate (20) thickness is 8mm to 25mm.
8. waterproof five-layer solid wood floor according to claim 1 is characterized in that: the bottom surface of described backing material plate (20) also is provided with moisture sealer (30).
9. waterproof five-layer solid wood floor according to claim 8 is characterized in that: described moisture sealer (30) is that aluminum-plastic composite membrane, copper are moulded composite membrane, plastic sheeting or thermosetting resin balance layer.
10. waterproof five-layer solid wood floor according to claim 1 is characterized in that: the bottom surface of described backing material plate (20) also is provided with thermosetting resin wood grain paper decorative layer facing.
CN200910035572A 2009-09-25 2009-09-25 Waterproof five-layer solid wood floor Pending CN101713247A (en)