CN102964975B - 一种pu高丰满度抗下陷亮光白面漆 - Google Patents
一种pu高丰满度抗下陷亮光白面漆 Download PDFInfo
- Publication number
- CN102964975B CN102964975B CN201210433763.6A CN201210433763A CN102964975B CN 102964975 B CN102964975 B CN 102964975B CN 201210433763 A CN201210433763 A CN 201210433763A CN 102964975 B CN102964975 B CN 102964975B
- Authority
- CN
- China
- Prior art keywords
- component
- ratio
- sag
- weight
- butyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明一种PU高丰满度抗下陷亮光白面漆由甲组份用饱和聚酯树脂、合成脂肪酸树脂、丙烯酸树脂、PU高级亮光白面浆、分散剂、流平剂、消泡剂、等加上环保型溶剂制备而成，将醋酸正丁酯和固化剂配制成乙组份，丙组份用醋酸正丁酯、甲苯等溶剂配备而成，将甲、乙、丙组份配合成聚氨酯亮光白面漆。本发明的聚氨酯白面漆，经检测和试用证明，其耐黄性十分优秀，涂层附着力强、硬度高、耐磨抗划，耐热性好，施工和流平性好，丰满度极高、抗下陷性优异，环保性能符合GB18581中指标。
Description
技术领域
本发明涉及一种亮光白面漆。
背景技术
目前现有技术，PU高丰满度抗下陷亮光白面漆是一种综合性能优良的环保型涂料，具有抗下陷性好、白度高、丰满度好，耐黄变优等特点，广泛用于高档套房家具和高档橱柜家具的面漆涂装。市售同类产品施工后，常见缺点表现为干速慢、丰满度差、附着力一般、耐黄变一般等，这是一直困扰涂料行业的一道难题，而本发明克服了市售产品的缺点。
发明内容
本发明的目的是：提供一种PU高丰满度抗下陷亮光白面漆，它在木器家具或套房家具的表面形成了一层丰满度高、抗下陷性极好、白度极高、耐黄变优、环保的表面涂层。
本发明是这样实现的：一种PU高丰满度抗下陷亮光白面漆，其重量份数比为：
甲组份1，乙组份0.8，丙组份0.5；
所述甲组分的重量份数比如下：
合成脂肪酸树脂10～15，饱和聚脂树脂10～15，
丙烯酸树脂15～20，PU高级亮光白面浆60～65，
流平剂0.1～0.3，消泡剂0.4～0.6，
助剂0.8～1，醋酸正丁酯3.4～4；
配制时依次加入分散至充分均匀，粘度控制在4500±200cps/25℃；
所述乙组分的重量份数比如下：
醋酸正丁酯50，固化剂50；
所述丙组分的重量份数比如下：
醋酸正丁酯40～60，甲苯40～60；
所述PU高级亮光白面浆的重量份数比如下：
合成脂肪酸树脂45～55，分散剂1～1.2，
气相二氧化硅0.4～0.6，钛白粉45～55，
莎哈利本MICRO硫酸钡5-10，醋酸正丁酯0.5～1；
配制时，依次加入分散,并过砂磨机至细度在20μm以下，粘度控制在15000±1000cps/25℃。
具体实施方式
下面结合实施例对本发明作进一步描述。
实施例1
一种PU高丰满度抗下陷亮光白面漆，其重量份数比为：
甲组份1，乙组份0.8，丙组份0.5；
丙组份不参与化学反应，仅起调稀施工作用。
所述甲组分的重量份数比如下：
合成脂肪酸树脂10，饱和聚脂树脂10，
丙烯酸树脂15，PU高级亮光白面浆60，
流平剂0.1，消泡剂0.4，
助剂0.8，醋酸正丁酯3.4；
配制时依次加入分散至充分均匀，粘度控制在4500±200cps/25℃；
所述乙组分的重量份数比如下：
醋酸正丁酯50，固化剂50；
所述丙组分的重量份数比如下：
醋酸正丁酯40，甲苯60；
所述PU高级亮光白面浆的重量份数比如下：
合成脂肪酸树脂45，分散剂1，
气相二氧化硅0.4，钛白粉45，
莎哈利本MICRO硫酸钡5，醋酸正丁酯0.5；
配制时，依次加入分散,并过砂磨机至细度在20μm以下，粘度控制在15000±1000cps/25℃。
合成脂肪酸树脂型号：A931-80台湾大立公司出品。
饱和聚脂树脂型号CS8800晨晟公司。
丙烯酸树脂型号DSU4370-XP浙江德尚化工科技有限公司。
流平剂型号：BYK-333德国毕克。
