CN103014441A - 一种用于高压铸造薄铝合金制备方法 - Google Patents

一种用于高压铸造薄铝合金制备方法 Download PDF

Info

Publication number
CN103014441A
CN103014441A CN2012105059163A CN201210505916A CN103014441A CN 103014441 A CN103014441 A CN 103014441A CN 2012105059163 A CN2012105059163 A CN 2012105059163A CN 201210505916 A CN201210505916 A CN 201210505916A CN 103014441 A CN103014441 A CN 103014441A
Authority
CN
China
Prior art keywords
aluminium alloy
aluminium
pressure casting
strontium
zirconium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012105059163A
Other languages
English (en)
Inventor
姚芸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012105059163A priority Critical patent/CN103014441A/zh
Publication of CN103014441A publication Critical patent/CN103014441A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种用于高压铸造薄铝合金制备方法,包括有配料、熔炼、降温步骤,其配料组成按重量百分比为,5.8-7.5%的硅、0.1-0.3%的锰、0.1-0.3%的镍、0.1-0.15%的镁、1.0-1.2%的铜、0.8-1.2%的铁、0.1-0.3%的铬、0.01-0.02%的锆、0.01-0.02%的锶、0.3-0.5%的钛、0.01-0.03%的硼、0.01-0.03%的钒、0.1-0.3%的锡、余量为铝。通过在铝合金中加入锶、钛、锆、钒、硼元素,能够抑制铝合金中形成硅-铝棒状晶粒的形成,并形成细小的晶粒。

Description

一种用于高压铸造薄铝合金制备方法
技术领域
本发明属于铝合金领域,特别是指一种用于高压铸造薄铝合金制备方法。
背景技术
纯铝的密度小、耐腐蚀性高、熔点低,大约为660℃,且具有很高的塑性,易于加工。但纯铝的强度低,为了能够提高铝的适用范围,通过长期的研究,通过在纯铝中加入某些其它元素制得铝合金后能够提高强度的同时,依然保持纯铝的耐腐蚀性能、高塑性性能。而且在添加了某些元素如钛金属的情况下,其强度超过很多合金钢,而且比重轻,已经被广泛用于机械制造、航空工业、汽车及建材领域以替代铁或铁合金,以实现减轻自重及降低能耗。
铝合金的强度高,超过许多合金钢的强度,但是在铸造时,特别是加工薄的板材时,还存在以下缺陷,就是在铸造过程中,因为在高压铸造过程中,会导致铝合金组织内的结构改变,而引起铝合金表面出现裂纹等现象,这一现象导致了产品的性能及耐腐蚀性能出现缺陷。
发明内容
本发明的目的是提供一种用于高压铸造薄铝合金的材料及制备方法,通过本技术方案,其生产的铝合金板材更薄,而且性能稳定无裂纹等特点。
本发明是通过以下技术方案实现的:
一种用于高压铸造薄铝合金制备方法是:
配料,按重量百分比为,5.8-7.5%的硅、0.1-0.3%的锰、0.1-0.3%的镍、0.1-0.15%的镁、1.0-1.2%的铜、0.8-1.2%的铁、0.1-0.3%的铬、0.01-0.02%的锆、0.01-0.02%的锶、0.3-0.5%的钛、0.01-0.03%的硼、0.01-0.03%的钒、0.1-0.3%的锡、余量为铝进行配料;
熔炼,首先加入按上述配料计算的铝的量的一半及其它材料进行熔炼,待熔化成液体后加入剩余的铝继续进行熔炼并保温30-60分钟后进行浇铸;
降温,保持匀速降温至130-150℃后回火至180-200℃并保温1-2小时,自然冷却。
所述降温速度维持在25-30℃/分钟。
采用上述的铝合金进行高压铸造得到所需要的板材。
作为进一步的改进,所述用于高压铸造薄铝合金的材料,其组成按重量百分比为,6.2-6.5%的硅、0.2-0.3%的锰、0.2-0.25%的镍、0.1-0.15%的镁、1.0-1.2%的铜、0.8-1.0%的铁、0.25-0.28%的铬、0.01-0.02%的锆、0.01-0.02%的锶、0.35-0.45%的钛、0.01-0.03%的硼、0.01-0.03%的钒、0.1-0.3%的锡、余量为铝。
所述锶、锆、钛、钒分别以锶铝合金、锆铝合金、钛铝合金、钒铝合金的方式加入。
本发明同现有技术相比的有益效果是:
1、通过在铝合金中加入锶、钛、锆、钒、硼元素,能够抑制铝合金中形成硅-铝棒状晶粒的形成,并形成细小的晶粒。
2、通过本发明的制备方法,在浇铸过程中,已经使合金中的晶粒进行充分的生长,因此在后期的高压铸造过程中,不会因为温度的升高而引起晶粒再次过分生长。
具体实施方式
以下通过具体的实施例来详细说明本发明的具体技术方案,应当理解的是,以下的实施例仅能用来解释本发明而不能用来解释是对本发明的限制。
实施例1
所述制备方法是:
配料,按重量百分比为,5.8%的硅、0.1%的锰、0.1%的镍、0.1%的镁、1.0%的铜、0.8%的铁、0.1%的铬、0.01%的锆、0.01%的锶、0.3%的钛、0.01%的硼、0.01%的钒、0.1%的锡、余量为铝进行配料;其中锶、锆、钛、钒要计算锶铝合金、锆铝合金、钛铝合金、钒铝合金的量,及最后的铝的量;
熔炼,首先加入按上述配料计算的铝的量的一半及其它材料进行熔炼,待熔化成液体后加入剩余的铝继续进行熔炼并保温30分钟后进行浇铸;
降温,保持降温速度维持在25-30℃/分钟匀速降温至130-150℃后回火至180-200℃并保温1小时,自然冷却。
采用上述的铝合金进行高压铸造得到所需要的板材。
实施例2
所述制备方法是:
配料,按重量百分比为,7.5%的硅、0.3%的锰、0.3%的镍、0.15%的镁、1.2%的铜、1.2%的铁、0.3%的铬、0.02%的锆、0.02%的锶、0.5%的钛、0.03%的硼、0.03%的钒、0.3%的锡、余量为铝进行配料;其中锶、锆、钛、钒要计算锶铝合金、锆铝合金、钛铝合金、钒铝合金的量,及最后的铝的量;
熔炼,首先加入按上述配料计算的铝的量的一半及其它材料进行熔炼,待熔化成液体后加入剩余的铝继续进行熔炼并保温60分钟后进行浇铸;
降温,保持降温速度维持在25-30℃/分钟匀速降温至130-150℃后回火至180-200℃并保温1.5小时,自然冷却。
采用上述的铝合金进行高压铸造得到所需要的板材。
实施例3
所述制备方法是:
配料,按重量百分比为,6.2%的硅、0.2%的锰、0.2%的镍、0.1%的镁、1.0%的铜、0.8%的铁、0.25%的铬、0.01%的锆、0.01%的锶、0.35%的钛、0.01%的硼、0.01%的钒、0.1%的锡、余量为铝进行配料;其中锶、锆、钛、钒要计算锶铝合金、锆铝合金、钛铝合金、钒铝合金的量,及最后的铝的量;
熔炼,首先加入按上述配料计算的铝的量的一半及其它材料进行熔炼,待熔化成液体后加入剩余的铝继续进行熔炼并保温45分钟后进行浇铸;
降温,保持降温速度维持在25-30℃/分钟匀速降温至130-150℃后回火至180-200℃并保温1.5小时,自然冷却。
采用上述的铝合金进行高压铸造得到所需要的板材。
实施例4
配料,按重量百分比为,6.5%的硅、0.3%的锰、0.25%的镍、0.15%的镁、1.2%的铜、1.0%的铁、0.28%的铬、0.02%的锆、0.02%的锶、0.45%的钛、0.03%的硼、0.03%的钒、0.3%的锡、余量为铝进行配料;其中锶、锆、钛、钒要计算锶铝合金、锆铝合金、钛铝合金、钒铝合金的量,及最后的铝的量;
熔炼,首先加入按上述配料计算的铝的量的一半及其它材料进行熔炼,待熔化成液体后加入剩余的铝继续进行熔炼并保温45分钟后进行浇铸;
降温,保持降温速度维持在25-30℃/分钟匀速降温至130-150℃后回火至180-200℃并保温1.5小时,自然冷却。
采用上述的铝合金进行高压铸造得到所需要的板材。

