CN102827576A - 一种相变温度为33℃的无机相变材料(pcm-33) - Google Patents

一种相变温度为33℃的无机相变材料(pcm-33) Download PDF

Info

Publication number
CN102827576A
CN102827576A CN2011101635465A CN201110163546A CN102827576A CN 102827576 A CN102827576 A CN 102827576A CN 2011101635465 A CN2011101635465 A CN 2011101635465A CN 201110163546 A CN201110163546 A CN 201110163546A CN 102827576 A CN102827576 A CN 102827576A
Authority
CN
China
Prior art keywords
phase
change
temperature
inorganic
change material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101635465A
Other languages
English (en)
Inventor
杨玉生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIJING ZRS NEW ENERGY TECHNOLOGY CO LTD
Original Assignee
BEIJING ZRS NEW ENERGY TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING ZRS NEW ENERGY TECHNOLOGY CO LTD filed Critical BEIJING ZRS NEW ENERGY TECHNOLOGY CO LTD
Priority to CN2011101635465A priority Critical patent/CN102827576A/zh
Publication of CN102827576A publication Critical patent/CN102827576A/zh
Pending legal-status Critical Current

Abstract

一种相变温度为33℃的无机相变材料(PCM-33)本发明涉及一种无机相变恒温材料，含有质量比35％的六水氯化钙、11.5％的六水氯化锶、8％的二氧化硅、7％的丙烯酸、6％的氯化钠、3.5％的羟甲基纤维素钠和29％的水。本发明所提供的相变材料相变温度在33℃，过冷度为0.5℃，相变潜热为230KJ/KG，相变过程可逆，可循环使用次数为10000次以上，原材料均为规模生产，无毒无腐蚀，易于推广。此相变材料在常温时为无色透明雪化状晶体，便于各储能领域开发利用。

