CN102873731B - Wood material regeneration method - Google Patents
Wood material regeneration method Download PDFInfo
- Publication number
- CN102873731B CN102873731B CN201210360212.1A CN201210360212A CN102873731B CN 102873731 B CN102873731 B CN 102873731B CN 201210360212 A CN201210360212 A CN 201210360212A CN 102873731 B CN102873731 B CN 102873731B
- Authority
- CN
- China
- Prior art keywords
- branch
- regeneration method
- wood material
- material regeneration
- curing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a wood material regeneration method, which comprises the following steps of: (1) swelling a tree branch; (2) peeling; and (3) binding and pressing. By the technical scheme, waste tree branches can be successfully regenerated and used; and a final product is non-toxic and has an extremely good mothproof effect.
Description
Technical field
The present invention relates to a kind of timber reuse method, belong to wood processing field.
Background technology
Since reform and opening-up, with the sustainable growth of economy and improving constantly of living standards of the people, urbanization paces are accelerated, and city capital construction is fast-developing, and tourist industry, decorative craft, upholstery, catering trade, exhibition industry are surging forward.Above factors. none does not form the powerful demand to timber and goods thereof.So month by month and year by year a large amount of timber pours in city endlessly.Synchronous therewith, producing a large amount of timber " rubbish " again towards the city of the fast race of target of modernization when every day is per.In fact, be this characteristic of resource of reusable edible from timber, it is obviously extremely inappropriate for being called rubbish.Say accurately. timber discards should be referred to as.Especially in the harvesting of wood and Urban Gardens eliminate always withered, sick, rotten and be not suitable with city cultivate a large amount of pruning brush woods.This kind of brush wood is little due to diameter, and adopt conventional decortication process peeling operation loaded down with trivial details, cost is high, and tend goes out of use, and causes the waste of a large amount of timber resources.
Summary of the invention
The present invention be directed to branch waste this phenomenon serious and carry out one and innovate technologies, adopt special technological means, not only can be good at utilizing discarded brush wood to regenerate timber, and regeneration timber also having the high characteristic of nontoxic quality.
For solving the problem, the present invention by the following technical solutions:
(1) branch swelling: be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 0.4-2.0mpa, 80-120 DEG C, 1-3h, soaks 48-72 hour;
(2) peel: the branch after soaking is taken out, heated-air drying 2-4h, then the bark come off is separated with wooden by air blast;
(3) bond: adopt epoxy resin and rear abrasive dust to the 800 object fine powder of the synthesis such as mylar, curing agent, in tiling closed container, 45 DEG C time, pressure reaches 8-20mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.
Pressure described in step (1) is preferably 0.8-1.6mpa; Preferred, 1.0-1.2mpa.
The preferred 40-80 DEG C of heated-air drying described in step (2); Preferred, the every 10min of baking temperature heightens 5 DEG C, until modulation 40-80 DEG C.Slow adjustment temperature can make the tincture of iodine in even lumber and moisture, and the effect that bark is peeled off is better.
Epoxy resin described in step (3) and mylar, curing agent weight ratio are 3-8:4-8:1-3; Described curing agent is preferably one or more in 2-ethyl-4-methylimidazole, dicyandiamide or HHPA.
After soaking, the tincture of iodine immerses in timber, and after HTHP, because timber is different with the coefficient of expansion of bark, bark and timber are loosened, and even part is peeled off.Timber after immersion is through heated-air drying, and the alcohol volatilization in timber, thoroughly peels off bark and timber after iodine heating sublimation.After bark is peeled off, timber is pulverized, after grinding to form wood powder, then add that namely resin agitating is even, compressing can realize object of the present invention.
Adopt technical scheme of the present invention, achieve the regeneration of discarded branch smoothly, final product is nontoxic, also has good mothproof effect simultaneously.
