CN102887558A - 一种含纳米硒的饮用水净化材料及制备方法 - Google Patents
一种含纳米硒的饮用水净化材料及制备方法 Download PDFInfo
- Publication number
- CN102887558A CN102887558A CN2011102055927A CN201110205592A CN102887558A CN 102887558 A CN102887558 A CN 102887558A CN 2011102055927 A CN2011102055927 A CN 2011102055927A CN 201110205592 A CN201110205592 A CN 201110205592A CN 102887558 A CN102887558 A CN 102887558A
- Authority
- CN
- China
- Prior art keywords
- water purifying
- purifying material
- selenium
- drinking water
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种含纳米硒的饮用水净化材料及制备方法,该方法步骤是将活性炭、纳米竹炭、电气石纳米粉末、纳米硒、热溶粉末等按一定重量比混合均匀后,挤压成形并高温定型而成。相关原料重量比具体为:10-100nm的纳米硒2-4%,10-100nm的电气石纳米粉末15-20%,热溶粉末15-25%,10-1000nm的纳米竹炭25-30%,100-120目的活性炭余量%。本发明涉及一种饮用水的净化处理技术,特别涉及一种饮用水净化材料及制备方法,属于水质净化技术领域。本发明的目的是提供一种具备水质净化、杀菌、补充人体必需的微量元素硒的功能的饮用水净化材料。
Description
【技术领域】
本发明涉及一种饮用水的净化处理技术,特别涉及一种含纳米硒的饮用水净化材料及制备方法。属于水质净化技术领域。
【背景技术】
随着社会经济的不断进步和发展,人民生活水平的不断提高,人们对健康的要求也在不断的提高,同时环境、水质污染却日益严重,因此对于空气净化、水质净化的要求标准也越来越高,特别是人们对于饮用水的安全标准要求也越来越高。
日常用的自来水经过加氯杀菌处理后,导致大量的致癌的有机氯化物的生成,使得自来水的水质及其口感都很差;且国内的自来水均没有针对有机污染物进行净化处理。光催化技术可以杀菌和净化有机污染物,可在不用氯气的情况下对饮用水进行杀菌和有机污染物的净化,提高饮用水的质量和口感,也可以利用光催化技术直接净化游泳池而不需要投加化学药剂,可以发展为家庭、宾馆的末端光催化净化组件或大型净化组件,但此项技术具有局限性即必须保证净化处理材料的见光性。开发水不溶性的纳米无机抗菌和杀菌材料,采用无机复合氧化物制备技术,合成具有抗菌和杀菌性能的纳米无机材料以及多孔无机膜,目前已经应用于口杯的水净化及应用于抗菌电器和家具、循环冷却水、卫生陶瓷,防生物武器的杀菌过滤器等。纤维状多孔炭孔隙结构发达,表面有大量的含氧官能团,比表面积大,吸附能力强,且具有一定的强度和良好的形态,不易粉碎,在水处理中压力损失小,填充层不会轻易发生堵塞现象,再生相对容易,有望在饮用水净化中发挥积极作用,但此类材料制备成本高昂,如能降低多孔炭产品的成本,有望促进其在饮用水中的大规模应用。另纳米竹炭在水净化处理方面由于其具有的具有的强大吸附能力,释放负离子、远红外线,电磁屏蔽作用,还能把吸附的有毒物质如氨、甲醛、苯酚等分解成无毒无害的二氧化碳和水,并对吸附的细菌如葡萄球菌、大肠杆菌、白色念球菌具有良好的杀菌抑制作用,在水净化领域具有广阔的应用前景。
另外,已出现的饮用水有桶装净化水、饮用水过滤器等,对饮用水进行过滤杂质、净化、消毒、杀菌、乃至添加营养和保健成分。目前,市场上还出现了一些有改变水的pH值功能的水杯产品,例如,托玛琳活效清肠杯,利用盖上的矿物磁场和杯底的托玛琳矿石,产生永久磁场,在真空的密合回路的作用下,产生涡流磁电场引力,配合杯壁纳米银涂层的水平传导相互推动,来电解水并释放大量的活效元素,进而将普通的饮用水电解为弱碱性的生物活水。
然而,上述技术存在一定的局限性、功能单一、使用麻烦,或者基本上只是具有改变水的pH值(酸碱功能),另外有时会产生二次或多次污染的问题。特别是,现实生活中,尽管人们对饮用水采用了多种的净化方式,但忽视了纯净水中缺少了人体必需的微量元素如锗、硒等,影响了人的饮水健康。
硒是动物和人体中一些抗氧化酶(谷胱甘肽过氧化物酶)和硒-P蛋白的重要组成部分,在体内起着平衡氧化还原氛围的作用,研究证明具有提高动物免疫力作用,在国际上硒对于免疫力影响和癌症预防的研究是该领域的热点问题,因此,硒可作为动物饲料微量添加剂,也在植物肥料中添加微量元素肥,提高农副产品含硒量。硒已被作为人体必需的微量元素,目前,中国营养学会推荐的成人摄入量为每日50-250微克,而我国2/3地区硒摄入量低于最低推荐值,因此,中国是一个既有丰富硒资源,又存在大面积硒缺乏地区。补充硒的摄入对于癌症的预防、抗氧化、增强机体免疫力、防治糖尿病、防治白内障、防治心脑血管疾病、防治克山病、关节炎等具有重要的作用。
