Ice stick beater plate and preparation method thereof
Technical field
The present invention relates to the sports movement apparatus field, especially relate to a kind of anti-packing and the ice stick beater plate of light weight and preparation method thereof.
Background technology
The durability of ice stick beater plate is an important quality index of ice stick, and when adopting low density material to do the packing material of ice stick beater plate, beater plate is low weight, and is relatively dexterousr during use; Not enough is that the durable resistance of beater plate is poor.
When adopting the high material of density to do the packing material of ice stick beater plate, the durable resistance of beater plate increases substantially, and batting is sturdy, shake less, good hand touch.Not enough is, quality is bigger, causes attack performance not enough, and automaticity is poor.
Therefore, press for a kind of not only anti-beating but also the ice stick beater plate of light weight at present.
Chinese patent mandate publication number: CN101843970A authorizes open day on September 29th, 2010, discloses a kind of high-intensity ice stick, comprises club and beater plate, and said beater plate is by shell and be arranged in the shell timber filler and form.This invention is to adopt the inside packing material of timber as beater plate.
Summary of the invention
The present invention can not satisfy anti-deficiency of beating with light weight simultaneously in order to overcome beater plate of the prior art, and a kind of anti-packing and the ice stick beater plate of light weight and preparation method thereof is provided.
To achieve these goals, the present invention adopts following technical scheme:
A kind of ice stick beater plate, said beater plate is spliced to form by upper plate body and lower body, is provided with tack coat between upper plate body and the lower body, and the density of lower body is greater than the density of upper plate body, and the right part of the outer surface of beater plate is provided with clad.
The material that tack coat adopted is a polyurethane.The material that clad adopted is a carbon fiber.
About 2 centimetres of ice hockey height, the height of beater plate is about 6 centimetres to 8 centimetres, and at square stance, the height that ice hockey contacts with beater plate can be lower than the half the of beater plate height.
Therefore, the lower body that contacts with ball among the present invention adopts the high packing material of density; And upper plate body adopts low density packing material, and the packing material that upper and lower plate body adopted all density than normally used ABS plastic of beater plate or timber is low.
The structure of beater plate had both guaranteed the durable resistance of beater plate; Alleviate quality again, increased the dexterity when using.Clad has cushioned the impulsive force of ball, has further strengthened the durable resistance of beater plate.
As preferably, be provided with the groove that opening makes progress between the left and right end of the upper surface of said lower body, the bottom of said upper plate body is provided with and the corresponding insertion end of groove.
As preferably, the cross section of said groove is for trapezoidal.
As preferably, said lower body is the Long Circle plate, and said upper plate body is a stripe board, and the stripe board left end is provided with the arcwall face that upwards arches upward and be connected smoothly with the lower body left side; The stripe board bottom righthand side is provided with the fishtail plate that is connected as a single entity with stripe board; The fishtail plate is positioned at the right-hand of lower body right-hand member; The upper right side of stripe board is provided with the triangular plate that is connected as a single entity with stripe board, and fishtail plate and triangular plate constitute the arc notch of opening surface to the upper right side.
As preferably, the material that upper plate body adopted is that density is the epoxy resin expanded material of 0.05 gram/cubic centimetre to 0.08 gram/cubic centimetre.
As preferably, the material that lower body adopted is that density is the foam-filled material of 0.3 gram/cubic centimetre to 0.5 gram/cubic centimetre.
As preferably, the material that tack coat adopted is a polyurethane.
As preferably, the distance between the upper and lower end face of lower body is more than or equal to half height of beater plate.
A kind of preparation method of ice stick beater plate is characterized in that, comprises the steps:
(1) foam-filled material cut is become the shape of upper plate body;
Adopt laser cutting machine tabular foam-filled material cut to be become the shape of desired upper plate body.
(2) the plastotype mould of the upper plate body of well cutting being put into foam-filled material is heated to the first predetermined temperature range; Foam-filled material cooled after plastotype is good is to predetermined chilling temperature;
First temperature range and chilling temperature are different because of concrete foam-filled material.
After heating and cooling, the structure of foam-filled material changes, thereby makes the intensity enhancing of foam-filled material, and toughness increases, and soft durometer changes, increase service life, and shape also can produce certain change.
(3) will bond together with polyurethane bonding material with the epoxy resin expanded material and the moulding good foam-filled material of quality such as lower body;
(4) the plastotype mould of the epoxy resin expanded material that bonds together and foam-filled material being put into the epoxy resin expanded material is heated to the second predetermined temperature range; Epoxy resin expanded material plastotype becomes the shape of lower body;
Second temperature range is different because of the difference of the concrete composition of epoxy resin expanded material.
