CN102993403A - 聚氨酯组合料及其制备方法 - Google Patents

聚氨酯组合料及其制备方法 Download PDF

Info

Publication number
CN102993403A
CN102993403A CN2012105664601A CN201210566460A CN102993403A CN 102993403 A CN102993403 A CN 102993403A CN 2012105664601 A CN2012105664601 A CN 2012105664601A CN 201210566460 A CN201210566460 A CN 201210566460A CN 102993403 A CN102993403 A CN 102993403A
Authority
CN
China
Prior art keywords
group
polyurethane combined
group material
parts
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012105664601A
Other languages
English (en)
Inventor
莫维永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jiatai Coal Mining Technology Co Ltd
Original Assignee
Anhui Jiatai Coal Mining Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jiatai Coal Mining Technology Co Ltd filed Critical Anhui Jiatai Coal Mining Technology Co Ltd
Priority to CN2012105664601A priority Critical patent/CN102993403A/zh
Publication of CN102993403A publication Critical patent/CN102993403A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种聚氨酯组合料及其制备方法，它由A组物料和B组物料组成，A组物料含有按质量份计：10-70份的聚醚5-10份的三乙烯二胺、1-10份的阻燃剂DMMP和70-10份的石粉；B组物料含有按质量份计：10-90份的异氰酸酯和90-10的石粉，将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料；本发明的聚氨酯组合料与现有的聚脲弹性体相比具有高阻燃、低反应热、抗静电等特点，该聚氨酯组合料可代替传统聚脲弹性体广泛应用于煤矿锚喷支护、锚固、煤岩体加固、密闭、封堵、抢险、防水、建筑、水电、隧道、地铁等领域。

Description

聚氨酯组合料及其制备方法
技术领域
本发明涉及一种混凝土及其制备方法，特别是一种聚氨酯组合料及其制备方法。
背景技术
聚脲弹性体也称SPUA，是国外近十年来，为适应环保需求而研发的一种新型施工材料。传统聚脲弹性体在煤矿煤岩体加固等方面已经得到应用，但是内部反应温度高，经常给煤矿生产带来安全隐患，同时成本高。
发明内容
本申请的发明目的在于克服现有的聚脲弹性体的缺点，而提供一种聚氨酯组合料及其制备方法。
为了完成本申请的发明目的，本申请采用以下技术方案：
本发明一种聚氨酯组合料，它由A组物料和B组物料组成，其中：
A组物料按质量份计的组份如下：
B组物料按质量比计的组份如下：
异氰酸酯    10-70份
石粉        70-10份
将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料；
本发明的聚氨酯组合料，其中：所述的A组物料还包括：按质量份计1-30份的导电石墨；
本发明的聚氨酯组合料，其中：所述的B组物料还包括：按质量份计1-30份的导电石墨；
本发明的聚氨酯组合料，其中：所述聚醚的羟值在1至1000之间，它是一种或几种聚醚的混合物；所述异氰酸酯是聚氨酯黑料中的任何一种；
本发明的聚氨酯组合料，其中：所述石粉目数在20目以上；导电石墨的目数在80目以上；
本发明制备聚氨酯组合料的方法，包括以下步骤：
（1）A组物料的制备方法：
在常温条件下，将所述聚醚、三乙烯二胺和阻燃剂DMMP按比例混合并且搅拌均匀后；再加入石粉，充分搅拌，使沉淀物完全悬浮，得到A组物料；
（2）B组物料的制备方法：
将石粉按比例加入到异氰酸酯中，搅拌均匀后得到B组物料；
（3）将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料。
本发明的聚氨酯组合料与现有的聚脲弹性体相比具有高阻燃、低反应热、抗静电等特点，本发明由于无机物的添加，一是可以大大降低了生产成本。石粉仅是异氰酸酯或聚醚的单价的二十分之一；二是降低了反应温度。无机物减缓了反应速度，而且其散热均匀（石粉比聚脲弹性体热传导系数大的多）。该聚氨酯组合料可代替传统聚脲弹性体广泛应用于煤矿锚喷支护、锚固、煤岩体加固、密闭、封堵、抢险、防水、建筑、水电、隧道、地铁等领域。
具体实施方式
实施例1
本发明聚氨酯组合料，它由A组物料和B组物料组成，其中：
A组物料按质量份计的组份如下：
Figure BDA00002641862700021
B组物料按质量比计的组份如下：
异氰酸酯    10-70份
石粉        70-10份
将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料。
聚醚的羟值在1至1000之间，它是一种或几种聚醚的混合物；如江苏钟山化工有限公司生产的聚醚，其商品牌号可以是N-403，ZS-4110等等其中的一种或几种的混合物。异氰酸酯是聚氨酯黑料中的任何一种，如MDI M20S，5005，44V20，PM-200，M200等等。石粉目数应在20目以上。
制备聚氨酯组合料的方法，它包括以下步骤：
（1）A组物料的制备方法：
在常温条件下，将上述聚醚、三乙烯二胺和阻燃剂DMMP按比例混合并且搅拌均匀后；再加入石粉，充分搅拌，使沉淀物完全悬浮，得到A组物料；
（2）B组物料的制备方法：
将石粉按比例加入到异氰酸酯中，搅拌均匀后得到B组物料；
（3）将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料。
实施例2
A组物料按质量份计的组份如下：
B组物料按质量比计的组份如下：
异氰酸酯    10-70份
石粉        70-10份
导电石墨    1-30份
将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料。
聚醚的羟值在1至1000之间，它是一种或几种聚醚的混合物；如江苏钟山化工有限公司生产的聚醚，其商品牌号可以是N-403，ZS-4110等等其中的一种或几种的混合物。异氰酸酯是聚氨酯黑料中的任何一种，如MDI M20S，5005，44V20，PM-200，M200等等。石粉目数应在20目以上。导电石墨的目数应在80目以上。
制备聚氨酯组合料的方法，它包括以下步骤：
（1）A组物料的制备方法：
在常温条件下，将所述聚醚、导电石墨、三乙烯二胺和阻燃剂DMMP按比例混合并且搅拌均匀后；再加入石粉，充分搅拌，使沉淀物完全悬浮，得到A组物料；
（2）B组物料的制备方法：
将石粉和导电石墨按比例加入到异氰酸酯中，搅拌均匀后得到B组物料；
（3）将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料。
实施例1和实施例2的区别在于：在实施例2中的A和B物料中均加入了导电石墨。
按照国家安全生产北京矿山井下设备与油品检测中心制定的《煤矿用高分子化学煤岩体加固剂（征求意见稿）》对所得聚氨酯组合料进行了检测，得到下列数据：
Figure BDA00002641862700041
以上描述是对本发明的解释，不是对发明的限定，本发明所限定的范围参见权利要求，在不违背本发明的精神的情况下，本发明可以作任何形式的修改。

