CN102965924A - 一种糟朽丝绸文物的氨基酸接枝加固法 - Google Patents

一种糟朽丝绸文物的氨基酸接枝加固法 Download PDF

Info

Publication number
CN102965924A
CN102965924A CN2012104699694A CN201210469969A CN102965924A CN 102965924 A CN102965924 A CN 102965924A CN 2012104699694 A CN2012104699694 A CN 2012104699694A CN 201210469969 A CN201210469969 A CN 201210469969A CN 102965924 A CN102965924 A CN 102965924A
Authority
CN
China
Prior art keywords
amino acid
silk fabric
cultural relic
solution
silk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104699694A
Other languages
English (en)
Other versions
CN102965924B (zh
Inventor
姚清清
何俊
张硕
胡智文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Sci Tech University ZSTU
Original Assignee
Zhejiang Sci Tech University ZSTU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Sci Tech University ZSTU filed Critical Zhejiang Sci Tech University ZSTU
Priority to CN201210469969.4A priority Critical patent/CN102965924B/zh
Publication of CN102965924A publication Critical patent/CN102965924A/zh
Application granted granted Critical
Publication of CN102965924B publication Critical patent/CN102965924B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种糟朽丝绸文物的氨基酸接枝加固法,其步骤如下:a、按质量份数取L-半胱氨酸1~3份,L-赖氨酸1~3份,L-丙氨酸3~5份,混合均匀,并配制成重量百分比浓度为1.0%~1.5%的氨基酸水溶液;b、将步骤a得到的氨基酸水溶液均匀的喷洒在糟朽丝绸文物表面,直到丝绸文物被该水溶液均匀湿透而滴水为止;c、完成步骤b后等待15min,然后将重量百分比浓度为0.5%~1.5%的4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯溶液均匀地喷到糟朽丝绸文物上,直到丝绸文物被溶液均匀湿透,让其自然干燥;d、将质量百分浓度为1.0%~3.5%的乙二醇二缩水甘油基乙醚水溶液均匀地喷洒到丝绸文物表面上,直至滴水为止,自然干燥,获得加固的丝绸文物;本发明具有更好的加固效果。

