CN102964102A - Ceramsite concrete slab - Google Patents
Ceramsite concrete slab Download PDFInfo
- Publication number
- CN102964102A CN102964102A CN2012104382218A CN201210438221A CN102964102A CN 102964102 A CN102964102 A CN 102964102A CN 2012104382218 A CN2012104382218 A CN 2012104382218A CN 201210438221 A CN201210438221 A CN 201210438221A CN 102964102 A CN102964102 A CN 102964102A
- Authority
- CN
- China
- Prior art keywords
- haydite
- concrete plate
- size
- concrete slab
- haydite concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a ceramsite concrete slab. The ceramsite concrete slab per cubic meter mainly comprises the following raw materials: 380-410kg of cement, 790-900kg,coal ash or furnace clinker, 173-180kg of ceramsite, 115-120kg of water and a wire mesh. The ceramsite concrete slab provided by the invention has high strength, freezing resistance and anti-swelling efficiency and can be used as an outer wall of a building; the ceramsite concrete slab can be made into a small size so as to meet the break joint requirement during installation, is suitable for strength during installation and rigidity requirement of the wall space and has wide applicable range; the ceramsite concrete slab achieves the anti-seismic effect in the structure, has low density, is light in mass, and has convenience in transportation and field cutting installation; and the ceramsite concrete slab has good heat preservation effect and sound insulation effect and can realize the self heat preservation function.
Description
Technical field
The present invention relates to a kind of material of construction, specifically, relate to a kind of haydite concrete plate.
Background technology
Ceramsite board is a kind of structural lumber of being processed into take haydite as main raw material.Compare with other lightweight concrete slabs, ceramsite board has that intensity is large, lightweight, cost is low, without the advantage such as combustion-supporting, that the scope of application is extensive, and therefore, building trade has extensively adopted ceramsite board to replace common fragment of brick.But be take large-sized ceramsite board or brick as main in the market, and the ceramsite board of small area is more extensive than the scope of application of large-sized ceramsite board, has more embodied its value.Particularly on shock resistance, has unrivaled effect.In addition, present ceramsite board is because its undercapacity is enough high, and only the material of construction as the non-bearing partition uses.
Summary of the invention
Technical problem to be solved by this invention provides a kind of haydite concrete plate, has higher intensity.
Technical scheme of the present invention is as follows:
A kind of haydite concrete plate, every m
3Described haydite concrete plate mainly comprise following raw material: cement 380 ~ 410kg, sand, flyash or slag 790 ~ 900kg, haydite 173 ~ 180kg, water 115 ~ 120kg and wire cloth.
Further: described cement comprises sulplo-aluminate or normal silicate.
Further: described sand is middle rough sand, and described middle rough sand comprises stone flour, ore deposit sand or Jiang Sha.
Further: the diameter of described haydite is 5 ~ 10mm, 5 ~ 15mm or 5 ~ 20mm.
Further: the wire diameter of described wire cloth is 0.7 ~ 1mm, and the size of mesh opening of described wire cloth is 15mm * 15mm ~ 25mm * 25mm, and described wire cloth is two-layer.
Further: the material of described wire cloth is iron or steel, and is zinc-plated on the described wire cloth.
Further: described concrete slab is of a size of 900mm * 1200mm, and described wire cloth is of a size of 880mm * 1180mm.
Further: described concrete slab is of a size of 900mm * 900mm, and described wire cloth is of a size of 880mm * 880mm.
Further: described concrete slab is of a size of 900mm * 600mm, and described wire cloth is of a size of 880mm * 580mm.
Further: described concrete slab is of a size of 800mm * 800mm, and described wire cloth is of a size of 795mm * 795mm.
Technique effect of the present invention is as follows:
1, haydite concrete plate of the present invention has higher intensity, frost resistance and the wet rate that rises, and can be used as external wall and uses.
2, haydite concrete plate of the present invention can be made less size, the fissure of displacement needs when installing to satisfy, and the intensity when adapting to installation and the rigid demand of metope, applicable is wider general; Structurally reach the effect of antidetonation.
