CN102831973B - 一种低蠕变铝包钢架空导线及其制备方法 - Google Patents

一种低蠕变铝包钢架空导线及其制备方法 Download PDF

Info

Publication number
CN102831973B
CN102831973B CN201210296182.2A CN201210296182A CN102831973B CN 102831973 B CN102831973 B CN 102831973B CN 201210296182 A CN201210296182 A CN 201210296182A CN 102831973 B CN102831973 B CN 102831973B
Authority
CN
China
Prior art keywords
coated
low creep
carbon steel
steel wire
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210296182.2A
Other languages
English (en)
Other versions
CN102831973A (zh
Inventor
陈天生
邵剑波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Chun Xing and new material Co. Ltd.
Original Assignee
WUJIN HENGTONG METAL STEEL WIRE CO Ltd CHANGZHOU CITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIN HENGTONG METAL STEEL WIRE CO Ltd CHANGZHOU CITY filed Critical WUJIN HENGTONG METAL STEEL WIRE CO Ltd CHANGZHOU CITY
Priority to CN201210296182.2A priority Critical patent/CN102831973B/zh
Publication of CN102831973A publication Critical patent/CN102831973A/zh
Application granted granted Critical
Publication of CN102831973B publication Critical patent/CN102831973B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种低蠕变铝包钢架空导线，包括含0.7%-0.9%C的高碳钢和包裹在高碳钢外圈的铝层，其特征在于：所述高碳钢中还包括铬0.8-2.0%、钼0.2-0.6%和稀土元素0.02-0.06%，按重量百分数计算，本发明提高了产品晶界扩散晶活能，提高材料的蠕变极限，具有高导电率、高耐热行、低蠕变等特性。