Description

一种相变温度为33℃的无机相变材料(PCM-33)
技术领域：
本发明涉及一种无机相变恒温材料及其制备方法，特别设计一种相变温度在33℃的相变材料。 
背景技术：
在食品、化工、物流、医疗应用、通信信息机房、车间、军事等众多行业中，普遍利用制冷机来对环境或储藏需要的特定温度进行恒温。制冷机停电时，因而温度回升快、无法维持最佳的环境温度。在无相变恒温材料的制冷系统中，提供恒温环境时，制冷机工作启动频繁，因而降低了其使用寿命，耗电量多。 
相变恒温材料即潜热蓄冷，是相变恒温系统中存储冷量的功能材料。在夜间用电低谷期利用物质潜热将冷量储存在相变恒温材料中，在白天用电高峰时将冷量释放出来或利用气温较低时吸收自然冷量，温度高时将冷量释放出来从而满足环境或生活所需要温度。这样的制冷系统，大部分时间运行在夜间用电低谷峰期或利用夜间气温低时吸收自然冷量，而在白天高温用电高峰期只有辅助设备运行，从而实现电网“错峰用冷、移峰填谷”，有利于缓解能量双方供求矛盾。 
目前国内外对相变蓄冷材料的研究还比较少，但在食品、化工、低温物流、医疗应用、通信信息机房、车间、军事等众多行业，对恒温材料有着巨大的需求。因此研究相变恒温材料，研制出相变温度为33℃，相变潜热大，过冷度小，无相分离、性能稳定的新型、相变恒温材料，显得尤为重要。 
本发明所提供的相变材料性能稳定，相变温度在33℃，过冷度为0.5℃，相变潜热为230KJ/KG，相变过程可逆，可循环使用次数为10000次以上，原材料均为规模生产，无毒无腐蚀，易于推广。此相变材料在常温时为结晶雪花状，便于各储能领域开发利用。 
发明内容：
本发明的目的在于提供一种由无机盐类物质合成，性能稳定，相变潜热大，无毒无腐蚀，易塑性好的无机相变恒温材料。 
本发明的无机相变恒温材料，按重量百分比由以下组成： 
Figure BSA00000519682500011
具体的制备方法： 
1、在45～80℃条件下在配置皿中将总配置量为7％的丙烯酸与总配置量为9％水配成水溶液； 
2、将总配置量为11.5％的六水氯化锶加入到步骤1的水溶液中，混合均匀，制成混合溶液； 
3、向步骤2的混合溶液中加入总配置量为8％的二氧化硅，再加总配置比例为5％的水，搅拌均匀，加热1小时，温度保持在60℃左右让其充分反应。 
4、将总配置量为6％的氯化钠放到总配置量为5％水中，混合均匀，制成混合溶液； 
5、向步骤4的混合溶液中总配置量为3.5％羟甲基纤维素钠，搅拌均匀； 
6、将步骤3的溶液与步骤5中溶液进行搅拌均匀； 
7、向步骤6的混合溶液里加入总配置量为35％六水氯化钙，在60～70℃、常压条件下反应0.5～1.5小时。 
8、将步骤7制备的高分子材料中加入剩余总配置比例为10％的水，搅拌均匀，放置10～15分钟即可。 
9、最终化学成份“无机相变液体高分子材料” 
附图一本发明的制备工艺流程图 
A为35％的六水氯化钙 
B为11.5％的六水氯化锶 
C为8％二氧化硅 
D为7％的丙烯酸 
E为6％的氯化钠 
F为3.5％羟甲基纤维素钠 
G为9％的水 
H为5％的水 
I为5％的水 
J为10％的水 
K为步骤一产生的水溶液 
L为步骤二产生的混合溶液 
M为步骤三产生的混合溶液 
N为步骤四产生的混合溶液 
O为步骤五产生的混合溶液 
P为步骤六产生的混合溶液 
Q为步骤七产生的混合溶液 
R为本发明相变恒温材料 
1在45～80℃条件下混合 
2搅拌加热1小时，温度保持在60℃左右 
3在60～70℃、常压条件下反应0.5～1.5小时 
4搅拌均匀，放置10～15分钟 
本发明的无机相变材料产品规格为 
密度： 1.40g/cm3(25℃)
相变点： 33℃
潜热： 230kJ/kg
导热系数： 0.55W/m.k
过冷度： 0.5℃
使用次数 10000此次以上
本发明的无机相变材料重新凝结的温度与时间的关系 
重新凝结是使相变材料的再凝结以便开始另一个能量吸收-释放循环。 
本无机相变恒温材料在32.5℃时开始重新凝结，凝结时间为6.5小时，随着温度的降低，凝结时间也相应缩短，24℃时凝结时间为4小时，17℃时凝结时间为2.5小时，13℃时凝结时间为2小时，10℃时凝结时间为1小时。 
结果表明：重新凝结的时间随着温差的变大而迅速增加。 
附图二为本发明无机相变材料重新凝结的温度-时间关系 
本发明的无机相变材料控制温度与时间的关系 
当环境温度为40℃时，相变材料控制温度能力与时间成反比，随着时间的增加，相变材料释放的冷量开始减小，本相变材料在33℃时开始释放冷量，并可保持温度时间为16小时，然后才会逐渐升温，直至相变材料完全融化，则与环境温度相等。 
附图三为相变材料控制温度时间曲线。 

Claims (3)

  1. 一种相变温度为33℃的无机相变材料(PCM-33)
    1.本发明涉及一种由无机盐类物质合成，性能稳定，相变潜热大，无毒无腐蚀，易塑性好的无机相变恒温材料。
    本发明的无机相变恒温材料，按重量百分比由以下组成：
  2. 2.按照权利要求1所述的无机相变恒温材料其特征是：所使用的材料都为无机物。
  3. 3.根据权利要求1或2所述的无机相变恒温材料其特征是：相变温度在33℃，过冷度为0.5℃，相变潜热为230KJ/KG，相变过程可逆，可循环使用次数为10000次以上。
CN2011101635465A 2011-06-17 2011-06-17 一种相变温度为33℃的无机相变材料(pcm-33) Pending CN102827576A (zh)