CN103042031B - The casting-rolling production method of metal sheet material - Google Patents
The casting-rolling production method of metal sheet material Download PDFInfo
- Publication number
- CN103042031B CN103042031B CN201110307010.6A CN201110307010A CN103042031B CN 103042031 B CN103042031 B CN 103042031B CN 201110307010 A CN201110307010 A CN 201110307010A CN 103042031 B CN103042031 B CN 103042031B
- Authority
- CN
- China
- Prior art keywords
- sheet material
- casting
- metal sheet
- metal
- millimeters
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The casting-rolling production method of a kind of metal sheet material of disclosure, belongs to method for metal working. Mainly solve the technical barrier of metal sheet material disposal molding processing. Its technical scheme is the first step, lead, silver, calcium, strontium are put into by component proportioning and carry out melting in smelting furnace 1, second step, melted metal is poured in holding furnace 2,3rd step, metal is banished again in crystallizer 3,4th step, the lead alloy material after crystallization is introduced casting and rolling machine 5 is carried out casting by lip 4,5th step, the metal sheet material of casting molding is introduced cutter 6, be cut out metal sheet material 7. The present invention disposable can produce metal sheet material.
Description
Technical field
Disclosure one metal sheet production method, the specifically casting-rolling production method of a kind of metal sheet material.
Background technology
Metal sheet material is a kind of common used material, therefore, how to improve its production efficiency and is always up the emphasis that industrial technology is paid close attention to.
Existing production method always first carries out smelting, then through casting, after through shearing grinding process molding. Production process operation is independent more, and energy consumption and material wave are useless big, very unreasonable, it is also very desirable to be innovated. Known to the technical staff of this enterprise, until before disclosure, the production method that neither one is good in metal sheet material produces obtains industrialized implementation or application.
The present invention is that the existing production method drawback of breakthrough, it is thus achieved that brand-new metal sheet material manufacturing technique method.
Summary of the invention
The goal of the invention of the present invention is exactly the production method of the openly disposable acquisition metal sheet material of a kind of direct casting-rolling method.
Realization the technical scheme is that such: the casting-rolling production method of metal sheet material, and its metal percentage ratio component is lead 99.85%��98.85%, silver 0.1%��0.9%, calcium 0.04%��0.15%, strontium 0.01%��0.1%.
Its production method process is: the first step, lead, silver, calcium, strontium is put into by component proportioning and carries out melting in smelting furnace 1; Second step, pouring in holding furnace 2 by melted metal, temperature is maintained in 400 DEG C �� 10 DEG C; 3rd step, being banished by metal in crystallizer 3, temperature controls in 250 DEG C �� 50 DEG C again; 4th step, the lead alloy material after crystallization is introduced casting and rolling machine 5, roll casting speed 0.10 m/min��0.50 m/min by lip 4; 5th step, the metal sheet material of casting molding is introduced cutter 6, be cut out satisfactory metal sheet material 7.
The metal sheet material of its produced molding, size can reach wide 1300 millimeters��500 millimeters, long 1000 millimeters��2000 millimeters, thickness 3 millimeters��14 millimeters.
The beneficial effects of the present invention is: production process is continuous, and production procedure is short, rolling density is high, saves material, substantially reduces energy consumption; The method adopting casting first is directly produced out metal sheet material, it is achieved that the important breakthrough of this industrial technology.
Accompanying drawing explanation
Fig. 1 is the production process of the present invention, equipment use schematic diagram.
In figure, 1 it is smelting furnace, 2 is holding furnace, 3 is crystallizer, 4 is lip, 5 is casting and rolling machine, 6 is cutter, 7 is metal sheet material.
Detailed description of the invention
Below in conjunction with the accompanying drawing of the present invention, further describe its detailed description of the invention.
Embodiment 1: the casting-rolling production method of metal sheet material
The casting-rolling production method of metal sheet material, its metal percentage ratio component is lead 99.85%, silver 0.1%, calcium 0.04%, strontium 0.01%.
Its production method process is: the first step, lead, silver, calcium, strontium is put into by component proportioning and carries out melting in smelting furnace 1; Second step, pouring in holding furnace 2 by melted metal, temperature is maintained in 400 DEG C �� 10 DEG C; 3rd step, being banished by metal in crystallizer 3, temperature controls in 250 DEG C �� 50 DEG C again; 4th step, the lead alloy material after crystallization is introduced casting and rolling machine 5, roll casting speed 0.10 m/min by lip 4; 5th step, the metal sheet material of casting molding is introduced cutter 6, be cut out satisfactory metal sheet material 7.
The metal sheet material of its produced molding, size can reach wide 1300 millimeters, long 1000 millimeters, thickness 3 millimeters.
Embodiment 2: the casting-rolling production method of metal sheet material
The casting-rolling production method of metal sheet material, its metal percentage ratio component is lead 98.85%, silver 0.9%, calcium 0.15%, strontium 0.1%.
Its production method process is: the first step, lead, silver, calcium, strontium is put into by component proportioning and carries out melting in smelting furnace 1; Second step, pouring in holding furnace 2 by melted metal, temperature is maintained in 400 DEG C �� 10 DEG C; 3rd step, being banished by metal in crystallizer 3, temperature controls in 250 DEG C �� 50 DEG C again; 4th step, the lead alloy material after crystallization is introduced casting and rolling machine 5, roll casting speed 0.50 m/min by lip 4; 5th step, the metal sheet material of casting molding is introduced cutter 6, be cut out satisfactory metal sheet material 7.
The metal sheet material of its produced molding, size can reach wide 500 millimeters, long 2000 millimeters, thickness 14 millimeters.
Claims (2)
1. the casting-rolling production method of metal sheet material, there are melting, casting, shear history, it is characterized in that: metal percentage ratio component is lead 99.85%��98.85%, silver 0.1%��0.9%, calcium 0.04%��0.15%, strontium 0.01%��0.1%, comprises the steps:
The first step, lead, silver, calcium, strontium are put in smelting furnace (1) by component proportioning carry out melting;
Second step, being poured into by melted metal in holding furnace (2), temperature is maintained in 400 DEG C �� 10 DEG C;
3rd step, being banished by metal in crystallizer (3) again, temperature controls in 250 DEG C �� 50 DEG C;
4th step, by the lead alloy material after crystallization by lip (4) introduce casting and rolling machine (5), roll casting speed 0.10 m/min��0.50 m/min;
5th step, the metal sheet material of casting molding is introduced cutter (6), be cut out satisfactory metal sheet material (7).
2. the casting-rolling production method of metal sheet material according to claim 1, is characterized in that: the metal sheet material of produced molding, and its size can reach wide 1300 millimeters��500 millimeters, long 1000 millimeters��2000 millimeters, thickness 3 millimeters��14 millimeters.