CN102863732A - Low-temperature impact-resistant extrusion-grade acrylonitrile butadiene styrene (ABS) alloy material - Google Patents
Low-temperature impact-resistant extrusion-grade acrylonitrile butadiene styrene (ABS) alloy material Download PDFInfo
- Publication number
- CN102863732A CN102863732A CN2012103361996A CN201210336199A CN102863732A CN 102863732 A CN102863732 A CN 102863732A CN 2012103361996 A CN2012103361996 A CN 2012103361996A CN 201210336199 A CN201210336199 A CN 201210336199A CN 102863732 A CN102863732 A CN 102863732A
- Authority
- CN
- China
- Prior art keywords
- alloy material
- low
- abs
- temperature impact
- grade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a low-temperature impact-resistant extrusion-grade acrylonitrile butadiene styrene (ABS) alloy material which comprises 70-95% of ABS resin, 0.1-20% of high glue powder (HRG), 0.1-10% of ethylene-vinyl alcohol (EVA), 0.01-1% of antioxidant and 0.01-1% of lubricating agent. The EVA is taken as toughening agent which is matched with the general HRG, so that the low-temperature impact-resistant extrusion-grade ABS alloy material can be obtained; the notch impact strengths of the alloy material respectively meet the lowest requirement of 16 KJ/m<2> and 20KJ/m<2> in the environment of 40 DEG C below zero along the transverse direction and the longitudinal direction, so that the alloy material meets the using requirements of a user; and the alloy material is simple in operation technology and has wide application prospect.
Description
Technical field
The present invention relates to technical field of polymer materials, be specifically related to a kind of low-temperature impact-resistant extrusion-grade ABS alloy material.
Background technology
ABS resin is with propylene cyanogen, divinyl, vinylbenzene is the synthetic terpolymer of monomer, can embody three kinds of synergisticing performances between the component, has high impact, high heat-resisting, resistance to chemical attack, electrical insulation capability is good, dimensional stability is excellent, molding shrinkage is little, the excellent specific properties such as processing characteristics is good, and prepared product appearance glossiness is good, can electroplate, the secondary processing such as spraying, be widely used in electronics, automotive industry, household electrical appliance, office equipment, electric product, the fields such as Communication Equipment are that a kind of consumption is large, broad-spectrum engineering plastics; Wherein, the ABS material of extrusion grade is mainly used in the fields such as household electrical appliances, automobile, and all there is the extrusion-grade ABS trade mark of oneself in each company, and the most general is strange beautiful 749SK and D120 of Taiwan.
Yet ABS extrusion board impact property at low temperatures is lower, can not satisfy client's requirement, as: strange beautiful D120 extrusion board is under the environment of 40 degrees below zero, and horizontal notched Izod impact strength is 12KJ/m
2, notched Izod impact strength is 16KJ/m longitudinally
2, so just cause this material can not be used for the automotive field of having relatively high expectations.The horizontal low temperature notched shock strength that automotive field requires to extrude ABS sheet material is not less than 16KJ/m
2, vertically the low temperature notched shock strength is not less than 20KJ/m
2, existing material can't reach high like this performance requriements, thereby has limited its further application.For improving the shock strength of material, generally realize by in material prescription, increasing toughner, common toughner is high glue powder or MBS, but the adding of high glue powder or MBS can not significantly improve the low-temperature impact-resistant intensity of alloy material, and prepared material can't reach above-mentioned requirements.The low temperature impact properties that how to increase ABS sheet material has been the primary study direction of each material producer.
Summary of the invention
The technical problem to be solved in the present invention is: a kind of low-temperature impact-resistant extrusion-grade ABS alloy material is provided, and the horizontal and vertical low temperature notched shock strength of the extrusion board of this alloy material is higher than respectively 16KJ/m
2And 20KJ/m
2
To achieve these goals, the technical solution used in the present invention is: a kind of low-temperature impact-resistant extrusion grade AB S alloy material, and by mass percentage, the prescription of this alloy material is:
ABS resin 70%～95%;
High glue powder (HRG) 0.1%～20%;
Ethylene-vinyl acetate (EVA) 0.1%～10%;
Oxidation inhibitor 0.01%～1.0%;
Lubricant 0.01%～1.0%;
The sum of said components is controlled to be 100%.
Described ABS resin is propylene cyanogen-divinyl and the styrol copolymer of low melt index, and its melting how is 1～10g/10min.
Described oxidation inhibitor is phosphorous acid esters and/or Hinered phenols antioxidant, is specially: irgasfos 168,1010,1076,245 or B900 in one or several.
Described lubricant is one or more in silicone oil, white mineral oil, Magnesium Stearate (MgSt), barium stearate (BaSt), calcium stearate (CaSt), Zinic stearas (ZnSt), sodium stearate (NaSt), pentaerythritol stearate (PETS), vinyl bis-stearamides (EBS) or the OP wax.
