CN102995047A - 钢件洗涤剂 - Google Patents

钢件洗涤剂 Download PDF

Info

Publication number
CN102995047A
CN102995047A CN2012103929735A CN201210392973A CN102995047A CN 102995047 A CN102995047 A CN 102995047A CN 2012103929735 A CN2012103929735 A CN 2012103929735A CN 201210392973 A CN201210392973 A CN 201210392973A CN 102995047 A CN102995047 A CN 102995047A
Authority
CN
China
Prior art keywords
percent
steel part
washing composition
sodium
deionized water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103929735A
Other languages
English (en)
Other versions
CN102995047B (zh
Inventor
张志明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210392973.5A priority Critical patent/CN102995047B/zh
Publication of CN102995047A publication Critical patent/CN102995047A/zh
Application granted granted Critical
Publication of CN102995047B publication Critical patent/CN102995047B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种钢件洗涤剂，由以下重量百分比组分组成的清洗剂：4.6-8.9％月桂醇聚氧乙烯醚、2.3-4.6％正丁醇、1.4-5.1％三乙醇胺、5.7-8.9％草酸、4.9-9.4％肌醇六磷酸酯、3.3-5.4％硅酸钠、3.5-5.6％苯甲酸钠、2.8-4.5％十二烷基苯磺酸钠、3.8-4.1％钼酸钠、4.0-6.8％苯并三氮唑、3.5-6.5％消泡剂span80、余量为去离子水。本发明能快速去除钢件表面的污垢，而且不会腐蚀钢件，可使清洗后的钢件表面洁净如新，清洗效果显著。

