CN102863252B - 一种发泡水泥保温板用稳泡分散剂 - Google Patents

一种发泡水泥保温板用稳泡分散剂 Download PDF

Info

Publication number
CN102863252B
CN102863252B CN201210402086.1A CN201210402086A CN102863252B CN 102863252 B CN102863252 B CN 102863252B CN 201210402086 A CN201210402086 A CN 201210402086A CN 102863252 B CN102863252 B CN 102863252B
Authority
CN
China
Prior art keywords
dispersion agent
stearate
foaming
agent
insulation board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210402086.1A
Other languages
English (en)
Other versions
CN102863252A (zh
Inventor
顾建荣
周松涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG XINBANG CHEMICAL CO Ltd
Original Assignee
NANTONG XINBANG CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG XINBANG CHEMICAL CO Ltd filed Critical NANTONG XINBANG CHEMICAL CO Ltd
Priority to CN201210402086.1A priority Critical patent/CN102863252B/zh
Publication of CN102863252A publication Critical patent/CN102863252A/zh
Application granted granted Critical
Publication of CN102863252B publication Critical patent/CN102863252B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种发泡水泥保温板用稳泡分散剂，它包含以下几种成分，工业硬脂酸钙、硬脂酸锌、硬脂酸铝、硬脂酸镁中的一种或几种复配物，轻质碳酸钙，水溶性高分子化合物如明胶、阿拉伯胶、羧甲基纤维素钠、三乙醇胺、脂肪醇聚氧乙烯醚硫酸钠的一种或几种复配物。按重量计，他们百分比如下：工业硬脂酸盐：20-80%；轻质碳酸钙：70-19%；水溶性高分子化合物：1-10%。本发明将发泡水泥保温板生产用助剂如防水剂、悬浮剂、稳泡剂、泡沫增强剂有机复配成一体，使用该产品生产发泡水泥保温板时工艺简化、质量稳定，能有效解决他们分开使用或单独使用时拌料不均易造成塌模、气泡大小不均（直径∮≤10mm）、分布不匀的产品缺陷。

