CN102952486A - 一种含有改性蒙脱石粉的滤清器用粘合剂胶片 - Google Patents

一种含有改性蒙脱石粉的滤清器用粘合剂胶片 Download PDF

Info

Publication number
CN102952486A
CN102952486A CN2012104165076A CN201210416507A CN102952486A CN 102952486 A CN102952486 A CN 102952486A CN 2012104165076 A CN2012104165076 A CN 2012104165076A CN 201210416507 A CN201210416507 A CN 201210416507A CN 102952486 A CN102952486 A CN 102952486A
Authority
CN
China
Prior art keywords
adhesive film
modified montmorillonite
filter
phenol
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104165076A
Other languages
English (en)
Other versions
CN102952486B (zh
Inventor
陈登宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI PHOENIX FILTER CO., LTD.
Original Assignee
Bengbu Phoenix International Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Phoenix International Co Ltd filed Critical Bengbu Phoenix International Co Ltd
Priority to CN201210416507.6A priority Critical patent/CN102952486B/zh
Publication of CN102952486A publication Critical patent/CN102952486A/zh
Application granted granted Critical
Publication of CN102952486B publication Critical patent/CN102952486B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有改性蒙脱石粉的滤清器用粘合剂胶片,其是由氯丁橡胶CR121、苯乙烯、2.4.6-三(二甲胺基甲基)苯酚、聚乙烯醇、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷、聚异丁烯、聚四氢呋喃醚二醇、改性蒙脱石粉粉、改性树木灰烬等原料制得。对蒙脱石以及树木灰烬的改性可以增加本发明的强度和韧性,制得的本发明耐温性能好、剪切强度高的同时具有优良的电绝缘性以及耐老化性,而且该粘合剂胶片固化后表面平整、韧性好、抗震效果好。