Buy the epoxy resin expanded material that comes and be block and in uneven thickness usually; Can't directly be used as the packing material of product; The epoxy resin expanded material at high temperature can soften, expands and have certain fluidity, and behind the plastotype mould plastotype through the epoxy resin expanded material, epoxy resin expanded material plastotype becomes the shape of lower body.
(5) right part of the beater plate outer surface behind plastotype is wrapped the carbon fiber clad.
Therefore, the present invention has following beneficial effect: (1) not only anti-to be beaten, quality but also light; (2) beater plate is flexible, laborsaving can satisfy aggressive requirement again; (3) moderate, applied widely.
Description of drawings
Fig. 1 is a kind of structural representation of beater plate of the present invention;
Fig. 2 is a kind of cross-sectional view of beater plate of the present invention;
Fig. 3 is the structural representation of a kind of cross section of beater plate of the present invention.
Among the figure: upper plate body 1, lower body 2, tack coat 3, clad 4, beater plate 5, arc notch 6.
The specific embodiment
Below in conjunction with the accompanying drawing and the specific embodiment the present invention is done further description.
Embodiment as shown in Figure 1 is a kind of ice stick beater plate; Beater plate 5 is spliced to form by upper plate body and lower body; Be provided with tack coat 3 between upper plate body 1 and the lower body 2, the density of lower body is greater than the density of upper plate body, and the right part of the outer surface of beater plate is provided with clad 4.Tack coat is made up of polyurethane bonding material.Distance between the upper and lower end face of lower body is more than or equal to half height of beater plate.The material that clad adopted is a carbon fiber.
Be provided with the groove that opening makes progress between the left and right end of the upper surface of lower body, the bottom of upper plate body is provided with and the corresponding insertion end of groove.The cross section of groove is for trapezoidal.
Lower body is the Long Circle plate, and said upper plate body is a stripe board, and the stripe board left end is provided with the arcwall face that upwards arches upward and be connected smoothly with the lower body left side; The stripe board bottom righthand side is provided with the fishtail plate that is connected as a single entity with stripe board; The fishtail plate is positioned at the right-hand of lower body right-hand member; The upper right side of stripe board is provided with the triangular plate that is connected as a single entity with stripe board, and fishtail plate and triangular plate constitute the arc notch 6 of opening surface to the upper right side.
The material that upper plate body adopted is that density is the epoxy resin expanded material of 0.07 gram/cubic centimetre.Epoxy resin expanded material light weight, low price is bread-like usually.
The material that lower body adopted is that density is that 0.3 gram/cubic centimetre is to the foam-filled material of the RIMA of 0.5 gram/cubic centimetre.
The foam-filled material price of RIMA is more expensive, is tabular usually; Before heating and the cooling processing, the foam-filled material of RIMA is more crisp, poor toughness, intensity difference; After heating and cooling processing, the intensity enhancing of the foam-filled material of RIMA, toughness increases, and soft durometer changes, increase service life, and shape also can produce certain change.
The preparation method of the ice stick beater plate of present embodiment comprises the steps:
(1) foam-filled material cut is become the shape of upper plate body;
(2) the plastotype mould of the upper plate body of well cutting being put into foam-filled material is heated to the temperature range of 195 degree-205 degree;
In the temperature range of 195 degree-205 degree, the structure of foam-filled material changes, thereby makes the intensity enhancing of foam-filled material, and toughness increases, and soft durometer changes, increase service life, and shape also can produce certain change.
Then, with plastotype below foam-filled material cooled to 60 degree after good;
(3) will bond together with polyurethane bonding material with the epoxy resin expanded material and the moulding good foam-filled material of quality such as lower body;
(4) the plastotype mould of the epoxy resin expanded material that bonds together and foam-filled material being put into the epoxy resin expanded material is heated to the temperature range of 60 degree-70 degree;
In the temperature range of 60 degree-70 degree, the epoxy resin expanded material softens, expands and has certain fluidity, and behind the plastotype mould plastotype through the epoxy resin expanded material, epoxy resin expanded material plastotype becomes the shape of lower body.
(5) right part of the beater plate outer surface behind plastotype is wrapped the carbon fiber clad.
Should be understood that present embodiment only to be used to the present invention is described and be not used in the restriction scope of the present invention.Should be understood that in addition those skilled in the art can do various changes or modification to the present invention after the content of having read the present invention's instruction, these equivalent form of values fall within the application's appended claims institute restricted portion equally.