CN102864454A - Anti-abrasion and anti-corrosion composite coating for automobile brake caliper - Google Patents
Anti-abrasion and anti-corrosion composite coating for automobile brake caliper Download PDFInfo
- Publication number
- CN102864454A CN102864454A CN2012103270304A CN201210327030A CN102864454A CN 102864454 A CN102864454 A CN 102864454A CN 2012103270304 A CN2012103270304 A CN 2012103270304A CN 201210327030 A CN201210327030 A CN 201210327030A CN 102864454 A CN102864454 A CN 102864454A
- Authority
- CN
- China
- Prior art keywords
- coating
- pvd
- resistant
- pavcd
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-abrasion and anti-corrosion composite coating for an automobile brake caliper. The anti-abrasion and anti-corrosion composite coating for the automobile brake caliper is provided with a bottom layer made of ferrous material, wherein the bottom layer is provided with a PVD/PAVCD (physical vapor deposition/plasma-assisted chemical vapor deposition) coating; an anti-corrosion layer is arranged on the coating; the PVD/PAVCD coating is provided with a pore; the anti-corrosion layer extends into the pore to be contacted with the bottom layer; and another PVD/PAVCD coating is formed on the anti-corrosion layer again.
Description
Technical field
The invention belongs to field of metal surface treatment, refer to especially the wear-resistant and erosion-resisting compound coating of a kind of automobile brake caliper.
Background technology
In order to protect the member that bears friction to avoid wearing and tearing; this high worn parts of automobile brake caliper particularly; existing technology particularly has under not having lubricating status in the material of relative movement generally by adopting coating way, by means of anti-wear more and more important with application corrosion-resistant coating.
Existing the whole bag of tricks improves rubbing characteristics targetedly, but these methods can't realize better anticorrosion effect, and does not have enough rubbing characteristicss such as wear-resistant degree according to the corrosion-resistant coating that prior art provides.Existing known anti-wear employing PVD (physical vapor deposition) or PAVCD (plasma auxiliary chemical vapor deposition) apply; the method wear-resistant respond well but corrosion resistance not enough; for protection against corrosion; known technology is to electroplate or chemistry or autocatalysis mode are come stopping off, but the abrasion resistance properties of this protective layer is very low.
Be again anti abrasive protected mode of protection against corrosion in order to solve; prior art has proposed the mixed bedding opinion; namely after the member bottom applies corrosion-resistant coating, apply again PVD or PAVCD layer first, or on the member bottom, apply first first PVD or PAVCD layer and then coating corrosion-resistant coating.Although this composite bed mode can solve wear-resistant and anticorrosive problem in some aspects simultaneously, if the duty etch resistant layer then can't solve wear-resistant problem upper, if anti abrasion layer upper then when sport injury occurring, corrosion that on the contrary can acceleration means.
Summary of the invention
The objective of the invention is to improve existing rub resistance and erosion-resisting composite bed system, realizing that this composite bed namely has good rubbing characteristics and has again good anti-corrosion property, and technique is simple.
The present invention is achieved by the following technical solutions:
A kind of automobile brake caliper is wear-resistant and erosion-resisting compound coating, has the bottom of being made by ferrous material, has the PVD/PAVCD coating on the described bottom, and has corrosion-resistant coating on this coating; Described PVD/PAVCD coating has hole, and described corrosion-resistant coating extend among the hole and with bottom and contacts; On described corrosion-resistant coating, form again the PVD/PAVCD coating.
Described corrosion-resistant coating namely has the covalent compound attribute, has again ionic compound or metallic compound attribute.
The thickness of described outermost layer PVD/PAVCD coating is the 1/5-1/3 of the PVD/PAVCD coat-thickness of internal layer.
Described corrosion-resistant coating is to have plating, coating chemistry or autocatalysis.
The manufacture method of described wear-resistant and erosion-resisting compound coating may further comprise the steps:
1), provides the bottom of being made by ferrous material;
2), the PVD/PAVCD coating is coated on the described bottom;
Erosion shield that 3), will electroplate, chemistry or autocatalysis is coated on the described PVD/PAVCD coating;
4), again a PVD/PAVCD coating is coated on 3) on the coating.
The invention has the beneficial effects as follows:
When guaranteeing abrasion resistance properties, provide corrosion resistance, and corrosion resistance has improved erosion resistance not directly in the face of friction layer.
Embodiment
Below the present invention is described in detail, a kind of automobile brake caliper is wear-resistant and erosion-resisting compound coating, has the bottom of being made by ferrous material, has the PVD/PAVCD coating on the described bottom, and has corrosion-resistant coating on this coating; Described PVD/PAVCD coating has hole, and described corrosion-resistant coating extend among the hole and with bottom and contacts; On described corrosion-resistant coating, form again the PVD/PAVCD coating.
Described corrosion-resistant coating namely has the covalent compound attribute, has again ionic compound or metallic compound attribute.
The thickness of described outermost layer PVD/PAVCD coating is the 1/5-1/3 of the PVD/PAVCD coat-thickness of internal layer.
Described corrosion-resistant coating is to have plating, coating chemistry or autocatalysis.
Described a kind of automobile brake caliper is wear-resistant and the manufacture method of erosion-resisting compound coating, may further comprise the steps:
1), provides the bottom of being made by ferrous material;
2), the PVD/PAVCD coating is coated on the described bottom;
Erosion shield that 3), will electroplate, chemistry or autocatalysis is coated on the described PVD/PAVCD coating;
4), again a PVD/PAVCD coating is coated on 3) on the coating.
Claims (5)
1. the wear-resistant and erosion-resisting compound coating of automobile brake caliper has the bottom of being made by ferrous material, it is characterized in that: have the PVD/PAVCD coating on the described bottom, and have corrosion-resistant coating on this coating; Described PVD/PAVCD coating has hole, and described corrosion-resistant coating extend among the hole and with bottom and contacts; On described corrosion-resistant coating, form again the PVD/PAVCD coating.
2. the wear-resistant and erosion-resisting compound coating of automobile brake caliper according to claim 1, it is characterized in that: described corrosion-resistant coating namely has the covalent compound attribute, has again ionic compound or metallic compound attribute.
3. the wear-resistant and erosion-resisting compound coating of automobile brake caliper according to claim 1, it is characterized in that: the thickness of described outermost layer PVD/PAVCD coating is the 1/5-1/3 of the PVD/PAVCD coat-thickness of internal layer.
4. the wear-resistant and erosion-resisting compound coating of automobile brake caliper according to claim 1 and 2 is characterized in that: described corrosion-resistant coating is to have plating, coating chemistry or autocatalysis.
5. the manufacture method of the wear-resistant and erosion-resisting compound coating of described automobile brake caliper according to claim 1 is characterized in that: may further comprise the steps:
1), provides the bottom of being made by ferrous material;
2), the PVD/PAVCD coating is coated on the described bottom;
Erosion shield that 3), will electroplate, chemistry or autocatalysis is coated on the described PVD/PAVCD coating;
4), again a PVD/PAVCD coating is coated on 3) on the coating.