CN102825888A - Printed UV wear-resistant coating processing technology - Google Patents
Printed UV wear-resistant coating processing technology Download PDFInfo
- Publication number
- CN102825888A CN102825888A CN2011101620544A CN201110162054A CN102825888A CN 102825888 A CN102825888 A CN 102825888A CN 2011101620544 A CN2011101620544 A CN 2011101620544A CN 201110162054 A CN201110162054 A CN 201110162054A CN 102825888 A CN102825888 A CN 102825888A
- Authority
- CN
- China
- Prior art keywords
- wear
- resisting
- mass parts
- lacquer
- printed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a printed UV wear-resistant coating processing technology. According to the processing technology, a plastic film is coated with a wear-resistant UV paint and a wear-resistant high-temperature glue solution once; then, a pattern is printed on the wear-resistant UV coating; the wear-resistant UV printed film is pressed on a base material and dried; and the printed UV wear-resistant coating can be formed on the surface of the base material after the drying process. The technology requires simple steps, is convenient to implement, has advantages of high production efficiency, low production cost and less power consumption, and can be realized only by a few investment and personnel. The surface of the printed UV wear-resistant coating prepared by the technology is as smooth as a mirror. The quality of the product is good. In addition, by the adoption of the technology, pollution will not be generated during the production process. The technology provided by the invention has advantages of low carbon and environmental protection.
Description
Technical field
The present invention relates to a kind of UV lacquer coating process, particularly a kind of processing technology that can form stamp UV wear-resistant coating at substrate surface.
Background technology
Along with the raising of Chinese economic development and people's living standard, people become increasingly high to the quality requirements of life staying idle at home.And not only require appearance looks elegant for the furniture people, and require environmental protection, so the requirement of this respect is also increasingly high concerning furniture manufacturing enterprise.The UV lacquer is to use furniture lacquer more widely at present, and it is different from common wealth furniture enterprise PU lacquer commonly used, PE lacquer and NC lacquer, is a kind of paint of real environmental protection, does not contain any volatile substance, uses Product Green, health, the environmental protection of UV paint production.UV lacquer is handled stable, the Chang Xin for a long time of back color and luster through the intensive ultraviolet photocuring, can solve effectively that sheet material fades and the aberration problem; The minute surface of plate surface that scribbles UV lacquer is pure flat effective, and the full no tangerine peel of paint film; And the higher scratch resistance of its hardness is drawn, acid and alkali-resistance, not yielding, so the UV lacquer has obtained using very widely at furniture industry.
UV lacquer is coated on the surface of base material and shines through ultraviolet ray and can form the UV lacquer coat, and along with the development of technology in recent years, people are to the wear-resisting revolution of UV lacquer coat, and promptly its surperficial abrasion resistance requires increasingly high.In order to improve the wear-resisting revolution on UV lacquer coat surface, people can mix alundum (Al usually in the UV lacquer, improve the abrasion resistance of UV lacquer coat through alundum (Al.If but in the UV lacquer, once added too many alundum (Al, then could cause adverse influence to the performance of UV lacquer.Therefore at present for the wear-resisting revolution method commonly used that improves the UV lacquer coat be exactly substrate surface repeatedly coating multiple contain the wear-resisting UV lacquer of a small amount of alundum (Al.
With 1500 change wear-resisting rotating speed the UV lacquer coat be example, its processing technology generally needs following steps: 1) at first at substrate surface coating one deck UV lacquer as prime paint, and shine through ultraviolet and to make its curing, and through the sanding of oil-sand machine; 2) on the surface of sanding, be coated with wear-resisting UV lacquer then, and carry out drying through ultraviolet lamp; 3) then carry out drying at the surface coated UV light priming paint of wear-resisting UV lacquer and through the outside line lamp again, carry out sanding through the sanding of oil-sand machine again; 4) follow continuous repeating step 2,3 four to five times, so just can process qualified UV lacquer coat.
