Summary of the invention
Technical problem to be solved by this invention is the deficiency for existing anticorrosion furane resin material resistance to elevated temperatures, proposes a kind of heat resist modification furan resin anticorrosive material composition.
Technical problem to be solved by this invention is achieved through the following technical solutions.The present invention is a kind of heat resist modification furan resin anticorrosive material composition, and it comprises furane resin, fire resistant resin, acid resistance filler and reactive curing agent.
Described heat resist modification furan resin anticorrosive material composition, is characterized in, the per-cent that described furane resin account for composition total mass is 15-22%.
Described a kind of heat resist modification furan resin anticorrosive material composition, is characterized in, the per-cent that described fire resistant resin accounts for composition total mass is 15-20%.
Described a kind of heat resist modification furan resin anticorrosive material composition, is characterized in, described fire resistant resin is polyimide resin, bimaleimide resin, benzoxazine colophony, polyphenylene oxide resin wherein one or more composition.
Described a kind of heat resist modification furan resin anticorrosive material composition, is characterized in, described acid resistance filler is silica powder, Graphite Powder 99, glass fibre wherein one or more composition.
Described a kind of heat resist modification furan resin anticorrosive material composition, is characterized in, the per-cent that described reactive curing agent accounts for composition total mass is 1-18%.
Described a kind of heat resist modification furan resin anticorrosive material composition, be characterized in, described reactive curing agent is the composition of oxalic acid and Sulphanilic Acid, and the two mass ratio is 1:1.1 to 1:2.5.
Utilize the clay obtained by the present invention, mortar, concrete and furans glass reinforced plastic sizing material in the maintenance acid-alkali-corrosive-resisting performance of common furane resin and the basis of mechanical property, the use temperature of 10-230 DEG C can be tolerated simultaneously for a long time, metallurgy, chemical industry, building materials, ore, all kinds of antiseptic project of chemical fertilizer can be widely used in.
Embodiment
embodiment 1.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Polyimide resin 15%;
Silica powder 69%;
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of above-mentioned composition mesoxalic acid and Sulphanilic Acid is 1:1.1.
Utilize above composition to configure furan resin mortar, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 2.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Bimaleimide resin 15%;
Silica powder 69%;
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.7.
Utilize above composition to configure furan resin mortar, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 3.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Benzoxazine colophony 15%;
Silica powder 69%;
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:2.5.
Utilize above composition to configure furane resin mortar, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 4.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Polyphenylene oxide resin 15%;
Graphite Powder 99 69%;
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:2.5.
Utilize above composition to configure furane resin mortar, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 5.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 22%;
Polyimide resin 10%;
Bimaleimide resin 5%;
Graphite Powder 99 62%;
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.7.
Utilize above composition to configure furan resin concrete, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 6.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 22%;
Polyimide resin 10%;
Bimaleimide resin 2%;
Benzoxazine colophony 3%;
Silica powder 55%;
Glass fibre 7%
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.8.
Utilize above composition to configure furan resin concrete, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 7.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 22%;
Polyphenylene oxide resin 15%;
Silica powder 55%;
Glass fibre 7%;
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.9.
Utilize above composition to configure furan resin concrete, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 8.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Polyimide resin 5%;
Benzoxazine colophony 15%;
Silica powder 56%;
Glass fibre 8%;
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.1.
Utilize above composition to configure furans glass reinforced plastic sizing material, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 9.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Bimaleimide resin 10%;
Benzoxazine colophony 10%;
Silica powder 55%;
Glass fibre 9%;
The composition 1% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.6.
Utilize above composition to configure furans glass reinforced plastic sizing material, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 10.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Polyimide resin 15%;
Silica powder 52%;
The composition 18% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:2.5.
Utilize above composition to configure furans glass reinforced plastic sizing material, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 11.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Benzoxazine colophony 15%;
Graphite Powder 99 52%;
The composition 18% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:2.0.
Utilize above composition to configure furan resin concrete, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 12.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 18%;
Bimaleimide resin 20%;
Silica powder 52%;
The composition 10% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:2.0.
Utilize above composition to configure furan resin concrete, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 13.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 20%;
Polyphenylene oxide resin 17%;
Silica powder 45%;
The composition 18% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.1.
Utilize above composition to configure furane resin mortar, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 14.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 15%;
Polyimide resin 9%;
Polyphenylene oxide resin 9%;
Graphite Powder 99 56%;
The composition 11% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.5.
Utilize above composition to configure furane resin mortar, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.
embodiment 15.
A kind of heat resist modification furan resin anticorrosive material composition is prepared by following mass percent:
Furane resin 22%;
Bimaleimide resin 6%;
Benzoxazine colophony 10%;
Silica powder 57%;
The composition 5% of oxalic acid and Sulphanilic Acid.
The mass ratio of oxalic acid and Sulphanilic Acid is 1:1.2.
Utilize above composition to configure furan resin mortar, make the square test block of 100mm × 100mm × 100mm, be placed in 230 DEG C of thermostat containers 24 hours, then be placed in 10 DEG C of thermostat containers 24 hours, 50 times so repeatedly.Through inspection, the acid resistance of test block and mechanical property all reach the requirement of industry standard CECS01:2004.