CN102897096A - Manufacture method for ushering pedal identification with stainless steel bright strip - Google Patents
Manufacture method for ushering pedal identification with stainless steel bright strip Download PDFInfo
- Publication number
- CN102897096A CN102897096A CN2012104160551A CN201210416055A CN102897096A CN 102897096 A CN102897096 A CN 102897096A CN 2012104160551 A CN2012104160551 A CN 2012104160551A CN 201210416055 A CN201210416055 A CN 201210416055A CN 102897096 A CN102897096 A CN 102897096A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- steel plate
- mirror face
- face stainless
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a manufacture method for an ushering pedal identification with a stainless steel bright strip, which comprises the following steps of: 1) gluing; 2) baking for the first time; 3) exposing; 4) carrying out vacuum processing; 5) developing; 6) cleaning for the first time; 7) baking for the second time; 8) carrying out belt-type etching; 9) carrying out glue retreating processing; and 10) cleaning for the second time. According to the manufacture method disclosed by the invention, a pattern protection layer is formed on mirror surface stainless steel in a picture development mode; then, unnecessary positions are corroded into a frosting surface by etching equipment; finally, a protection layer is cleaned to obtain the required pattern; the pattern can be revised according to the requirement; the formed product is fashionable and has an elegant appearance; meanwhile, the whole set of equipment occupies small lands, the equipment is convenient to install to realize mass production, and the product quality consistency is guaranteed.
Description
Technical field
The invention belongs to the production method of auto pedal, the method for making that especially identifies with corrosion-resistant steel bright wisp meeting pedal.
Background technology
Along with the fast development of World Auto Industry, be widely used on the automobile with the meeting pedal of corrosion-resistant steel bright wisp, and have from luxury car and turn to low and middle-grade cars, joint brand car turns to the development tendency of independent brand car.Common corrosion-resistant steel sign is produced and is accepted by advertising company, but makees an exemplar mostly the time, does not become mass production, even if the short run producton conformability is also uncontrollable.Let alone product design.Because it is inferior to demonstrate immediately higher gears behind the automobile installation meeting pedal, a lot of automobiles are all using, and the output of the automobile corrosion-resistant steel bright wisp that sales volume is slightly good is tens of thousands.Common process can't satisfy the needs of production in enormous quantities.
Summary of the invention
For above deficiency, the object of the present invention is to provide a kind of method for making with corrosion-resistant steel bright wisp meeting pedal sign, adopt gluing, application of vacuum, exposure, etching, secondary baking, secondary cleaning to make device therefor formation one cover conveyor line in the production of corrosion-resistant steel bright wisp, reach the purpose of batch manufacturing, guarantee simultaneously the conformability of product design.
Technical scheme of the present invention is achieved in the following ways: the method for making with corrosion-resistant steel bright wisp meeting pedal identifies may further comprise the steps: 1) gluing, 2) once baking, 3) exposure, 4) application of vacuum, 5) development, 6) once cleaning, 7) secondary baking, 8) belt etching, 9) move back glue processing, 10) secondary cleaning; It is characterized in that:
1), gluing: the mirror face stainless steel plate of getting thickness and be 0.6mm is got the load-transfer device overall length and is 460mm, enters automatic glue application in the film applicator with the speed of 60mm/s, makes gluing thickness reach 0.1mm;
2), once baking: glue-coated mirror face stainless steel plate is put into belt drying tunnel case toast: oven temperature is 95 ℃ ± 2 ℃, and the drying tunnel overall length is 10m, and the baking temperature is 5-10 minute;
3), exposure: after baking finishes the mirror face stainless steel plate neatly is emitted on the shelf, glue faces down and puts into indoor temperature and expose at 10 ℃-25 ℃ exposure machine, and the exposure time is 20s;
4), application of vacuum: cover on the mirror face stainless steel plate with the thick cloth of light proof, close cover plate, carry out application of vacuum: vacuum time is 30s, and indoor temperature is 10 ℃-25 ℃;
5), develop: mirror face stainless steel plate glue is put into middle development of load-transfer device of developing machine facing up: the conveying belt length of developing machine is 4m, and the time is 120s;
The mixed solution that adds natrium carbonate 5L, water 100L in the described development develops.
6), once clean: the mirror face stainless steel plate after the development is put into the conventional cleaning of clear water;
7), secondary baking: the mirror face stainless steel plate is put into baking oven carry out secondary baking:
Described oven temperature is 180 ℃-200 ℃, and stoving time is 50-50 minute.
8), belt etching: the mirror face stainless steel plate is put into the etching of etching machine load-transfer device: etching machine load-transfer device overall length 6m, time are that 300-400s, temperature are controlled at 15 ℃-30 ℃, and mirror face stainless steel plate etch depth is 0.03mm;
Add 280L phosphoric acid, 87L leveling agent and 162L water in the described etching machine.
9), moving back glue processes: with hook the mirror face stainless steel plate is caught on and put into water temperature and moved back the glue processing in 5-10 minute at 50 ℃ ± 2 ℃ the quiet bubble in sodium hydroxide pond;
10), secondary cleaning: the mirror face stainless steel plate that has moved back glue cleans with clear water again.
