CN102899553A - 一种新型含硼热轧板卷及其生产方法 - Google Patents
一种新型含硼热轧板卷及其生产方法 Download PDFInfo
- Publication number
- CN102899553A CN102899553A CN2012103366538A CN201210336653A CN102899553A CN 102899553 A CN102899553 A CN 102899553A CN 2012103366538 A CN2012103366538 A CN 2012103366538A CN 201210336653 A CN201210336653 A CN 201210336653A CN 102899553 A CN102899553 A CN 102899553A
- Authority
- CN
- China
- Prior art keywords
- hot
- steel
- production method
- rolled coil
- hot rolled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型含硼热轧板卷,属于钢材技术领域。该热轧板卷化学成分质量百分数分别为:C0.07~0.09%,Si≤0.03%,Mn0.70~0.80%,P≤0.020%,S≤0.015%,Alt0.01~0.04%,B0.0008~0.0020%,其余为Fe和杂质。本发明还公开了该热轧板卷的生产方法,包括热连轧,热连轧过程中加热炉加热至1160~1220℃,加热时间2.5~4.0h,精轧终轧温度为800~860℃,卷取温度为520~580℃。采用该生产方法可生产出可满足Q235及其相近钢级技术要求的热轧板卷,具有适用于热装热送工艺,且产品表面质量好,加工成型后适于进行表面涂镀的特点。
Description
技术领域
本发明涉及钢材技术领域,特别涉及一种新型含硼热轧板卷及其生产方法。
背景技术
硼是一种重要的合金元素,具有提高淬透性的能力极强,具有最佳含量而且此含量极小的特点。由于硼的最主要的作用是提高钢的淬透性,因而可以增大钢材的可淬透尺寸,或者提高淬火后钢材截面内组织和性能的均匀性,因此主要应用于冷热轧高强钢。
随着国内钢铁产量的迅速扩大,国家对钢铁产品出口退税政策进行相应调整,明确规定钢中硼含量低于8ppm的普通热轧钢板不再列入享受出口退税政策的产品名单。因此国内各钢铁企业为提高经济效益,逐步开始在部分出口的中低强度级别钢材(如Q235、SS400及相似钢级产品)中添加廉价的硼元素以获得出口退税。这些中低强度钢主要采用C-Si-Mn的成分体系,C含量均在0.12%以上,当钢中加入8ppm以上硼元素时使得铸坯裂纹敏感性增大导致铸坯表面裂纹急剧增多,使得各钢铁企业不能采用热装热送工艺,只能将铸坯下线清理,既降低生产效率也增加了生产经营的成本和难度。
发明内容
本发明提出了一种新型含硼热轧板卷及其生产方法,通过采用低碳低硅的成分体系即可生产出能够满足Q235及其相近钢级要求的热轧板卷。
本发明提供的新型含硼热轧板卷的化学成分质量百分数分别为:C0.07~0.09%,Si≤0.03%,Mn0.70~0.80%,P≤0.020%,S≤0.015%,Alt0.01~0.04%,B0.0008~0.0020%,其余为Fe和杂质。
基于本发明提供的热轧板卷的生产方法包括热连轧,在所述热连轧过程中再加热的温度为1160~1220℃,加热时间2.5~4.0小时。
作为优选,在所述热连轧过程中精轧的终轧温度为800~860℃。
作为优选,在所述热连轧过程中卷取的温度为520~580℃。
本发明提供的热轧板卷及其生产方法的有益效果在于:
本发明通过将钢中的碳元素和硼元素含量进行优化组合,可显著降低该钢级含硼钢铸坯裂纹敏感性,采用常规方法即可生产出表面无缺陷铸坯,适用于热装热送工艺,其热轧产品可满足Q235及其相近钢级的技术要求。而且由于Si含量低,产品表面质量好,加工成型后适于进行表面涂镀处理。
具体实施方式
为了深入了解本发明,下面根据具体实施例对本发明进行详细说明。
实施例1
采用常规连铸方法形成化学成分质量百分数分别为C0.09%、Si0.02%、Mn0.78%、P0.017%、S0.013%、Alt0.016%,B0.0010%,其余为Fe和杂质的板坯,规格为厚×宽=230mm×1500mm。然后,令板坯经过热连轧机组即依次经过加热、粗轧除鳞、粗轧、切头尾、精轧除鳞、精轧、层流冷却、卷取进行热连轧,其中,加热炉加热温度为1775℃,加热时间为3.5小时,精轧机组终轧温度为813℃,卷取温度为576℃。这样,经过粗轧、精轧、层流冷却后,经过卷取机卷取,最后获得化学成分质量百分数分别为C0.09%、Si0.02%、Mn0.78%、P0.017%、S0.013%、Alt0.016%,B0.0010%,其余为Fe和杂质的规格为厚×宽=7.0mm×1500mm的Q235B热轧板卷。
该Q235B热轧板卷屈服强度为295MPa、抗拉强度为434MPa,延伸率为34%,20℃冲击值为78J,70J,71J,平均为73J,1.5倍冷弯合格。
实施例2
采用常规连铸方法形成化学成分质量百分数分别为C0.07%、Si0.01%、Mn0.73%、P0.011%、S0.005%、Alt0.033%,B0.0017%,其余为Fe和杂质的板坯,规格为厚×宽=230mm×1300mm。然后,令板坯经过热连轧机组即依次经过加热、粗轧除鳞、粗轧、切头尾、精轧除鳞、精轧、层流冷却、卷取进行热连轧,其中,加热炉加热温度为1217℃,加热时间为3.0小时,精轧机组终轧温度为851℃,卷取温度为541℃。这样,经过粗轧、精轧、层流冷却后,经过卷取机卷取,最后获得化学成分质量百分数分别为C0.07%、Si0.01%、Mn0.73%、P0.011%、S0.005%、Alt0.033%,B0.0017%,其余为Fe和杂质的规格为厚×宽=2.75mm×1250mm的Q235B热轧板卷。
该Q235B热轧板卷屈服强度为315MPa、抗拉强度为425MPa,延伸率为37%,1.5倍冷弯合格。
本发明通过将钢中的碳元素和硼元素含量进行优化组合,可显著降低该钢级含硼钢铸坯裂纹敏感性,采用常规方法即可生产出表面无缺陷铸坯,适用于热装热送工艺,其热轧产品可满足Q235及其相近钢级的技术要求。而且由于Si含量低,产品表面质量好,加工成型后适于进行表面涂镀处理。
以上所述的具体实施方式,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所应理解的是,以上所述仅为本发明的具体实施方式而已,并不用于限制本发明,凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (4)
1.一种新型含硼热轧板卷,其特征在于,所述热轧板卷的化学成分质量百分数分别为:C0.07~0.09%,Si≤0.03%,Mn0.70~0.80%,P≤0.020%,S≤0.015%,Alt0.01~0.04%,B0.0008~0.0020%,其余为Fe和杂质。
2.基于权利要求1所述的热轧板卷的生产方法,其特征在于,包括热连轧,在所述热连轧过程中再加热的温度为1160~1220℃,加热时间2.5~4.0小时。
3.根据权利要求2所述的生产方法,其特征在于,在所述热连轧过程中精轧的终轧温度为800~860℃。
4.根据权利要求3所述的生产方法,其特征在于,在所述热连轧过程中卷取的温度为520~580℃。