CN102977853A - 一种含有橄榄的汽车玻璃防雾剂的制备方法 - Google Patents
一种含有橄榄的汽车玻璃防雾剂的制备方法 Download PDFInfo
- Publication number
- CN102977853A CN102977853A CN 201210512131 CN201210512131A CN102977853A CN 102977853 A CN102977853 A CN 102977853A CN 201210512131 CN201210512131 CN 201210512131 CN 201210512131 A CN201210512131 A CN 201210512131A CN 102977853 A CN102977853 A CN 102977853A
- Authority
- CN
- China
- Prior art keywords
- olive
- reactor
- agent
- deionized water
- chlor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种汽车玻璃防雾剂的制备方法,具体讲是涉及一种含有橄榄的汽车玻璃防雾剂的制备方法,其属于防雾剂领域,其原料为:明矾、橄榄油、氯化钠、硅酸镁、甜菜碱、乙醇、甘油和去离子水,各个组分都是对人体没有危害的,其中不含有任何污染环境和对人体不低的成分,并且以乙醇和去离子水为溶剂,使得个物质充分溶解在溶剂中,很好的去除玻璃上的雾气,并且制作简单,使用寿命长。
Description
技术领域
本发明涉及一种汽车玻璃防雾剂的制备方法,具体讲是涉及一种含有橄榄的汽车玻璃防雾剂的制备方法,其属于防雾剂领域。
背景技术
汽车玻璃在潮湿空气或寒凉环境下,由于车内温度高于车外温度,空气中的水蒸汽在玻璃表面遇冷凝结,形成雾滴,影响视线。汽车上设有风机,可向挡风玻璃吹风,通过加速空气流动,以利于水雾蒸发,但其效果不好,不能彻底除雾。
发明内容
鉴于现有技术存在的问题,本发明的目的是要提供一种简单、安全的含有橄榄的汽车玻璃防雾剂的制备方法。
为了实现上述目的,本发明所采用的技术方案是一种含有橄榄的汽车玻璃防雾剂的制备方法,其原料为:明矾、橄榄油、氯化钠、硅酸镁、甜菜碱、乙醇、甘油和去离子水,各个物质的重量百分比为:明矾1~10%、橄榄油0.5~5%、氯化钠3~10%、硅酸镁2~6%、甜菜碱5~8%、乙醇8~15%、甘油3~6%和余量去离子水;其步骤如下:
1)将去离子水和乙醇按比例混合;
2)步骤1)的混合液加入反应釜内,并向反应釜内加入氯化钠,在10~15度条件下搅拌,直至氯化钠完全溶解;
3)向反应釜内加入硅酸镁和明矾,搅拌均匀,在加入甜菜碱搅拌;
4)向反应釜内加入橄榄油和甘油,在10度条件下搅拌10分钟,静置20分钟,将反应釜升温至15度,在搅拌30分钟,静置2~3小时;
5)过滤制得成品。
所述去离子水为水通过220伏50Hz电源产生频率的2M以上的高频电场作用,发生物理变化制得的。
本发明的优点在于:各个组分都是对人体没有危害的,其中不含有任何污染环境和对人体不低的成分,并且以乙醇和去离子水为溶剂,使得个物质充分溶解在溶剂中,很好的去除玻璃上的雾气,并且制作简单,使用寿命长。
具体实施方式
一种含有橄榄的汽车玻璃防雾剂的制备方法,其原料为:明矾、橄榄油、氯化钠、硅酸镁、甜菜碱、乙醇、甘油和去离子水,各个物质的重量百分比为:明矾1~10%、橄榄油0.5~5%、氯化钠3~10%、硅酸镁2~6%、甜菜碱5~8%,乙醇8~15%、甘油3~6%和余量去离子水;其步骤如下:
1)将去离子水和乙醇按比例混合;
2)步骤1)的混合液加入反应釜内,并向反应釜内加入氯化钠,在10~15度条件下搅拌,直至氯化钠完全溶解;
3)向反应釜内加入硅酸镁和明矾,搅拌均匀,在加入甜菜碱搅拌;
4)向反应釜内加入橄榄油和甘油,在10度条件下搅拌10分钟,静置20分钟,将反应釜升温至15度,在搅拌30分钟,静置2~3小时;
5)过滤制得成品。
Claims (2)
1.一种含有橄榄的汽车玻璃防雾剂的制备方法,其原料为:明矾、橄榄油、氯化钠、硅酸镁、甜菜碱、乙醇、甘油和去离子水,各个物质的重量百分比为:明矾1~10%、橄榄油0.5~5%、氯化钠3~10%、硅酸镁2~6%、甜菜碱5~8%、乙醇8~15%、甘油3~6%和余量去离子水;其步骤如下:
1)将去离子水和乙醇按比例混合;
2)步骤1)的混合液加入反应釜内,并向反应釜内加入氯化钠,在10~15度条件下搅拌,直至氯化钠完全溶解;
3)向反应釜内加入硅酸镁和明矾,搅拌均匀,在加入甜菜碱搅拌;
4)向反应釜内加入橄榄油和甘油,在10度条件下搅拌10分钟,静置20分钟,将反应釜升温至15度,在搅拌30分钟,静置2~3小时;
5)过滤制得成品。
2.根据权利要求1所述的一种含有橄榄的汽车玻璃防雾剂的制备方法,其特征在于:所述去离子水为水通过220伏50Hz电源产生频率的2M以上的高频电场作用,发生物理变化制得的。