Description

一种含有改性蒙脱石粉的滤清器用粘合剂胶片
技术领域
本发明涉及滤清器设备领域,确切地说是一种含有改性蒙脱石粉的滤清器用粘合剂胶片。
背景技术
    滤清器原本是通过对有害杂质的滤清,使发动机能够在各种工况下正常工作,并能达到规定的使用寿命。而原始滤清效率不合格的产品使用时则不能将对发动机有害的灰尘杂质进行有效滤除,会造成机动车的发动机早期磨损,减少使用寿命,危害发动机甚至酿成事故。
    生产中的胶粘工艺没有掌握好,或胶粘剂本身质量不好,使得滤清器的滤纸与端盖间不能保持密封状态从而使灰尘从缝隙里流过,从而导致滤清器品质不合格。滤纸的选择和加工工艺、滤纸胶粘工艺是滤清器生产流程中的两个关键质量控制点。有些厂家为了降低生产成本,采购较便宜的不合格的滤纸和胶粘剂,或粘合时间短、刷胶过少或不均匀等等,都会造成原始滤清效率不合格。
尤其对于空气滤清器而言,其使用的粘合剂以环氧树脂为主要原料,该类型的粘合剂为液态粘合剂,使用前必须充分搅拌,再采用浸渍法、喷涂法、刷涂法、辊涂法、转移法等方法进行操作,因此工艺上较为复杂,易出现粘合剂分布不均匀以及造成浪费等现象;而且,粘合剂固化后很脆,不耐冲击,在后续加工、运输和安装过程中很容易损坏,致使滤清器使用寿命短。
    传统的橡胶粘结剂已不能满足新的要求,急需性能更好的的橡胶粘合剂来提高滤清器的品质。
发明内容
本发明的目的在于提供一种具有较高的胶结强度和韧性的含有改性蒙脱石粉的滤清器用粘合剂胶片。
上述目的通过以下方案实现:
    一种含有改性蒙脱石粉的滤清器用粘合剂胶片,其特征在于:其是由下述重量份的原料制得:氯丁橡胶(CR121)135-145、苯乙烯15-20、2.4.6-三(二甲胺基甲基)苯酚1-2、聚乙烯醇8-12、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷2-3、聚异丁烯2-3、聚四氢呋喃醚二醇2-3、氯化丁基橡胶1066  10-15、羧甲基纤维素钠5-8、环氧亚麻籽油2-5、邻苯二甲酸聚酯2-5、一缩二乙二醇苯甲酸酯2-5、乙酰柠檬酸三乙酯3-5、硫磺1-2、氧化镁1-2、硬脂酸钙1-2、N660炭黑20-25、纳米膨润土30-35、改性蒙脱石粉30-35、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯1-2、抗氧剂1035 1-2、防焦剂CTP 1-2、促进剂TMTD 1-2、促进剂DM 3-4、促进剂TETD 1-2、防老剂TPPD 1-2、防老剂ODA 1-2、二茂铁1-2、改性树木灰烬1-2;
    所述的改性蒙脱石粉的制备方法为:取蒙脱石于600-800℃下煅烧8-10小时,然后于浓度为10-15%的双氧水溶液中浸泡2-4小时,研磨后过100-200目筛即得;
所述的改性树木灰烬的制备方法为:
(1)、将树木灰烬用浓度为15-20%的氢氧化钠溶液浸泡2-3小时后,再用去离子水洗涤至中性,烘干;
(2)、再于烘干的树木灰烬中加入相当于其重量1-2%的纳米碳、1-2%的2.4.6-三(二甲胺基甲基)苯酚、2-3%的a-氰基丙烯酸酯、1-2%的交联剂 TAC、2-4%的氢氧化铝,在4000-4500转/分下搅拌30-40分钟后,烘干粉碎成超细粉末即得。
      所述的一种含有改性蒙脱石粉的滤清器用粘合剂胶片,其特征在于:制备方法为:将氯丁橡胶CR121按重量份加入到苯乙烯中,加热到100-110℃,搅拌10-15分钟,再按重量份加入2.4.6-三(二甲胺基甲基)苯酚、聚乙烯醇、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷、聚异丁烯、聚四氢呋喃醚二醇,搅拌,反应1-2小时;再按重量份加入其余原料,混炼至所需厚度,最后剪切至所需尺寸即可。
    本发明的有益效果为:对蒙脱石以及树木灰烬的改性可以增加本发明的强度和韧性,制得的本发明耐温性能好、剪切强度高的同时具有优良的电绝缘性以及耐老化性,而且该粘合剂胶片固化后表面平整、韧性好、抗震效果好。
具体实施方式
 一种含有改性蒙脱石粉的滤清器用粘合剂胶片,其是由下述重量份(kg)的原料制得:氯丁橡胶(CR121)136、苯乙烯 16、2.4.6-三(二甲胺基甲基)苯酚1、聚乙烯醇 12、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷 3、聚异丁烯3、聚四氢呋喃醚二醇 3、氯化丁基橡胶1066  13、 羧甲基纤维素钠 5、 环氧亚麻籽油3、邻苯二甲酸聚酯3、一缩二乙二醇苯甲酸酯5、乙酰柠檬酸三乙酯3、硫磺1、氧化镁2、硬脂酸钙1、N660炭黑 25、纳米膨润土 33、改性蒙脱石粉34、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯1、抗氧剂1035  2、防焦剂CTP  2、促进剂TMTD  2、促进剂DM  4、促进剂TETD  2、防老剂TPPD 1、防老剂ODA  1、二茂铁 2、改性树木灰烬1;
    所述的改性蒙脱石粉的制备方法为:取蒙脱石于700℃下煅烧9小时,然后于浓度为15%的双氧水溶液中浸泡4小时,研磨后过200目筛即得;
所述的改性树木灰烬的制备方法为:
(1)、将树木灰烬用浓度为20%的氢氧化钠溶液浸泡3小时后,再用去离子水洗涤至中性,烘干;
(2)、再于烘干的树木灰烬中加入相当于其重量2%的纳米碳、2%的2.4.6-三(二甲胺基甲基)苯酚、2%的a-氰基丙烯酸酯、1%的交联剂 TAC、2%的氢氧化铝,在4000转/分下搅拌30分钟后,烘干粉碎成超细粉末即得。
      所述的一种含有改性蒙脱石粉的滤清器用粘合剂胶片,制备方法为:将氯丁橡胶CR121按重量份加入到苯乙烯中,加热到110℃,搅拌15分钟,再按重量份加入2.4.6-三(二甲胺基甲基)苯酚、聚乙烯醇、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷、聚异丁烯、聚四氢呋喃醚二醇,搅拌,反应2小时;再按重量份加入其余原料,混炼至所需厚度,最后剪切至所需尺寸即可。
    本发明含有改性蒙脱石粉的滤清器用粘合剂胶片具有较高的剪切强度和韧性,使用后常温剪切强度可达到265- 278 公斤每平方厘米,150 ℃的剪切强度可达到106-113 公斤每平方厘米,不均匀拉伸强度可达到52-54 公斤每平方厘米。
使用时,将本发明胶片粘上滤清器滤纸与端盖,然后在加温硫化,可大大提高其韧性及端盖与滤纸的粘合强度,经久耐用。保持密封状态,不会发生灰尘从缝隙里流过。