Above-mentioned processing technology not only complicated steps, working strength of workers is big, production efficiency is low; And production cost is very high; Need to drop into machinery equipment about the 25-30 platform, admittedly produce the about 100-200 about ten thousand of equipment funds, total electricity consumption is at 230-270 kilowatt; Artificial amount needs greatly in process, also can pollute environment about 15 people.
Summary of the invention
To the deficiency of above-mentioned prior art, the technical problem that the present invention will solve provides the stamp UV wear-resistant coating processing technology that a kind of method is simple, production efficiency is high, input cost is low.
For solving the problems of the technologies described above, the present invention adopts following technical scheme:
A kind of stamp UV wear-resistant coating processing technology is characterized in that it comprises the steps:
1) the wear-resisting UV lacquer of coating on plastic sheeting, said wear-resisting UV lacquer is made up of the UV glue of 80-120 mass parts and the alundum (Al of 40-60 mass parts, through the ultraviolet ray irradiation wear-resisting UV lacquer is solidified after coating is accomplished;
2) on the wear-resisting UV enamelled coating that is cured, stamp required pattern and curing;
3) paint the wear-resisting high temperature glue of coating at the wear-resisting UV that is cured, said wear-resisting high temperature glue is made up of the anticracking oil of 80-120 mass parts, the curing agent of 80-120 mass parts and the alundum (Al of 20-40 mass parts;
4) one side that plastic sheeting is scribbled wear-resisting high temperature glue is pressed on the base material and carries out drying, after the drying
With tearing on the plastic film substrate, can form UV stamp wear-resistant coating at substrate surface like this.
Preferably, said wear-resisting UV lacquer is made up of the UV glue of 100 mass parts and the alundum (Al of 50 mass parts, and said wear-resisting high temperature glue is made up of the anticracking oil of 100 mass parts, the curing agent of 100 mass parts and the alundum (Al of 30 mass parts.
Preferably, the baking temperature of step 3) is a normal temperature
Preferably, in step 2) in required pattern be through embossing plate UV lacquer or water color ink to be printed at the wear-resisting UV enamelled coating that is cured to form.
Technique scheme has following beneficial effect: this stamp UV wear-resistant coating processing technology only needs disposable wear-resisting UV lacquer and the wear-resisting high temperature glue of on plastic sheeting, being coated with; Then plastic sheeting is pressed in drying on the base material, can forms the UV lacquer wearing layer of stamp after dry the completion on the surface of base material.This processing step is simple, and it is convenient to implement, and production efficiency is high, and production cost is low, and power consumption is little, only needs a spot of fund and personnel to realize.Adopt the stamp UV wear-resistant coating smooth surface such as the mirror of this explained hereafter, good product quality, and adopt this technology can not produce pollution in process of production, have the advantage of low-carbon environment-friendly.
The specific embodiment
This stamp UV wear-resistant coating processing technology is characterized in that it comprises the steps:
1) the wear-resisting UV lacquer of coating on plastic sheeting; After accomplishing, coating wear-resisting UV lacquer is solidified through the ultraviolet ray irradiation; Wear-resisting UV lacquer is made up of the UV glue of 80-120 mass parts and the alundum (Al of 40-60 mass parts; Preferably, wear-resisting UV lacquer is made up of the UV glue of 100 mass parts and the alundum (Al of 50 mass parts.
2) on the wear-resisting UV enamelled coating that is cured, stamp required pattern and solidify, required pattern is through embossing plate UV lacquer or water color ink to be printed at the wear-resisting UV enamelled coating that is cured to form, need shine after printed do, curing.
3) paint the wear-resisting high temperature glue of coating at the wear-resisting UV that is cured; Said wear-resisting high temperature glue is made up of the anticracking oil of 80-120 mass parts, the curing agent of 80-120 mass parts and the alundum (Al of 20-40 mass parts; Preferably, wear-resisting high temperature glue is made up of the anticracking oil of 100 mass parts, the curing agent of 100 mass parts and the alundum (Al of 30 mass parts.
