CN102925266B - Multipurpose aluminum-magnesium drawing oil and production method thereof - Google Patents
Multipurpose aluminum-magnesium drawing oil and production method thereof Download PDFInfo
- Publication number
- CN102925266B CN102925266B CN201210453049.3A CN201210453049A CN102925266B CN 102925266 B CN102925266 B CN 102925266B CN 201210453049 A CN201210453049 A CN 201210453049A CN 102925266 B CN102925266 B CN 102925266B
- Authority
- CN
- China
- Prior art keywords
- oil
- magnesium
- shared
- press
- distribution ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a multipurpose aluminum-magnesium drawing oil and a production method of the multipurpose aluminum-magnesium drawing oil. The oil is prepared by the following components: low-viscosity mineral base oil, a non-ferrous metal corrosion inhibitor, an oiliness additive, antioxidant and an antiwear agent; the low-viscosity mineral base oil is three-time-hydrogenation base oil 60N which is of 91.5% of the oil based on percentage; the non-ferrous metal corrosion inhibitor is a metal corrosion inhibitor RP3359 which is of 1% of the oil based on the percentage; the oiliness additive is an oiliness additive 6150 which is of 5% of the oil based on the percentage; the antioxidant is the antioxidant T531 which is of 0.5% of the oil based on the percentage; and the antiwear agent is an antiwear agent P7900 which is of 2% of the oil based on the percentage. According to the multipurpose aluminum-magnesium drawing oil and the production method, mineral oil which is refined by hydrogenating for three times is the base oil, so that the multipurpose aluminum-magnesium drawing oil is low in volatility, higher in flash point, and higher in oxidation resistance; a plurality of additives are added, so that a processing capacity of the oil is improved, oil steam is reduced, and injury to a human body can be reduced; and the multipurpose aluminum-magnesium drawing oil is high in flash point, the fire is hardly caused, so that safety in use can be improved.
Description
Technical field
The present invention relates to multi-usage magnalium wire drawing oil and production method thereof.
Background technology
At present, the producer of domestic production wire drawing oil mainly adopts the oil for drawing process of low viscosity mineral base oil modulation.Because traditional low viscosity mineral oil volatility under hot conditions is large, oil vapour is large to harm, and the flash-point of low viscosity mineral oil is low, easily catches fire, and is prone to accidents; Traditional mineral spirits processing procedure degree is not dark, and oxidation-resistance is also relatively poor, and the work-ing life of oil product is short, is conventionally no more than 3 months duration of service.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of multi-usage magnalium wire drawing oil, and oil product volatility is little, and flash-point is higher, and antioxidant property is fabulous, safe to use, and has extended oil product work-ing life.
For addressing the above problem, the present invention is achieved through the following technical solutions: multi-usage magnalium wire drawing oil, this oil is to comprise following composition: low viscosity mineral base oil, the anticorrosion inhibitor of non-ferrous metal, oiliness improver, oxidation inhibitor and anti-wear agent, described low viscosity mineral base oil is three hydrogenated base oil 60N, press 91.5% of shared this oil of per distribution ratio, the anticorrosion inhibitor of described non-ferrous metal is anti-corrosion of metal inhibitor RP3359, press 1% of shared this oil of per distribution ratio, described oiliness improver is oiliness improver 6150, press 5% of shared this oil of per distribution ratio, described oxidation inhibitor is oxidation inhibitor T531, press 0.5% of shared this oil of per distribution ratio, described anti-wear agent is anti-wear agent P7900, press 2% of shared this oil of per distribution ratio.
Further, three times described hydrogenated base oil 60N are low viscosity oil, and its technical indicator is: colourity is not more than 2.0, and flash-point is not less than 170 DEG C, 40 DEG C of kinematic viscosity 10-35 mm2/s, and acid number is not more than 0.3mgKOH/g.
Further, described anti-corrosion of metal inhibitor is the multi-functional anti-corrosion anti-abrasion agent of RP3359 of thinking sensitization work, is mainly for suppressing the corrosion of non-ferrous metal burn into, strengthening resistance to abrasion, oilness.
Further, described oiliness improver is that methyl ester 6150 fingers are added in hydrogenated base oil, can reduce frictional coefficient, improves oilness, increase aluminium, aluminum magnesium alloy surface smoothness.
Further, described oxidation inhibitor is that T531 N-phenyl-αnaphthylamine refers to improve oil product resistance of oxidation, extends oil product work-ing life
Further, described anti-wear agent is that phosphoric acid ester P7900 refers to be added on and in base oil, has the oil product of enhancing abrasion resistance, reduces wear.
Another technical problem to be solved by this invention is to provide a kind of multi-usage magnalium wire drawing oil and production method thereof, and oil product volatility is little, and flash-point is higher, and antioxidant property is fabulous, safe to use, and has extended oil product work-ing life, and production technique is simple.
The present invention is achieved through the following technical solutions: the production method of described oil is as follows:
First in blending equipment, pacifying under formula rate adds in three hydrogenated base oil 60N and methyl ester 6150 and phosphoric acid ester PB7900, Heating temperature to 50～60 DEG C, after stirring and evenly mixing, add the anticorrosion inhibitor RP3359 of non-ferrous metal, at 50～60 DEG C of temperature of constant temperature, continue to stir 0.5 hour, sampling checks it is that additive is no solvent, after solvent, under whipped state, add oxidation inhibitor, anti-wear agent and oiliness improver, Heating temperature to 70 DEG C stirs and can obtain product after evenly in 1.5 hours again.