Claims (2)

1.一种含有改性蒙脱石粉的滤清器用粘合剂胶片,其特征在于:其是由下述重量份的原料制得:氯丁橡胶CR121  135-145、苯乙烯15-20、2.4.6-三(二甲胺基甲基)苯酚1-2、聚乙烯醇8-12、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷2-3、聚异丁烯2-3、聚四氢呋喃醚二醇2-3、氯化丁基橡胶1066  10-15、羧甲基纤维素钠5-8、环氧亚麻籽油2-5、邻苯二甲酸聚酯2-5、一缩二乙二醇苯甲酸酯2-5、乙酰柠檬酸三乙酯3-5、硫磺1-2、氧化镁1-2、硬脂酸钙1-2、N660炭黑20-25、纳米膨润土30-35、改性蒙脱石粉30-35、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯1-2、抗氧剂1035 1-2、防焦剂CTP 1-2、促进剂TMTD 1-2、促进剂DM 3-4、促进剂TETD 1-2、防老剂TPPD 1-2、防老剂ODA 1-2、二茂铁1-2、改性树木灰烬1-2
    所述的改性蒙脱石粉的制备方法为:取蒙脱石于600-800℃下煅烧8-10小时,然后于浓度为10-15%的双氧水溶液中浸泡2-4小时,研磨后过100-200目筛即得;
所述的改性树木灰烬的制备方法为:
(1)、将树木灰烬用浓度为15-20%的氢氧化钠溶液浸泡2-3小时后,再用去离子水洗涤至中性,烘干;
(2)、再于烘干的树木灰烬中加入相当于其重量1-2%的纳米碳、1-2%的2.4.6-三(二甲胺基甲基)苯酚、2-3%的a-氰基丙烯酸酯、1-2%的交联剂 TAC、2-4%的氢氧化铝,在4000-4500转/分下搅拌30-40分钟后,烘干粉碎成超细粉末即得。
2.根据权利要求1所述的一种含有改性蒙脱石粉的滤清器用粘合剂胶片,其特征在于:制备方法为:将氯丁橡胶CR121按重量份加入到苯乙烯中,加热到100-110℃,搅拌10-15分钟,再按重量份加入2.4.6-三(二甲胺基甲基)苯酚、聚乙烯醇、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷、聚异丁烯、聚四氢呋喃醚二醇,搅拌,反应1-2小时;再按重量份加入其余原料,混炼至所需厚度,最后剪切至所需尺寸即可。
CN201210416507.6A 2012-10-27 2012-10-27 一种含有改性蒙脱石粉的滤清器用粘合剂胶片 Active CN102952486B (zh)