3, haydite concrete plate of the present invention has less density, and lighter weight is convenient to transportation, is convenient to cut at the scene installation.
4, the high insulating effect of haydite concrete plate of the present invention can realize the function of self-heat conserving.
5, the soundproof effect of haydite concrete plate of the present invention is good.
Embodiment
Below in conjunction with embodiment the specific embodiment of the present invention is described.
Embodiment 1
The composition of haydite concrete plate is as follows: sulplo-aluminate 425# cement 380kg, stone flour 850kg, haydite 173kg, water 115kg and two-layer wire netting.Wherein, the diameter of haydite is 5 ~ 20mm.Obtain mixture after sulplo-aluminate 425# cement, stone flour, haydite and water stirred, in mould, put into first the mixture that a part stirs.In mould, place again one deck wire netting.Then, the mixture that stirs put into mould after, repave one deck wire netting, enter the operation of vibrating.This wire netting is of a size of 795mm * 795mm.The diameter of this wire netting is 0.7mm, and size of mesh opening is 15mm * 15mm.This galvanized wire mesh mainly plays the elastic effect that strengthens the haydite concrete plate.
The haydite concrete plate for preparing after the form removal maintenance is of a size of 800mm * 800mm.This haydite concrete plate thickness only is 25mm, and transportation and installation are all very convenient.
Test the salient features of this haydite concrete plate, test result sees Table 1.As can be seen from Table 1, to have higher intensity, light, insulation and a soundproof effect good for this haydite concrete plate.
Embodiment 2
The composition of haydite concrete plate is as follows: sulplo-aluminate 425# cement 385kg, ore deposit husky 790kg, haydite 175kg, water 115kg and two-layer wire netting.Wherein, the diameter of haydite is 5 ~ 10mm.Obtain mixture after sulplo-aluminate 425# cement, ore deposit is husky, haydite and water stir, in mould, put into first the mixture that a part stirs.In mould, place again one deck wire netting.Then, the mixture that stirs put into mould after, repave one deck wire netting, enter the operation of vibrating.This wire netting is of a size of 880mm * 580mm.The diameter of this wire netting is 0.72mm, and size of mesh opening is 19mm * 19mm.This galvanized wire mesh mainly plays the elastic effect that strengthens the haydite concrete plate.
The haydite concrete plate for preparing after the form removal maintenance is of a size of 900mm * 600mm.This haydite concrete plate thickness only is 25mm, and transportation and installation are all very convenient.
Test the salient features of this haydite concrete plate, test result sees Table 1.As can be seen from Table 1, to have higher intensity, light, insulation and a soundproof effect good for this haydite concrete plate.
Embodiment 3
The composition of haydite concrete plate is as follows: normal silicate 425# cement 396kg, flyash 900kg, haydite 179kg, water 117kg and two-layer woven wire.Wherein, the diameter of haydite is 5 ~ 15mm.Obtain mixture after normal silicate 425# cement, flyash, haydite and water stirred, in mould, put into first the mixture that a part stirs.In mould, place again the layer of steel wire net.Then, the mixture that stirs put into mould after, repave the layer of steel wire net, enter the operation of vibrating.This woven wire is of a size of 880mm * 880mm.The diameter of this woven wire is 0.83mm, and size of mesh opening is 23mm * 23mm.This Galvanized Steel Wire Netting mainly plays the elastic effect that strengthens the haydite concrete plate.
The haydite concrete plate for preparing after the form removal maintenance is of a size of 900mm * 900mm.This haydite concrete plate thickness only is 25mm, and transportation and installation are all very convenient.
Test the salient features of this haydite concrete plate, test result sees Table 1.As can be seen from Table 1, to have higher intensity, light, insulation and a soundproof effect good for this haydite concrete plate.
Embodiment 4
The composition of haydite concrete plate is as follows: normal silicate 425# cement 410kg, slag 820kg, haydite 180kg, water 120kg and two-layer woven wire.Wherein, the diameter of haydite is 5 ~ 20mm.Obtain mixture after normal silicate 425# cement, slag, haydite and water stirred, in mould, put into first the mixture that a part stirs.In mould, place again the layer of steel wire net.Then, the mixture that stirs put into mould after, repave the layer of steel wire net, enter the operation of vibrating.This woven wire is of a size of 880mm * 1180mm.The diameter of this woven wire is 1mm, and size of mesh opening is 25mm * 25mm.This Galvanized Steel Wire Netting mainly plays the elastic effect that strengthens the haydite concrete plate.
