CN102863806A - 一种高弹性废旧沥青改性剂及其制备方法 - Google Patents

一种高弹性废旧沥青改性剂及其制备方法 Download PDF

Info

Publication number
CN102863806A
CN102863806A CN2012103929468A CN201210392946A CN102863806A CN 102863806 A CN102863806 A CN 102863806A CN 2012103929468 A CN2012103929468 A CN 2012103929468A CN 201210392946 A CN201210392946 A CN 201210392946A CN 102863806 A CN102863806 A CN 102863806A
Authority
CN
China
Prior art keywords
preparation
waste asphalt
asphalt modifier
snappiness
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103929468A
Other languages
English (en)
Other versions
CN102863806B (zh
Inventor
张少高
黄燕生
曾小华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen City Kezhongda Traffic Building Material Co Ltd
Original Assignee
Shenzhen City Kezhongda Traffic Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen City Kezhongda Traffic Building Material Co Ltd filed Critical Shenzhen City Kezhongda Traffic Building Material Co Ltd
Priority to CN201210392946.8A priority Critical patent/CN102863806B/zh
Publication of CN102863806A publication Critical patent/CN102863806A/zh
Application granted granted Critical
Publication of CN102863806B publication Critical patent/CN102863806B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高弹性废旧沥青改性剂及其制备方法，其配方为：含芳香分重质油75％-90％，增溶分散剂3％-5％，粘合树脂20％-30％，蜡晶分散剂2％-5％，防老化剂1％-2％。采用本发明配方制备的高弹性废旧沥青改性剂具有良好的可塑性和高抗变形能力。

Description

一种高弹性废旧沥青改性剂及其制备方法
技术领域
本发明属于废旧沥青再生技术，具体是涉及一种高弹性废旧沥青改性剂及其制备方法。
背景技术
沥青在长期使用过程中所表现出的物化性质或机械性能的不可逆变化称为老化，包括物理老化喝化学老化。沥青在老化过程中的宏观上表现为软化点升高、针入度降低及延度下降等使用性能的衰竭。
我国每年约需要高质量的沥青4Mt，其中70％左右用于修建道路路面。沥青路面经过一定年限的使用，受交变应力、循环应力以及沥青老化和冰冻、高温的交替作用，会出现诸如网裂、车辙、沉陷、、等各种病害，并逐步扩展。维护处理的方法就是对出现病害的路面进行铣刨，然后重新铺筑。这样每年会产生相当数量的沥青混合料废弃物。这些废弃物造成三大问题：一是堆放需要场地，二是污染环境，三是浪费了大量的不可再生资源。道路沥青的再生利用，能够节约大量的沥青，节约工程成本，同时有利于处理废料、保护环境，因而具有显著的经济效益和社会、环境效益。今年来，随着人们对环保、社会效益的关注，道路沥青的再生利用技术越来越受到重视。
发明内容
本发明的目的在于提供一种具有良好的可塑性和高抗变形能力的高弹性废旧沥青改性剂及其制备方法。
为实现上述目的，本发明采用如下技术方案：
一种高弹性废旧沥青改性剂及其制备方法，包括组分和含量(重量百分数)：
Figure BSA00000790036900011
更优的是：所述的含芳香分重质油为环烷基原油的减三或减四馏分油、糠醛抽出油、催化裂化油、润滑油中的一种或几种。
更优的是：所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的增溶分散剂为阴离子含氟表面活性剂中的羧酸盐、硬酸盐、磷酸盐类中的一种。
更优的是：所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的粘合树脂为为石油树脂；即一种由石油裂解所副产的C5、C9馏份，经前处理、聚合、蒸馏等工艺生产的一种热塑性树脂，为分子量介于300-3000的低聚物。
更优的是：所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的蜡晶分散剂为3，6-氧桥-1，2，3，6-四氢笨-1，2-二甲酸高级酰胺。
更优的是：所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的防老化剂为6-乙氧基-2，2，4-三甲基-1，2-二氢化喹啉、2，2，4-1，2-二氢化喹聚合体、N-苯基-α-苯胺、N-苯基-β-苯胺、2，6-二叔丁基-4-甲基苯酚中的一种或几种混合。
本发明还提供了一种制备高弹性废旧沥青改性剂及其制备方法的方法，包括步骤：在搅拌状态下把含芳香分重质油加温到80℃-90℃，将石油树脂投入重质油中，升温，在100℃-130℃状态下搅拌一个小时，待冷却到60℃-65℃时投入增溶分散剂、蜡晶分散剂和防老化剂，继续搅拌30分钟后，冷却至常温下得到粘稠的液态混合物即为本发明产物。
具体实施方式
下面结合具体实施例对本发明做进一步详细说明。
实施例1
在搅拌状态下将72％环烷基原油的减三或减四馏分油加温到80℃-90℃，再将20％石油树中，升温，在100℃-130℃状态下搅拌一个小时，待冷却到60℃-65℃时投入增溶分散剂、蜡晶分散剂和防老化剂，继续搅拌30分钟后，冷却至常温下得到粘稠的液态混合物即为本发明产物。
具体实施方式
下面结合具体实施例对本发明做进一步详细说明。
实施例1
在搅拌状态下将72％环烷基原油的减三或减四馏分油加温到80℃-90℃，再将20％石油树脂投入环烷基原油的减三或减四馏分油中，升温，在100℃-130℃状态下搅拌一个小时，待冷却到60℃-65℃时再分别投入4％增溶分散剂、3％蜡晶分散剂和1％防老化剂，继续搅拌30分钟后，冷却至常温下得到粘稠的液态混合物即为本发明所述的一种高弹性废旧沥青改性剂。
实施例2
在搅拌状态下将70％催化裂化油加温到80℃-90℃，再将24％石油树脂投入环烷基原油的减三或减四馏分油中，升温，在100℃-130℃状态下搅拌一个小时，待冷却到60℃-65℃时再分别投入3％增溶分散剂、2％蜡晶分散剂和1％防老化剂，继续搅拌30分钟后，冷却至常温下得到粘稠的液态混合物即为本发明所述的一种高弹性废旧沥青改性剂。
实施例3
在搅拌状态下将73％糠醛抽出油加温到80℃-90℃，再将20％石油树脂投入环烷基原油的减三或减四馏分油中，升温，在100℃-130℃状态下搅拌一个小时，待冷却到60℃-65℃时再分别投入3％增溶分散剂、3％蜡晶分散剂和1％防老化剂，继续搅拌30分钟后，冷却至常温下得到粘稠的液态混合物即为本发明所述的一种高弹性废旧沥青改性剂。
以上内容是结合具体的优选实施方式对本发明所作的进一步详细说明，不能认定本发明的具体实施只局限于这些说明。对于本发明所属技术领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干简单推演或替换，都应当视为属于发明型的保护范围。