Description

一种低蠕变铝包钢架空导线及其制备方法
技术领域
本发明涉及一种架空导线及其制备方法，特别是耐高温，低蠕变的铝包钢架空导线。
背景技术
随着各国经济社会的高速发展，用电量的日益增加，增加输出容量，降低输电损耗，提高蠕变性能成为全球输电线路领域研究探索的三大目标，现在世界各国的电力传输的架空线路基本采用铝包钢芯铝绞线，为了增加输出电容量，将线路的连续使用温度从70度提高到140度，则线路载流量可提高一倍，但高温下蠕变大，弧垂增大，线路对地以及交叉跨越的空气间隙距离减少，影响电网的安全，目前有一种新钢种“殷钢”，属于铁镍合金的一种，其成分为镍36%，铁63.8%，碳0.2%。这种材料最大的特点就是随温度的变形极小，适合于制作对温度变形有严格要求的零件。由于其化学成分中含有36%的金属元素镍，既提高强度，又有很好的蠕变性能，作成“铝包殷钢”的低蠕变钢芯，但由于镍元素稀缺，价格昂贵，“铝包殷钢”每吨十几万元人民币，是普通铝包钢芯的十倍以上，限制了其大范围应用的可能。
发明内容
为克服上述缺陷，本发明提供一种价格实惠且具有高导电率、高耐热性、低蠕变的架空导线已经制造该导线的方法。
为实现上述目的，本发明的技术方案为：
一种低蠕变铝包钢架空导线，包括含0.65%-0.9%C的高碳钢芯线和包覆在高碳钢芯线外表的工业纯铝层，所述高碳钢中还包括铬0.8-2.0%、钼0.2-0.6%和稀土元素0.02-0.06%，按重量百分数计算。
一种制备权利要求1所述架空导线的制备方法，所述制造步骤为：
(a)在高碳钢中添加铬0.8-2.0%、钼0.2-0.6%和稀土元素0.02-0.06%进行真空冶炼；
(b)按照正常程序轧制成钢丝；
(c)钢丝加热至900-980度奥氏体化处理后，在450℃-550℃熔融的铅液中进行等温冷却，并控制其组织细化到60-90nm，且均匀化；
(d)采用连续挤压包覆工艺：控制包覆模腔内的温度至420-500度，压力至350-500Mpa，使铝达到塑性流动状态后均匀致密包覆在钢丝上；
(e)采用压力模拉拔技术，实现双金属同步变形。
本发明：提高了产品晶界扩散激活能，提高材料的蠕变极限，具有高导电率、高耐热性、低蠕变等特性，而且增加的元素用量少且价格适中。
具体实施方式
下面结合附图与具体实施例对本发明作进一步说明。
实施例1：本发明涉及一种低蠕变铝包钢架空导线，包括含0.70%C的高碳钢芯线和包覆在高碳钢芯线外表的工业纯铝层，在高碳钢的熔炼中添加铬1.0%、钼0.45%和稀土元素0.05%，按重量百分数计算。本产品提高产品晶界扩散激活能，提高材料的蠕变极限，避免了采用大量的镍元素稀缺资源，降低了产品的价格，节约能源。
制备上述架空导线的方法所需步骤为：
（a）按照上述要求配料；
（b）在高碳钢中添加铬1.0%、钼0.45%和稀土元素0.05%进行真空冶炼，避免冶炼中杂质元素和气体在晶界偏聚，减少气体和杂质，强化晶界；
（c）按照正常程序轧制成钢丝；
（d）钢丝加热到950度奥氏体化处理后，在510度熔融的铅液中进行等温冷却，并控制其组织细化到80nm，且均匀化；这样可以提高产品晶界扩散激活能，提高材料的蠕变极限。
（e）采用连续挤压包覆工艺：控制包覆模腔内的温度至450度，压力至460Mpa，使铝达到塑性流动状态后直接均匀致密包覆在钢丝上，上述过程完全属于物理成型，不污染环境，节能减排，生产效率高；
（f）采用压力模拉拔技术，实现双金属同步变形。
实施例2：本发明涉及一种低蠕变铝包钢架空导线，包括含0.80%C的高碳钢芯线和包覆在高碳钢芯线外表的工业纯铝层，在高碳钢的熔炼中添加铬1.5%、钼0.5%和稀土元素0.03%，按重量百分数计算。
制备上述架空导线的方法所需步骤为：
（a）按照上述要求配料；
（b）在高碳钢中添加铬1.5%、钼0.6%和稀土元素0.03%进行真空冶炼；减少气体和杂质，强化晶界；
（c）按照正常程序轧制成钢丝；
（d）钢丝加热到920度奥氏体化处理后，在480度熔融的铅液中进行等温冷却，并控制其组织细化到70nm，且均匀化；
（e）采用连续挤压包覆工艺：控制包覆模腔内的温度至480度，压力至420Mpa，使铝达到塑性流动状态后直接均匀致密包覆在钢丝上；
（f）采用压力模拉拔技术，实现双金属同步变形。
经过性能的试验研究，本产品的拉伸强度达到1100Mpa,预计产品10年的蠕变量小于1/1000，完全达到并超过电网设计的要求，但本产品的价格只要约9000元/吨左右，完全适应我国范围大、用量大和镍元素稀缺的国情。

Claims (1)

1.一种制备低蠕变铝包钢架空导线制备方法，其特征在于：所述制造步骤为：（a）在含0.65%-0.9%C的高碳钢中添加铬0.8-2.0%、钼0.2-0.6%和稀土元素0.02-0.06%进行真空冶炼，按重量百分数计算；
（b）按照正常程序轧制成钢丝；
（c）钢丝加热至900-980度奥氏体化处理后，在450℃-550℃熔融的铅液中进行等温冷却，并控制其组织细化到60-90nm，且均匀化；
（d）采用连续挤压包覆工艺：控制包覆模腔内的温度至420-500度，压力至350-500Mpa，使工业纯铝达到塑性流动状态后均匀致密包覆在钢丝上；
（e）采用压力模拉拔技术，实现双金属同步变形。
CN201210296182.2A 2012-03-22 2012-08-20 一种低蠕变铝包钢架空导线及其制备方法 Active CN102831973B (zh)