消泡剂型号：BYK-141德国毕克。
助剂型号：BYK-OK德国毕克。
固化剂型号：HDI3390拜耳化工。
气相二氧化硅德固萨R972。
莎哈利本MICRO硫酸钡德国莎哈利本化学公司产。
钛白粉型号：R706杜邦化工。
实施例2
一种PU高丰满度抗下陷亮光白面漆，其重量份数比为：
甲组份1，乙组份0.8，丙组份0.5；
所述甲组分的重量份数比如下：
合成脂肪酸树脂15，饱和聚脂树脂15，
丙烯酸树脂20，PU高级亮光白面浆65，
流平剂0.3，消泡剂0.6，
助剂1，醋酸正丁酯4；
配制时依次加入分散至充分均匀，粘度控制在4500±200cps/25℃；
所述乙组分的重量份数比如下：
醋酸正丁酯50，固化剂50；
所述丙组分的重量份数比如下：
醋酸正丁酯60，甲苯40；
所述PU高级亮光白面浆的重量份数比如下：
合成脂肪酸树脂55，分散剂1.2，
气相二氧化硅0.6，钛白粉55，
莎哈利本MICRO硫酸钡10，醋酸正丁酯1；
配制时，依次加入分散,并过砂磨机至细度在20μm以下，粘度控制在15000±1000cps/25℃。
实施例3
一种PU高丰满度抗下陷亮光白面漆，其重量份数比为：
甲组份1，乙组份0.8，丙组份0.5；
所述甲组分的重量份数比如下：
合成脂肪酸树脂13，饱和聚脂树脂13，
丙烯酸树脂17，PU高级亮光白面浆62，
流平剂0.2，消泡剂0.5，
助剂0.9，醋酸正丁酯3.7；
配制时依次加入分散至充分均匀，粘度控制在4500±200cps/25℃；
所述乙组分的重量份数比如下：
醋酸正丁酯50，固化剂50；
所述丙组分的重量份数比如下：
醋酸正丁酯45，甲苯50；
所述PU高级亮光白面浆的重量份数比如下：
合成脂肪酸树脂47，分散剂1.1，
气相二氧化硅0.5，钛白粉47，
莎哈利本MICRO硫酸钡7，醋酸正丁酯0.8；
配制时，依次加入分散,并过砂磨机至细度在20μm以下，粘度控制在15000±1000cps/25℃。
本发明的PU木器亮光白面漆，经检测和试用证明，其涂层的附着力强，硬度高，耐磨、耐温、耐水、耐化学性好，施工性、流平性也十分优秀，特别是在抗下陷和丰满度方面，有领先地位。
本发明的白面漆与市面上购回的白面漆的性能比较，见下表：
| 检验项目 | 本发明 | 样品A | 样品B |
| 表干 | 26min | 31min | 28min |
| 实干h | 48 | 55 | 51 |
| 附着力 | 1级 | 1级 | 2级 |
| 柔韧性mm | 1 | 3 | 2 |
| 耐热性 | 通过 | 通过 | 通过 |
| 耐黄性（曝晒1个月） | 无黄变 | 黄变明显 | 严重变色 |
| 抗下陷性（放置1个月） | 基本无下陷 | 下陷严重 | 下陷严重 |
| 耐冲击 | ≥30 | 20 | 25 |
本发明的技术指标如下表：
本发明的目的在于从制漆用的原材料上进行控制，通过选用优异性能的原材料，在木器家具或套房家具的表面形成了一层丰满度高、抗下陷性极好、白度极高、耐黄变优、环保的表面涂层。特殊材料对漆膜性能影响如：合成脂肪酸树脂具备了丰满度，HDI固化剂保证了耐黄性，极大的提高了高丰满度亮光白面漆的丰满度、耐黄变等；PU高级白面浆采用了国外最先进技术生产的钛白粉，有效提高了PU的白度、遮盖力等，充分运用力学原理和材料极性原理，使本发明具备其他同类油漆不能比拟的特殊力学效果；生产丙组份充分考虑环境友好性，充分利用材料的极性原理，采用无苯低污染性溶剂作为材料，使生产出的产品各项检测指标均远远低于国家备案的企业标准；
检测方法：性能指标可参照GB/T23997-2009，限量物参照GB18581-2009。
由以上数据可知，本发明亮光白面漆是一种丰满度、附着力、耐黄变及抗下陷性十分优秀的高档套房家具和高档橱柜家具的面漆涂装。
Claims (1)
1.一种PU高丰满度抗下陷亮光白面漆，其特征在于：其重量份数比为：
甲组份1，乙组份0.8，丙组份0.5；
所述甲组分的重量份数比如下：
配制时依次加入分散至充分均匀，粘度控制在4500±200cps/25℃；
所述乙组分的重量份数比如下：
醋酸正丁酯50，固化剂50；
所述丙组分的重量份数比如下：
醋酸正丁酯40～60，甲苯40～60；
所述PU高级亮光白面浆的重量份数比如下：
配制时，依次加入分散,并过砂磨机至细度在20μm以下，粘度控制在15000±1000cps/25℃。