The invention has the beneficial effects as follows: product of the present invention adopts three hydrorefined mineral oil as base oil, oil product volatility is little, flash-point is higher, antioxidant property is fabulous, after adding multiple additives, not only improved oil product processing characteristics, mainly reduced oil vapour and reduced harm lowly, flash-point is high, be difficult for catching fire, improve safety in utilization.Oil product extends work-ing life, reaches 6 months; Reduce the demand to petroleum resources.
Brief description of the drawings
Fig. 1 is procedure of processing schematic diagram of the present invention.
Embodiment
Following examples are used for illustrating the present invention, but are not used for limiting the scope of the invention.
Embodiment 1
Multi-usage magnalium wire drawing oil, this oil is to comprise following composition: low viscosity mineral base oil, the anticorrosion inhibitor of non-ferrous metal, oiliness improver, oxidation inhibitor and anti-wear agent, described low viscosity mineral base oil is three hydrogenated base oil 60N, press 91.5% of shared this oil of per distribution ratio, the anticorrosion inhibitor of described non-ferrous metal is anti-corrosion of metal inhibitor RP3359, press 1% of shared this oil of per distribution ratio, described oiliness improver is oiliness improver 6150, press 5% of shared this oil of per distribution ratio, described oxidation inhibitor is oxidation inhibitor T531, press 0.5% of shared this oil of per distribution ratio, described anti-wear agent is anti-wear agent P7900, press 2% of shared this oil of per distribution ratio.
Three times described hydrogenated base oil 60N are low viscosity oil, and its technical indicator is: colourity is 2.0, and flash-point is 170 DEG C, 40 DEG C of kinematic viscosity 35 mm2/s, and acid number is 0.3mgKOH/g.
Described anti-corrosion of metal inhibitor is the multi-functional anti-corrosion anti-abrasion agent of RP3359 of thinking sensitization work, is mainly for suppressing the corrosion of non-ferrous metal burn into, strengthening resistance to abrasion, oilness.
Described oiliness improver is that methyl ester 6150 fingers are added in hydrogenated base oil, can reduce frictional coefficient, improves oilness, increase aluminium, aluminum magnesium alloy surface smoothness.
Described oxidation inhibitor is that T531 N-phenyl-αnaphthylamine refers to improve oil product resistance of oxidation, extends oil product work-ing life
Described anti-wear agent is that phosphoric acid ester P7900 refers to be added on and in base oil, has the oil product of enhancing abrasion resistance, reduces wear.
The production method of described oil is as follows:
First in blending equipment, pacifying under formula rate adds in three hydrogenated base oil 60N and methyl ester 6150 and phosphoric acid ester PB7900, Heating temperature to 50～60 DEG C, after stirring and evenly mixing, add the anticorrosion inhibitor RP3359 of non-ferrous metal, at 50～60 DEG C of temperature of constant temperature, continue to stir 0.5 hour, sampling checks it is that additive is no solvent, after solvent, under whipped state, add oxidation inhibitor, anti-wear agent and oiliness improver, Heating temperature to 70 DEG C stirs and can obtain product after evenly in 1.5 hours again.
Procedure of processing as shown in Figure 1.
The invention has the beneficial effects as follows: product of the present invention adopts three hydrorefined mineral oil as base oil, oil product volatility is little, flash-point is higher, antioxidant property is fabulous, after adding multiple additives, not only improved oil product processing characteristics, mainly reduced oil vapour and reduced harm lowly, flash-point is high, be difficult for catching fire, improve safety in utilization.Oil product extends work-ing life, reaches 6 months, reduces the demand to petroleum resources.
The present invention is not limited to above-mentioned preferred forms, and other any or akin products identical with the present invention that anyone draws under enlightenment of the present invention, within all dropping on protection scope of the present invention.
Claims (2)
1. multi-usage magnalium wire drawing oil, it is characterized in that: this oil is to comprise following composition: low viscosity mineral base oil, the anticorrosion inhibitor of non-ferrous metal, oiliness improver, oxidation inhibitor and anti-wear agent, described low viscosity mineral base oil is three hydrogenated base oil 60N, press 91.5% of shared this oil of per distribution ratio, the anticorrosion inhibitor of described non-ferrous metal is anti-corrosion of metal inhibitor RP3359, press 1% of shared this oil of per distribution ratio, described oiliness improver is methyl ester 6150, press 5% of shared this oil of per distribution ratio, described oxidation inhibitor is oxidation inhibitor T531, press 0.5% of shared this oil of per distribution ratio, described anti-wear agent is phosphoric acid ester P7900, press 2% of shared this oil of per distribution ratio.
2. multi-usage magnalium wire drawing oil according to claim 1, is characterized in that: three times described hydrogenated base oil 60N are low viscosity oil, and its technical indicator is: colourity is not more than 2.0, and flash-point is not less than 170 DEG C, 40 DEG C of kinematic viscosity 10-35mm
2/ s, acid number is not more than 0.3mgKOH/g.