CN102838954B - 热塑性聚烯烃类防水卷材胶粘剂及其制备方法 - Google Patents
热塑性聚烯烃类防水卷材胶粘剂及其制备方法 Download PDFInfo
- Publication number
- CN102838954B CN102838954B CN201210360299.2A CN201210360299A CN102838954B CN 102838954 B CN102838954 B CN 102838954B CN 201210360299 A CN201210360299 A CN 201210360299A CN 102838954 B CN102838954 B CN 102838954B
- Authority
- CN
- China
- Prior art keywords
- rubber
- mixing
- thermoplastic polyolefin
- petroleum resin
- sbr
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种热塑性聚烯烃类防水卷材胶粘剂及其制备方法,由下述重量百分比的原料组成:氯丁橡胶混炼胶5-25%、丁苯橡胶混炼胶5-25%、C5石油树脂1-15%、C9石油树脂10-20%、萜烯酚醛树脂5-35%、甲苯15-30%、乙酸乙酯10-35%和120#溶剂油10-30%。其制备方法将上述原料加入到溶解槽内,得到热塑性聚烯烃类防水卷材胶粘剂。本发明专用于热塑性聚烯烃类防水卷材与水泥、金属等材料的粘接。
Description
技术领域
本发明涉及防水卷材使用的胶粘剂,是一种热塑性聚烯烃类防水卷材胶粘剂及其制备方法。
背景技术
热塑性聚烯烃类防水卷材主要用于建筑外露或非外露式屋面防水层,也用于容易变形的建筑地下防水,由于这种防水卷材具有强度高、重量轻、节能效果好及防水防结露效果好等诸多优点,已被做为高挡防水卷材使用。但是这种防水卷材主要是由橡胶和聚烯烃构成,其分子中极性基团和活性官能团较少,结晶度高,表面张力小,材料表面吸附能力很差,因此,采用现有胶粘剂极难粘接。当采用现有胶粘剂将热塑性聚烯烃类防水卷材与水泥、金属等材料粘接时,经常出现开裂等现象,使维修量大幅增加,防水效果受到严重影响,严重影响工程质量,导致此类防水卷材的应用受到较大限制。
发明内容
本发明的目的是,提供一种热塑性聚烯烃类防水卷材胶粘剂及其制备方法,它专用于热塑性聚烯烃类防水卷材与水泥、金属等材料的粘接。
本发明为实现上述目的,通过以下技术方案实现:热塑性聚烯烃类防水卷材胶粘剂,由下述重量百分比的原料组成:氯丁橡胶混炼胶5-25%、丁苯橡胶混炼胶5-25%、C5石油树脂1-15%、C9石油树脂10-20%、萜烯酚醛树脂5-35%、甲苯15-30%、乙酸乙酯10-35%和120#溶剂油10-30%。
所述的热塑性聚烯烃类防水卷材胶粘剂,由下述重量百分比的原料组成:氯丁橡胶混炼胶5%、丁苯橡胶混炼胶10%、C5石油树脂4%、C9石油树脂10%、萜烯酚醛树脂5%、甲苯15%、乙酸乙酯35%和120#溶剂油16%。
所述的热塑性聚烯烃类防水卷材胶粘剂,由下述重量百分比的原料组成:氯丁橡胶混炼胶5%、丁苯橡胶混炼胶7%、C5石油树脂3%、C9石油树脂10%、萜烯酚醛树脂6%、甲苯30%、乙酸乙酯20%和120#溶剂油19%。
所述的热塑性聚烯烃类防水卷材胶粘剂的制备方法,包括下述步骤:
①取氯丁橡胶、氧化锌和氧化镁按100:4-5:2-3的重量比混合后,置入双辊压延机上混炼10-20分钟,得到片状氯丁橡胶混炼胶,备用;