Description

一种发泡水泥保温板用稳泡分散剂
技术领域
本发明涉及建筑材料领域，具体说是发泡水泥保温板生产用的稳泡分散剂，是一种生产用助剂。
背景技术
随着国家对建筑节能要求不断提高，内外墙体防火阻燃保温材料不断涌现，但质量和性能千差万别，主要是防火阻燃性能不佳，近年来央视新址大楼大火、上海静安寺教师公寓大火等高层建筑大火损失惨重，外墙装修的保温材料可燃是主要原因。公通字【2009】46号《民用建筑外保温系统及外墙装饰防火暂行规定》和公通字【2011】65号《关于进一步明确民用建筑外墙保温材料消防监督管理有关要求的通知》明确要求阻燃性能A1级，特别是对高层建筑外墙保温禁止使用有机发泡材料。发泡水泥保温板以其质轻、不燃性等优点满足要求，市场迅速扩大，厂家和产量也猛增，但由于技术水平参差不齐，质量时好时坏，主要是生产时易塌模、气泡大小不均、分布不匀，次品率高，这些问题困扰了一些厂家，我们发明的发泡水泥保温板用稳泡分散剂能有效帮助他们改善产品质量，因此市场前景十分广阔。
发明内容
本发明所要解决的技术问题是生产水泥发泡保温板时易塌模、气泡大小不均、分布不匀，次品率高，目的是通过提供发泡水泥保温板用稳泡分散剂配方及生产方法。生产发泡水泥保温板用稳泡分散剂满足发泡水泥保温板行业稳定发展需求。
本发明的技术方案：
将发泡水泥保温板生产用助剂如防水剂、悬浮剂、稳泡剂、泡沫增强剂有机复配成一体，生产出一种发泡水泥保温板用稳泡分散剂，克服它们分开使用是物料配比不准确，分散不均匀，使用效果不好的难题。该助剂的使用，气泡壁加厚，气孔稳定，孔径小（直径∮≤5mm），分布匀称。
本发泡水泥保温板用稳泡分散剂，按重量百分比组成为：
工业硬脂酸盐：20-80%；
轻质碳酸钙：70-19%；
水溶性高分子化合物：1-10%。
一种发泡水泥保温板用稳泡分散剂的制备方法：
将固体物料粉碎至粒径小于120目，各种物料均匀加入搅拌锅中搅拌混合均匀，再用锤片式粉碎机粉碎混合，经旋风分离器收集为成品。
本发明的优点：
1.制备工艺简单，不易变质，运输方便；
2.生产发泡水泥保温板时添加该助剂有利于气泡壁加厚，气孔稳定，孔径小（直径∮≤5mm），分布匀称；
3.该助剂适用性广，可用于硫铝酸水泥或525高标号普通硅酸盐水泥制作发泡水泥保温板，也可用于多孔性其他轻质墙体材料；
4.使用方法简单，按规定或推荐量加入水泥、粉煤灰等原料中搅拌均匀即可。
具体实施方式
实施例1：
将工业硬脂酸钙、硬脂酸镁，轻质碳酸钙，羧甲基纤维素钠、脂肪醇聚氧乙烯醚硫酸钠用120目筛过筛，进行复配，搅拌混合均匀，用锤片式粉碎机再粉碎至120——200目，经旋风分离器常规分离后包装的成品。
其上述原料重量百分比为：
工业硬脂酸钙：20
工业硬脂酸镁：5
轻质碳酸钙：73
羧甲基纤维素钠：1
脂肪醇聚氧乙烯醚硫酸钠：1
制备的稳泡分散剂的掺入量为水泥总重量的5%，搅拌混合均匀使用，制得长60cm，宽60cm，厚5.0cm的板材。
实施例2：
将工业硬脂酸钙、硬脂酸镁，轻质碳酸钙，羧甲基纤维素钠、脂肪醇聚氧乙烯醚硫酸钠用120目筛过筛，进行复配，搅拌混合均匀，用锤片式粉碎机再粉碎至120——200目，经旋风分离器常规分离后包装的成品。
其上述原料重量百分比为：
工业硬脂酸钙：45
工业硬脂酸镁：6
轻质碳酸钙：45
羧甲基纤维素钠：2
脂肪醇聚氧乙烯醚硫酸钠：2
制备的稳泡分散剂的掺入量为水泥总重量的3%，搅拌混合均匀使用，制得长60cm，宽60cm，厚5cm的板材。
实施例3：
将工业硬脂酸钙、硬脂酸镁，轻质碳酸钙，羧甲基纤维素钠、脂肪醇聚氧乙烯醚硫酸钠用120目筛过筛，进行复配，搅拌混合均匀，用锤片式粉碎机再粉碎至120——200目，经旋风分离器常规分离后包装的成品。
其上述原料重量百分比为：
工业硬脂酸钙：70
工业硬脂酸镁：10
轻质碳酸钙：15
羧甲基纤维素钠：3
脂肪醇聚氧乙烯醚硫酸钠：2
制备的稳泡分散剂的掺入量为水泥总重量的1%，搅拌混合均匀使用，制得长60cm，宽60cm，厚5cm的板材。
试验：
将上述实施例1-3的板材进行检测，结果如下：
1.保温性能优：导热系数为0.080－0.125 W/(mk)，热阻约为普通混凝土的20－30倍；
2.燃烧性能：不能燃烧。燃烧等级A级；
3.隔音效果佳：泡沫混凝土中包含大量的独立气泡，且分布均匀，吸音能力为0.12－0.30%，是普通混凝土的6-7倍，具备有效隔音的功能；
4.密度低：干体积密度为小于250 kg /m3，是普通混凝土密度的1/5－1/8，可减轻建筑物整体荷载；
5.抗压强度较高：抗压强度为3.8-5.6Mpa；
6.较好的防水性：独立密集的气泡及良好的整体性，使其具有一定的防水性能；
7.抗裂纹：收缩率低，抗裂性是普通混凝土的8倍；
8.寿命长：与主体工程寿命相同。

Claims (1)

1.一种发泡水泥保温板用稳泡分散剂，其特征在于：稳泡分散剂的重量百分比组成为：
     工业硬脂酸盐 20-80%
轻质碳酸钙   70-19%
水溶性高分子化合物 1-10%；
制备工艺如下：将固体物料用锤片式粉碎机粉碎至粒径小于120目，各种物料均匀加入搅拌锅中搅拌混合均匀，再用锤片式粉碎机粉碎混合，经旋风分离器收集为成品；
所述的工业硬脂酸盐为硬脂酸钙或硬脂酸锌或硬脂酸铝或硬脂酸镁中的一种或几种复配物；
所述的水溶性高分子化合物为明胶或阿拉伯胶或羧甲基纤维素钠或脂肪醇聚氧乙烯醚硫酸钠中的一种或几种。
CN201210402086.1A 2012-10-22 2012-10-22 一种发泡水泥保温板用稳泡分散剂 Active CN102863252B (zh)