CN102995791A - 一种钢结构泡沫石膏复合墙体 - Google Patents
一种钢结构泡沫石膏复合墙体 Download PDFInfo
- Publication number
- CN102995791A CN102995791A CN2012105200147A CN201210520014A CN102995791A CN 102995791 A CN102995791 A CN 102995791A CN 2012105200147 A CN2012105200147 A CN 2012105200147A CN 201210520014 A CN201210520014 A CN 201210520014A CN 102995791 A CN102995791 A CN 102995791A
- Authority
- CN
- China
- Prior art keywords
- foamed gypsum
- gypsum
- steel
- wall body
- semi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种钢结构泡沫石膏复合墙体,所述钢结构泡沫石膏复合墙体的外部为钢板层,内部为泡沫石膏填充层;所述泡沫石膏填充层各组分的重量百分比如下:β-半水石膏为45%~55%,三聚氰胺减水剂为0.1%~0.2%,柠檬酸为0.1%~0.3%,十二烷基硫酸钠为0.1%~0.2%,稳泡剂为0.05%~0.1%,羟丙基甲基纤维素醚为0.1%~0.2%,余量为水。本发明能够避免开裂空鼓等工程问题,整个墙体均可循环使用,且对人体无害,环保节能。
Description
【技术领域】
本发明涉及一种建筑材料领域,特别涉及一种钢结构泡沫石膏复合墙体。
【背景技术】
砌体材料是房屋建筑材料中的重要部分,由于环境保护及节能需要,砌体材料从传统的粘土砖到目前混凝土空心砌块、粉煤灰加气硅酸盐砌块、加气混凝土砌块等新型墙体材料,形式多样。
目前粘土砖因破坏耕地等原因已被禁用或限用。由于砌体与混凝土、水泥砂浆等材料共同作用时,其干缩变形数值相差很大,甚至相差几倍,在长期使用过程中容易产生裂缝,容易发生渗漏,影响住户的正常使用,发生渗漏后还可能产生其他连发的质量或安全事故。而框架结构的填充墙墙材循环利用率普遍较低,或循环利用成本较大,施工效率低。另外,钢结构目前的内填充主要采用玻璃棉等无机纤维或泡沫混凝土,而玻璃棉在安装拆卸过程会损伤施工人员的皮肤和呼吸器官,泡沫混凝土较难循环利用。
因此,有待挖掘一种新的墙体结构,来解决上述问题。
【发明内容】
本发明要解决的技术问题,在于提供一种钢结构泡沫石膏复合墙体,能够避免开裂空鼓等工程问题,整个墙体均可循环使用,且对人体无害,环保节能。
本发明是这样实现的:
一种钢结构泡沫石膏复合墙体,所述钢结构泡沫石膏复合墙体的外部为钢板层,内部为泡沫石膏填充层;所述泡沫石膏填充层各组分的重量百分比如下:
β-半水石膏为45%~55%,三聚氰胺减水剂为0.1%~0.2%,柠檬酸为0.1%~0.3%,十二烷基硫酸钠为0.1%~0.2%,稳泡剂为0.05%~0.1%,羟丙基甲基纤维素醚为0.1%~0.2%,余量为水。
进一步地,所述β-半水石膏为的重量百分比为50%。
本发明具有如下优点:
本发明外层采用钢板层,能够解决常见的开裂空鼓等工程问题,并提高施工效率;泡沫石膏作为内填充,能够为解决玻璃棉对人体的损害,并实现整个墙体可循环使用,非常的节能环保;在操作过程中可采用泵送浇筑技术进行钢板层内泡沫石膏的填充,可进一步提高施工效率;发明采用特殊配比的泡沫石膏,水灰比可达1:1,大幅节省了石膏资源,其中,β-半水石膏可使用各种工业副产废渣石膏,实现了节能利废,更为环保;另外,泵送效果极佳,并且降低了墙体的自重,提高了墙体的保温隔热、隔声效果。
【具体实施方式】
本发明涉及一种钢结构泡沫石膏复合墙体,所述钢结构泡沫石膏复合墙体的外部为钢板层,内部为泡沫石膏填充层;所述泡沫石膏填充层各组分的重量百分比如下:
β-半水石膏为45%~55%,三聚氰胺减水剂为0.1%~0.2%,柠檬酸为0.1%~0.3%,十二烷基硫酸钠为0.1%~0.2%,稳泡剂为0.05%~0.1%,羟丙基甲基纤维素醚为0.1%~0.2%,余量为水。
较优的,所述β-半水石膏为的重量百分比为50%。
下面结合实施例对本发明作进一步的说明。
实施例一:向装有50kgβ-半水石膏的搅拌设备中加入49.4kg水,向水中添加0.1kg三聚氰胺减水剂、0.15kg柠檬酸、0.15kg十二烷基磺酸钠、0.1kg稳泡剂、0.1kg羟丙基纤维素醚,即为泡沫石膏,再高速搅拌1分钟。最后,利用泵将搅拌好的泡沫石膏抽送填充到钢板层中。
实施例二:向装有50kgβ-半水石膏的搅拌设备中加入49kg水,向水中添加0.2kg三聚氰胺减水剂、0.3kg柠檬酸、0.2kg十二烷基磺酸钠、0.1kg稳泡剂、0.2kg羟丙基甲基纤维素醚,高速搅拌1分钟。最后,利用泵将搅拌好的泡沫石膏抽送填充到钢板层中。
实施例三:向装有50kgβ-半水石膏的搅拌设备中加入49kg水,向水中添加0.2kg三聚氰胺减水剂、0.1kg柠檬酸、0.15kg十二烷基磺酸钠、0.1kg稳泡剂、0.2kg羟丙基甲基纤维素醚,高速搅拌1分钟。最后,利用泵将搅拌好的泡沫石膏抽送填充到钢板层中。
本发明外层采用钢板层,能够解决常见的开裂空鼓等工程问题,并提高施工效率;泡沫石膏作为内填充,能够为解决玻璃棉对人体的损害,并实现整个墙体可循环使用,非常的节能环保;在操作过程中可采用泵送浇筑技术进行钢板层内泡沫石膏的填充,可进一步提高施工效率;发明采用特殊配比的泡沫石膏,水灰比可达1:1,大幅节省了石膏资源,其中,β-半水石膏可使用各种工业副产废渣石膏,实现了节能利废,更为环保;另外,泵送效果极佳,并且降低了墙体的自重,提高了墙体的保温隔热、隔声效果
虽然以上描述了本发明的具体实施方式,但是熟悉本技术领域的技术人员应当理解,我们所描述的具体的实施例只是说明性的,而不是用于对本发明的范围的限定,熟悉本领域的技术人员在依照本发明的精神所作的等效的修饰以及变化,都应当涵盖在本发明的权利要求所保护的范围内。
Claims (2)
1.一种钢结构泡沫石膏复合墙体,其特征在于:所述钢结构泡沫石膏复合墙体的外部为钢板层,内部为泡沫石膏填充层;所述泡沫石膏填充层各组分的重量百分比如下:
β-半水石膏为45%~55%,三聚氰胺减水剂为0.1%~0.2%,柠檬酸为0.1%~0.3%,十二烷基硫酸钠为0.1%~0.2%,稳泡剂为0.05%~0.1%,羟丙基甲基纤维素醚为0.1%~0.2%,余量为水。
2.根据权利要求1所述的一种钢结构泡沫石膏复合墙体,其特征在于:所述β-半水石膏的重量百分比为50%。