CN102275447A - Method for producing checkered plate on mirror surface - Google Patents
Method for producing checkered plate on mirror surface Download PDFInfo
- Publication number
- CN102275447A CN102275447A CN2010101964631A CN201010196463A CN102275447A CN 102275447 A CN102275447 A CN 102275447A CN 2010101964631 A CN2010101964631 A CN 2010101964631A CN 201010196463 A CN201010196463 A CN 201010196463A CN 102275447 A CN102275447 A CN 102275447A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- plate
- printing ink
- film
- etching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for producing a checkered plate on a mirror surface, which comprises material preparing, surface polishing, pattern copying through ruling onto the surface of a steel plate for eroding the pattern on the surface according to a order: a, spraying printing ink on the surface of a steel plate; b, drying and cooling the sprayed steel plate; c, placing the steel plate onto an exposure station, flattening a ruling film with the surface of a medicinal membrane downwards on steel plate for smoothing, putting a vacuum membrane, compacting the periphery; drawing off air between the steel plate and the ruling film, then expositing by an iodine gallium light; taking the ruling film and the vacuum membrane away; d, placing the steel plate into a development container, flushing the surface of the steel plate by a NaOH solution and scrubbing the surface of the steel plate, cleaning the residual NaOH solution and air drying; e, controlling the temperature and the conveying speed of an etching solution in an etching machine, eroding the surface of the steel plate to a required depth; f, flushing the residual etching solution on the surface of the steel plate by oxalic acid, and flushing by clear water; removing the printing ink on the surface of the steel plate; taking the steel plate out for cleaning and forming the surface pattern.
Description
Technical field
The present invention relates to a kind of production method of minute surface diamond plate.
Background technology
Development along with the Modern Decorative technology, increasing sheet metal is applied to the decoration field, from appliance shell, furniture even to wall body decoration, the application of metallic element style is also more and more, present use for some sheet metals, be limited to mostly and adopt machining process to carry out the decorative pattern processing, for example produce the decorative pattern of plate face by modes such as punching press, annular knurl and engravings; Such production method makes production cost higher, and does not meet the shorter and shorter characteristic of the capable trend replacement of decorative pattern plate current; For example will get mould in advance ready when adopting process for stamping processing decorative pattern, the life cycle of mould also will influence its cost sharing, and mould cycle time is also longer; Such mode of production will have a strong impact on the market manifestation of product and be unfavorable for the complicated market environment of manufacturing enterprise's reply.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of production cost lower, especially is fit to the minute surface diamond plate production method of small lot batch manufacture.
Its technical problem to be solved can be implemented by the following technical programs.
A kind of minute surface diamond plate production method may further comprise the steps:
(1), select corrosion resistant plate, get the raw materials ready;
(2), adopt polishing with the stainless steel blank flat polishing of getting ready, reach 600～650 degree to the surface reflection rate;
(3), copy the decorative pattern that designs to scribble printing ink mirror steel plate surface by the film, carry out the surface detail corrosion in the following order:
The spraying of a, mirror steel plate surface ink;
With printing ink and diluent ratio proportioning with 3: 2, stir evenly, evenly be sprayed at the mirror steel plate surface with spray gun;
B, the steel plate that above-mentioned spraying is good place drying in oven, and room temperature is put to cooling;
C, the steel plate of cooling is lain against on the exposure desk, get film sheet medicine face and be tiled in down and catch up with flatly on the steel plate, vacuum diaphragm is spread in the upper end, around compressing; Open the air that vavuum pump extracted between steel plate and the film sheet in 5～10 minutes, then with 1000w Iodine gallium light exposure 200～500 seconds; Take down film sheet and vacuum diaphragm;
D, steel plate is placed in the developer container, is 5% NaOH solution flushing surface of steel plate printing ink 5～10 minutes and scrubs surface of steel plate with mass percent; With the NaOH solution of clear water remained on surface, wipe the surface and stay water and dry;
E, etching solution temperature in the etching machine is controlled at 40～60 ℃, adjusts between etching machine transmission speed to 3～30m/h, the corrosion surface of steel plate is to requiring the degree of depth;
After f, etching finish, at once with the residual etching solution of 5% oxalic acid water flushing surface of steel plate, clear water flushing again; Then steel plate is put into mass percent and be 30% NaOH solution 5～10 minutes, and removed surface of steel plate printing ink;
Steel plate is taken out cleaning, and the surface of steel plate decorative pattern forms.