Description

一种糟朽丝绸文物的氨基酸接枝加固法
技术领域
本发明涉及一种丝绸文物的保护方法,特别是一种糟朽丝绸文物的氨基酸接枝加固法,主要适用于糟朽丝绸文物的加固保护。
背景技术
丝绸是中华文明的重要象征之一,丝绸文物更是我国古代劳动人民智慧的结晶,具有很高的科学价值、艺术价值和历史价值,是研究我国古代政治、经济、艺术、科技等方面极为重要的历史实物资料。然而,蚕丝是一种天然的高分子蛋白质,容易受到水、光、热、氧、酸、碱以及微生物等诸多因素的影响而发生降解或者是破坏,致使蚕丝纤维大分子链大量的断裂,其结果必然是蚕丝纤维的强度大幅下降。
发明内容
本发明是要克服上述现有技术中存在的不足,提供一种操作简单方便、成本低、效果好的糟朽丝绸文物的氨基酸接枝加固法,以大幅提高糟朽丝绸文物强度。
本发明所采用的技术方案是:一种糟朽丝绸文物的氨基酸接枝加固法,其特征在于步骤如下:
a、按质量份数取L-半胱氨酸1~3份,L-赖氨酸1~3份,L-丙氨酸3~5份,混合均匀,并配制成重量百分比浓度为1.0%~1.5%的氨基酸水溶液;
b、将步骤a得到的氨基酸水溶液均匀的喷洒在糟朽丝绸文物表面,直到丝绸文物被该水溶液均匀湿透而滴水为止;
c、完成步骤b后等待15min,然后将重量百分比浓度为0.5%~1.5%的4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯溶液均匀地喷到糟朽丝绸文物上,直到丝绸文物被溶液均匀湿透,让其自然干燥;
d、将质量百分浓度为1.0%~3.5%的乙二醇二缩水甘油基乙醚水溶液均匀地喷洒到丝绸文物表面上,直至滴水为止,自然干燥,获得加固的丝绸文物。
所述4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯溶液的溶剂为无水乙醇。
本发明的有益效果是:本发明直接以构成丝蛋白肽链的基本组成单位——氨基酸作为接枝单体,以4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯和乙二醇二缩水甘油基乙醚为接枝助剂,对断裂的丝素多肽链进行交联接枝,较之现有技术仅以乙二醇二缩水甘油基乙醚水溶液作为交联剂的方法,具有更好的加固效果。
具体实施方式
本发明直接以构成丝蛋白肽链的基本组成单位——氨基酸作为接枝单体,以4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯和乙二醇二缩水甘油基乙醚为接枝助剂,对断裂的丝素多肽链进行交联接枝,从而达到加固糟朽丝绸的目的。
下面结合实施例对本发明作进一步说明:
实施例1:糟朽丝绸文物的氨基酸接枝加固法,其特征在于步骤如下:
a、按质量份数取L-半胱氨酸1份,L-赖氨酸1份,L-丙氨酸3份,混合均匀,并配制成重量百分比浓度为1.0%的氨基酸水溶液;
b、将步骤a得到的氨基酸水溶液均匀的喷洒在糟朽丝绸文物表面,直到丝绸文物被该水溶液均匀湿透而滴水为止;
c、完成步骤b后等待15min,然后将重量百分比浓度为0.5%的4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯溶液(选用无水乙醇作为溶剂)均匀地喷到糟朽丝绸文物上,直到丝绸文物被溶液均匀湿透,让其自然干燥;
d、将质量百分浓度为1.0%的乙二醇二缩水甘油基乙醚水溶液均匀地喷洒到丝绸文物表面上,直至滴水为止,自然干燥,获得加固的丝绸文物。
实施例2:糟朽丝绸文物的氨基酸接枝加固法,其特征在于步骤如下:
a、按质量份数取L-半胱氨酸2份,L-赖氨酸2份,L-丙氨酸4份,混合均匀,并配制成重量百分比浓度为1.25%的氨基酸水溶液;
b、将步骤a得到的氨基酸水溶液均匀的喷洒在糟朽丝绸文物表面,直到丝绸文物被该水溶液均匀湿透而滴水为止;
c、完成步骤b后等待15min,然后将重量百分比浓度为1%的4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯溶液(选用无水乙醇作为溶剂)均匀地喷到糟朽丝绸文物上,直到丝绸文物被溶液均匀湿透,让其自然干燥;
d、将质量百分浓度为2.5%的乙二醇二缩水甘油基乙醚水溶液均匀地喷洒到丝绸文物表面上,直至滴水为止,自然干燥,获得加固的丝绸文物。
实施例3:糟朽丝绸文物的氨基酸接枝加固法,其特征在于步骤如下:
a、按质量份数取L-半胱氨酸3份,L-赖氨酸3份,L-丙氨酸5份,混合均匀,并配制成重量百分比浓度为1.5%的氨基酸水溶液;
b、将步骤a得到的氨基酸水溶液均匀的喷洒在糟朽丝绸文物表面,直到丝绸文物被该水溶液均匀湿透而滴水为止;
c、完成步骤b后等待15min,然后将重量百分比浓度为1.5%的4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯溶液(选用无水乙醇作为溶剂)均匀地喷到糟朽丝绸文物上,直到丝绸文物被溶液均匀湿透,让其自然干燥;
d、将质量百分浓度为3.5%的乙二醇二缩水甘油基乙醚水溶液均匀地喷洒到丝绸文物表面上,直至滴水为止,自然干燥,获得加固的丝绸文物。

Claims (2)

1.一种糟朽丝绸文物的氨基酸接枝加固法,其特征在于步骤如下:
a、按质量份数取L-半胱氨酸1~3份,L-赖氨酸1~3份,L-丙氨酸3~5份,混合均匀,并配制成重量百分比浓度为1.0%~1.5%的氨基酸水溶液;
b、将步骤a得到的氨基酸水溶液均匀的喷洒在糟朽丝绸文物表面,直到丝绸文物被该水溶液均匀湿透而滴水为止;
c、完成步骤b后等待15min,然后将重量百分比浓度为0.5%~1.5%的4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯溶液均匀地喷到糟朽丝绸文物上,直到丝绸文物被溶液均匀湿透,让其自然干燥;
d、将质量百分浓度为1.0%~3.5%的乙二醇二缩水甘油基乙醚水溶液均匀地喷洒到丝绸文物表面上,直至滴水为止,自然干燥,获得加固的丝绸文物。
2.根据权利要求1所述的糟朽丝绸文物的氨基酸接枝加固法,其特征在于:所述4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯溶液的溶剂为无水乙醇。
CN201210469969.4A 2012-11-19 2012-11-19 一种糟朽丝绸文物的氨基酸接枝加固法 Expired - Fee Related CN102965924B (zh)