CN103028715A - 双吸式叶轮的离心浇注铸造方法 - Google Patents

双吸式叶轮的离心浇注铸造方法 Download PDF

Info

Publication number
CN103028715A
CN103028715A CN2011102921040A CN201110292104A CN103028715A CN 103028715 A CN103028715 A CN 103028715A CN 2011102921040 A CN2011102921040 A CN 2011102921040A CN 201110292104 A CN201110292104 A CN 201110292104A CN 103028715 A CN103028715 A CN 103028715A
Authority
CN
China
Prior art keywords
sandbox
casting
casting method
double
molding box
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102921040A
Other languages
English (en)
Other versions
CN103028715B (zh
Inventor
杨德柱
李洪林
付建翔
王民生
张志勇
张述祥
刘敏华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Electric Construction Group Zhengzhou Pump Co., Ltd.
Original Assignee
ZHENGZHOU POWER EQUIPMENT WORKS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHENGZHOU POWER EQUIPMENT WORKS filed Critical ZHENGZHOU POWER EQUIPMENT WORKS
Priority to CN201110292104.0A priority Critical patent/CN103028715B/zh
Publication of CN103028715A publication Critical patent/CN103028715A/zh
Application granted granted Critical
Publication of CN103028715B publication Critical patent/CN103028715B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种双吸式叶轮的离心浇注铸造方法，该方法包括下列步骤：(1)将双吸式叶轮的熔模精铸模壳放入砂箱内，并在砂箱内装水玻璃、砂，吹干；（2）将装有熔模精铸模壳的砂箱进行焙烧；（3）将砂箱固定在转盘上；(4)使转盘旋转；(5)使转盘按照75~80转每分的转速平稳旋转后开始浇注；(6)在浇注完成后在砂箱的冒口上盖覆盖剂保温；（7）提高转盘的转速至120-150转每分，运转20~30分钟后停转；(8)打开砂箱、清砂、取出铸件。本方法能提高工艺出品率，后期制造费用比常规方法能降低40％以上；该离心浇注铸造方法制造的双吸叶轮内部组织致密，内在质量较高，大大提高了叶轮使用寿命，提高了整泵性能和质量。

Description

双吸式叶轮的离心浇注铸造方法
技术领域
发明涉及铸造领域，特别涉及熔模精密铸造生产工艺，具体是双吸式叶轮的离心浇注铸造方法。
背景技术
双吸叶轮是前置泵、凝结水泵的水力核心部件，其质量的好坏直接关系着整个给水系统的性能。因此，双吸叶轮的技术要求也很高，内部不允许存在缩松（孔）、裂纹等缺陷。双吸叶轮一般采用精密铸造工艺制造毛坯。双吸叶轮叶片扭曲，壁厚较薄，结构复杂，因盖板与轮毂之间仅有4-6mm厚的叶片相连接。由于精铸工艺的局限，补缩通道不畅，叶轮在加工过程中，后盖板与叶片交接处缩孔缺陷严重。双吸叶轮缩孔缩松质量缺陷在国内水泵制造行业普遍存在，目前仍没有一套彻底解决其质量问题的措施。
发明内容
本发明的目的在于提供一种双吸式叶轮的离心浇注铸造方法，它可克服现有的熔模铸造技术中存在的局限性，解决上述双吸式叶轮的铸件存在的缩孔缩松质量缺陷。
本发明采用的目的是通过以下技术方案实现的：该方法包括下列步骤： (1)将双吸式叶轮的熔模精铸模壳(2)放入砂箱（3）内，并在砂箱内装水玻璃砂，吹干；（2）将装有熔模精铸模壳的砂箱进行焙烧；（3）钢水冶炼符合出钢条件后，将砂箱吊出、固定在转盘(4)上，期间，熔模精铸模壳(2)温度不低于工艺要求的700℃温度；(4)砂箱在工作台上紧固可靠后使转盘（4）旋转；(5) 使转盘按照75~80转每分的转速平稳旋转后开始浇注；(6) 在浇注完成后在砂箱的冒口（1）上盖覆盖剂保温；（7）提高转盘的转速至120~150转每分，运转20~30分钟后停转；(8)打开砂箱(3)、清砂、取出铸件，完成一个生产周期。
在步骤（1）之后对熔模精铸模壳（2）进行焙烧，再将其装入砂箱进行焙烧。
在台车式电阻炉内对熔模精铸模壳进行焙烧。
本发明可以用于各类双吸叶轮的铸造生产，以及类似结构的其它回转体及异行铸件。该发明操作方便、安全可靠，对解决双吸叶轮缩孔类缺陷效果显著，在水泵制造过程中，不仅提高了产品质量，而且大大降低了制造费用，缩短了制造过程中因质量问题而影响的生产进度，能提高工艺出品率，降低加工过程中的焊补费用和加工周期，后期制造费用比常规方法能降低40％以上，后期加工周期每件叶轮能缩短7天以上；该离心浇注铸造方法制造的双吸叶轮内部组织致密，内在质量较高，大大提高了叶轮使用寿命，提高了整泵性能和质量。
附图说明：
图1为本发明工艺路线图。
具体实施方式：
下面结合附图对本发明作进一步的描述：
如图1所示，该发明的压蜡、焊接、制壳、脱蜡工序均与正常熔模精密铸造完全一样。由于模壳浇注时，模壳还要承受离心力作用，故离心浇注方法对模壳的强度有更高要求。为了保证模壳强度，防止漏钢钻钢、涨箱，模壳要进行装箱、填砂，然后进行焙烧。同时，为了保证模壳干强度，焙烧工艺也与正常熔模精密铸造不同，采用“一次焙烧-装箱-二次焙烧”工艺。
钢水冶炼符合出港要求后模壳出炉，模壳和砂箱一起固定在转盘上，使转盘以75~80转每分的转速转动，待运转平稳后开始浇注。10~20秒钟浇注完毕，提高转盘的转速至120~150转每分的转速，使高温钢水在离心力作用下完成充型和补缩。浇注后铸件的清砂、退火、清整与入库工序与正常熔模铸造工艺相同。

Claims (3)

1.一种双吸式叶轮的离心浇注铸造方法，其特征在于：该方法包括下列步骤： (1)将双吸式叶轮的熔模精铸模壳(2)放入砂箱（3）内，并在砂箱内装水玻璃、砂，吹干；（2）将装有熔模精铸模壳的砂箱进行焙烧；（3）钢水冶炼符合出钢条件后，将砂箱吊出、固定在转盘(4)上，期间，熔模精铸模壳(2)温度不低于工艺要求的700℃温度； (4)砂箱在工作台上紧固可靠后使转盘（4）旋转；(5) 使转盘按照75~80转每分的转速平稳旋转后开始浇注；(6) 在浇注完成后在砂箱的冒口（1）上盖覆盖剂保温；（7）提高转盘的转速至120~150转每分，运转20~30分钟后停转；(8)打开砂箱(3)、清砂、取出铸件，完成一个生产周期。
2.如权利要求1所述的双吸式叶轮的离心浇注铸造方法，其特征在于：在步骤（1）之后对熔模精铸模壳（2）进行焙烧，再将其装入砂箱进行焙烧。
3.如权利要求2所述的双吸式叶轮的离心浇注铸造方法，其特征在于：在台车式电阻炉内对熔模精铸模壳进行焙烧。
CN201110292104.0A 2011-09-29 2011-09-29 双吸式叶轮的离心浇注铸造方法 Active CN103028715B (zh)