Further improvement as the technical program, this method can also comprise that the form by the copy of the film repeatedly copies decorative pattern to scribble printing ink mirror steel plate surface, and then carries out the step that corresponding surface detail is shaped in proper order according to surface detail corrosion noted earlier respectively.Wherein, when finishing repeatedly film copy decorative pattern, comprise the step of each time film alignment, for example according to the linea angulata on the film sheet or to the direct alignment of version line or the aligning respectively of marking in addition.
As the further improvement of the technical program, the transporting velocity of steel plate baking oven when drying in oven preferably is controlled in the scope of 5～15m/h, and bake out temperature is controlled at 120 ℃.
Wherein, the corrosion resistant plate base material of this minute surface diamond plate can be selected the corrosion resistant plate of models such as SUS304/2B, SUS410, SUS630 or SUS633 for use.
Also as the improvement of the technical program, the etching solution temperature is 50～60 ℃ in described etching machine, and when described etching machine transmission speed was 3～18m/h, described surface of steel plate etch depth was 6～30 μ.Perhaps the etching solution temperature is 40～50 ℃ in etching machine, and when described etching machine transmission speed was 18～30m/h, carrying out the surface of steel plate etch depth was the decorative pattern corrosion of 1～6 μ.
Adopt the minute surface diamond plate production method of this technical scheme,, can realize minute surface diamond plate production fast, easily, help tackling the market situation of continuous variation by adopting the method for polishing after etching; Simultaneously can be by in batches, the different decorative pattern of difference etching that multistep is rapid, the perhaps decorative pattern of etching different depth; , better effects if abundanter with the level that reaches the surface of steel plate decorative pattern.
The specific embodiment
The minute surface diamond plate technological process of production provided by the invention is as follows:
1, choose base material:
Select SUS304/2B, SUS410, SUS630 or SUS633 stainless steel;
2, polishing:
The blank flat of buy thrown surface of steel plate with polishing brightly spend between 650 degree to reflecting rate 600.
3, decorative pattern corrosion:
Copy the decorative pattern that designs to scribble printing ink mirror board surface by the film.
1., the spraying of surface of steel plate printing ink.
With printing ink and diluent with 3: 2 ratio proportioning, stir evenly, evenly be sprayed at the mirror steel plate surface with spray gun.
2., will spray good steel plate and put the baking oven porch, the transporting velocity of adjusting baking oven is at 5～15m/h, temperature 120 degree with the liquid ink oven dry, are placed on the dolly until cooling.
3., the steel plate of oven dry is lain against on the exposure desk, film sheet is tiled in down with medicine face catches up with flatly on the steel plate, spread vacuum diaphragm, around compressing.Open vavuum pump, take out the air between the steel plate and the film, about 5～10 minutes, open 1000w/ Iodine gallium light only, exposed 200～500 seconds, close vavuum pump, take down all coverings of surface of steel plate.
4., steel plate is moved in the developing pool, with 5%NaH0 solution flushing surface of steel plate printing ink, scrubbed 2～5 bouts in surface gently with scrubbing brush in about 5～10 minutes.Wash out remained on surface 5%NaH0 with clear water, wipe the surface with rag and stay water and dry.