4) one side that plastic sheeting is scribbled wear-resisting high temperature glue is pressed on the base material and carries out under the environment of 500 degree-700 degree, carrying out drying; Preferred 550 degree of environment temperature; With tearing on the plastic film substrate, can form UV stamp wear-resistant coating at substrate surface like this after the drying.
This stamp UV wear-resistant coating processing technology can improve 200% working efficiency and also effectively energy savings reach more than 90%; It is a kind of new technology of low-carbon environment-friendly; This process reform the highly energy-consuming of background technology, high pollution, technology troublesome operation difficulty is big and benefit is low shortcoming; Be a kind of energy-conserving and environment-protective, low high production, safe and reliable technology easy to operate, can effectively improve the quality of products quality, the benefit of dropping into.As shown in the table, this processing step is simple, and it is convenient to implement, and production efficiency is high, and production cost is low, and power consumption is little, only needs a spot of fund and personnel to realize.
| Sequence number | Project | Prior art | The present invention's technology | Contrast is practiced thrift |
| 1 | Investment | 2,000,000 | 200,000 | 90％ |
| 2 | Power consumption | 250 kilowatts | 15 kilowatts | 95％ |
| 3 | Artificial | 15 people | 4 people | 90％ |
| 4 | The abrasive band | Each 6 | Need not | 100％ |
| 5 | Pollute | Highly | Cleaning | \ |
| 6 | The place | 2000 squares | 200 squares | 90％ |
| 7 | The japanning amount | 100 | 10 | 90％ |
| 8 | Wear-resisting revolution | 1000-1500 | 1000-1500 | \ |
| 9 | \ | \ | \ | Average saving 90% |
Go up a kind of stamp UV wear-resistant coating processing technology that the embodiment of the invention provided has been carried out detailed introduction; For one of ordinary skill in the art; According to the thought of the embodiment of the invention, the part that on the specific embodiment and range of application, all can change, in sum; This description should not be construed as limitation of the present invention, and all any changes of making according to design philosophy of the present invention are all within protection scope of the present invention.
Claims (4)
1. a stamp UV wear-resistant coating processing technology is characterized in that it comprises the steps:
1) the wear-resisting UV lacquer of coating on plastic sheeting, said wear-resisting UV lacquer is made up of the UV glue of 80-120 mass parts and the alundum (Al of 40-60 mass parts, through the ultraviolet ray irradiation wear-resisting UV lacquer is solidified after coating is accomplished;
2) on the wear-resisting UV enamelled coating that is cured, stamp required pattern and curing;
3) the wear-resisting high temperature glue of coating on printed patterned layer, said wear-resisting high temperature glue is made up of the anticracking oil of 80-120 mass parts, the curing agent of 80-120 mass parts and the alundum (Al of 20-40 mass parts;
4) one side that plastic sheeting is scribbled wear-resisting high temperature glue is pressed on the base material and carries out drying, with tearing on the plastic film substrate, can form UV stamp wear-resistant coating at substrate surface like this after the drying.
2. stamp UV wear-resistant coating processing technology according to claim 1; It is characterized in that: said wear-resisting UV lacquer is made up of the UV glue of 100 mass parts and the alundum (Al of 50 mass parts, and said wear-resisting high temperature glue is made up of the anticracking oil of 100 mass parts, the curing agent of 100 mass parts and the alundum (Al of 30 mass parts.
3. stamp UV wear-resistant coating processing technology according to claim 1, it is characterized in that: the baking temperature of step 3) is a normal temperature.
4. stamp UV wear-resistant coating processing technology according to claim 1 is characterized in that: in step 2) in required pattern be through embossing plate UV lacquer or water color ink to be printed at the wear-resisting UV enamelled coating that is cured to form.