CN102964970A - Epoxy acrylic anticorrosive paint - Google Patents
Epoxy acrylic anticorrosive paint Download PDFInfo
- Publication number
- CN102964970A CN102964970A CN 201210565420 CN201210565420A CN102964970A CN 102964970 A CN102964970 A CN 102964970A CN 201210565420 CN201210565420 CN 201210565420 CN 201210565420 A CN201210565420 A CN 201210565420A CN 102964970 A CN102964970 A CN 102964970A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy acrylic
- anticorrosive paint
- catalyzer
- acrylic paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an epoxy acrylic anticorrosive paint which is prepared from the following raw materials in parts by weight: 20-50 parts of epoxy acrylic resin, 2-5 parts of styrene, 3-6 parts of 2-hydroxyethylacrylate, 2-4 parts of polymerization inhibitor, 5-8 parts of catalyst, 10-15 parts of amino resin and 8-15 parts of alkyd resin. The epoxy acrylic anticorrosive paint disclosed by the invention has the advantages of excellent binding capacity, excellent adhesive force, low shrinkage, quick drying, corrosion inhibition, favorable mechanical properties and no color bleeding phenomenon.
Description
Technical field
The present invention relates to technical field of coatings, be specifically related to a kind of anticorrosive epoxy acrylic paint.
Background technology
Coating take acrylic resin as main film forming substance is called acrylic resin paint, is divided into thermoplastic acrylic paint and thermosetting acrylic coating.Based on lacquer remarkable light fastness and anti-outdoor aging performance, at present, the market of acrylic coating maximum is car paint, in addition, the industry such as light industry, household electrical appliance, art metal furniture, aluminum products, coiled material industry, instrument, instrument, building textiles, plastics, woodwork, papermaking all are widely used.Decorate occasion with lacquer as height, such as the waved plate of motorway both sides, bridge, TV pylon etc., also usually adopt acrylic coating.
In view of there is no the comparatively perfect polyurethane water-based paint of over-all properties in the prior art, be difficult to satisfy again people's demand in performance in view of simple aqueous polyurethane, therefore utilize the outstanding ability of cohering of Resins, epoxy, high-modulus, high strength, good sticking power, low-shrinkage and water-fast, the advantages such as chemical resistant properties is good and acrylate be water tolerance preferably, physics characteristic and weather resistance and characteristics with low cost, by the graft copolymerization mode both resins are introduced in the aqueous polyurethane segment, aqueous polyurethane is carried out modification, make by this research that environmental protection and various aspects of performance all can be significantly improved and have positive effect.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is, provide a kind of have the outstanding ability of cohering, good sticking power, low-shrinkage, quick-drying, resistance erosion, good mechanical property again without the bleeding phenomenon anticorrosive epoxy acrylic paint.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of anticorrosive epoxy acrylic paint, raw material by following parts by weight is made: epoxy acrylic resin 20-50 part, vinylbenzene 2-5 part, vinylformic acid-2 hydroxyl ethyl ester 3-6 part, stopper 2-4 part, catalyzer 5-8 part, aminoresin 10-15 part, Synolac 8-15 part.
Above-mentioned anticorrosive epoxy acrylic paint is made by the raw material of following parts by weight: 40 parts of epoxy acrylic resins, 4 parts of vinylbenzene, 5 parts of vinylformic acid-2 hydroxyl ethyl esters, 3 parts of stoppers, 6 parts of catalyzer, 12 parts in aminoresin, 12 parts of Synolac.
Above-mentioned anticorrosive epoxy acrylic paint, described stopper are p methoxy phenol.
Above-mentioned anticorrosive epoxy acrylic paint, described catalyzer are dibutyl tin laurate.
Anticorrosive epoxy acrylic paint advantage of the present invention is:
1, anticorrosive epoxy acrylic paint of the present invention has the outstanding ability of cohering, good sticking power, low-shrinkage, quick-drying, resistance erosion, good mechanical property again without the bleeding phenomenon.
Embodiment
The invention will be further described below in conjunction with embodiment.
Embodiment 1, and a kind of anticorrosive epoxy acrylic paint is made by the raw material of following parts by weight: 20 parts of epoxy acrylic resins, 2 parts of vinylbenzene, 3 parts of vinylformic acid-2 hydroxyl ethyl esters, 2 parts of stoppers, 5 parts of catalyzer, 10 parts in aminoresin, 8 parts of Synolac.
Above-mentioned stopper is p methoxy phenol.
Above-mentioned catalyzer is dibutyl tin laurate.
Embodiment 2, and a kind of anticorrosive epoxy acrylic paint is made by the raw material of following parts by weight: 40 parts of epoxy acrylic resins, 4 parts of vinylbenzene, 5 parts of vinylformic acid-2 hydroxyl ethyl esters, 3 parts of stoppers, 6 parts of catalyzer, 12 parts in aminoresin, 12 parts of Synolac.
Above-mentioned stopper is p methoxy phenol.
Above-mentioned catalyzer is dibutyl tin laurate.
Embodiment 3, and a kind of anticorrosive epoxy acrylic paint is made by the raw material of following parts by weight: 50 parts of epoxy acrylic resins, 5 parts of vinylbenzene, 6 parts of vinylformic acid-2 hydroxyl ethyl esters, 4 parts of stoppers, 8 parts of catalyzer, 15 parts in aminoresin, 15 parts of Synolac.
Above-mentioned stopper is p methoxy phenol.
Above-mentioned catalyzer is dibutyl tin laurate.
Certainly, above-mentioned explanation is not to be limitation of the present invention, and the present invention also is not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement all should belong to protection scope of the present invention.
Claims (4)
1. anticorrosive epoxy acrylic paint, it is characterized in that: the raw material by following parts by weight is made: epoxy acrylic resin 20-50 part, vinylbenzene 2-5 part, vinylformic acid-2 hydroxyl ethyl ester 3-6 part, stopper 2-4 part, catalyzer 5-8 part, aminoresin 10-15 part, Synolac 8-15 part.
2. anticorrosive epoxy acrylic paint according to claim 1, it is characterized in that: the raw material by following parts by weight is made: 40 parts of epoxy acrylic resins, 4 parts of vinylbenzene, 5 parts of vinylformic acid-2 hydroxyl ethyl esters, 3 parts of stoppers, 6 parts of catalyzer, 12 parts in aminoresin, 12 parts of Synolac.
3. anticorrosive epoxy acrylic paint according to claim 1, it is characterized in that: described stopper is p methoxy phenol.
4. anticorrosive epoxy acrylic paint according to claim 1, it is characterized in that: described catalyzer is dibutyl tin laurate.