Detailed description of the invention
embodiment 1
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 0.4mpa, 80 DEG C, 1h, soaks 48 hours; Taken out by branch after soaking, the every 10min of baking temperature heightens 5 DEG C, 40 DEG C of heated-air drying 2h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 3:4:1 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 8mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is 2-ethyl-4-methylimidazole, dicyandiamide and HHPA mixture.
embodiment 2
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 2.0mpa, 120 DEG C, 3h, soaks 72 hours; Taken out by branch after soaking, the every 10min of baking temperature heightens 5 DEG C, 80 DEG C of heated-air drying 4h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 8:8:3 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 20mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is 2-ethyl-4-methylimidazole and dicyandiamide mixture.
embodiment 3
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 0.8mpa, 120 DEG C, 2h, soaks 60 hours; Taken out by branch after soaking, the every 10min of baking temperature heightens 5 DEG C, 60 DEG C of heated-air drying 4h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 5:6:2 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 10mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is 2-ethyl-4-methylimidazole and HHPA mixture.
embodiment 4
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 1.6mpa, 100 DEG C, 3h, soaks 54 hours; Taken out by branch after soaking, the every 10min of baking temperature heightens 5 DEG C, 70 DEG C of heated-air drying 4h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 6:4:1 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 12mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is 2-ethyl-4-methylimidazole.
embodiment 5
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 1.0mpa, 90 DEG C, 3h, soaks 64 hours; Taken out by branch after soaking, the every 10min of baking temperature heightens 5 DEG C, 40-80 DEG C of heated-air drying 3h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 4:6:2 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 10.0mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is HHPA.
embodiment 6
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 1.2mpa, 120 DEG C, 3h, soaks 72 hours; Taken out by branch after soaking, the every 10min of baking temperature heightens 5 DEG C, 50 DEG C of heated-air drying 3h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 7:5:3 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 16mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is 2-ethyl-4-methylimidazole and dicyandiamide mixture.
embodiment 7
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 0.6mpa, 90 DEG C, 2h, soaks 72 hours; Taken out by branch after soaking, the every 10min of baking temperature heightens 5 DEG C, 45 DEG C of heated-air drying 3h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 3:8:2.5 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 18mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is dicyandiamide.
embodiment 8
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 0.4-2.0mpa, 80-120 DEG C, 1-3h, soaks 48-72 hour; Taken out by branch after soaking, the every 30min of baking temperature heightens 5 DEG C, 40-80 DEG C of heated-air drying 2-4h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 7:4:1.5 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 11mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is 2-ethyl-4-methylimidazole.
embodiment 9
Be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 1.8mpa, 110 DEG C, 2.5h, soaks 58 hours; Taken out by branch after soaking, the every 10min of baking temperature heightens 5 DEG C, 75 DEG C of heated-air drying 2-4h, more dried branch is ground into the segment of 10-20cm, and the bark come off is separated with Kimura by air blast; Adopt epoxy resin, mylar and curing agent weight ratio 7:7:3 to mix, pulverized powder crosses 800 mesh sieves, and in tiling closed container, 45 DEG C time, pressure reaches 14mpa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.Curing agent is 2-ethyl-4-methylimidazole and HHPA.
Claims (7)
1. a Wood material regeneration method, comprises the steps:
(1) branch swelling: be cut into the long section of about 0.5-1 rice by discarded, branch is placed in airtight container, adds the tincture of iodine, 0.4-2.0MPa, 80-120 DEG C, 1-3h, soaks 48-72 hour;
(2) peel: taken out by the branch after soaking, heated-air drying 2-4h, then the segment dried branch being ground into 10-20cm, air blast is by the bark that comes off and wood seperation;
(3) bond: adopt epoxy resin and mylar, rear abrasive dust to the 800 object fine powder of curing agent mixing, in tiling closed container, 45 DEG C time, pressure reaches 8-20MPa, by compressing for instantaneous high-temperature 180 DEG C of baking ovens after complete for binder powders penetrated wood, to obtain final product.
2. Wood material regeneration method according to claim 1, is characterized in that, the pressure described in step (1) is 0.8-1.6MPa.
3. Wood material regeneration method according to claim 2, is characterized in that, described pressure is 1.0-1.2MPa.
4. Wood material regeneration method according to claim 1, is characterized in that, the heated-air drying temperature 40-80 DEG C described in step (2).
5. Wood material regeneration method according to claim 4, is characterized in that, the every 10min of described baking temperature heightens 5 DEG C, until modulation 40-80 DEG C.
6. Wood material regeneration method according to claim 1, is characterized in that, the epoxy resin described in step (3) and mylar, curing agent weight ratio are 3-8:4-8:1-3.
7. the Wood material regeneration method according to claim 1 or 6, is characterized in that, described curing agent is one or more in 2-ethyl-4-methylimidazole, dicyandiamide or HHPA.