CN103030920A - 用于激光雕刻的树脂组合物及其制备方法 - Google Patents
用于激光雕刻的树脂组合物及其制备方法 Download PDFInfo
- Publication number
- CN103030920A CN103030920A CN2012105778956A CN201210577895A CN103030920A CN 103030920 A CN103030920 A CN 103030920A CN 2012105778956 A CN2012105778956 A CN 2012105778956A CN 201210577895 A CN201210577895 A CN 201210577895A CN 103030920 A CN103030920 A CN 103030920A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin combination
- laser sculpture
- weight
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于激光雕刻的树脂组合物,包括如下重量份数的组分:50~80份基础树脂,5~25份聚苯乙烯,5~10份相溶改进剂,5~10份玻璃纤维,1~3份发泡剂,1~3份阻燃剂,0.5~2份抗静电颜料,所述基础树脂选自ABS树脂、聚烯烃和橡胶中的一种或多种。本发明提供的用于激光雕刻的树脂组合物不但具有现有树脂组合物的耐酸碱、耐磨、环保等优点,还具有良好的防腐、防燃、耐高温等安全性能,可满足一些特殊条件下的应用,应用范围广。
Description
技术领域
本发明属于复合材料技术领域,尤其涉及一种用于激光雕刻的树脂组合物及其制备方法。
背景技术
ABS树脂是目前产量最大,应用最广泛的聚合物,它将PS,SAN,BS的各种性能有机地统一起来,兼具韧,硬,刚相均衡的优良力学性能。ABS是丙烯腈、丁二烯和苯乙烯的三元共聚物,A代表丙烯腈,B代表丁二烯,S代表苯乙烯。ABS树脂广泛应用于塑料产品的制备,往往与根据需要加入的助剂一起形成组合物注塑成型。
现有技术的树脂组合物制成的塑料制品,虽然解决了表面形成文字或图案、耐酸碱、耐磨的问题,但未在防腐、防燃等安全性问题上给予足够的关注,且无法满足激光雕刻的要求,尤其无法满足特殊条件下的应用要求。
发明内容
为解决现有技术存在的技术问题,发明人在树脂组合物的助剂选择、使用量方面进行大量的探索,预料不到地发现,通过基础树脂、聚苯乙烯、相溶改进剂、玻璃纤维、发泡剂、阻燃剂和抗静电颜料的协同作用可以得到性能优异的树脂组合物,不但具有现有树脂组合物的耐酸碱、耐磨、环保等优点,还具有良好的防腐、防燃、耐高温等安全性能,可满足激光雕刻的要求,可满足一些特殊条件下的应用,应用范围广。
一个方面,本发明提供一种用于激光雕刻的树脂组合物,包括如下重量份数的组分:50~80份基础树脂,5~25份聚苯乙烯,5~10份相溶改进剂,5~10份玻璃纤维,1~3份发泡剂,1~3份阻燃剂,0.5~2份抗静电颜料,所述基础树脂选自ABS树脂、聚烯烃和橡胶中的一种或多种。
基础树脂作为主要成分,可以根据具体需要选择不同类型的树脂或同时使用。
聚苯乙烯具有优良的隔热、绝缘、抗压性能,稳定性好,可起到改善树脂组合物成型产品的刚度的作用,还可防潮、防腐蚀。聚苯乙烯包括普通聚苯乙烯,发泡聚苯乙烯,高抗冲聚苯乙烯及间规聚苯乙烯,可以根据具体需要,选择合适的聚苯乙烯。
相溶改进剂用于使基础树脂和各种助剂成分充分混匀,提高基础树脂与玻璃纤维等成分的结合力,可改善组合物材料的微观形态和表观效果。
玻璃纤维具有耐高温、阻燃、防腐、绝缘性好等优点,通过与其他助剂的协调作用,可作为增强材料,提升树脂组合物的优异性能,尤其是安全方面的性能,且克服了自身耐磨方面的缺陷。
阻燃剂可增强树脂组合物耐高温、阻燃的性能。
抗静电颜料的添加可以赋予树脂组合物的抗静电性能。
作为本发明的进一步改进,所述相溶改进剂选自聚苯乙烯-马来酸酐共聚物、苯乙烯-马来酸酐共聚物、聚苯醚-马来酸酐共聚物和有机硅油中的一种或多种。
作为本发明的进一步改进,所述发泡剂选自偶氮二甲酰胺。当然,也可以根据具体需要选择现有的其他发泡剂。
作为本发明的进一步改进,所述阻燃剂选自六溴环十二烷、聚溴苯乙烯、四溴苯酚和多磷酸铵中的一种或多种。
作为本发明的进一步改进,所述抗静电颜料选自抗静电炭黑。也可以根据产品颜色要求灵活选择其他现有的抗静电颜料。
作为本发明的进一步改进,所述用于激光雕刻的树脂组合物包括如下重量份数的组分:70份基础树脂,10份聚苯乙烯,10份相溶改进剂,5份玻璃纤维,2份发泡剂,2份阻燃剂,1份抗静电颜料。
作为本发明的进一步改进,还包括如下重量份数的组分:1~5份抗氧剂、1~5份硬脂酸和0.5~2份润滑剂。通过上述助剂的添加,可进一步增强树脂组合物的稳定性、相溶性、表面光洁度,且有利于制品的成型脱模。
