CN102910886A - Silico-calcium light wall board and preparation method thereof - Google Patents
Silico-calcium light wall board and preparation method thereof Download PDFInfo
- Publication number
- CN102910886A CN102910886A CN 201210450140 CN201210450140A CN102910886A CN 102910886 A CN102910886 A CN 102910886A CN 201210450140 CN201210450140 CN 201210450140 CN 201210450140 A CN201210450140 A CN 201210450140A CN 102910886 A CN102910886 A CN 102910886A
- Authority
- CN
- China
- Prior art keywords
- weight
- wall board
- silico
- parts
- light wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of building materials and provides a preparation method of a silico-calcium light wall board. The preparation method comprises the following steps of: a, by weight, taking 30-40 parts of gypsum, 8-12 parts of cement, 50-60 parts of coal cinder powder as a first group of raw materials; b, by weight, preparing a retarder the weight of which is 0.01-0.02% of that of gypsum; and c, by weight, preparing a crystal modifier the weight of which is 1.6-2.0% of that of the first group of raw materials; adding water in the gypsum and the prepared retarder and then fully stirring, then adding the weighed cement, coal cinder powder and crystal modifier, fully stirring, feeding the obtained mixture into an extrusion molding machine for molding, wherein the retarder is a mixture of citric acid, sodium hexametaphosphate and sodium tripolyphosphate, the crystal modifier is a mixture of aluminum potassium sulfate and sodium citricate. The wall board is comfortable in living, has the advantages of reducing cost and recycling wastes, meets the time requirement of panel extruding; and the wall board has the effects of no dropping and no splitting and has the advantages of high strength, light weight and durability.
Description
Technical field
The present invention relates to building materials technology field, relate in particular to a kind of silico-calcium light wall board, also relate to the manufacture method of this silico-calcium light wall board.
Background technology
The contriver is in the patent No. 200610059751.6, title is in the patent of " calcium silicate plant fibre Light trabs and manufacture method thereof ", a kind of method of making wallboard is disclosed, employed main raw material is vegetable fibre, in the past few years, obtain the approval of society, but such manufacture method exists that raw material is more, complex process, shortcoming that cost is high.
In the prior art, the main raw material that indoor wallboard is used or cement because the setting time of gypsum is shorter, the general usefulness of indoor wallboard be extruding shaping technique, need the long time, so the application of gypsum in the wallboard manufacturing is restricted.
On the other hand, along with building a conservation-minded society, require refuse to take full advantage of, and in the reality, the utilization ratio of industrial residue or on the low side, many refuses that are used as discard, and also can take up room as the waste residue of refuse; In the wallboard manufacture of prior art, mix waste residue often because of the unreasonable intensity that can affect wallboard of technique.
Summary of the invention
Purpose of the present invention is exactly for above-mentioned shortcoming, provide a kind of technique simple, satisfy the silico-calcium light wall board manufacture method that the process time requires, cost is low, also provide a kind of intensity high, not aliquation, do not fall the silico-calcium light wall board of piece, health environment-friendly.
The manufacture method of silico-calcium light wall board of the present invention is achieved in that a kind of manufacture method of silico-calcium light wall board, may further comprise the steps:
A, by weight gets 30-40 parts gypsum, 8-12 parts cement, 50-60 parts cinder powder as raw material for standby, is as first group of raw material;
B, by weight gets 0.01-0.02% retardant of gypsum weight;
C, by weight gets 1.6-2.0% crystal modifier of first group of raw material;
After gypsum and the retardant got added water and fully stir, add again the cement, cinder powder, the crystal modifier that weigh up and fully stir, send in the single-lead-screw extruding briquetting machine namely plastic.
Preferably, used retardant is the mixture of citric acid, Sodium hexametaphosphate 99 and tripoly phosphate sodium STPP.
Preferably, used crystal modifier is the mixture of potassium aluminium sulfate and Trisodium Citrate.
Silico-calcium light wall board of the present invention is the plaster wall sheet material that uses aforesaid method to make.
The invention has the beneficial effects as follows:
1, the wallboard that has used gypsum to make as main raw material can utilize the character of gypsum, can automatically adjust indoor moisture content; When room air was dry, sheet material can discharge moisture; When indoor humidity, sheet material can absorb moisture, plays the effect of regulating air, lives more comfortable;
2, use more cinder powder, can reduce cost, utilization of waste material;
3, the centre adds the setting time that retardant can prolong gypsum, meets the time requirement of extrusion plate;
4, the centre has added crystal modifier, the gypsum sheet material of making is had do not come off, the effect of aliquation not;
5, this silico-calcium light wall board also has high, lightweight, the long-lived advantage of intensity.
Embodiment
The invention will be further described below in conjunction with embodiment.
Embodiment 1
A, by weight gets 30 kilograms gypsum, 8 kilograms cement, 50 kilograms cinder powder as first group of raw material for standby;
B, by weight gets 0.01% of gypsum, i.e. 0.003 kilogram retardant;
C, by weight gets 1.6% of first group of raw material, i.e. 1.408 kilograms crystal modifier;
After gypsum and the retardant got added water and fully stir, add again cement, cinder powder, the crystal modifier got and fully stir, namely plastic in the single-lead-screw extruding briquetting machine of making a gift to someone.