A kind of low-temperature impact-resistant extrusion-grade ABS alloy material, adopt following preparation technology:
With the proportionally weighing of ABS resin, HRG, EVA, oxidation inhibitor, lubricant, in high-speed mixer, fully mix, send into twin screw extruder through measuring apparatus, conveying, shearing and mixing lower at screw rod, material melting, compound, again through extrude, tie rod, cooling, pelletizing, packing, obtain low-temperature impact-resistant extrusion-grade ABS alloy material.
Described twin screw extruder has temperature control unit and vacuum extractor, and screw slenderness ratio is 36～44, and extruder temperature is controlled at 180～240 ℃, and the screw speed scope is 50～1200rpm.
EVA in the prescription of the present invention is polar material; its in system with AB S in propylene cyanogen interact to form the EVA protective layer; this protective layer protects rigidity propylene cyanogen and vinylbenzene to avoid external impact and break in low temperature environment; thereby improve the resistance to low temperature of system; extrusion board still has preferably toughness at low temperatures; in-40 ℃ environment, horizontal and vertical upper notched Izod impact strength satisfies respectively 16KJ/m
2And 20KJ/m
2Minimum requirements.
Beneficial effect: compared with prior art, the present invention adopts EVA as toughner, cooperates general toughner high glue powder, obtains a kind of low-temperature impact-resistant extrusion-grade ABS alloy material, this alloy material is in-40 ℃ environment, and horizontal and vertical upper notched Izod impact strength satisfies respectively 16KJ/m
2And 20KJ/m
2Minimum requirements, can satisfy client's service requirements, operating procedure is simple, has broad application prospects.
Embodiment
The invention will be further described below in conjunction with specific embodiment, and listed embodiment only is further described the present invention, and is not thereby limiting the invention.
ABS resin is strange beautiful D120,3513 of Gaoqiao Petrochemical Company; High glue powder is IM5100AH(Thailand petrochemical industry); EVA is the EVA260 of Du Pont; Oxidation inhibitor is 168 and 1076 of Ciba; Lubricant is the Magnesium Stearate (MgSt) of Faci.
At first with above-mentioned ABS resin D120,3513, toughner IM5100AH, EVA260, oxidation inhibitor, lubricant proportionally prepare, and stir through high-speed mixer, mix; Then the said mixture accurate measurement is sent in the forcing machine, in the shearing of twin screw, conveying, mixing lower, fully fusing, compound, again through head extrude, tie rod, pelletizing, drying, be packaged as at last finished product.
The screw slenderness ratio of twin screw extruder is 40, and the front end Temperature Setting is 190 ℃, and the stage casing Temperature Setting is 200 ℃, and the head extrusion temperature is 210 ℃, and screw speed is 350rpm.
The concrete ratio of each component is as shown in table 1 among the embodiment.
Table 1:
| Component | Comparative Examples 1 | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| D120 | 49.5 | 49.5 | 49.5 | 49.5 |
| 3513 | 30 | 30 | 30 | 30 |
| IM5100AH | 20 | 17 | 15 | 13 |
| EVA260 | 3 | 5 | 7 | |
| 168 | 0.1 | 0.1 | 0.1 | 0.1 |
| 1076 | 0.1 | 0.1 | 0.1 | 0.1 |
| MgSt | 0.3 | 0.3 | 0.3 | 0.3 |
The material sample that each embodiment is prepared directly cuts into various standard Mechanics Performance Testing battens according to national standard from its extrusion board, test according to standard, and standard is as shown in table 2:
Table 2:
| Physicals | Testing method |
| Melting index (220 ℃ of 10Kg@) | GB/T 3682 |
| Tensile strength (50mm/min) | GB/T 1040 |
| Modulus in flexure (2mm/min) | GB/T 9341 |
| Notched Izod impact strength (4.0mm) | GB/T 1043 |
The performance test data of embodiment sample is shown in Table 3:
Table 3:
As can be seen from the above-described embodiment, the sheet material of low-temperature impact-resistant extrusion-grade ABS alloy material preparation of the present invention, its low temperature is improved to notched Izod impact strength in length and breadth, considerable change does not occur in other performance index simultaneously, improved the overall performance of product, satisfy the service requirements of high-end customer, expanded the Application Areas of product.
Claims (4)
1. low-temperature impact-resistant extrusion-grade ABS alloy material, it is characterized in that: by mass percentage, the prescription of this alloy material is:
ABS resin 70%～95%;
HRG 0.1%～20%；
EVA 0.1%～10%；
Oxidation inhibitor 0.01%～1.0%;
Lubricant 0.01%～1.0%;
The sum of said components is controlled to be 100%.
2. low-temperature impact-resistant extrusion grade AB S alloy material as claimed in claim 1, it is characterized in that: described ABS resin is propylene cyanogen-divinyl and the styrol copolymer of low melt index, and its melting index scope is 1～10g/10min.
3. low-temperature impact-resistant extrusion grade AB S alloy material as claimed in claim 1 is characterized in that: described oxidation inhibitor be irgasfos 168,1010,1076,245 or B900 in one or several.
4. low-temperature impact-resistant extrusion grade AB S alloy material as claimed in claim 1, it is characterized in that: described lubricant is one or more in silicone oil, white mineral oil, MgSt, BaSt, CaSt, ZnSt, NaSt, PETS, EBS or the OP wax.