②取丁苯橡胶、氧化锌和氧化镁按100:4-5:2-3的重量比混合后,置入双辊压延机上混炼10-20分钟,得到片状丁苯橡胶混炼胶,备用;
③取甲苯15-30%、乙酸乙酯10-35%和120#溶剂油10-30%加入溶胶槽内;
④在搅拌状态下将氯丁橡胶混炼胶5-25%、丁苯橡胶混炼胶5-25%在30分钟内缓慢加入到溶解槽内溶解;
⑤搅拌溶解30分钟后,依次将C5石油树脂1-15%、C9石油树脂10-20%、萜烯酚醛树脂5-35%加入到溶解槽内,搅拌溶解8-10小时后得到热塑性聚烯烃类防水卷材胶粘剂。
步骤①所述的氯丁橡胶、氧化锌和氧化镁的重量比为100:5:3。
步骤②所述的丁苯橡胶、氧化锌和氧化镁的重量比为100:5:3。
所述的热塑性聚烯烃类防水卷材胶粘剂的制备方法,具体步骤如下:
①取氯丁橡胶、氧化锌和氧化镁按100:5:3的重量比混合后,置入双辊压延机上混炼15分钟,得到片状氯丁橡胶混炼胶,备用;
②取丁苯橡胶、氧化锌和氧化镁按100:5:3的重量比混合后,置入双辊压延机上混炼15分钟,得到片状丁苯橡胶混炼胶,备用;
③取甲苯30%、乙酸乙酯20%和120#溶剂油19%加入溶胶槽内;
④在搅拌状态下将氯丁橡胶混炼胶5%、丁苯橡胶混炼胶7%在30分钟内缓慢加入到溶解槽内溶解;
⑤搅拌溶解30分钟后,依次将C5石油树脂3%、C9石油树脂10%、萜烯酚醛树脂6%加入到溶解槽内,搅拌溶解9小时后得到热塑性聚烯烃类防水卷材胶粘剂。
本发明胶粘剂中氯丁橡胶混炼胶和丁苯橡胶混炼胶的结合及优选比例能使胶粘剂产生较好的粘结性和物理性能,C5石油树脂、C9石油树脂、萜烯酚醛树脂能进一步增加胶粘剂对热塑性聚烯烃类防水卷材的粘结力,提高剥离强度,各原料组合使热塑性聚烯烃类防水卷材胶粘剂具有粘接性好、能解决现有胶粘剂难以粘结的技术问题。本发明提供的热塑性聚烯烃类防水卷材胶粘剂,专用于热塑性聚烯烃类防水卷材与水泥、金属的大面积粘接,以及热塑性聚烯烃类防水卷材间的粘接。热塑性聚烯烃类防水卷材胶粘剂初粘力好,固体含量大于27%,粘度为1000mPa.s~3500mPa.s,与水泥剥离强度大于22N/cm,具有便于施工等优点,高温80℃、低温零下40℃试验表明,粘结性能良好。
具体实施方式
本发明的热塑性聚烯烃类防水卷材胶粘剂,由下述重量百分比的原料组成:氯丁橡胶混炼胶5-25%、丁苯橡胶混炼胶5-25%、C5石油树脂1-15%、C9石油树脂10-20%、萜烯酚醛树脂5-35%、甲苯15-30%、乙酸乙酯10-35%和120#溶剂油10-30%。
本发明所述的热塑性聚烯烃类防水卷材胶粘剂的制备方法,包括下述步骤:
①取氯丁橡胶、氧化锌和氧化镁按100:4-5:2-3的重量比混合后,置入双辊压延机上混炼10-20分钟,得到片状氯丁橡胶混炼胶,备用;
②取丁苯橡胶、氧化锌和氧化镁按100:4-5:2-3的重量比混合后,置入双辊压延机上混炼10-20分钟,得到片状丁苯橡胶混炼胶,备用;
③取甲苯15-30%、乙酸乙酯10-35%和120#溶剂油10-30%加入溶胶槽内;
④在搅拌状态下将氯丁橡胶混炼胶5-25%、丁苯橡胶混炼胶5-25%在30分钟内缓慢加入到溶解槽内溶解;
⑤搅拌溶解30分钟后,依次将C5石油树脂1-15%、C9石油树脂10-20%、萜烯酚醛树脂5-35%加入到溶解槽内,搅拌溶解8-10小时后得到热塑性聚烯烃类防水卷材胶粘剂。
本发明的步骤①所述的氯丁橡胶、氧化锌和氧化镁的重量比为100:5:3。
本发明的步骤②所述的丁苯橡胶、氧化锌和氧化镁的重量比为100:5:3。
