CN102863675A - ABS (acrylonitrile-butadiene-styrene) white functional master batch - Google Patents
ABS (acrylonitrile-butadiene-styrene) white functional master batch Download PDFInfo
- Publication number
- CN102863675A CN102863675A CN2012103500607A CN201210350060A CN102863675A CN 102863675 A CN102863675 A CN 102863675A CN 2012103500607 A CN2012103500607 A CN 2012103500607A CN 201210350060 A CN201210350060 A CN 201210350060A CN 102863675 A CN102863675 A CN 102863675A
- Authority
- CN
- China
- Prior art keywords
- parts
- abs
- master batch
- functional master
- white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an ABS (acrylonitrile-butadiene-styrene) white functional master batch, belonging to the technical field of high polymer materials. The ABS white functional master batch is prepared from the following raw materials in parts by weight: 10-20 parts of silicon dioxide, 40-50 parts of titanium white, 2-3 parts of lubricant, 0.3-0.8 parts of coupling agent and 10-20 parts of compound resin. The invention can easily control the cost, can be easily dispersed, has the advantages of uniform color and the like, and can not easily generate dust.
Description
Technical field
The invention belongs to technical field of polymer materials, be specifically related to a kind of ABS white functional master batch
Background technology
The problems such as adding man-hour, normal operation toner or Masterbatch are painted, but there is easy diffusion in Masterbatch, pollutes the shortcoming of operating area, is seldom adopted by producer, and colour batch easy color and luster inequality that occurs when painted, and aberration is restive.Therefore, when the ABS material was painted, control color and luster all even aberration was the problem of needing at present solution badly
Summary of the invention
Task of the present invention is to provide a kind of ABS white functional master batch, has to be easy to disperse the uniform characteristics of color and luster.
Task of the present invention is finished like this, a kind of ABS white functional master batch, and its raw material by following parts by weight forms:
0 ~ 20 part of silica 1;
40 ~ 50 parts of titanium dioxides;
2 ~ 3 parts of lubricants;
0.3 ~ 0.8 part of coupling agent;
10 ~ 20 parts of compound resins.
In a specific embodiment of the present invention, described silicon-dioxide is the silicon-dioxide that vapor phase process is produced.
In another specific embodiment of the present invention, described titanium dioxide is anatase thpe white powder.
In another specific embodiment of the present invention, described lubricant is stearic acid.
In another specific embodiment of the present invention, described coupling agent is γ-mercaptopropyl trimethoxysilane.
Also have in the specific embodiment of the present invention, described compound resin is that 80% polyethylene and mass percent are that 20% ABS resin forms by mass percent.
Have cost by ABS white functional master batch provided by the invention and be easy to control, be easy to disperse, color and luster is even, is difficult for producing the strong points such as dust.
Embodiment
Embodiment 1:
20 parts of the silicon-dioxide that vapor phase process is produced;
40 parts of anatase thpe white powders;
2 parts of stearic acid;
0.6 part of γ-mercaptopropyl trimethoxysilane;
Compound resin (mass percent is that 80% polyethylene and mass percent are that 20% ABS resin forms)
16 parts.
Embodiment 2:
0 part of the silica 1 that vapor phase process is produced;
45 parts of anatase thpe white powders;
2.2 parts of stearic acid;
0.3 part of γ-mercaptopropyl trimethoxysilane;
Compound resin (mass percent is that 80% polyethylene and mass percent are that 20% ABS resin forms)
10 parts.
Embodiment 3:
5 parts of the silica 1s that vapor phase process is produced;
42 parts of anatase thpe white powders;
2.6 parts of stearic acid;
0.5 part of γ-mercaptopropyl trimethoxysilane;
Compound resin (mass percent is that 80% polyethylene and mass percent are that 20% ABS resin forms)
20 parts.
Embodiment 4:
8 parts of the silica 1s that vapor phase process is produced;
44 parts of anatase thpe white powders;
3 parts of stearic acid;
0.8 part of γ-mercaptopropyl trimethoxysilane;
Compound resin (mass percent is that 80% polyethylene and mass percent are that 20% ABS resin forms)
15 parts
Claims (6)
1.
A kind of ABS white functional master batch is characterized in that its raw material by following parts by weight forms:
0 ~ 20 part of silica 1;
40 ~ 50 parts of titanium dioxides;
2 ~ 3 parts of lubricants;
0.3 ~ 0.8 part of coupling agent;
10 ~ 20 parts of compound resins.
2.
ABS white functional master batch according to claim 1 is characterized in that described silicon-dioxide is the silicon-dioxide that vapor phase process is produced.
3.
ABS white functional master batch according to claim 1 is characterized in that described titanium dioxide is anatase thpe white powder.
4.
ABS white functional master batch according to claim 1 is characterized in that described lubricant is stearic acid.
5.
ABS white functional master batch according to claim 1 is characterized in that described coupling agent is γ-mercaptopropyl trimethoxysilane.
6.
ABS according to claim 1 white functional master batch is characterized in that described compound resin is that 80% polyethylene and mass percent are that 20% ABS resin forms by mass percent