Ice stick beater plate and preparation method thereof
Technical field
The present invention relates to sports movement apparatus field, especially relate to a kind of resistance to packing and ice stick beater plate that quality is light and preparation method thereof.
Background technology
The durability of ice stick beater plate is an important quality index of ice stick, and while adopting low density material to do the packing material of ice stick beater plate, beater plate is low weight, dexterousr during use; Not enough, the durable resistance of beater plate is poor.
While adopting the high material of density to do the packing material of ice stick beater plate, the durable resistance of beater plate increases substantially, and batting is sturdy, shake less, good hand touch.Not enough, quality is larger, causes attack performance not enough, and automaticity is poor.
Therefore, in the urgent need to a kind of not only resistance to, beat but also ice stick beater plate that quality is light at present.
Chinese patent mandate publication number: CN101843970A, authorizes open day on September 29th, 2010, discloses a kind of high-intensity ice stick, comprises club and beater plate, and described beater plate is by shell and be arranged at timber media assemblage in shell.This invention is to adopt timber as the inside packing material of beater plate.
Summary of the invention
The present invention can not meet resistance to beat and the light deficiency of quality in order to overcome beater plate of the prior art simultaneously, and a kind of resistance to packing and ice stick beater plate that quality is light and preparation method thereof is provided.
To achieve these goals, the present invention is by the following technical solutions:
An ice stick beater plate, described beater plate is spliced to form by upper plate body and lower body, between upper plate body and lower body, is provided with tack coat, and the density of lower body is greater than the density of upper plate body, and the right part of the outer surface of beater plate is provided with clad.
The material that tack coat adopts is polyurethane.The material that clad adopts is carbon fiber.
Approximately 2 centimetres of ice hockey height, the height of beater plate is about 6 centimetres to 8 centimetres, and at square stance, the height that ice hockey contacts with beater plate can be lower than half of beater plate height.
Therefore the lower body, contacting with ball in the present invention adopts the high packing material of density; And upper plate body adopts low density packing material, the packing material that upper and lower plate body adopts is all low than the density of the normally used ABS plastic of beater plate or timber.
The structure of beater plate had both guaranteed the durable resistance of beater plate; Alleviate again quality, increased the dexterity while using.Clad has cushioned the impulsive force of ball, has further strengthened the durable resistance of beater plate.
As preferably, between the left and right end of the upper surface of described lower body, be provided with the groove of opening upwards, the bottom of described upper plate body is provided with the insertion end corresponding with groove.
As preferably, the cross section of described groove is inverted trapezoidal.
As preferably, described lower body is Long Circle plate, and described upper plate body is stripe board, and stripe board left end is provided with the arcwall face that upwards arches upward and be connected smoothly with lower body left side; Stripe board bottom righthand side is provided with the fishtail plate being connected as a single entity with stripe board, fishtail plate is positioned at the right-hand of lower body right-hand member, the upper right side of stripe board is provided with the triangular plate being connected as a single entity with stripe board, and fishtail plate and triangular plate form opening surface to top-right arc notch.
As preferably, the material that upper plate body adopts is that density is the foam-filled material of 0.05 gram/cc to 0.08 gram/cc.
As preferably, the material that lower body adopts is that density is the epoxy resin expanded material of 0.3 gram/cc to 0.5 gram/cc.
As preferably, the material that tack coat adopts is polyurethane.
As preferably, the distance between the upper and lower end face of lower body is more than or equal to half height of beater plate.
A preparation method for ice stick beater plate, is characterized in that, comprises the steps:
(1) foam-filled material is cut into the shape of upper plate body;
Adopt laser cutting machine tabular foam-filled material to be cut into the shape of desired upper plate body.
(2) upper plate body of well cutting is put into the first temperature range that the plastotype mould of foam-filled material is heated to be scheduled to; Foam-filled material cooled after plastotype is good is to below predetermined chilling temperature;
The first temperature range and chilling temperature are because of the difference difference of concrete foam-filled material.
By heating and cooling after, the structure of foam-filled material changes, thereby makes the strength-enhanced of foam-filled material, toughness increases, soft durometer changes, increase service life, shape also can produce certain change.
(3) by the epoxy resin expanded material with the quality such as lower body and moulding good foam-filled material with together with polyurethane bonding material binding;
(4) the epoxy resin expanded material being bonded together and foam-filled material are put into the second temperature range that the plastotype mould of epoxy resin expanded material is heated to be scheduled to; Epoxy resin expanded material plastotype becomes the shape of lower body;
The second temperature range is because of the difference difference of the concrete composition of epoxy resin expanded material.