Such silico-calcium light wall board has advantages of that intensity is high, cost is low, do not solidify before the moulding, do not come off, aliquation not, and the gypsum sets time is 35 minutes, also has high, lightweight, the long-lived advantage of intensity.
Need to prove:
1, used cinder powder is common industrial cinder, sieves, removes bulk;
2, employed retardant, crystal modifier market are on sale;
3, water mixing does not have certain ratio in first group of raw material, generally rests in to stir defensive position and cannot not grab loosely, lands the degree of scattering, and watering quantity is 20-30% of the first raw material, and described technical field personnel can grasp.
Above explanation is applicable following examples also:
Embodiment 2
A, by weight gets 40 kilograms gypsum, 12 kilograms cement, 60 kilograms cinder powder as the first raw material for standby;
B, by weight gets 0.02% of gypsum, i.e. 0.008 kilogram retardant;
C, by weight gets 2% of first group of raw material, i.e. 2.024 kilograms crystal modifier;
After gypsum and the retardant got added water and fully stir, add again the cement of getting, cinder powder, crystal modifier and add water and fully stir, namely plastic in the single-lead-screw extruding briquetting machine of making a gift to someone.
Such silico-calcium light wall board has advantages of that intensity is high, cost is low, do not solidify before the moulding, do not come off, aliquation not, and the gypsum sets time is 40 minutes, also has high, lightweight, the long-lived advantage of intensity.
Embodiment 3
Among the step a of contriver with embodiment 1, the desulfurated plaster that 30 kilograms gypsum is used 2 parts fluorgypsum and 5 parts instead mixes, and namely the desulfurated plaster of 8.6 kilograms fluorgypsum and 21.4 kilograms is done same test.
Such silico-calcium light wall board has advantages of that also later strength is better except having above-mentioned advantage.
Embodiment 4
The contriver uses 2 parts fluorgypsum and 5 parts desulfurated plaster to mix in 40 kilograms gypsum among the step a of embodiment 2, and namely the desulfurated plaster of 11.4 kilograms of fluorgypsums and 28.6 kilograms is done same test.
Such silico-calcium light wall board has advantages of that also later strength is better except having above-mentioned advantage.
Embodiment 5
The contriver will use the retardant of same weight among above-described embodiment 1,2,3,4 the step b, use the retardant of own exchange---be 1 part of citric acid, 1 part of Sodium hexametaphosphate 99 and 1 part of tripoly phosphate sodium STPP mixture by weight, can be controlled at 30-40 minutes to setting time, satisfy the demand of extrusion molding.
Such silico-calcium light wall board also has the sheet material of making and has in the water and can not soak in 10 days piece, non-scaling advantage except having above-mentioned advantage.
Embodiment 6
The contriver uses the retardant of same weight with among above-described embodiment 1,2,3,4,5 the step c, uses the crystal modifier of own exchange---and be the mixture of 2-3 part potassium aluminium sulfate and 1 part of Trisodium Citrate by weight,
Such silico-calcium light wall board also has the sheet material of making and has in the water and can not soak in 10 days piece, non-scaling advantage except having above-mentioned advantage.
Embodiment 7
The contriver uses the crystal modifier of own exchange with among above-described embodiment 1,2,3,4,5 the step c---and be the mixture of 9 parts of potassium aluminium sulfates and 4 parts of Trisodium Citrates by weight,
Such silico-calcium light wall board also has the sheet material of making and has in the water and can not soak in 15 days fast, non-scaling advantage except having above-mentioned advantage.
Claims (8)
1. the manufacture method of a silico-calcium light wall board may further comprise the steps:
A, by weight gets 30-40 parts gypsum, 8-12 parts cement, 50-60 parts cinder powder as first group of raw material;
B, by weight gets 0.01-0.02% retardant of gypsum weight;
C, by weight gets 1.6-2.0% crystal modifier of first group of raw material;
After gypsum and the retardant got added water and fully stir, add again the cement, cinder powder, the crystal modifier that weigh up and fully stir, send in the single-lead-screw extruding briquetting machine namely plastic.
2. the manufacture method of silico-calcium light wall board according to claim 1, it is characterized in that: described gypsum is that 2 parts fluorgypsum and 5 parts desulfurated plaster mix.
3. the manufacture method of silico-calcium light wall board according to claim 1 and 2, it is characterized in that: described retardant is 1 part of citric acid, 1 part of Sodium hexametaphosphate 99 and 1 part of tripoly phosphate sodium STPP.
4. the manufacture method of silico-calcium light wall board according to claim 1 and 2, it is characterized in that: described crystal modifier is the mixture of 2-3 part potassium aluminium sulfate and 1 part of Trisodium Citrate by weight.
5. the manufacture method of silico-calcium light wall board according to claim 3, it is characterized in that: described crystal modifier is the mixture of 2-3 part potassium aluminium sulfate and 1 part of Trisodium Citrate by weight.
6. the manufacture method of silico-calcium light wall board according to claim 4, it is characterized in that: described crystal modifier is the mixture of 9 parts of potassium aluminium sulfates and 4 parts of Trisodium Citrates by weight.
7. the manufacture method of silico-calcium light wall board according to claim 5, it is characterized in that: described crystal modifier is the mixture of 9 parts of potassium aluminium sulfates and 4 parts of Trisodium Citrates by weight.
8. a silico-calcium light wall board is characterized in that: the wallboard that has used the claims 1-7 to make.