Claims (7)

1.一种高弹性废旧沥青改性剂及其制备方法，包括组分和含量(重量百分数)：
Figure FSA00000790036800011
2.如权利要求1所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的含芳香分重质油为环烷基原油的减三或减四馏分油、糠醛抽出油、催化裂化油、润滑油中的一种或几种。
3.如权利要求1所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的增溶分散剂为阴离子含氟表面活性剂中的羧酸盐、硬酸盐、磷酸盐类中的一种。
4.如权利要求1所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的粘合树脂为为石油树脂；即一种由石油裂解所副产的C5、C9馏份，经前处理、聚合、蒸馏等工艺生产的一种热塑性树脂，为分子量介于300-3000的低聚物。
5.如权利要求1所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的蜡晶分散剂为3，6-氧桥-1，2，3，6-四氢笨-1，2-二甲酸高级酰胺。
6.如权利要求1所述的高弹性废旧沥青改性剂及其制备方法，其特征是：所述的防老化剂为6-乙氧基-2，2，4-三甲基-1，2-二氢化喹啉、2，2，4-1，2-二氢化喹聚合体、N-苯基-α-苯胺、N-苯基-β-苯胺、2，6-二叔丁基-4-甲基苯酚中的一种或几种混合。
7.权利要求1～7任意一项所述沥青混合料改性剂的制备方法，包括步骤：
在搅拌状态下把含芳香分重质油加温到80℃-90℃，将石油树脂投入重质油中，升温，在100℃-130℃状态下搅拌一个小时，待冷却到60℃-65℃时投入增溶分散剂、蜡晶分散剂和防老化剂，继续搅拌30分钟后，冷却至常温下得到粘稠的液态混合物即为本发明产物。
CN201210392946.8A 2012-10-16 2012-10-16 一种高弹性废旧沥青改性剂及其制备方法 Active CN102863806B (zh)