作为本发明的进一步改进,所述抗氧剂选自抗氧剂1010、抗氧剂1076和抗氧剂168中的一种或多种;所述润滑剂选自硅酮、聚乙烯蜡和丽科蜡中的一种或多种。
另一方面,本发明还提供用于激光雕刻的树脂组合物的制备方法,包括如下步骤:
A) 将各组分按相应的重量份数投入高速混合机中混匀,粉磨;
B) 将粉磨后的原料加热捏合后,经双螺杆挤出机混炼挤出,造粒。
与现有技术相比,本发明的有益效果是:本发明提供的用于激光雕刻的树脂组合物不但具有现有树脂组合物的耐酸碱、耐磨、环保等优点,还具有良好的防腐、防燃、耐高温等安全性能,抗静电性能好,表面光洁度高,可满足激光雕刻的要求,可满足一些特殊条件下的应用,应用范围广。此外,本发明提供的制备方法还具有工艺简单,成本低廉等优点。
具体实施方式
下面通过具体实施例对本发明做进一步详细说明。
实施例一 用于激光雕刻的树脂组合物。
称量70重量份数的ABS树脂,10重量份数的聚苯乙烯,10重量份数的聚苯乙烯-马来酸酐共聚物,5重量份数的玻璃纤维,2重量份数的偶氮二甲酰胺,2重量份数的六溴环十二烷和1重量份数的炭黑,将上述成分投入高速混合机中混匀,粉磨;将粉磨后的原料在高压、真空,160℃条件下混炼30分钟,加热捏合后,经双螺杆挤出机混炼挤出,造粒,可直接包装,或进一步加工成型。
本实施例制得的树脂组合物具有耐酸碱、耐磨、环保、防腐、防燃、耐高温等优良性能,抗静电性能好,表面光洁度高,可满足激光雕刻的要求。
实施例二 用于激光雕刻的树脂组合物。
称量60重量份数的ABS树脂,15重量份数的聚苯乙烯,10重量份数的有机硅油,7重量份数的玻璃纤维,1重量份数的偶氮二甲酰胺,2重量份数的六溴环十二烷和2重量份数的炭黑,将上述成分投入高速混合机中混匀,粉磨;将粉磨后的原料在高压、真空,160℃条件下混炼30分钟,加热捏合后,经双螺杆挤出机混炼挤出,造粒,可直接包装,或进一步加工成型。
本实施例制得的树脂组合物具有耐酸碱、耐磨、环保、防腐、防燃、耐高温等优良性能,抗静电性能好,表面光洁度高,可满足激光雕刻的要求。
实施例三 用于激光雕刻的树脂组合物。
称量50重量份数的ABS树脂,30重量份数的橡胶,20重量份数的聚苯乙烯,8重量份数的有机硅油,5重量份数的玻璃纤维,2重量份数的偶氮二甲酰胺,1重量份数的六溴环十二烷和1重量份数的抗静电深蓝色颜料(由钛青蓝和红粉混合物形成),将上述成分投入高速混合机中混匀,粉磨;将粉磨后的原料在高压、真空,160℃条件下混炼40分钟,加热捏合后,经双螺杆挤出机混炼挤出,造粒,可直接包装,或进一步加工成型。
本实施例制得的树脂组合物具有耐酸碱、耐磨、环保、防腐、防燃、耐高温等优良性能,抗静电性能好,表面光洁度高,可满足激光雕刻的要求。
以上内容是结合具体的优选实施方式对本发明所作的进一步详细说明,不能认定本发明的具体实施只局限于这些说明。对于本发明所属技术领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干简单推演或替换,都应当视为属于本发明的保护范围。
Claims (9)
1.一种用于激光雕刻的树脂组合物,其特征在于:包括如下重量份数的组分:50~80份基础树脂,5~25份聚苯乙烯,5~10份相溶改进剂,5~10份玻璃纤维,1~3份发泡剂,1~3份阻燃剂,0.5~2份抗静电颜料,所述基础树脂选自ABS树脂、聚烯烃和橡胶中的一种或多种。
2.根据权利要求1所述的用于激光雕刻的树脂组合物,其特征在于:所述相溶改进剂选自聚苯乙烯-马来酸酐共聚物、苯乙烯-马来酸酐共聚物、聚苯醚-马来酸酐共聚物和有机硅油中的一种或多种。
3.根据权利要求1所述的用于激光雕刻的树脂组合物,其特征在于:所述发泡剂选自偶氮二甲酰胺。
4.根据权利要求1所述的用于激光雕刻的树脂组合物,其特征在于:所述阻燃剂选自六溴环十二烷、聚溴苯乙烯、四溴苯酚和多磷酸铵中的一种或多种。
5.根据权利要求1所述的用于激光雕刻的树脂组合物,其特征在于:所述抗静电颜料选自抗静电炭黑。
6.根据权利要求1所述的用于激光雕刻的树脂组合物,其特征在于:包括如下重量份数的组分:70份基础树脂,10份聚苯乙烯,10份相溶改进剂,5份玻璃纤维,2份发泡剂,2份阻燃剂,1份抗静电颜料。
7.根据权利要求1至6中任一项所述的用于激光雕刻的树脂组合物,其特征在于:还包括如下重量份数的组分:1~5份抗氧剂、1~5份硬脂酸和0.5~2份润滑剂。
8.根据权利要求7所述的用于激光雕刻的树脂组合物,其特征在于:所述抗氧剂选自抗氧剂1010、抗氧剂1076和抗氧剂168中的一种或多种;所述润滑剂选自硅酮、聚乙烯蜡和丽科蜡中的一种或多种。
9.根据权利要求1至8中任一项所述用于激光雕刻的树脂组合物的制备方法,其特征在于:包括如下步骤:
A)将各组分按相应的重量份数投入高速混合机中混匀,粉磨;
B)将粉磨后的原料加热捏合后,经双螺杆挤出机混炼挤出,造粒。