CN102898608A - 一种超轻发泡鞋底材料的制备方法 - Google Patents
一种超轻发泡鞋底材料的制备方法 Download PDFInfo
- Publication number
- CN102898608A CN102898608A CN2012103558684A CN201210355868A CN102898608A CN 102898608 A CN102898608 A CN 102898608A CN 2012103558684 A CN2012103558684 A CN 2012103558684A CN 201210355868 A CN201210355868 A CN 201210355868A CN 102898608 A CN102898608 A CN 102898608A
- Authority
- CN
- China
- Prior art keywords
- mass
- mass parts
- parts
- preparation
- sole material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种超轻发泡鞋底材料的制备方法，该方法的制备步骤如下：将60-66质量份天然橡胶、80-85质量份甲苯二异氰酸酯、10-12质量份三乙醇胺、10质量份一氯三氟甲烷、3-6质量份硬脂酸、6质量份十八叹烷酸、2.5质量份硫黄、3质量份偶氮二甲酰胺和2.5质量份聚二甲基硅油加入高速搅拌混合机中混合10min；然后加入到双螺杆挤出机中熔融接枝3h后，即得到所述鞋底材料。本发明的有益效果：该方法的制备工艺简单，生产成本低，制备出的产物耐磨性高，还具有质轻舒适的性能。
Description
技术领域
本发明涉及一种超轻发泡鞋底材料的制备方法。
技术背景
目前，市面上的发泡鞋底大多数具有轻便，舒适，加工成型快等性能，虽然材料的柔软性达到要求但是其强度仍较差，特别是耐磨耗不理想，降低鞋子的使用寿命；所以一些人为了进一步改进性能，一般要掺入大量的填料，树脂和油品，这样不光大大提高的生产成本，还会大大增加了鞋材的密度。
发明内容
本发明目的是为了克服现有技术的不足，提供一种超轻发泡鞋底材料的制备方法，该方法制得鞋底材料耐磨性强，且该方法的制备工艺简单。
为解决上述问题，本发明的一个技术方案是：一种超轻发泡鞋底材料的制备方法，该方法的制备步骤如下：将60-66质量份天然橡胶、80-85质量份甲苯二异氰酸酯、10-12质量份三乙醇胺、10质量份一氯三氟甲烷、3-6质量份硬脂酸、6质量份十八叹烷酸、2.5质量份硫黄、3质量份偶氮二甲酰胺和2.5质量份聚二甲基硅油加入高速搅拌混合机中混合10min；然后加入到双螺杆挤出机中熔融接枝3h后，即得到所述鞋底材料。
本发明的有益效果：该方法的制备工艺简单，生产成本低，且制备出的产物耐磨性高，还具有质轻舒适的性能。
具体实施方式
实施例1
一种超轻发泡鞋底材料的制备方法，该方法的制备步骤如下：将60-66质量份天然橡胶、80-85质量份甲苯二异氰酸酯、10-12质量份三乙醇胺、10质量份一氯三氟甲烷、3-6质量份硬脂酸、6质量份十八叹烷酸、2.5质量份硫黄、3质量份偶氮二甲酰胺和2.5质量份聚二甲基硅油加入高速搅拌混合机中混合10min；然后加入到双螺杆挤出机中熔融接枝3h后，即得到所述鞋底材料。对该鞋底材料的性能检测效果如下：相对密度：0.2，硬度（A）55，拉伸强度/MPa：2.8，回弹率：30%。
Claims (1)
1.一种超轻发泡鞋底材料的制备方法，其特征在于该方法的步骤如下：将60-66质量份天然橡胶、80-85质量份甲苯二异氰酸酯、10-12质量份三乙醇胺、10质量份一氯三氟甲烷、3-6质量份硬脂酸、6质量份十八叹烷酸、2.5质量份硫黄、3质量份偶氮二甲酰胺和2.5质量份聚二甲基硅油加入高速搅拌混合机中混合10min；然后加入到双螺杆挤出机中熔融接枝3h后，即得到所述鞋底材料。