本发明的热塑性聚烯烃类防水卷材胶粘剂的原料还可由下述多种重量组成:
1、氯丁橡胶混炼胶5%、丁苯橡胶混炼胶5%、C5石油树脂5%、C9石油树脂10%、萜烯酚醛树脂5%、甲苯30%、乙酸乙酯15%和120#溶剂油25%。
2、氯丁橡胶混炼胶10%、丁苯橡胶混炼胶5%、C5石油树脂5%、C9石油树脂10%、萜烯酚醛树脂5%、甲苯20%、乙酸乙酯20%和120#溶剂油25%。
3、氯丁橡胶混炼胶25%、丁苯橡胶混炼胶5%、C5石油树脂10%、C9石油树脂15%、萜烯酚醛树脂5%、甲苯15%、乙酸乙酯10%和120#溶剂油10%。
4、氯丁橡胶混炼胶5%、丁苯橡胶混炼胶25%、C5石油树脂5%、C9石油树脂20%、萜烯酚醛树脂10%、甲苯15%、乙酸乙酯10%和120#溶剂油10%。
5、氯丁橡胶混炼胶5%、丁苯橡胶混炼胶5%、C5石油树脂5%、C9石油树脂15%、萜烯酚醛树脂10%、甲苯20%、乙酸乙酯10%和120#溶剂油30%。
6、氯丁橡胶混炼胶5%、丁苯橡胶混炼胶6%、C5石油树脂4%、C9石油树脂18%、萜烯酚醛树脂12%、甲苯30%、乙酸乙酯25%和120#溶剂油10%。
7、氯丁橡胶混炼胶8%、丁苯橡胶混炼胶7%、C5石油树脂10%、C9石油树脂10%、萜烯酚醛树脂5%、甲苯15%、乙酸乙酯35%和120#溶剂油10%。
8、氯丁橡胶混炼胶10%、丁苯橡胶混炼胶10%、C5石油树脂5%、C9石油树脂10%、萜烯酚醛树脂10%、甲苯25%、乙酸乙酯20%和120#溶剂油10%。
9、氯丁橡胶混炼胶15%、丁苯橡胶混炼胶5%、C5石油树脂8%、C9石油树脂12%、萜烯酚醛树脂15%、甲苯15%、乙酸乙酯15%和120#溶剂油15%。
10、氯丁橡胶混炼胶5%、丁苯橡胶混炼胶10%、C5石油树脂4%、C9石油树脂10%、萜烯酚醛树脂5%、甲苯15%、乙酸乙酯35%和120#溶剂油16%。
11、氯丁橡胶混炼胶5%、丁苯橡胶混炼胶7%、C5石油树脂3%、C9石油树脂10%、萜烯酚醛树脂6%、甲苯30%、乙酸乙酯20%和120#溶剂油19%。
本发明上述实施例的热塑性聚烯烃类防水卷材胶粘剂的制备方法,具体步骤如下:
① 取氯丁橡胶、氧化锌和氧化镁按100:5:3的重量比混合后,置入双辊压延机上混炼15分钟,得到片状氯丁橡胶混炼胶,备用;
② 取丁苯橡胶、氧化锌和氧化镁按100:5:3的重量比混合后,置入双辊压延机上混炼15分钟,得到片状丁苯橡胶混炼胶,备用;
③ 取甲苯30%、乙酸乙酯20%和120#溶剂油19%加入溶胶槽内;
④ 在搅拌状态下将氯丁橡胶混炼胶5%、丁苯橡胶混炼胶7%在30分钟内缓慢加入到溶解槽内溶解;
⑤搅拌溶解30分钟后,依次将C5石油树脂3%、C9石油树脂10%、萜烯酚醛树脂6%加入到溶解槽内,搅拌溶解9小时后得到热塑性聚烯烃类防水卷材胶粘剂。
Claims (1)
1.热塑性聚烯烃类防水卷材胶粘剂的制备方法,其特征在于:具体步骤如下:
①取氯丁橡胶、氧化锌和氧化镁按100:5:3的重量比混合后,置入双辊压延机上混炼15分钟,得到片状氯丁橡胶混炼胶,备用;
②取丁苯橡胶、氧化锌和氧化镁按100:5:3的重量比混合后,置入双辊压延机上混炼15分钟,得到片状丁苯橡胶混炼胶,备用;
③取甲苯30%、乙酸乙酯20%和120#溶剂油19%加入溶胶槽内;
④在搅拌状态下将氯丁橡胶混炼胶5%、丁苯橡胶混炼胶7%在30分钟内缓慢加入到溶解槽内溶解;
⑤搅拌溶解30分钟后,依次将C5石油树脂3%、C9石油树脂10%、萜烯酚醛树脂6%加入到溶解槽内,搅拌溶解9小时后得到热塑性聚烯烃类防水卷材胶粘剂。