CN1028320C - 铸铁与钢的电阻点焊工艺 - Google Patents
铸铁与钢的电阻点焊工艺 Download PDFInfo
- Publication number
- CN1028320C CN1028320C CN 93100953 CN93100953A CN1028320C CN 1028320 C CN1028320 C CN 1028320C CN 93100953 CN93100953 CN 93100953 CN 93100953 A CN93100953 A CN 93100953A CN 1028320 C CN1028320 C CN 1028320C
- Authority
- CN
- China
- Prior art keywords
- cast iron
- welding
- steel
- spot welding
- steel plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种铸铁与钢的电阻点焊工艺,其特征是:钢板侧电极端面直径为3~8mm,当钢板与铸铁板厚度比小于1∶3时,铸铁侧电极端面直径为钢板侧电极端面直径的1~4倍。工件的被焊部位涂抹的添加剂组成成分是(重量%):石墨粉(>200目)50~100%、镍粉(>120目)0~20%、铝粉(>120目)0~30%。焊接时,采用“一点两火”的电阻点焊方法。该焊接工艺焊接的工件表面光滑美观,接头性能高于铸铁母材;工艺简单,生产效率高。可广泛用于铸铁板与钢板之间的焊接。
Description
本发明属于一种焊接工艺,特别涉及一种铸铁与钢的电阻点焊工艺。
目前,铸铁与钢的连接大致有以下几种方法:1电弧焊方法,一般只适用于比较厚的大工件连接。因为加热面积大,所以变形大,接头部位容易产生裂纹。2气焊方法,一般适用于厚的大铸铁件与钢件之间的连接,该焊接方法变形更大,而且生产效率低。3铆接或螺栓连接方法,一般用于板件之间的连接。该方法工件表面存在铆钉头或螺栓头,工件表面不平整,不美观,影响使用;并且工序多,生产效率低。4胶接方法,该方法虽然可适用于各种厚度的铸铁与钢的连接,但接头只能在低温下使用,而且强度差,同时对工件表面清理要求高、成本高。对于工件表面要求平整、美观,而且在高温下使用的铸铁与钢的连接,目前尚没有一种比较理想的连接方法。
本发明的目的是克服现有技术中的不足而提供一种铸铁与钢的电阻点焊工艺。
本发明的目的可以通过以下措施来实现:
铸铁与钢的电阻点焊工艺是将工件的待焊部位清理后搭接,放于电焊机的上、下铜合金电极之间进行点焊,其工艺条件是:
(1)、钢板侧电极端面直径为3~8mm,当钢板与铸铁板厚度比小于1∶3时,铸铁侧电极端面直径为钢板侧电极端面直径的1~4倍;
(2)、施焊前,在工件的被焊部位涂抹添加剂,其添加剂的组成成分是(重量%):
石墨粉(>200目) 50~100%
镍粉(>120目) 0~20%
铝粉(>120目) 0~30%
(3)、施焊时,采用“一点两火”的点焊方法,即对同一焊接部位连续点焊两次的焊接方法。
本发明与现有技术相比有如下优点:
由于钢板的熔点高,钢板侧电极端面面积小,电流密度就大,产热速度就高,升温就快;铸铁侧电极端面面积大,电流密度就小,产热速度就低,升温就慢,因此就可以使钢和铸铁同时达到熔化温度,同时形成熔核,而不致引起熔核偏移及铸铁侧熔核喷溅。铸铁的焊接接缝易产生白口、马氏体,因此脆性大。在工件被焊部位涂上本发明中的添加剂后,可以大幅度降低甚至消除白口组织,并且显著降低马氏体脆性,降低焊接应力,因而改善结合部位性能,提高韧性和抗裂性。
下面结合实施例对本发明作进一步详述:
实施例1
口径为280mm、壁厚为1.5mm的铸铁炒锅与壁厚为1mm的A3钢柄之间的连接,其工艺如下:
(1)、用砂纸消除铸锅和钢柄被焊部位的明显锈迹及油污;
(2)、由于铸锅表面存在一薄层石墨粉,所以可不涂抹添加剂;
(3)、将铸锅和钢柄的被焊部位搭接紧密,放于DN-100型普通工频点焊机两电极之间,采用“一点两火”的点焊方法,即对同一焊接部位连续点焊两次的焊接方法。其工艺条件是:
a、采用铬铜合金电极,上、下电极直径D=16mm,钢柄侧上电极端面直径d=5mm,铸锅侧下电极端面直径d=8mm。
b、焊接电流I=7.2KA。
c、电极压力Fw=5000牛顿。
d、加热时间为15周。
经检验,焊接强度满足使用要求。
实施例2
厚1.5mm的铸铁板与厚3mm的钢板之间连接,其焊接工艺步骤是:
(1)、配制添加剂:将200克、250目的石墨粉与120克、200目的铝粉和80克、200目的镍粉放在一起混合均匀待用。
(2)、用砂纸清除铸铁板和钢板待焊部位的锈迹及油污。
(3)、在铸铁板和钢板待焊部位涂抹上一薄层配制好的添加剂。
(4)、将铸铁板和钢板待焊部位搭接紧密,放于DN-100型普通工频点焊机两电极之间,采用“一点两火”的点焊方法。其工艺条件是:
a、选用镍铜合金电极,上、下电极直径D=40mm,钢板侧上电极端面直径d=5mm,铸铁板侧下电极端面直径d=16mm。
b、焊接电流I=8KA。
c、电极压力Fw=10000牛顿。
d、加热时间为20周。
经检验,焊接部位强度大于铸铁基体强度。
实施例3
厚3mm的铸铁板与厚2mm的钢板之间连接,其焊接工艺步骤如下:
(1)、配制添加剂:将400克、200目的石墨粉与50克、150目的镍粉和50克、150目的铝粉放在一起混合均匀待用。
(2)、用砂纸清除铸铁板和钢板待焊部位的锈迹及油污。
(3)、在铸铁板和钢板待焊部位涂抹上一薄层配制好的添加剂。
(4)、将铸铁板和钢板待焊部位搭接紧密,放于DM-100型交流脉冲焊机两电极之间,进行一次脉冲点焊,其工艺条件是:
a、选用硅铜合金电极,上、下电极直径D=40mm,钢板侧上电极端面直径d=8mm,铸铁板侧下电极端面直径d=16mm。
b、焊接电流I=15KA。
c、电极压力Fw=20000牛顿。
d、加热时间为10个脉冲。
经检验,焊接部位强度大于铸铁基体强度。
Claims (1)
1、一种焊接工艺,是将工件的待焊部位清理后搭接,放于电焊机的上、下铜合金电极之间进行焊接,其特征在于:用于铸铁与钢的电阻点焊工艺,其工艺条件是:
(1)、钢板侧电极端面直径为3~8mm,当钢板与铸铁板厚度比小于1∶3时,铸铁侧电极端面直径为钢板侧电极端面直径的1~4倍;
(2)、施焊前,在工件的被焊部位涂抹添加剂,其添加剂的组成成分是(重量%):
石墨粉(>200目) 50~100%
镍粉(>120目) 0~20%
铝粉(>120目) 0~30%
(3)、施焊时,采用“一点两火”的点焊方法,即对同一焊接部位连续点焊两次的焊接方法。