Description

钢件洗涤剂
技术领域
本发明涉及一种钢件洗涤剂，属于清洁技术领域。
背景技术
据申请人了解，现有洗涤剂很难将钢件表面的油污彻底清洗干净。亟需一种针对性强的高效洗涤剂。
发明内容
本发明所要解决的技术问题是：克服现有技术存在的问题，提供一种钢件洗涤剂，能快速去除钢件表面的污垢，而且不会腐蚀钢件，可使清洗后的钢件表面洁净如新，清洗效果显著。
本发明解决其技术问题的技术方案如下：一种钢件洗涤剂，其特征是，由以下重量百分比的组分组成：
余量为去离子水。
上述洗涤剂的制备方法，包括以下步骤：
（1）在搅拌机内依次按重量百分比加入4.6-8.9％月桂醇聚氧乙烯醚、2.3-4.6％正丁醇、1.4-5.1％三乙醇胺、5.7-8.9％草酸、4.9-9.4％肌醇六磷酸酯、3.3-5.4％硅酸钠、3.5-5.6％苯甲酸钠、2.8-4.5％十二烷基苯磺酸钠、3.8-4.1％钼酸钠、4.0-6.8％苯并三氮唑、3.5-6.5％消泡剂span80；最后加入去离子水使总重量百分比为100％；
（2）搅拌均匀得洗涤剂成品。
采用上述洗涤剂的洗涤方法，包括以下步骤：
（1）采用由以下重量百分比组分组成的清洗剂：4.6-8.9％月桂醇聚氧乙烯醚、2.3-4.6％正丁醇、1.4-5.1％三乙醇胺、5.7-8.9％草酸、4.9-9.4％肌醇六磷酸酯、3.3-5.4％硅酸钠、3.5-5.6％苯甲酸钠、2.8-4.5％十二烷基苯磺酸钠、3.8-4.1％钼酸钠、4.0-6.8％苯并三氮唑、3.5-6.5％消泡剂span80、余量为去离子水；
（2）将所述洗涤剂倾倒至超声清洗槽内；
（3）将钢件放入超声清洗槽，于35℃-40℃条件下清洗3-5分钟；然后取出钢件，用清水将钢件表面冲洗干净，再晾干即完成清洗。
本发明申请人经过反复、深入地实验研究才得出采用上述配方的洗涤剂，该洗涤剂能快速去除钢件表面的污垢，而且不会腐蚀钢件，可使清洗后的钢件表面平滑光亮，清洗效率大于99％，是本发明申请人付出大量心血的结晶。
具体实施方式
下面结合实施例对本发明作进一步详细描述。但是本发明不限于所给出的例子。
实施例1
本实施例的钢件洗涤剂由以下重量百分比的组分组成：
Figure BDA00002264511400021
余量为去离子水。
上述洗涤剂的制备方法，包括以下步骤：
（1）在搅拌机内依次按重量百分比加入4.6％月桂醇聚氧乙烯醚、2.3％正丁醇、1.4％三乙醇胺、5.7％草酸、4.9％肌醇六磷酸酯、3.3％硅酸钠、3.5％苯甲酸钠、2.8％十二烷基苯磺酸钠、3.8％钼酸钠、4.0％苯并三氮唑、3.5％消泡剂span80；最后加入去离子水使总重量百分比为100％；
（2）搅拌均匀得洗涤剂成品。
采用上述洗涤剂的洗涤方法，包括以下步骤：
（1）采用由以下重量百分比组分组成的清洗剂：4.6％月桂醇聚氧乙烯醚、2.3％正丁醇、1.4％三乙醇胺、5.7％草酸、4.9％肌醇六磷酸酯、3.3％硅酸钠、3.5％苯甲酸钠、2.8％十二烷基苯磺酸钠、3.8％钼酸钠、4.0％苯并三氮唑、3.5％消泡剂span80、余量为去离子水；
（2）将所述洗涤剂倾倒至超声清洗槽内；
（3）将钢件放入超声清洗槽，于35℃-40℃条件下清洗3-5分钟；然后取出钢件，用清水将钢件表面冲洗干净，再晾干即完成清洗。
清洗后的钢件表面平滑光亮，清洗效率大于99％，效果显著。
实施例2
本实施例的钢件洗涤剂由以下重量百分比的组分组成：
余量为去离子水。
上述洗涤剂的制备方法，包括以下步骤：
（1）在搅拌机内依次按重量百分比加入8.9％月桂醇聚氧乙烯醚、4.6％正丁醇、5.1％三乙醇胺、8.9％草酸、9.4％肌醇六磷酸酯、5.4％硅酸钠、5.6％苯甲酸钠、4.5％十二烷基苯磺酸钠、4.1％钼酸钠、6.8％苯并三氮唑、6.5％消泡剂span80；最后加入去离子水使总重量百分比为100％；
（2）搅拌均匀得洗涤剂成品。
采用上述洗涤剂的洗涤方法，包括以下步骤：
（1）采用由以下重量百分比组分组成的清洗剂：8.9％月桂醇聚氧乙烯醚、4.6％正丁醇、5.1％三乙醇胺、8.9％草酸、9.4％肌醇六磷酸酯、5.4％硅酸钠、5.6％苯甲酸钠、4.5％十二烷基苯磺酸钠、4.1％钼酸钠、6.8％苯并三氮唑、6.5％消泡剂span80、余量为去离子水；
（2）将所述洗涤剂倾倒至超声清洗槽内；
（3）将钢件放入超声清洗槽，于35℃-40℃条件下清洗3-5分钟；然后取出钢件，用清水将钢件表面冲洗干净，再晾干即完成清洗。
清洗后的钢件表面平滑光亮，清洗效率大于99％，效果显著。
实施例3
本实施例的钢件洗涤剂由以下重量百分比的组分组成：
Figure BDA00002264511400041
余量为去离子水。
上述洗涤剂的制备方法，包括以下步骤：
（1）在搅拌机内依次按重量百分比加入5.3％月桂醇聚氧乙烯醚、3.2％正丁醇、2.5％三乙醇胺、6.1％草酸、5.4％肌醇六磷酸酯、4.6％硅酸钠、4.2％苯甲酸钠、3.2％十二烷基苯磺酸钠、3.9％钼酸钠、4.9％苯并三氮唑、4.2％消泡剂span80；最后加入去离子水使总重量百分比为100％；
（2）搅拌均匀得洗涤剂成品。
采用上述洗涤剂的洗涤方法，包括以下步骤：
（1）采用由以下重量百分比组分组成的清洗剂5.3％月桂醇聚氧乙烯醚、3.2％正丁醇、2.5％三乙醇胺、6.1％草酸、5.4％肌醇六磷酸酯、4.6％硅酸钠、4.2％苯甲酸钠、3.2％十二烷基苯磺酸钠、3.9％钼酸钠、4.9％苯并三氮唑、4.2％消泡剂span80、余量为去离子水；
（2）将所述洗涤剂倾倒至超声清洗槽内；
（3）将钢件放入超声清洗槽，于35℃-40℃条件下清洗3-5分钟；然后取出钢件，用清水将钢件表面冲洗干净，再晾干即完成清洗。
清洗后的钢件表面平滑光亮，清洗效率大于99％，效果显著。
实施例4
本实施例的钢件洗涤剂由以下重量百分比的组分组成：
余量为去离子水。
上述洗涤剂的制备方法，包括以下步骤：
（1）在搅拌机内依次按重量百分比加入7.6％月桂醇聚氧乙烯醚、4.1％正丁醇、3.5％三乙醇胺、7.5％草酸、8.2％肌醇六磷酸酯、5.1％硅酸钠、5.2％苯甲酸钠、4.1％十二烷基苯磺酸钠、4.0％钼酸钠、6.1％苯并三氮唑、5.4％消泡剂span80；最后加入去离子水使总重量百分比为100％；
（2）搅拌均匀得洗涤剂成品。
采用上述洗涤剂的洗涤方法，包括以下步骤：
（1）采用由以下重量百分比组分组成的清洗剂7.6％月桂醇聚氧乙烯醚、4.1％正丁醇、3.5％三乙醇胺、7.5％草酸、8.2％肌醇六磷酸酯、5.1％硅酸钠、5.2％苯甲酸钠、4.1％十二烷基苯磺酸钠、4.0％钼酸钠、6.1％苯并三氮唑、5.4％消泡剂span80、余量为去离子水；
（2）将所述洗涤剂倾倒至超声清洗槽内；
（3）将钢件放入超声清洗槽，于35℃-40℃条件下清洗3-5分钟；然后取出钢件，用清水将钢件表面冲洗干净，再晾干即完成清洗。
清洗后的钢件表面平滑光亮，清洗效率大于99％，效果显著。

Claims (3)

1.一种钢件洗涤剂，其特征是，由以下重量百分比的组分组成：
Figure FDA00002264511300011
余量为去离子水。
2.根据权利要求1所述的钢件洗涤剂，其特征是，由以下重量百分比的组分组成：
Figure FDA00002264511300012
余量为去离子水。
3.根据权利要求1所述的钢件洗涤剂，其特征是，由以下重量百分比的组分组成：
Figure FDA00002264511300013
Figure FDA00002264511300021
余量为去离子水。
CN201210392973.5A 2012-10-17 2012-10-17 钢件洗涤剂 Expired - Fee Related CN102995047B (zh)