CN102841193A - 一种环氧灌浆材料快速检测方法 - Google Patents
一种环氧灌浆材料快速检测方法 Download PDFInfo
- Publication number
- CN102841193A CN102841193A CN2012103585713A CN201210358571A CN102841193A CN 102841193 A CN102841193 A CN 102841193A CN 2012103585713 A CN2012103585713 A CN 2012103585713A CN 201210358571 A CN201210358571 A CN 201210358571A CN 102841193 A CN102841193 A CN 102841193A
- Authority
- CN
- China
- Prior art keywords
- temperature
- epoxy grouting
- day
- slurry
- grouting material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种环氧灌浆材料快速检测方法。包括下列步骤：配制环氧灌浆材料浆液，浆液物理性能检测，配制浆液在23±2℃温度下放置1天后按标准制作检测试件，将试件在30±0.5℃温度下恒温养护1天，升温至33±0.5℃温度下恒温养护7天，降至23±2℃温度下放置1天，性能检测。本发明通过改变固化温度、控制温度波动等方法缩短了固化要求时间，实现了环氧灌浆材料快速检测，检测结果与标准检测结果一致性较好，能满足环氧灌浆材料快速检测的需要。
Description
技术领域
本发明属于材料检测技术领域，尤其属于化学材料性能检测技术领域，特别涉及环氧灌浆材料快速检测检测方法。
背景技术
目前，国内相关部门颁布、实施的对环氧树脂灌浆材料物理力学性能检测按常规标准进行。其中规定以20±3℃条件下，固化物性能测定（试）凝期为28d。依据常规标准在使用合格的环氧树脂前经取样、制样、测试和出报告时间必须等待30d以上才能取得环氧浆材检测报告。送往具有资质的检测单位委托其检测，往往需要更多时日，通常送相关建筑材料检测院需要85d以上方能知道报告结果。送至现场检测机构进行检测最少也需要35d的时间。
在实际施工应用中，常常需要及时、快速地对灌浆材料进行检测，故研究快速检测试验方法以确保灌浆质量的工作已成为水利水电建设施工中对灌浆技术要求的一个重要组成部分。
发明内容
本发明根据现有技术的不足公开了一种环氧灌浆材料快速检测方法。本发明要解决的问题是提供一种能在短时间完成并与标准检测方法检测结果一致性较好的环氧灌浆材料快速检测检测方法。
本发明通过以下技术方案实现：
环氧灌浆材料快速检测方法，包括下列步骤：
1）配制环氧灌浆材料浆液，按灌浆需要组成比例配制环氧灌浆材料浆液；
2）浆液物理性能检测，进行外观、密度、初始粘度及粘度变化曲线检测；
3）步骤1）配制浆液在23±2℃温度下放置1天后按标准制作检测试件；
4）将步骤3）试件在30±0.5℃温度下恒温养护1天；
5）将步骤4）后试件升温至33±0.5℃温度下恒温养护7天；
6）将步骤5）后试件降至23±2℃温度下放置1天；
7）对步骤6）后试件进行浆液固化物力学性能检测。
上述用于基础处理的环氧树脂灌浆材料，其主剂是环氧树脂、稀释剂、固化剂和添加剂等，产生固化的主要化学反应是环氧树脂及含环氧环的添加剂的开环反应、稀释剂的活性化反应等;其机理主要是与固化剂间的加成开环反应、稀释剂的自聚、共聚及其产物与环氧树脂的共聚或固化剂间的反应，其遵循马尔柯夫尼科夫定律。如此，历经链增长、交联并形成立体网络结构、固结、力学性能上升等阶段，使其胶结物的力学性能满足技术指标。
上述固化过程从简单小分子反应到胶结体力学性能上升的速度，即固化化学反应速度与其所处的温度密切相关，这是本发明的理论依据。本发明探索通用试验条件，使其在可接受的寻常环境条件下实现快速反应，经与“标准条件”下的试件对比其一致性，从而能在较短时间内获得被认可的测试结果。
本发明通过改变固化温度、控制温度波动等方法缩短了固化要求时间，实现了环氧灌浆材料快速检测，检测结果与标准检测结果一致性较好，能满足环氧灌浆材料快速检测的需要。
具体实施方式
下面通过实施例对本发明进行具体的描述，有必要在此指出的是本实施例只用于对本发明进行进一步的说明，但不能理解为对本发明保护范围的限制，该领域的技术熟练人员可以根据上述本发明的内容作出一些非本质的改进和调整。
实施例1
环氧灌浆材料快速检测方法，包括下列步骤：
1）配制环氧灌浆材料浆液，按灌浆需要组成比例配制环氧灌浆材料浆液；
2）浆液物理性能检测，进行外观、密度、初始粘度及粘度变化曲线检测；
3）步骤1）配制浆液在23±2℃温度下放置1天后按标准制作检测试件；
4）将步骤3）试件在30±0.5℃温度下恒温养护1天；
5）将步骤4）后试件升温至33±0.5℃温度下恒温养护7天；
6）将步骤5）后试件降至23±2℃温度下放置1天；
7）对步骤6）后试件进行浆液固化物力学性能检测。
检测例
1、试件制作根据JC1041-2007中规定的方法及要求进行制作。
2、对比方法的标准检测按标准JC/T1041-2007和GB/T2567—2008进行。
3、本发明检测方法按实施例1方法进行。
4、检测及试件制作设备：旋转粘度计；GH-120G真溶液相对密度；浓度测试仪；XTIR红外光谱仪；X热分析仪；电动分样筛；万能试验机；恒温箱；抗渗仪；各类制样模具。
5、对某型号PSI-501环氧浆材（质量比6.0:1.0）分别在不同时间进行三组快速检测成果与标准检测成果试验数据统计如下：
环氧浆材物理性能检测实验对比统计表一
表1
环氧浆材物理性能检测实验对比统计表（二）
表2
环氧浆材物理性能检测实验对比统计表三
表3
通过表1、表2、表3验数据对比统计，以及结合其他相关检测试验数据看出，环氧浆材力学性能快速检测成果与常规检测成果基本一致，同时快速检测结果均满足相关设计要求。
Claims (1)
1.一种环氧灌浆材料快速检测方法，其特征是包括下列步骤：
1）配制环氧灌浆材料浆液，按灌浆需要组成比例配制环氧灌浆材料浆液；2）浆液物理性能检测，进行外观、密度、初始粘度及粘度变化曲线检测；
3）步骤1）配制浆液在23±2℃温度下放置1天后按标准制作检测试件；
4）将步骤3）试件在30±0.5℃温度下恒温养护1天；
5）将步骤4）后试件升温至33±0.5℃温度下恒温养护7天；
6）将步骤5）后试件降至23±2℃温度下放置1天；
7）对步骤6）后试件进行浆液固化物力学性能检测。