CN102977737A - Reflective coating for pavement - Google Patents
Reflective coating for pavement Download PDFInfo
- Publication number
- CN102977737A CN102977737A CN2012104230982A CN201210423098A CN102977737A CN 102977737 A CN102977737 A CN 102977737A CN 2012104230982 A CN2012104230982 A CN 2012104230982A CN 201210423098 A CN201210423098 A CN 201210423098A CN 102977737 A CN102977737 A CN 102977737A
- Authority
- CN
- China
- Prior art keywords
- parts
- lacquer
- pavement
- coats
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a reflective coating for a pavement. The reflective coating comprises, by weight, 15 to 25 parts of an epoxy resin, 10 to 13 parts of ethylene glycol monoethyl acetate, 5 to 8 parts of a polyamide resin, 8 to 12 parts of coal tar pitch, 3 to 5 parts of chlorinated paraffin, 4 to 8 parts of calcium carbonate, 5 to 8 parts of methyl isobutyl ketone, 1 to 5 parts of gypsum, 8 to 10 parts of an acrylate resin, 10 to 15 parts of fluorescent powder, 3 to 10 parts of a photoinitiator, 2 to 5 parts of an antifoaming agent, 0.8 to 2.5 parts of m-phenylenediamine, 3 to 8 parts of a pigment and 10 to 20 parts of a solvent, wherein the antifoaming agent is emulsified silicone oil or n-octyl alcohol, the pigment is one or more selected from the group consisting of titanium dioxide, iron oxide red, carbon black and talcum powder, the photoinitiator is benzoin methyl ether or chlorinated acetophenone, and the solvent is glycol or xylene. The reflective coating for the pavement has strong wear resistant and pressure resistance and strong reflective capability.
Description
Technical field
The invention provides a kind of pavement reflecting lacquer, belong to technical field of coatings.
Background technology
Raising along with people's living standard, private car is more and more, traffic accident also increases thereupon, wherein the road surface indicatrix is unclear also is one of reason of accident generation, and when especially the light such as rainy day, greasy weather or night were bad, the effect of road surface indicatrix was particularly important, double amber lines, single yellow line or white dashed line etc., be directly connected to the driver's driving circuit, if not giving up the place head hastily of head, will certainly increase the danger that collides with the back car.Because wear resistance, the resistance to pressure of prevailing roadway lacquer are inadequate, can not adapt to now current condition bustling with vehicles, therefore usually to will again draw road sign every for some time, waste time and energy, cause the waste of manpower and materials.
Summary of the invention
The purpose of this invention is to provide a kind of pavement reflecting lacquer, have strong wear-resisting withstand voltage properties, and have strong reflecting power, when the light such as rainy day, greasy weather or night are bad, still can clearly bring into play the effect of road sign.
To achieve these goals, technical scheme of the present invention is: a kind of pavement reflecting lacquer, include following component by weight: 15～25 parts of Resins, epoxy, 10～13 parts of ethylene glycol ether esters, 5～8 parts of polyamide resins, 8～12 parts of coal tar pitches, 3～5 parts of clorafins, 4～8 parts in calcium carbonate, 5～8 parts of methyl iso-butyl ketone (MIBK), 1～5 part in gypsum, 8～10 parts of acrylate resins, 10 ~ 15 parts in fluorescent material, 3 ~ 10 parts of light triggers, 2 ~ 5 parts of defoamers, 0.8 ~ 2.5 part of mphenylenediamine, 3 ~ 8 parts of pigment, 10～20 parts of solvents.
Described defoamer is silicone emulsion or n-Octanol.
Described pigment is one or several in titanium dioxide or red iron oxide or carbon black or the talcum powder.
Described light trigger is benzoin methyl ether or chloroacetophenone.
Described solvent is ethylene glycol or dimethylbenzene.
Preparation method: solvent, Resins, epoxy, ethylene glycol ether ester, polyamide resin, acrylate resin are mixed in proportion to get mixture A, then coal tar pitch, clorafin, methyl iso-butyl ketone (MIBK), gypsum are heated to 160 ~ 200 ℃ of complete miscibilities and get solution B, with A in B and calcium carbonate fluorescent material, light trigger, defoamer, mphenylenediamine, pigment are mixed and heated to 120 ℃, stir 3 ~ 5h, get finished product.
A kind of pavement reflecting lacquer provided by the invention has strong wear-resisting withstand voltage properties, and has strong reflecting power, still can clearly bring into play the effect of road sign when the light such as rainy day, greasy weather or night are bad.
Embodiment
Embodiment 1:
A kind of pavement reflecting lacquer, include following component by weight: 15 parts of Resins, epoxy, 13 parts of ethylene glycol ether esters, 5 parts of polyamide resins, 12 parts of coal tar pitches, 3 parts of clorafins, 8 parts in calcium carbonate, 5 parts of methyl iso-butyl ketone (MIBK), 5 parts in gypsum, 8 parts of acrylate resins, 15 parts in fluorescent material, 3 parts of chloroacetophenones, 5 parts of silicone emulsions, 2.5 parts of mphenylenediamines, 3 parts of titanium dioxides, 2 parts of carbon blacks, 3 parts of talcum powder, 20 parts of solvent ethylene glycol.
Embodiment 2:
A kind of pavement reflecting lacquer, include following component by weight: 25 parts of Resins, epoxy, 10 parts of ethylene glycol ether esters, 8 parts of polyamide resins, 8 parts of coal tar pitches, 5 parts of clorafins, 4 parts in calcium carbonate, 8 parts of methyl iso-butyl ketone (MIBK), 1 part in gypsum, 10 parts of acrylate resins, 10 parts in fluorescent material, 10 parts of benzoin methyl ethers, 2 parts of n-Octanols, 0.8 part of mphenylenediamine, 3 parts of red iron oxides, 10 parts of solvent xylenes.
Claims (5)
1. a pavement reflecting coats with lacquer, include following component by weight: 15～25 parts of Resins, epoxy, 10～13 parts of ethylene glycol ether esters, 5～8 parts of polyamide resins, 8～12 parts of coal tar pitches, 3～5 parts of clorafins, 4～8 parts in calcium carbonate, 5～8 parts of methyl iso-butyl ketone (MIBK), 1～5 part in gypsum, 8～10 parts of acrylate resins, 10 ~ 15 parts in fluorescent material, 3 ~ 10 parts of light triggers, 2 ~ 5 parts of defoamers, 0.8 ~ 2.5 part of mphenylenediamine, 3 ~ 8 parts of pigment, 10～20 parts of solvents.
2. pavement reflecting according to claim 1 coats with lacquer, and it is characterized in that: described defoamer is silicone emulsion or n-Octanol.
3. pavement reflecting according to claim 1 coats with lacquer, and it is characterized in that: described pigment is one or several in titanium dioxide or red iron oxide or carbon black or the talcum powder.
4. pavement reflecting according to claim 1 coats with lacquer, and it is characterized in that: described light trigger is benzoin methyl ether or chloroacetophenone.
5. pavement reflecting according to claim 1 coats with lacquer, and it is characterized in that: described solvent is ethylene glycol or dimethylbenzene.