Claims (10)

1.一种聚氨酯组合料，其特征在于：它由A组物料和B组物料组成，其中： 
A组物料按质量份计的组份如下： 
Figure FDA00002641862600011
B组物料按质量比计的组份如下： 
异氰酸酯    10-70份 
石粉        70-10份 
将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料。 
2.根据权利要求1所述的聚氨酯组合料，其特征在于：所述的A组物料还包括：按质量份计1-30份的导电石墨。 
3.根据权利要求1或2所述的聚氨酯组合料，其特征在于：所述的B组物料还包括：按质量份计1-30份的导电石墨。 
4.根据权利要求3所述的聚氨酯组合料，其特征在于：所述聚醚的羟值在1至1000之间，它是一种或几种聚醚的混合物；所述异氰酸酯是聚氨酯黑料中的任何一种。 
5.根据权利要求4所述的聚氨酯组合料，其特征在于：所述石粉目数在20目以上；导电石墨的目数在80目以上。 
6.一种制备如权利要求1所述聚氨酯组合料的方法，其包括以下步骤： 
（1）A组物料的制备方法： 
在常温条件下，将所述聚醚、三乙烯二胺和阻燃剂DMMP按比例混合并且搅拌均匀后；再加入石粉，充分搅拌，使沉淀物完全悬浮，得到A组物料； 
（2）B组物料的制备方法： 
将石粉按比例加入到异氰酸酯中，搅拌均匀后得到B组物料； 
（3）将上述等质量的A组物料与上述等质量的B组物料混合均匀，得到本发明的聚氨酯组合料。 
7.根据权利要求6所述聚氨酯组合料的制备方法，其特征在于：所述步骤（1）中，将按质量份计1-30份的导电石墨加入所述聚醚、三乙烯二胺和阻燃剂DMMP中混合并且搅拌均匀后；再加入石粉。 
8.根据权利要求6或7所述聚氨酯组合料的制备方法，其特征在于：所述B组物料的制备方法的中还加入按质量份计1-30份的导电石墨。 
9.根据权利要求8所述的聚氨酯组合料，其特征在于：所述聚醚的羟值在1至1000之间，它是一种或几种聚醚的组合物；所述异氰酸酯是聚氨酯黑料中的任何一种。 
10.根据权利要求9所述的聚氨酯组合料，其特征在于：所述石粉目数在20目以上；导电石墨的目数在80目以上。 
CN2012105664601A 2012-12-24 2012-12-24 聚氨酯组合料及其制备方法 Pending CN102993403A (zh)