5., etching solution humidity in the etching machine is risen between 40～60 degree, adjust between etching machine transmission speed 3～30m/h, surface of steel plate is eroded away require the degree of depth;
The table of comparisons such as following table 1:
Table 1
6., after etching finishes, at once with the residual etching solution of 5% oxalic acid water flushing surface of steel plate, clear water washes steel plate put into is furnished with NaH0 30%, temperature in the pond, is removed surface of steel plate printing ink, about 5～10 minutes between 80～100 degree, take out and clean, etching finishes, and the surface of steel plate decorative pattern forms.
In addition, if cover figure requirement is arranged, can repeat in 3 1., 2., 3., 4., 5., 6. operation, second film to be aimed at first film loci when having only the tiling in 3., slightly different with the first time.By repeatedly decorative pattern etching, and adjust the decorative pattern corrosion depth, abundanter with the level that reaches decorative pattern, better effects if.
Claims (7)
1. a minute surface diamond plate production method is characterized in that, may further comprise the steps:
(1), select corrosion resistant plate, get the raw materials ready;
(2), adopt polishing with the stainless steel blank flat polishing of getting ready, reach 600～650 degree to the surface reflection rate;
(3), copy the decorative pattern that designs to scribble printing ink mirror steel plate surface by the film, carry out the surface detail corrosion in the following order:
The spraying of a, mirror steel plate surface ink;
With printing ink and diluent ratio proportioning with 3: 2, stir evenly, evenly be sprayed at the mirror steel plate surface with spray gun;
B, the steel plate that above-mentioned spraying is good place drying in oven, and room temperature is put to cooling;
C, the steel plate of cooling is lain against on the exposure desk, get film sheet medicine face and be tiled in down and catch up with flatly on the steel plate, vacuum diaphragm is spread in the upper end, around compressing; Open the air that vavuum pump extracted between steel plate and the film sheet in 5～10 minutes, then with 1000w Iodine gallium light exposure 200～500 seconds; Take down film sheet and vacuum diaphragm;
D, steel plate is placed in the developer container, is 5% NaOH solution flushing surface of steel plate printing ink 5～10 minutes and scrubs surface of steel plate with mass percent; With the NaOH solution of clear water remained on surface, wipe the surface and stay water and dry;
E, etching solution temperature in the etching machine is controlled at 40～60 ℃, adjusts between etching machine transmission speed to 3～30m/h, the corrosion surface of steel plate is to requiring the degree of depth;
After f, etching finish, at once with the residual etching solution of 5% oxalic acid water flushing surface of steel plate, clear water flushing again; Then steel plate is put into mass percent and be 30% NaOH solution 5～10 minutes, and removed surface of steel plate printing ink;
Steel plate is taken out cleaning, and the surface of steel plate decorative pattern forms.
2. minute surface diamond plate production method according to claim 1, it is characterized in that, this method comprises by the copy of the film repeatedly and copies decorative pattern to scribble printing ink mirror steel plate surface, and carries out the step that corresponding surface detail is shaped in proper order according to described surface detail corrosion respectively.
3. minute surface diamond plate production method according to claim 2 is characterized in that, finishes the step that comprises each time film alignment when the described repeatedly film copies decorative pattern.
4. according to claim 1,2 or 3 described minute surface diamond plate production methods, it is characterized in that the transporting velocity of steel plate baking oven when drying in oven is 5～15m/h, bake out temperature is 120 ℃.
5. minute surface diamond plate production method according to claim 1 is characterized in that described corrosion resistant plate is selected from SUS304/2B, SUS410, SUS630 or SUS633.
6. according to claim 1,2 or 3 described minute surface diamond plate production methods, it is characterized in that the etching solution temperature is 50～60 ℃ in the described etching machine, described etching machine transmission speed is 3～18m/h, and described surface of steel plate etch depth is 6～30 μ.
7. according to claim 1,2 or 3 described minute surface diamond plate production methods, it is characterized in that the etching solution temperature is 40～50 ℃ in the described etching machine, described etching machine transmission speed is 18～30m/h, and described surface of steel plate etch depth is 1～6 μ.