CN103015547B - 一种利用建筑废弃物制备的无机发泡保温板 - Google Patents

一种利用建筑废弃物制备的无机发泡保温板 Download PDF

Info

Publication number
CN103015547B
CN103015547B CN201210565392.7A CN201210565392A CN103015547B CN 103015547 B CN103015547 B CN 103015547B CN 201210565392 A CN201210565392 A CN 201210565392A CN 103015547 B CN103015547 B CN 103015547B
Authority
CN
China
Prior art keywords
warming plate
inorganic foamed
building
foamed warming
prepare
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210565392.7A
Other languages
English (en)
Other versions
CN103015547A (zh
Inventor
张瑞军
王海燕
孙皓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen city Yiyiyi Environmental Technology Co. Ltd.
Original Assignee
GUANGZHOU SHIZHENG ENVIRONMENTAL PROTECTION SCIENCE AND TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGZHOU SHIZHENG ENVIRONMENTAL PROTECTION SCIENCE AND TECHNOLOGY DEVELOPMENT Co Ltd filed Critical GUANGZHOU SHIZHENG ENVIRONMENTAL PROTECTION SCIENCE AND TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN201210565392.7A priority Critical patent/CN103015547B/zh
Publication of CN103015547A publication Critical patent/CN103015547A/zh
Application granted granted Critical
Publication of CN103015547B publication Critical patent/CN103015547B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用建筑废弃物制备的无机发泡保温板，该保温板采用建筑废弃物粉体为主要原料，通过添加水泥，经发泡成型制备而成。本发明提供的无机发泡保温板，密度低、热导率小、稳固性能好、工程造价低，具有优良的隔音效果和环保性能，并达到国家A1级防火标准。本发明提供的无机发泡保温板作为建筑节能材料用于建筑外墙保温技术领域具有明显的优势。

Description

一种利用建筑废弃物制备的无机发泡保温板
技术领域
本发明涉及建筑节能材料开发与建筑外墙保温技术领域，具体涉及一种利用建筑废弃物制备的无机发泡保温板，该无机发泡保温板密度低、热导率小、稳固性好、成本低，具有优良的隔音效果和环保性能，并达到国家A1级防火标准。
背景技术
气候变暖和能源短缺己成为全球可持续发展面临的两大严峻挑战。在未来几十年，建筑能耗将成为主要的能源消耗增长点，包括建筑建造过程中产生的能耗（建筑材料、建筑设备、建筑施工等）和建筑使用过程中产生的能耗（生活能耗、采暖空调等）。据统计数字显示，我国既有的建筑面积近400亿平方米，95%以上是高能耗建筑。因此，建筑节能己经成为我国实现可持续性发展和国家节能规划目标的重要措施之一。
在建筑节能中，对建筑围护结构进行保温隔热处理是实现建筑节能的重要形式。保温隔热目前最常用的措施是在外墙上黏结保温板材，然而，我国目前的外墙保温板材大多使用易燃保温材料，此类材料的大量使用所引发的火灾时有发生，导致建筑大火来势迅猛，难以扑救，并且燃烧时释放的大量有毒烟气，是导致人员伤亡的重要原因。例如2010年11月15日，上海静安区胶州教师公寓外墙保温板因电焊引发火灾，死亡59人的事件令人触目惊心。
在我国，建材工业属于资源消耗型行业，物质资源消耗占原材料比重的90%以上。为了顺应我国循环经济的发展要求，必须提高建材产品中再生资源的利用量，大量消化吸收各种建筑废弃物，以实现“减量化、再利用、资源化”的技术改造。
我国每年产生的建筑废弃物近2亿吨，然而其产生和再利用并没有引起很大重视，通常是直接采用露天堆放或填埋的方式进行处理。随着我国城市化进程正在大踏步向前迈进，建筑废弃物加剧了土地和资源的紧张局面，严重影响到社会经济和生态环境的协调发展。因此，加强建筑废弃物的综合利用迫在眉睫。
为了促进建筑节能工作的开展，满足市场需求，针对目前我国外墙保温板在使用中存在的不足，我们利用建筑废弃物为原料发明了一种用于建筑使用的无机发泡保温板，将填补国内相关技术的空白。本发明提供的利用建筑废弃物制备的无机发泡保温板，密度低、热导率小、稳固性好、成本低，具有优良的隔音效果和环保性能，并达到国家A1级防火标准。
发明内容
针对现有技术中存在的不足，本发明提供一种利用建筑废弃物制备的无机发泡保温板。
本发明提供的利用建筑废弃物制备的无机发泡保温板，以建筑废弃物粉体为主要原料，通过添加水泥，经发泡成型制备而成。其中，建筑废弃物粉体用料为30%~85%，粉体粒料细度在0.075mm以下，水泥用料为10%~30%，添加剂用料为 0%~5%。本发明提供的利用建筑废弃物制备的无机发泡保温板，密度低、热导率小、稳固性能好、工程造价低，具有优良的隔音效果和环保性能，并达到国家A1级防火标准。以下分别对该无机发泡保温板的性能特点作详细描述：
(1) 质量轻：其密度在130~230kg/m3之间，能有效减轻建筑物的负载；
(2) 热导率小：其导热系数在0.05~0.01之间，能有效降低建筑物墙体的导热能力，具有良好的保温特性；
(3) 稳固性能好：通过特殊制剂的加入保持良好的稳固性能和抗老化性能，抗压强度为0.6~1.0Mpa、抗冻性为质量损失2.0，强度损失18.0。同为无机材料，与建筑物同寿命；
(4) 工程造价低：以建筑废弃物粉体为主要原料，通过添加水泥，经发泡成型制备而成，工艺简单，工程造价低；
(5) 隔音效果好：通过发泡的保温板的孔隙保持各自封闭，其30mm的隔音可达到45分贝以上，充分解决建筑空间的私密性；
(6) 环保性能好：主要用料为建筑废弃物（粘土和水泥砂粉体），无毒无害，减少水泥使用量，减少碳排放。
(7) A级防火性能：保温板97%的成分是无机物，其它为发泡剂和稳定剂，为不燃材料，保温板孔隙各自封闭在一定厚度时确保良好的耐火性。
具体实施方式
以下结合2个实施例，对本发明做进一步的详细说明：
实施例1
按质量份数计，称取建筑废弃物粉体30%~85%、水泥10%~30%，发泡剂0~5%；将上述原料用水混合，充分搅拌后倒入模具加热发泡脱制而成，出模后切割成所需要规格。
制备后样品的密度为130~230kg/m3、导热系数为0.03~0.01、抗压强度为0.6~2.0Mpa、抗冻性为质量损失2.0，强度损失18.0、防火极限达A1级、产品规格为100~600mm×100~900mm×25~100mm。
上述实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。

Claims (1)

1.一种利用建筑废弃物制备的无机发泡保温板，其特征在于：该无机发泡保温板是采用建筑废弃物粉体为主要原料制备的; 按质量百分比计，称取建筑废弃物粉体30%-85%、水泥10%-30%，发泡剂0-5%；将上述原料用水混合，充分搅拌后倒入模具加热发泡脱制而成，出模后切割成所需要规格;制备后样品的密度为130-230kg/m3、导热系数为0.03-0.01、抗压强度为0.6-2.0Mpa、抗冻性为质量损失2.0，强度损失18.0、防火极限达A1级、产品规格为100-600mm×100-900mm×25-100mm。
CN201210565392.7A 2012-12-24 2012-12-24 一种利用建筑废弃物制备的无机发泡保温板 Expired - Fee Related CN103015547B (zh)