The haydite concrete plate for preparing after the form removal maintenance is of a size of 900mm * 1200mm.This haydite concrete plate thickness only is 25mm, and transportation and installation are all very convenient.
Test the salient features of this haydite concrete plate, test result sees Table 1.As can be seen from Table 1, to have higher intensity, light, insulation and a soundproof effect good for this haydite concrete plate.
Embodiment 5
The composition of the haydite concrete plate of embodiments of the invention 5 is as follows: normal silicate 425# cement 398kg, river husky 837kg, haydite 175kg, water 120kg and two-layer woven wire.Wherein, the diameter of haydite is 5 ~ 15mm.Obtain mixture after normal silicate 425# cement, Jiang Sha, haydite and water stirred, in mould, put into first the mixture that a part stirs.In mould, place again the layer of steel wire net.Then, the mixture that stirs put into mould after, repave the layer of steel wire net, enter the operation of vibrating.This woven wire is of a size of 880mm * 1180mm.The diameter of this woven wire is 1mm, and size of mesh opening is 25mm * 25mm.This Galvanized Steel Wire Netting mainly plays the elastic effect that strengthens the haydite concrete plate.
The haydite concrete plate for preparing after the form removal maintenance is of a size of 900mm * 1200mm.This haydite concrete plate thickness only is 25mm, and transportation and installation are all very convenient.
Test the salient features of this haydite concrete plate, test result sees Table 1.As can be seen from Table 1, to have higher intensity, light, insulation and a soundproof effect good for this haydite concrete plate.
The above only is the embodiment of invention.Protection scope of the present invention is not limited to this, anyly is familiar with those skilled in the art in the technical scope that the present invention discloses, and the variation that can expect easily or replacement all should be encompassed within protection scope of the present invention.
The performance perameter of the haydite concrete plate of table 1 embodiments of the invention
Claims (10)
1. a haydite concrete plate is characterized in that, every m
3Described haydite concrete plate mainly comprise following raw material: cement 380 ~ 410kg, sand, flyash or slag 790 ~ 900kg, haydite 173 ~ 180kg, water 115 ~ 120kg and wire cloth.
2. haydite concrete plate as claimed in claim 1, it is characterized in that: described cement comprises sulplo-aluminate or normal silicate.
3. haydite concrete plate as claimed in claim 1, it is characterized in that: described sand is middle rough sand, described middle rough sand comprises stone flour, ore deposit sand or Jiang Sha.
4. haydite concrete plate as claimed in claim 1, it is characterized in that: the diameter of described haydite is 5 ~ 10mm, 5 ~ 15mm or 5 ~ 20mm.
5. haydite concrete plate as claimed in claim 1, it is characterized in that: the wire diameter of described wire cloth is 0.7 ~ 1mm, and the size of mesh opening of described wire cloth is 15mm * 15mm ~ 25mm * 25mm, and described wire cloth is two-layer.
6. such as claim 1 or 5 described haydite concrete plates, it is characterized in that: the material of described wire cloth is iron or steel, and is zinc-plated on the described wire cloth.
7. haydite concrete plate as claimed in claim 1, it is characterized in that: described concrete slab is of a size of 900mm * 1200mm, and described wire cloth is of a size of 880mm * 1180mm.
8. haydite concrete plate as claimed in claim 1, it is characterized in that: described concrete slab is of a size of 900mm * 900mm, and described wire cloth is of a size of 880mm * 880mm.
9. haydite concrete plate as claimed in claim 1, it is characterized in that: described concrete slab is of a size of 900mm * 600mm, and described wire cloth is of a size of 880mm * 580mm.
10. haydite concrete plate as claimed in claim 1, it is characterized in that: described concrete slab is of a size of 800mm * 800mm, and described wire cloth is of a size of 795mm * 795mm.