因此,寻找一种同时具备水质净化、杀菌、补充人体必需的微量元素的功能的饮用水净化材料,具有广阔的应用前景。
【发明内容】
本发明的目的是提供一种具备水质净化、杀菌、补充人体必需的微量元素硒的功能的饮用水净化材料。
本发明的目的是通过如下技术方案实现的:
本发明所述的含纳米硒的饮用水净化处理材料,含有活性炭、纳米竹炭、电气石纳米粉末、纳米硒、热溶粉末等,相关原料配比如下:
硒为人体必需的微量元素,适量补充硒可以起到预防癌症、增强免疫力、防治糖尿病、防治关节炎等疾病的作用;
电气石(托玛琳)是一种含硼及成分复杂的硅酸盐矿物,一般为柱状结晶体形态,它具有独特的电压效应和热电效应,对人体健康有多种促进作用:可发射被称为“生命之光”的波长4-14微米的远红外线,与人体远红外波长相匹配,改善机体微循环;还可释放被称为“空气维生素”的负离子。
纳米竹炭具有强大的吸附能力,释放负离子、远红外线、具有电磁屏蔽作用,还能吸附水中的有害物质如氨、甲醛、苯并分解成无毒无害的二氧化碳和水,并对吸附的细菌如葡萄球菌、大肠杆菌、白色念球菌具有良好的杀菌抑制作用。
上述技术方案的优先实施方案中,其相关原料的含量配比如下:
上述技术方案中最优的实施方案,其相关原料的含量配比如下:
在上述技术方案中,所述饮用水净化处理材料所含热熔粉末的热熔度在80-100℃、粘度2000-7500厘泊、粒度80-120目的有机树脂粉末;
在上述技术方案中,所述饮用水净化处理材料所含热熔粉末选自聚乙烯、聚氯乙烯、聚酰胺、聚酯和聚酯胺中的一种;
所述的饮用水净化处理材料是通过以下方法制备的:将纳米硒、电气石纳米粉末、热熔粉末、纳米竹炭、及余量活性炭混合搅拌10-15分钟,向一端成形模内挤压成形,成形后以80-100℃定型1分钟-3分钟。
根据本技术方案制备的饮用水净化处理材料具有如下优点:(1)提升饮用水中含有的硒微量元素并具有较高的生物活性;(2)具有独特的远红外的电磁辐射等物理性能,能有效地吸附和过滤自来水中的铁锈、悬浮物、泥沙、水中异味、藻类、絮凝化学物质、有害胶着物,去除水中有害物质和重金属微量元素。在抗菌消毒的同时,经硒过滤处理的水具有抑制癌症病情的恶化,并具有提升人体免疫细胞的功能。
【具体实施方式】
为了进一步理解本发明,以下将结合实施例对本发明做出详细的、非限定性的说明。
实施例1
将10-100nm的纳米硒4克、10-100nm的电气石纳米粉末40克、聚乙烯粉末20克、10-1000nm纳米竹炭40克、及100-120目活性炭96克,混合搅拌10分钟,搅拌均匀后,向一端成形模内挤压成形,成形后以100℃定型1分钟。
实施例2
将10-100nm的纳米硒8克、10-100nm的电气石纳米粉末30克、聚酰胺粉末50克、10-1000nm纳米竹炭50克、及100-120目活性炭62克,混合搅拌15分钟,搅拌均匀后,向一端成形模内挤压成形,成形后以80℃定型3分钟。
实施例3
将10-100nm的纳米硒6克、10-100nm的电气石纳米粉末40克、聚酯胺粉末40克、10-1000nm纳米竹炭50克、及100-120目活性炭64克,混合搅拌13分钟,搅拌均匀后,向一端成形模内挤压成形,成形后以90℃定型2分钟。
实施例4
将10-100nm的纳米硒8克、10-100nm的电气石纳米粉末40克、聚氯乙烯粉末50克、10-1000nm纳米竹炭60克、及100-120目活性炭42克,混合搅拌10分钟,搅拌均匀后,向一端成形模内挤压成形,成形后以100℃定型1分钟。
实施例5
将10-100nm的纳米硒4克、10-100nm的电气石纳米粉末40克、聚酯粉末20克、10-1000nm纳米竹炭40克、及100-120目活性炭96克,混合搅拌10分钟,搅拌均匀后,向一端成形模内挤压成形,成形后以100℃定型1分钟。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员,在不脱离本发明方法的前提下,还可以做出若干改进和补充,这些改进和补充也应视为本发明的保护。
Claims (6)
2.如权利要求1所述的含纳米硒的饮用水净化材料,其特征在于所述的各原料配比包括:
4.如权利要求1所述的含纳米硒的饮用水净化材料,其特征在于,所述的热溶粉末选自聚乙烯、聚氯乙烯、聚酰胺、聚酯和聚酯酰胺中的一种。
5.如权利要求1或4所述的含纳米硒的饮用水净化材料,其特征在于,所述饮用水净化材料所含热熔粉末为热熔度在80-100℃、粘度2000-7500厘泊、粒度80-120目的有机树脂粉末。
6.如权利要求1所述含纳米硒的饮用水净化材料的制备方法,其特征在于将纳米硒、电气石纳米粉末、纳米竹炭、热熔粉末、活性炭按上述比例称取后,混合搅拌10-15分钟,向一端成开模内挤压成形,成形后以80-100℃定型1分钟-3分钟。