Claims (5)

1.一种用于高压铸造薄铝合金制备方法,其特征在于:
配料,按重量百分比为,5.8-7.5%的硅、0.1-0.3%的锰、0.1-0.3%的镍、0.1-0.15%的镁、1.0-1.2%的铜、0.8-1.2%的铁、0.1-0.3%的铬、0.01-0.02%的锆、0.01-0.02%的锶、0.3-0.5%的钛、0.01-0.03%的硼、0.01-0.03%的钒、0.1-0.3%的锡、余量为铝进行配料;
熔炼,首先加入按上述配料计算的铝的量的一半及其它材料进行熔炼,待熔化成液体后加入剩余的铝继续进行熔炼并保温30-60分钟后进行浇铸;
降温,保持匀速降温至130-150℃后回火至180-200℃并保温1-2小时,自然冷却。
2.根据权利要求1所述的用于高压铸造薄铝合金制备方法,其特征在于:所述降温速度维持在25-30℃/分钟。
3.根据权利要求1所述的用于高压铸造薄铝合金制备方法,其特征在于:采用上述的铝合金进行高压铸造得到所需要的板材。
4.根据权利要求1所述的用于高压铸造薄铝合金制备方法,其特征在于:所述用于高压铸造薄铝合金的材料,其组成按重量百分比为,6.2-6.5%的硅、0.2-0.3%的锰、0.2-0.25%的镍、0.1-0.15%的镁、1.0-1.2%的铜、0.8-1.0%的铁、0.25-0.28%的铬、0.01-0.02%的锆、0.01-0.02%的锶、0.35-0.45%的钛、0.01-0.03%的硼、0.01-0.03%的钒、0.1-0.3%的锡、余量为铝。
5.根据权利要求1所述的用于高压铸造薄铝合金制备方法,其特征在于:所述锶、锆、钛、钒分别以锶铝合金、锆铝合金、钛铝合金、钒铝合金的方式加入。
CN2012105059163A 2012-11-26 2012-11-26 一种用于高压铸造薄铝合金制备方法 Pending CN103014441A (zh)