CN102993845A - Wooden floor care agent - Google Patents
Wooden floor care agent Download PDFInfo
- Publication number
- CN102993845A CN102993845A CN2012104960260A CN201210496026A CN102993845A CN 102993845 A CN102993845 A CN 102993845A CN 2012104960260 A CN2012104960260 A CN 2012104960260A CN 201210496026 A CN201210496026 A CN 201210496026A CN 102993845 A CN102993845 A CN 102993845A
- Authority
- CN
- China
- Prior art keywords
- styrene
- deionized water
- diethylene glycol
- care agent
- nursing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a wooden floor care agent which comprises the following components in percentage by weight: 3%-6% of carnauba wax, 1%-5% of turpentine, 2%-5% of silicone oil, 0.5%-2% of camellia oil, 0.1%-0.3% of polyoxyethylene sorbitan monooleate, 3.5%-4.5% of styrene-acrylic resin, 5%-10% of diethylene glycol ether and the balance of deionized water. The wooden floor care agent disclosed by the invention can form a protecting film on the floor, thereby ensuring that the floor is bright and reduced in abrasion without skidding.
Description
Technical field
The present invention relates to a kind of wood floors nursing agent.
Background technology
Wood Flooring Industry is an emerging industry.Timber floor becomes the preferred material that people ground is modified with advantages such as its comfortable foot feeling, naturally warm, cool in summer and warm in winter, elegants.But timber floor all the situations such as wearing and tearing, distortion, protuberance can occur after using the several years, greatly affect the overall appearance in room.The both expensive of replaceable wooden floor more is so the daily maintenance of timber floor is extremely important.Although existing floor nursing agent is of a great variety, mostly existing needs polishing, the shortcoming of easily skidding.
Summary of the invention
The purpose of this invention is to provide a kind of wood floors nursing agent.This nursing agent can form protective membrane at wood floors, need not to polish and can not skid.
Wood floors nursing agent of the present invention is comprised of the component of following weight percent:
| Carnauba wax | 3-6% |
| Turps | 1-5% |
| Silicone oil | 2-5% |
| Camellia oil | 0.5-2% |
| Polyoxyethylenesorbitan sorbitan monooleate | 0.1-0.3% |
| The styrene-propene acid resin | 3.5-4.5% |
| Diethylene glycol ethyl ether | 5-10% |
| Surplus is deionized water. | ? |
The preparation method of above-mentioned wood floors nursing agent may further comprise the steps:
(1) 3-6% carnauba wax, 1-5% turps, 2-5% silicone oil, 0.5-2% Camellia oil, 3.5-4.5% styrene-propene acid resin and 5-10% diethylene glycol ethyl ether are mixed, be heated to 85-90 ℃, stir;
(2) add 0.1-0.3% polyoxyethylenesorbitan sorbitan monooleate and add deionized water and complement to 100% in the mixture of step (1);
(3) mixture with step (2) is heated to approximately 80 ℃ in emulsor, and vigorous stirring makes its emulsification, gets product after being down to room temperature.
Embodiment
Below in conjunction with embodiment the present invention is described in further detail.But the invention is not restricted to given example.
Embodiment 1
The wood floors nursing agent of the present embodiment is comprised of the component of following weight percent:
| Carnauba wax | 3% |
| Turps | 1% |
| Silicone oil | 2% |
| Camellia oil | 0.5% |
| Polyoxyethylenesorbitan sorbitan monooleate | 0.1% |
| The styrene-propene acid resin | 3.5% |
| Diethylene glycol ethyl ether | 5% |
| Surplus is deionized water. | ? |
The preparation method of the wood floors nursing agent of the present embodiment may further comprise the steps:
(1) 3% carnauba wax, 1% turps, 2% silicone oil, 0.5% Camellia oil, 3.5% styrene-propene acid resin and 5% diethylene glycol ethyl ether are mixed, be heated to 85-90 ℃, stir;
(2) add 0.1% polyoxyethylenesorbitan sorbitan monooleate and add deionized water and complement to 100% in the mixture of step (1);
(3) mixture with step (2) is heated to approximately 80 ℃ in emulsor, and vigorous stirring makes its emulsification, gets product after being down to room temperature.
Embodiment 2
The wood floors nursing agent of the present embodiment is comprised of the component of following weight percent:
| Carnauba wax | 4% |
| Turps | 2% |
| Silicone oil | 3% |
| Camellia oil | 1.5% |
| Polyoxyethylenesorbitan sorbitan monooleate | 0.2% |
| The styrene-propene acid resin | 4.0% |
| Diethylene glycol ethyl ether | 6% |
| Surplus is deionized water. | ? |
The preparation method of the wood floors nursing agent of the present embodiment may further comprise the steps:
(1) 4% carnauba wax, 2% turps, 3% silicone oil, 1.5% Camellia oil, 4.0% styrene-propene acid resin and 6% diethylene glycol ethyl ether are mixed, be heated to 85-90 ℃, stir;
(2) add 0.2% polyoxyethylenesorbitan sorbitan monooleate and add deionized water and complement to 100% in the mixture of step (1);
(3) mixture with step (2) is heated to approximately 80 ℃ in emulsor, and vigorous stirring makes its emulsification, gets product after being down to room temperature.
Embodiment 3
The vehicle glass water of the present embodiment is comprised of the component of following weight percent:
| Carnauba wax | 6% |
| Turps | 5% |
| Silicone oil | 5% |
| Camellia oil | 2% |
| Polyoxyethylenesorbitan sorbitan monooleate | 0.3% |
| The styrene-propene acid resin | 4.5% |
| Diethylene glycol ethyl ether | 10% |
| Surplus is deionized water. | ? |
The preparation method of the wood floors nursing agent of the present embodiment may further comprise the steps:
(1) 6% carnauba wax, 5% turps, 5% silicone oil, 2% Camellia oil, 4.5% styrene-propene acid resin and 10% diethylene glycol ethyl ether are mixed, be heated to 85-90 ℃, stir;
(2) add 0.3% polyoxyethylenesorbitan sorbitan monooleate and add deionized water and complement to 100% in the mixture of step (1);
(3) mixture with step (2) is heated to approximately 80 ℃ in emulsor, and vigorous stirring makes its emulsification, gets product after being down to room temperature.
During use, wood floors nursing agent of the present invention is sprayed on the floor gets final product.Wood floors nursing agent of the present invention can form protective membrane on the floor, makes the floor light, reduces wear, and can not skid.
Claims (2)
1. a wood floors nursing agent is characterized in that, and is composed of the following components:
Carnauba wax 3-6%
Turps 1-5%
Silicone oil 2-5%
Camellia oil 0.5-2%
Polyoxyethylenesorbitan sorbitan monooleate 0.1-0.3%
Styrene-propene acid resin 3.5-4.5%
Diethylene glycol ethyl ether 5-10%
Surplus is deionized water.
2. wood floors nursing agent as claimed in claim 1 is characterized in that, and is composed of the following components:
Carnauba wax 4%
Turps 2%
Silicone oil 3%
Camellia oil 1.5%
Polyoxyethylenesorbitan sorbitan monooleate 0.2%
Styrene-propene acid resin 4.0%
Diethylene glycol ethyl ether 6%
Surplus is deionized water.