The present invention uses the mode of printing the pictures to form the pattern protective cover at mirror face stainless steel, then frosting is corroded into etching machines in the N/R place, at last protective cover is cleaned, and can reach required pattern.Pattern can be changed as requested, the product fashion that forms, and outward appearance is generous, and simultaneously equipment package occupation of land is few, and equipment is easy for installation.Realize batch manufacturing, guarantee the conformability of product design.
The specific embodiment
Method for making with corrosion-resistant steel bright wisp meeting pedal sign may further comprise the steps:
1, gluing: get thickness and be the mirror face stainless steel plate of 0.6mm take the speed of 60mm/s, get the load-transfer device overall length as 460mm enters automatic glue application in the film applicator, make gluing thickness reach 0.1mm;
2, once baking: glue-coated mirror face stainless steel plate is put into belt drying tunnel case toast: oven temperature is 95 ℃ ± 2 ℃, and the drying tunnel overall length is 10m, and the baking temperature is 5-10 minute;
3, exposure: the mirror face stainless steel plate neatly is emitted on the shelf, and glue faces down and puts into indoor temperature and expose at 10 ℃-25 ℃ exposure machine, and the exposure time is 20s;
4, application of vacuum: cover on the mirror face stainless steel plate with the thick cloth of light proof, close cover plate, carry out application of vacuum: vacuum time is 30s, and indoor temperature is 10 ℃-25 ℃;
5, develop: mirror face stainless steel plate glue is put into middle development of load-transfer device of developing machine facing up: the developing machine load-transfer device is 4m, and the time is 120s; The mixed solution that adds natrium carbonate 5L, water 100L in the development develops;
6, once clean: the mirror face stainless steel plate after the development is put into the conventional cleaning of clear water;
7, secondary baking: the mirror face stainless steel plate is put into baking oven carry out secondary baking: oven temperature is 180 ℃-200 ℃, and stoving time is 50-50 minute.
8, belt etching: the mirror face stainless steel plate is put into the etching of etching machine load-transfer device: etching machine load-transfer device overall length 6m, time are that 300-400s, temperature are controlled at 15 ℃-30 ℃, and mirror face stainless steel plate etch depth is 0.03mm; Add 280L phosphoric acid, 87L leveling agent and 162L water in the etching machine.
9, moving back glue processes: with hook the mirror face stainless steel plate is caught on and put into water temperature and moved back the glue processing in 5-10 minute at 50 ℃ ± 2 ℃ the quiet bubble in sodium hydroxide pond;
10, secondary cleaning: the mirror face stainless steel plate that has moved back glue cleans with clear water again.
Claims (4)
1. the method for making that identifies with corrosion-resistant steel bright wisp meeting pedal may further comprise the steps: 1) gluing, 2) once baking, 3) exposure, 4) application of vacuum, 5) development, 6) once cleaning, 7) secondary baking, 8) belt etching, 9) move back glue processing, 10) secondary cleaning; It is characterized in that:
1), gluing: the mirror face stainless steel plate of getting thickness and be 0.6mm is got the load-transfer device overall length and is 460mm, enters automatic glue application in the film applicator with the speed of 60mm/s, makes gluing thickness reach 0.1mm;
2), once baking: glue-coated mirror face stainless steel plate is put into belt drying tunnel case toast: oven temperature is 95 ℃ ± 2 ℃, and the drying tunnel overall length is 10m, and the baking temperature is 5-10 minute;
3), exposure: the mirror face stainless steel plate neatly is emitted on the shelf, and glue faces down and puts into indoor temperature and expose at 10 ℃-25 ℃ exposure machine, and the exposure time is 20s;
4), application of vacuum: cover on the mirror face stainless steel plate with the thick cloth of light proof, close cover plate, carry out application of vacuum: vacuum time is 30s, and indoor temperature is 10 ℃-25 ℃;
5), develop: mirror face stainless steel plate glue is put into middle development of load-transfer device of developing machine facing up: the developing machine load-transfer device is 4m, and the time is 120s;
6), once clean: the mirror face stainless steel plate after the development is put into the conventional cleaning of clear water;
7), secondary baking: the mirror face stainless steel plate is put into baking oven carry out secondary baking:
8), belt etching: the mirror face stainless steel plate is put into the etching of etching machine load-transfer device: etching machine load-transfer device overall length 6m, time are that 300-400s, temperature are controlled at 15 ℃-30 ℃, and mirror face stainless steel plate etch depth is 0.03mm;
9), moving back glue processes: with hook the mirror face stainless steel plate is caught on and put into water temperature and moved back the glue processing in 5-10 minute at 50 ℃ ± 2 ℃ the quiet bubble in sodium hydroxide pond;
10), secondary cleaning: the mirror face stainless steel plate that has moved back glue cleans with clear water again.
2. the method for making with corrosion-resistant steel bright wisp meeting pedal sign according to claim 1, it is characterized in that: the mixed solution that adds natrium carbonate 5L, water 100L during described step 5) is developed develops.
3. the method for making with corrosion-resistant steel bright wisp meeting pedal sign according to claim 1, it is characterized in that: oven temperature is 180 ℃-200 ℃ in the described step 7), and stoving time is 50-50 minute.
4. the method for making with corrosion-resistant steel bright wisp meeting pedal sign according to claim 1 is characterized in that: add 280L phosphoric acid, 87L leveling agent and 162L water in the described step 8) in the etching machine.