CN102994808A - 一种镍铬合金的制备方法 - Google Patents

一种镍铬合金的制备方法 Download PDF

Info

Publication number
CN102994808A
CN102994808A CN 201210411322 CN201210411322A CN102994808A CN 102994808 A CN102994808 A CN 102994808A CN 201210411322 CN201210411322 CN 201210411322 CN 201210411322 A CN201210411322 A CN 201210411322A CN 102994808 A CN102994808 A CN 102994808A
Authority
CN
China
Prior art keywords
nickel
nichrome
chromium alloy
chromium
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210411322
Other languages
English (en)
Inventor
李翠
栾清杨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201210411322 priority Critical patent/CN102994808A/zh
Publication of CN102994808A publication Critical patent/CN102994808A/zh
Pending legal-status Critical Current

Abstract

一种镍铬合金的制备方法，属于有色金属材料技术领域，包括如下步骤：包括如下步骤：(1)备料；(2)溶化；(3)采用熔化炉将镍铬合金中的除镍和铬金属以外的其它合金元素金属在大气下或者真空、或者惰性气体保护下熔化，然后再进行精炼，精炼结束后将熔液温度维持在3000～5600℃；(4)将镍铬合金熔液从静置保温炉中浇注到充分预热过的金属型铸造模具中凝固成铸锭;或者将镍铬合金熔液输送到结晶器中，进行连续或半连续铸造。本发明的优点：采用此方法镍铬氧化和烧损比较小，能耗低，成品率高。

Description

一种镍铬合金的制备方法
技术领域
本发明属于有色金属材料技术领域，特别涉及一种镍铬合金的制备方法。 
背景技术
镍铬合金的传统熔炼方法是采用熔化炉先将所要熔炼的镍和铬一次全部熔化，然后将其它合金元素以纯金属或中间合金的形式直接加入到镍铬熔液中进行合金化。由于全部镍铬同时升温熔化，镍铬氧化和烧损比较大；由于熔化温度升高、延长熔化时间，加剧了镍铬合金熔炼过程中的氧化和烧损。 
发明内容
针对现有技术的不足，本发明提供一种镍铬合金的制备方法。 
本发明的制备方法包括如下步骤： 
    (1)、备料
按所要制备的镍和铬合金进行备料；
(2)、溶化
在熔化炉将镍和铬进行溶化，温度控制在3000～7500℃；合金化炉温度控制在2000～5000℃；
    (3)、采用熔化炉将镍铬合金中的除镍和铬金属以外的其它合金元素金属在大气下或者真空、或者惰性气体保护下熔化，然后再进行精炼，精炼结束后将熔液温度维持在3000～5600℃；
 (4)、将镍铬合金熔液从静置保温炉中浇注到充分预热过的金属型铸造模具中凝固成铸锭;或者将镍铬合金熔液输送到结晶器中，进行连续或半连续铸造。
本发明的优点：采用此方法镍铬氧化和烧损比较小，能耗低，成品率高。 
具体实施方式
本发明详细结构结合实施例加以说明。 
该包括如下步骤： 
(1)、备料
按所要制备的镍和铬合金进行备料；
(2)、溶化
在熔化炉将镍和铬进行溶化，温度控制在5000℃；合金化炉温度控制在3500℃；
    (3)、采用熔化炉将镍铬合金中的除镍铬金属以外的其它合金元素金属在大气下或者真空、或者惰性气体保护下熔化，然后再进行精炼，精炼结束后将熔液温度维持在4000℃；
 (4)、将镍铬合金熔液从静置保温炉中浇注到充分预热过的金属型铸造模具中凝固成铸锭;或者将镍铬合金熔液输送到结晶器中，进行连续或半连续铸造。

Claims (1)

1.一种镍铬合金的制备方法，其特征在于：包括如下步骤：
(1)、备料
按所要制备的镍和铬合金进行备料；
(2)、溶化
在熔化炉将镍和铬进行溶化，温度控制在3000～7500℃；合金化炉温度控制在2000～5000℃；
    (3)、采用熔化炉将镍铬合金中的除镍和铬金属以外的其它合金元素金属在大气下或者真空、或者惰性气体保护下熔化，然后再进行精炼，精炼结束后将熔液温度维持在3000～5600℃；
 (4)、将镍铬合金熔液从静置保温炉中浇注到充分预热过的金属型铸造模具中凝固成铸锭;或者将镍铬合金熔液输送到结晶器中，进行连续或半连续铸造。
CN 201210411322 2012-10-25 2012-10-25 一种镍铬合金的制备方法 Pending CN102994808A (zh)