CN102863250A - 无机水泥发泡外墙保温板配方 - Google Patents
无机水泥发泡外墙保温板配方 Download PDFInfo
- Publication number
- CN102863250A CN102863250A CN2012103319109A CN201210331910A CN102863250A CN 102863250 A CN102863250 A CN 102863250A CN 2012103319109 A CN2012103319109 A CN 2012103319109A CN 201210331910 A CN201210331910 A CN 201210331910A CN 102863250 A CN102863250 A CN 102863250A
- Authority
- CN
- China
- Prior art keywords
- water
- inorganic cement
- cement
- heat insulation
- insulation plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种无机水泥发泡外墙保温板配方,所述无机水泥发泡外墙保温板配方组成的重量是硬脂酸钙0.8kg、抗裂纤维0.4kg、三乙醇胺0.1kg、水泥50kg、双氧水3.1kg、减水剂0.08kg、增水剂0.1kg、粉煤灰20kg、灰钙粉0.5kg、硅粉3.4kg、水60kg;采用上述配方,实现了保温性能好,重量轻,成本低且能够阻燃的效果。
Description
技术领域
本发明涉及一种建筑用无机水泥发泡外墙保温板配方。本发明还涉及一种制备该无机水泥发泡外墙保温板配方的方法。
背景技术
目前,使用的外墙保温板大都使用泡沫材料,由于该泡沫材料易燃烧容易带来安全隐患,另外,即便使用混凝土浆料,由于未经发泡处理,在浇筑成型外墙保温板后重量大、成本高,易形成局部膨胀等缺陷,严重影响了外墙保温板质量。
发明内容
本发明的目的是提供一种结构简单,保温性能好,重量轻,成本低且能够阻燃的无机水泥发泡外墙保温板配方。
本发明的技术方案是一种无机水泥发泡外墙保温板配方,其特征在于:所述无机水泥发泡外墙保温板配方组成的重量是硬脂酸钙0.8kg 、抗裂纤维0.4kg、三乙醇胺0.1kg、水泥50kg、双氧水3.1kg、 减水剂0.08kg、粉煤灰20kg、灰钙粉0.5kg、硅粉3.4kg、水60kg。
本发明各种混料的组分重量百分比是:硬脂酸钙0.58%、抗裂纤维0.29%、三乙醇胺0.07%、水泥36.15%、双氧水2.24%、减水剂0.06%、粉煤灰14.45%、灰钙粉0.36%、硅粉2.46%、水43.33%。
本发明无机水泥发泡外墙保温板配方制备的方法是:(1)先加入水,
(2)添加三乙醇胺、硬脂酸钙、抗裂纤维、水泥、减水剂、增水剂、粉煤灰、灰钙粉、硅粉到步骤(1)的水中,
(3)搅拌步骤(2)混合物2-4分钟,
(4)添加双氧水到步骤(3)的混合物中,
(5)搅拌步骤(4)混合物10-20秒,
(6)由步骤(1)——(5)获得无机水泥发泡外墙保温板配方的混合物放入模具即可。
具体实施方式
本发明无机水泥发泡外墙保温板配方可以制成外墙保温板,也可以制成屋面隔热防水保温板。
本发明按照配方硬脂酸钙0.8kg 、抗裂纤维0.4kg、三乙醇胺0.1kg、水泥50kg、双氧水3.1kg、 减水剂0.08kg、粉煤灰20kg、灰钙粉0.5kg、硅粉3.4kg、水60kg,逐一对上述物质进行称量,(1)先加入水,(2)再添加三乙醇胺、硬脂酸钙、抗裂纤维、水泥、减水剂、粉煤灰、灰钙粉、硅粉到步骤(1)的水中,(3)搅拌步骤(2)混合物2-4分钟,(4)添加双氧水到步骤(3)的混合物中,(5)搅拌步骤(4)混合物10-20秒,(6)由步骤(1)——(5)获得无机水泥发泡外墙保温板配方的混合物放入模具即可。
通过实验表明本发明使用的原材料硬脂酸钙可以提高外墙保温板的强度;抗裂纤维可以提高外墙保温板的强度和抗弯性能;三乙醇胺可以提高水泥强度;双氧水可以起到发泡作用,减轻重量,降低成本;减水剂如萘磺酸盐甲醛聚合物可以减少水的用量;灰 钙 粉为气硬性胶凝材料,本身会产生强度,提高外墙保温板强度;硅 粉可以提高水泥制品的强度,抗冲击且耐磨,耐久等性能;采用上述配方,实现了保温性能好,重量轻,成本低且能够阻燃的效果。
Claims (3)
1.一种无机水泥发泡外墙保温板配方,其特征在于:所述无机水泥发泡外墙保温板配方组成的重量是硬脂酸钙0.8kg 、抗裂纤维0.4kg、三乙醇胺0.1kg、水泥50kg、双氧水3.1kg、 减水剂0.08kg、粉煤灰20kg、灰钙粉0.5kg、硅粉3.4kg、水60kg。
2.根据权利要求1所述的无机水泥发泡外墙保温板配方,其特征在于:所述配方中各种混料的组分重量百分比是:硬脂酸钙0.58%、抗裂纤维0.29%、三乙醇胺0.07%、水泥36.15%、双氧水2.24%、减水剂0.06%、粉煤灰14.45%、灰钙粉0.36%、硅粉2.46%、水43.33%。
3.一种制备权利要求1所述的无机水泥发泡外墙保温板配方的方法,其特征在于:(1)先加入水,
(2)添加三乙醇胺、硬脂酸钙、抗裂纤维、水泥、减水剂、粉煤灰、灰钙粉、硅粉到步骤(1)的水中,
(3)搅拌步骤(2)混合物2-4分钟,
(4)添加双氧水到步骤(3)的混合物中,
(5)搅拌步骤(4)混合物10-20秒,
(6)由步骤(1)——(5)获得无机水泥发泡外墙保温板配方的混合物放入模具即可。