Buy the epoxy resin expanded material coming and be conventionally block and in uneven thickness; Cannot directly be used as the packing material of product; Epoxy resin expanded material at high temperature can soften, expands and have certain mobility, and after the plastotype mould plastotype of epoxy resin expanded material, epoxy resin expanded material plastotype becomes the shape of lower body.
(5) right part of the beater plate outer surface after plastotype is wrapped carbon fiber clad.
Therefore, the present invention has following beneficial effect: (1) not only resistance to be beaten, quality but also light; (2) beater plate is flexible, laborsaving can meet aggressive requirement again; (3) moderate, applied widely.
Accompanying drawing explanation
Fig. 1 is a kind of structural representation of beater plate of the present invention;
Fig. 2 is a kind of cross-sectional view of beater plate of the present invention;
Fig. 3 is the structural representation of a kind of cross section of beater plate of the present invention.
In figure: upper plate body 1, lower body 2, tack coat 3, clad 4, beater plate 5, arc notch 6.
The specific embodiment
Below in conjunction with the drawings and specific embodiments, the present invention will be further described.
Embodiment is as shown in Figure 1 a kind of ice stick beater plate, beater plate 5 is spliced to form by upper plate body and lower body, between upper plate body 1 and lower body 2, be provided with tack coat 3, the density of lower body is greater than the density of upper plate body, and the right part of the outer surface of beater plate is provided with clad 4.Tack coat consists of polyurethane bonding material.Distance between the upper and lower end face of lower body is more than or equal to half height of beater plate.The material that clad adopts is carbon fiber.
The groove that is provided with opening upwards between the left and right end of the upper surface of lower body, the bottom of upper plate body is provided with the insertion end corresponding with groove.The cross section of groove is inverted trapezoidal.
Lower body is Long Circle plate, and described upper plate body is stripe board, and stripe board left end is provided with the arcwall face that upwards arches upward and be connected smoothly with lower body left side; Stripe board bottom righthand side is provided with the fishtail plate being connected as a single entity with stripe board, fishtail plate is positioned at the right-hand of lower body right-hand member, the upper right side of stripe board is provided with the triangular plate being connected as a single entity with stripe board, and fishtail plate and triangular plate form opening surface to top-right arc notch 6.
The material that upper plate body adopts is that density is the foam-filled material of RIMA of 0.07 gram/cc.The foam-filled material price of RIMA is more expensive, is conventionally tabular; Before heating and cooling processing, the foam-filled material of RIMA is more crisp, poor toughness, intensity difference; After heating and cooling processing, the strength-enhanced of the foam-filled material of RIMA, toughness increases, and soft durometer changes, increase service life, and shape also can produce certain change.
The material that lower body adopts is that density is the epoxy resin expanded material of 0.3 gram/cc to 0.5 gram/cc.Epoxy resin expanded material quality is light, and low price is bread-like conventionally.
The preparation method of the ice stick beater plate of the present embodiment, comprises the steps:
(1) foam-filled material is cut into the shape of upper plate body;
(2) the plastotype mould of the upper plate body of well cutting being put into foam-filled material is heated to the temperature range of 195 degree-205 degree;
In the temperature range of 195 degree-205 degree, the structure of foam-filled material changes, thereby makes the strength-enhanced of foam-filled material, and toughness increases, and soft durometer changes, increase service life, and shape also can produce certain change.
Then, below foam-filled material cooled to 60 degree after plastotype is good;
(3) by the epoxy resin expanded material with the quality such as lower body and moulding good foam-filled material with together with polyurethane bonding material binding;
(4) the plastotype mould of the epoxy resin expanded material being bonded together and foam-filled material being put into epoxy resin expanded material is heated to the temperature range of 60 degree-70 degree;
In the temperature range of 60 degree-70 degree, epoxy resin expanded material softens, expands and has certain mobility, and after the plastotype mould plastotype of epoxy resin expanded material, epoxy resin expanded material plastotype becomes the shape of lower body.
(5) right part of the beater plate outer surface after plastotype is wrapped carbon fiber clad.
Should be understood that the present embodiment is only not used in and limits the scope of the invention for the present invention is described.In addition should be understood that those skilled in the art can make various changes or modifications the present invention after having read the content of the present invention's instruction, these equivalent form of values fall within the application's appended claims limited range equally.